TY - CONF A1 - Stawski, Tomasz T1 - The structure of amorphous calcium sulfate and its role in the nucleation pathway and final mesostructure of CaSO 4 phases N2 - In recent years, we have come to appreciate the astounding intricacy of the formation process of minerals from ions in aqueous solutions. In this context, a number of studies have already revealed that nucleation in the CaSO4-H2O system is non-classical, where the formation of the different crystalline phases involves several steps including a common amorphous precursor. In this contribution a holistic view of the formation mechanism of gypsum and bassanite from solution will be presented. In short, our in situ and time-resolved scattering data demonstrate that calcium sulfate precipitation starts with the formation and aggregation of well-defined sub-3 nm primary species. These species constitute building “bricks'' of an amorphous precursor phase. We characterised the “bricks” by combining information obtained at different length-scales accessible at the mesoscale (from small-angle scattering) and at the atomic-length-scale (wide-angle scattering and high-energy diffraction). From these scattering data we derived pair distribution functions of the clusters and restricted their external shapes and dimensions. This allowed us to propose a structure of the primary species and to explore their dynamic properties with unbiased MD simulations using polarizable force fields. The formation of the amorphous phase involves the aggregation of these small primary species into larger disordered aggregates exhibiting “brick-in-the-wall” structure. The actual crystallisation occurs by the restructuring and coalescence of the “bricks” into a given calcium sulfate phase depending on the thermodynamic conditions of the solution. Importantly, these rearrangement processes by no means continue until a (nearly-)perfect homogeneous single crystal is obtained. Instead they come to a stop or at least significantly slow down. Such a process thus yields a final imperfect mesocrystal, composed of smaller domains rather than a continuous crystal structure, within which the domains are separated by an amorphous calcium sulfate phase. T2 - Goldschmidt Virtual 2021 CY - Online meeting DA - 04.07.2021 KW - Amorphous calcium sulfate KW - Scattering KW - SAXS/WAXS PY - 2021 UR - https://2021.goldschmidt.info/goldschmidt/2021/meetingapp.cgi/Paper/3847 AN - OPUS4-53621 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stawski, Tomasz T1 - Scattering is a powerful tool to follow nucleation and growth of minerals from solutions N2 - In recent years, we have come to appreciate the astounding intricacy of the formation process of minerals from ions in aqueous solutions. The original ‘textbook’ image o these phenomena, stemming from the adaptation of classical nucleation and growth theories, has increased in complexity due to the discovery of a variety of precursor and intermediate species [e.g. 1], including solute clusters (e.g. prenucleation clusters PNCs), liquid(-like) phases, as well as amorphous and nanocrystalline solids etc. In general, these precursor or intermediate species constitute different, often short-lived points along the pathway from dissolved ions to the final solids (typically crystals in this context). In this regard synchrotron-based scattering (SAXS/WAXS/HEXD appears to be the perfect tool to follow in situ and in a time-resolved manner the crystallization pathways because of the temporal and spatial length scales that can be directly accessed with these techniques. Here, I show how we used scattering to probe the crystallization mechanisms o calcium sulfate. CaSO4 minerals (i.e. gypsum, anhydrite and bassanite) are widespread in natural and industrial environments. During the last several years, a number o studies have revealed indeed that nucleation in the CaSO4-H2O system is non-classical My SAXS data demonstrate that gypsum precipitation, involves formation and aggregation of sub-3 nm primary species. These species constitute building blocks o an amorphous precursor phase [2]. Further, I show how in situ high-energy X-ray diffraction experiments and molecular dynamics (MD) simulations can be combined to derive the atomic structure of the primary CaSO4 clusters seen at small-angles [3]. fitted several plausible structures to the derived pair distribution functions and explored their dynamic properties using unbiased MD simulations based on