TY - JOUR A1 - Bajer, Kamila A1 - Braun, Ulrike T1 - Different aspects of the accelerated oxidation of polypropylene at increased pressure in an autoclave with regard to temperature, pretreatment and exposure media N2 - The aim of this study is to investigate and compare three different factors, temperature, pretreatment and exposure media, on the oxidation and aging behavior of polypropylene (PP) bulk samples in the autoclave test under increased oxygen pressure. The aging of polypropylene, in this case syringe material, was accelerated under different conditions. The samples were aged at 75°, 80° and 85 °C under pure oxygen and at 75 °C under ultrapure water. Further samples treated with 15 kGy (e-beam) were aged at 75 °C under pure oxygen. All experiments were carried out at an oxygen partial pressure of 50 bar. The different courses of aging were evaluated and compared. Color and transparency were used to assess the visual changes; weight, geometry and tensile test for the changes in technical properties; and DSC, FTIR and TDS-GC-MS to improve our physico-chemical understanding of the aging processes. The investigations showed that all factors tested influence oxidation/aging behaviour. Dry or wet exposure has no effect on aging during the induction time. However, after the point of maximum service time the degradation process of polymer changes significantly in the presence of water. The increase of aging temperature decreases the maximum service time; however a temperature higher than 80 °C changes the relative ratio of surface and bulk oxidation. The pretreatment with irradiation decreases the maximum service time further, because the irradiation partly damages the antioxidant, and the mobility of antioxidant fragments inside the polymer changes. These diffusion effects influence the relative ratio of bulk and surface oxidation of the polymer sample. KW - Autoclave test KW - Accelerated aging KW - Polypropylene KW - Electron radiation PY - 2014 U6 - https://doi.org/10.1016/j.polymertesting.2014.05.006 SN - 0142-9418 VL - 37 SP - 102 EP - 111 PB - Elsevier Science CY - Amsterdam [u.a.] AN - OPUS4-30867 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bajer, Kamila A1 - Braun, Ulrike A1 - Hintersteiner, I. T1 - The memory effect in polyolefinic products: A tool for confirming the steam sterilization process N2 - DSC-Messungen von dampfsterilisierten medizinischen Produkten aus Polyolefinen zeigen beim ersten Heizvorgang als auffällige Besonderheit eine zusätzliche Stufe, bekannt als Temperpeak. Das Ziel dieser Untersuchungen ist, dieses Phänomen nachzuvollziehen und zu verstehen, um es als Nachweis für die Dampfsterilisation nutzen zu können. Dafür wurden PP- und PE-Proben unter verschiedenen Bedingungen dampfsterilisiert und im Ofen thermisch behandelt. Anschließend wurden die Proben mittels DSC untersucht und die Einflüsse der thermischen Behandlung und der mechanischen Beanspruchung analysiert. Um den Einfluss unterschiedlicher Materialspezifikationen zu prüfen, wurden zusätzlich verschiedene Referenzmaterialien (PE und PP) untersucht und GPC-Messungen durchgeführt. Des Weiteren wurde die Beständigkeit des Signals gegenüber der Zeit und der Temperatureinflüssen betrachtet. Die Untersuchungen zeigen, dass sich ein stabiler Memory-Effekt erzeugen lässt. KW - Memory effect KW - Steam sterilization KW - Polypropylene KW - Polyethylene KW - DSC PY - 2015 U6 - https://doi.org/10.3139/120.110722 SN - 0025-5300 VL - 57 IS - 4 SP - 316 EP - 323 PB - Hanser CY - München AN - OPUS4-33104 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -