TY - CONF A1 - Grimault de Freitas, Tomás A1 - Konert, Florian A1 - Nietzke, Jonathan A1 - Krzysch, Zephanja A1 - Böllinghaus, Thomas A1 - Michler, Thorsten A1 - Wackermann, Ken A1 - Oesterlin, Heiner A1 - Tlili, Mohamed A1 - Puthur, Alen A1 - Elsen-Humberg, Stephan A1 - Koenigs, Timo A1 - Ruchti, Peter A1 - Systermans, Thomas A1 - Sobol, Oded T1 - Hollow Specimen Method for Tests in High-Pressure Hydrogen Gas: The Role of Strain-Rate and Surface Quality N2 - The feasibility of the method for slow strain tensile tests has been demonstrated in several studies, leading to the establishment of the ISO/TC 164/SC 1/WG 9 ISO committee for its standardisation. Questions have emerged during this process, that currently prevent the method from being standardised for hydrogen testing. These questions relate to specimen geometry, specimen manufacturing and gas quality and are being systematically addressed in the TransHyDE-H2HohlZug project. The first results addressing the questions regarding specimen manufacturing are presented in this poster. T2 - TrasnsHyDE Abschlusskonferenz CY - Berlin, Germany DA - 25.03.2025 KW - Hydrogen KW - Hydrogen Embrittlement KW - Hollow Specimen Technique KW - High-Pressure Gaseous Hydrogen KW - TransHyDE KW - H2HohlZug PY - 2025 AN - OPUS4-62809 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grimault de Freitas, Tomás T1 - The Impact Of Surface Condition on the Susceptibility to Hydrogen Embrittlement of Steel Using the Hollow Specimen Technique N2 - The hollow specimen technique is a simple and cost-effective method that has the potential to make materials qualification with pressurised gaseous hydrogen widely accessible to academia and industry. The applicability of this method has already been demonstrated in several studies, which led to the initiation of the ISO committee ISO/TC 164/SC 1/WG 9 for its standardisation in ISO 7039. Questions that emerged during this process are currently preventing the extension of ISO 7039 to hydrogen gas as an ambient medium. These questions relate to specimen geometry, specimen manufacturing and gas quality and are being systematically addressed in the TransHyDE-H2HohlZug project. The aim is to close the identified gaps towards the standardisation of this method for hydrogen testing. This contribution briefly presents the structure and milestones of the project and focuses on the results obtained from assessing the influence of specimen production and its response to hydrogen effects. Depending on the production method, different roughness and residual stresses can be expected on the inner hole surface of the specimens. This is relevant because an increase in stress concentration sites, e.g. notches, has been found to be associated with increased severity of hydrogen effects. The presence of strain-induced martensite caused by mechanical stress may also be detrimental and accelerate the embrittlement process of metastable austenitic stainless steel (ASS) such as AISI type 304. To assess this influence, the inner hole of the hollow specimens was manufactured in five different ways: 1) only drilling; 2) drilling followed by reaming; 3) drilling followed by honing; 4) electro-discharge machining (EDM) followed by honing; and 5) EDM followed by reaming. A representative steels that is widely used in hydrogen technologies was assessed, namely X5CrNi18-10 (AISI type 304). Roughness measurements, and electron back-scatter diffraction (EBSD) analysis have been performed previous to mechanical testing to infer on the effect of the different production methods on the surface of the inner hole. Next, the specimens were mechanically tested via slow strain rate tensile tests in argon and in hydrogen, both at 150 bar and room temperature. Here, a strain-rate sensibility analysis was performed to investigate the influence of strain-rate on hydrogen degradation. Based on the results an optimal specimen production method is proposed. T2 - SteelyHydrogen 2025 CY - Ghent, Belgium DA - 14.10.2025 KW - Slow Strain Rate Tensile Testing KW - Hollow Specimen Technique KW - High-Pressure Hydrogen Gas KW - Hydrogen Embrittlement KW - Surface Condition PY - 2025 AN - OPUS4-64406 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Grimault de Freitas, Tomás A1 - Konert, Florian A1 - Nietzke, Jonathan A1 - Krzysch, Zephanja A1 - Böllinghaus, Thomas A1 - Michler, Thorsten A1 - Wackermann, Ken A1 - Oesterlin, Heiner A1 - Tlili, Mohamed A1 - Ruchti, Peter A1 - Beitelschmidt, Denise A1 - Elsen-Humberg, Stephan A1 - Koenigs, Timo A1 - Systermans, Thomas A1 - Sobol, Oded T1 - Tensile testing in high-pressure gaseous hydrogen using the hollow specimen method N2 - Metallic materials, predominantly steels, are the most common structural materials in the various components along the hydrogen supply chain. Ensuring their sustainable and safe use in hydrogen technologies is a key factor in the ramp-up of the hydrogen economy. This requires extensive materials qualification, however, most of the accepted; and standardized test methods for determining the influence of gaseous hydrogen on metallic materials describe complex and costly procedures that are only available to a very limited extent worldwide. The hollow specimen technique is a simple, rapid, and economical method designed to overcome the limitations of the current methods for the qualification of metallic materials under high-pressure hydrogen gas. However, this technique is not yet standardized. The TransHyDE-H2Hohlzug project is presented in this article, along with the main steps required to optimize the hollow specimen technique. This includes closing knowledge gaps related to the specimen geometry, surface quality, and gas purity in dedicated working packages, thus contributing to a comprehensive standardization of the technique for tests in high-pressure hydrogen gas. KW - High-pressure Gaseous Hydrogen KW - Hydrogen Embrittlement KW - Tensile Testing KW - Hollow Specimen Technique PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-610557 DO - https://doi.org/10.1557/s43577-024-00776-9 VL - 49 SP - 1 EP - 9 PB - Springer Nature AN - OPUS4-61055 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Konert, Florian A1 - Nietzke, Jonathan A1 - Grimault de Freitas, Tomás A1 - Rhode, Michael A1 - Sobol, Oded A1 - Böllinghaus, Thomas T1 - Investigation of resistance to gaseous hydrogen of a longitudinal weld seam in a X65 pipeline using the hollow specimen technique N2 - The