polarizable force fields. Finally, based on combined SAXS/WAXS, broad-q-range measurements, show that the process of formation of bassanite, a less hydrated form of CaSO4, is very similar to the formation of gypsum: it also involves the aggregation of small primary species into larger disordered aggregates [4]. Based on these recent insights I formulated a tentative general model for calcium sulfate precipitation from solution. This model involves primary species that are formed through the assembly of multiple Ca2+ and SO42- ions into nanoclusters. These nanoclusters assemble into poorly ordered (i.e. amorphous) hydrated aggregates which in turn undergo ordering into coherent crystalline units of either gypsum o bassanite (and possibly anhydrite). Determination of the structure and (meta)stability of the primary species is important from both a fundamental, e.g. establishing a general non-classical nucleation model, and applied perspective; e.g. allow for an improved design of additives for greater control of the nucleation pathway T2 - BAM - Abteilungsseminar 6.3 CY - Online meeting DA - 21.02.2021 KW - Scattering KW - SAXS/WAXS KW - Calcium sulfate PY - 2021 AN - OPUS4-53713 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stawski, Tomasz T1 - Smart Machines, New Materials, Automated Future N2 - In pursuing the automated synthesis of metal nanoparticles (NPs), the capabilities of the “Chemputer” are deployed, for the first time, into the field of inorganic chemistry. Metal NPs have a substantial impact across different fields of science, such as photochemistry, energy conversion, and medicine. Among the commonly used nanoparticles, silver NPs are of special interest due to their antibacterial properties and applications in sensing and catalysis. However, many of the methods used to synthesize Ag NPs often do not result in well-defined products, the main obstacles being high polydispersity or a lack of particle size tunability. The Chemputer is a modular, automated platform developed by the Cronin group for execution of multi-step, solution based organic synthesis. The machine has been further implemented at BAM, where we used this setup to perform automated organic syntheses, autonomously controlled by feedback derived from online NMR. In the Chemputer liquids can be transferred across a backbone, constructed from HPLC selection valves and syringe pumps. The Chemputer operates in a batch mode, common laboratory devices, such as heaters and glassware like round bottom flasks, are connected to the backbone, forming reaction modules. Solutions can be manipulated in these modules, and as all operations are controlled through a software script, reproducibility among individual syntheses is high. Likewise, any adjustments of the synthesis conditions, if required, are straightforward to implement and are documented in the reaction log file and a code versioning system. We characterised Chemputer-synthesized nanoparticles using small-angle X-ray scattering, dynamic light scattering and further methods, showing that automated synthesis can yield colloids with reproducible and tuneable properties. The approach is an important first step towards the automation of nanoparticle syntheses in a modular, multipurpose platform. The modularity of the Chemputer opens many possibilities for the synthesis of a variety of different NP morphologies and sizes and potentially more complex structures. These advances and further work can help in the general investigations of silver nanoparticles by supplying a reliable and reproducible method of their synthesis and removing tacit knowledge by significantly reducing the experimental bias. T2 - Analytica 2022 CY - Munich, Germany DA - 21.06.2022 KW - Automated synthesis KW - Nanoparticles PY - 2022 AN - OPUS4-55198 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mishmastnehi, Moslem A1 - Stawski, Tomasz T1 - Crystals of Gypsum in Hands of Masters N2 - The microstructure of most Seljuk and Ilkhanid stucco decorations consists of micrometer-sized crystals of gypsum. The stucco-masters of these periods (neither nowadays stucco-masters) were not able to directly control the properties of these tiny crystals with their hands or centimeter-sized tools. There are, however, traces of chaîne opératoire accumulated in the materialistic body of these pieces, some of which could be explored through an interdisciplinary approach. Such an investigation requires very careful in situ observation of the macrostructure, and scientific analyses of the material to discover part of the production process for each body of stucco. Furthermore, there are deterioration factors, some of which are not yet fully understood, and should be identified using modern analytical instruments. These damaging factors could easily affect the micro and macro structure of a stucco decoration, influencing our interpretation. The concept of chaîne opératoire reframes our questions about the production process and probable dating technique of Seljuk and Ilkhanid stuccoes, while analyses of labmade replicas and historic materials enhance our understanding and interpretation of these materials. Here we present the results of such a study for a large body of Seljuk and Ilkhanid stucco decorations at various sites in Iran, and present the potential of this approach as a new perspective in this field of research. T2 - Stucco in the Architecture of Iran and Neighbouring Lands CY - Bamberg, Germany DA - 04.05.2022 KW - Gypsum KW - Stuccos KW - Crystallization PY - 2022 AN - OPUS4-54782 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stawski, Tomasz A1 - Van Driessche, A. E. S. T1 - Editorial for special issue "Formation of sulfate minerals in natural and industrial environments" N2 - Sulfate is abundant in the environment and, as a result, sulfate-containing minerals constitute a large and important focus of research. These minerals play an important role in many geochemical and industrial processes, including the sulfur cycle, the construction industry (e.g., plaster of Paris), fault tectonics, acid mine drainage, and even rare biominerals. Important to note are the abundant amounts of sulfate (minerals) located on the surface of Mars, and in meteorites, extending the relevance of this mineral group beyond the realm of our planet. In geological systems, sulfate minerals such as barite are also important for indicating certain sedimentation environments. In this regard, sulfate deposits can be used to evaluate the redox state of ancient oceans during early Earth time periods. KW - Calcium sulfate KW - Sulfates PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-546794 DO - https://doi.org/10.3390/min12030299 SN - 2075-163X VL - 12(3) IS - Special issue "Formation of sulfate minerals in natural and industrial environments" SP - 1 EP - 3 PB - MDPI CY - Basel AN - OPUS4-54679 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fink, Friedrich A1 - Stawski, Tomasz M. A1 - Stockmann, Jörg Manfred A1 - Emmerling, Franziska A1 - Falkenhagen, Jana T1 - Surface Modification of Kraft Lignin by Mechanochemical Processing with Sodium Percarbonate N2 - In this article, we present a novel one-pot mechanochemical reaction for the surface activation of lignin. The process involves environmentally friendly oxidation with hydrogen peroxide, depolymerization of fractions with high molecular mass, and introduction of new carbonyl functions into the lignin backbone. Kraft lignin was ground with sodium percarbonate and sodium hydroxide in a ball mill at different time intervals. Analyses by infrared spectroscopy (IR), nuclear magnetic resonance spectroscopy (NMR), size exclusion chromatography (SEC), dynamic vapor sorption (DVS), and small-angle X-ray scattering (SAXS) showed significant improvements. After only 5 min of reaction, there was a 47% reduction in mass-average molecular weight and an increase in carboxyl functionalities. Chemical activation resulted in an approximately 2.8-fold increase in water adsorption. Principal component analysis (PCA) provided further insight into the correlations between IR spectra and SAXS parameters KW - Kraft Lignin KW - Mechanochemical oxidation KW - SEC KW - FTIR KW - SAXS KW - PCA PY - 2023 DO - https://doi.org/10.1021/acs.biomac.3c00584 SN - 1525-7797 SP - 1 EP - 11 PB - American Chemical Society AN - OPUS4-58074 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Madeja, B. A1 - Gebauer, D. A1 - Marsiske, M. R. A1 - Ott, A. A1 - Rückel, M. A1 - Rosenberg, R. A1 - Baken, A. A1 - Stawski, Tomasz M. A1 - Fernandez-Martinez, A. A1 - Van Driessche, A.E.S. A1 - Cölfen, H. A1 - Kellermeier, M. T1 - New insights into the nucleation of portlandite and the effects of polymeric additives N2 - The crystallization of calcium hydroxide (Ca(OH)2, CH, portlandite) is a key process during the early stages of cement hydration. In the present work, we have revisited the formation of this mineral through nucleation and growth from supersaturated aqueous solutions, in the light of the currently emerging picture of multistage “non-classical” crystallization. To that end, we developed a titration-based assay, in which stock solutions of both relevant ions are added simultaneously into a reservoir, where supersaturation increases slowly at constant stoichiometry until nucleation occurs. This procedure allows both pre- and early post-nucleation phenomena to be analyzed quantitatively. Complementarily, the early stages of portlandite mineralization were probed by various advanced characterization techniques, including cryo-transmission electron microscopy (cryo-TEM), in-situ small-angle X-ray scattering (SAXS), pair distribution function (PDF) analysis of high-energy X-ray scattering (HEXS) data, and analytical ultracentrifugation (AUC). The experimental data show that the formation of calcium hydroxide starts with the association of ions into complexes and clusters, which subsequently coalesce to form amorphous nanoparticles – much like what has been observed in the case of calcium carbonate and other prominent minerals. Subsequently, these particles aggregate and build networks, which eventually transform into hexagonal Ca(OH)2 crystals. The presence of a soluble polycarboxylate – as a known inhibitor of portlandite crystallization – does not change the main characteristics of this multistep nucleation pathway, but it proved capable of significantly extending the lifetime of the amorphous intermediate phase and thus delaying the transition to the final crystalline phase. Our observations confirm the notion that “non-classical” crystallization is a much more common phenomenon than initially believed – and that, for minerals forming in aqueous environments, it may actually be the rule rather than the exception. KW - General Materials Science KW - Building and Construction PY - 2023 DO - https://doi.org/10.1016/j.cemconres.2023.107258 SN - 0008-8846 VL - 173 SP - 1 EP - 13 PB - Elsevier B.V. AN - OPUS4-58162 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Karafiludis, Stephanos A1 - Stawski, Tomasz T1 - Crystallization study of transition metal phosphates: Characterization of a non-classical crystallization pathway N2 - Industrial and agricultural waste streams (waste waters, sludges, tailings etc.), which contain high concentrations of NH4+, PO43- and transition metals, are environmentally harmful due to their toxic pollutants. At the same time, phosphorus and selective transition metals such as Cobalt could be potentially depleted as a critical raw material due to the high demand and rapidly declining natural ore deposits. Therefore, due to simultaneous scarcity and abundance, the phosphorus and 3d metal recovery from agricultural, industrial, mining, or urban wastewaters have been an important factor in sustaining our global consumption and preservation of the natural environment. Typically, separate pathways have been considered to extract hazardous substances such as transition metals or phosphate, independently from each other. Here, we investigate the crystallization of transition metal phosphate (TMP) compounds (NH4MPO4∙6H2O, M3(PO4)2∙8H2O with M = Ni2+, Co2+, NixCo1-x2+ M-struvite and M-phosphate octahydrate) out of aqueous solutions, which allow for P, ammonia and metal co-precipitation. The precipitation of these compounds from industrial and agricultural waste waters has high potential as a P- and 3d metal recovery route. For this purpose, a detailed understanding of the crystallization process beginning from combination of solved ions and ending in a final crystalline product is required. Through adjusting the reaction conditions, the stability, crystallite size and morphology of the as-obtained TMPs could be controlled. Detailed investigations of the precipitation process in time using ex- and in-situ techniques provided new insights into their non-classical crystallization mechanism/crystal engineering of these materials. These TMPs involve transitional colloidal nanophases during the crystallization process. Over time, their complex amorphous framework changes significantly resulting simultaneously in an agglomeration and densification of the compound. After extended reaction times these colloidal nanophases condensed to a final crystal. However, the reaction kinetics of the formation of a final crystalline product and the lifetime of these intermediate phases vary significantly depending on the metal cation involved in the precipitation process. Ni-struvite is stable in a wide reactant concentration range and at different metal/phosphorus (M/P)-ratios, whereas Co tends to form Co-struvite and/or Co-phosphate octahydrate depending on the (M/P)-ratio. The mixed NixCo1-x system shows a significantly different crystallization behavior and reaction kinetics of the precipitation compared to the pure endmembers. The observed various degree of stability could be linked to the octahedral metal coordination environment in these compounds. The achieved level of control over the precipitates, is highly desirable for 3d- and P-recovery methods. Under this paradigm, the crystals can be potentially upcycled as precursor materials for (electro)catalytical applications. T2 - HZB Usermeeting 2023 CY - Berlin, Germany DA - 22.06.2023 KW - Struvite KW - Transition metal KW - Phosphates KW - Crystallization KW - Amorphous phases PY - 2023 AN - OPUS4-57775 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Matamoros-Veloza, A. A1 - Stawski, Tomasz A1 - Vargas, S. A1 - Neville, A. T1 - Study of a Local Structure at the Interface between Corrosion Films and Carbon Steel Surface in Undersaturated CO2 Environments N2 - Industries transporting CO2 gas-saturated fluids have infrastructures made of carbon steel. This is a good material with great mechanical properties but prone to corrosion and potential failure. Corrosion in sweet environments involves the formation of FeCO3 as a corrosion film, which is recognized to play a protective role under certain conditions. This work on the dissolution of corrosion films in sweet environments, under acidic and undersaturated conditions, demonstrates that the effects on the integrity of steel are far more significant than the damage observed on the surface of the corrosion film. Our results prove that dissolution of FeCO3 involved the presence of an amorphous phase, the intermediate formation of FeCl2 or FeCl+, and the presence of a phase with short distance atom–atom correlations. The amorphous phase was identified as a mixture of retained γ-Fe and Fe3C. Partially broken α-Fe and Fe3C structures were identified to prove the damage on the material, confirming the interface zone without evident damage on the corrosion film. Dissolution affected both the α-Fe and FeCO3, with the lattice [102̅] from the FeCO3 crystalline structure being the fastest to dissolve. The damage of steel at the molecular scale was evident at the macroscale with pit depths of up to 250 μm. The impact on the integrity of steel can be, therefore, more drastic than frequently reported in industrial operations of CO2 transport industries that use cleaning procedures (e.g., acid treatment, pigging) as part of their operational activities. KW - Steel KW - Corrosion KW - Siderite KW - Diffraction KW - Pair distribution function KW - Synchrotron PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-572156 DO - https://doi.org/10.1021/acsomega.2c07631 SN - 2470-1343 VL - 8 IS - 9 SP - 8497 EP - 8504 PB - ACS AN - OPUS4-57215 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bui, M. A1 - Hoffmann, K. F. A1 - Braun, T. A1 - Riedel, S. A1 - Heinekamp, Christian A1 - Scheurell, K. A1 - Scholz, G. A1 - Stawski, Tomasz A1 - Emmerling, Franziska T1 - An Amorphous Teflate Doped Aluminium Chlorofluoride: A Solid Lewis-Superacid for the Dehydrofluorination of Fluoroalkanes N2 - Ananion-dopedaluminiumchlorofluoride AlCl0.1F2.8(OTeF5)0.1(ACF-teflate) was synthesized.The material contains pentafluor-oorthotellurate(teflate)groups, which mimic fluoride ions electronically, but are sterically more demanding. They are embedded into the amorphous structure. The latter was studied by PDF analysis, EXAFS data and MAS NMR spectroscopy. The mesoporous powder is a Lewis superacid, and ATR-IR spectra of adsorbed CD3CN reveal a blue-shift of the adsorption band by73 cm-1, which is larger than the shift for SbF5. Remarkably,ACF-teflate catalyzes dehydrofluorination reactions of mono-fluoroalkanes to yield olefins in C6D6. In these cases,no Friedel-Crafts products were formed. KW - Aluminium fluorides KW - Aluminium teflates KW - C-F bond activation KW - Lewis superacids KW - Silanes PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-572290 DO - https://doi.org/10.1002/cctc.202300350 SN - 1867-3880 SP - 1 EP - 7 PB - Wiley VHC-Verlag AN - OPUS4-57229 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -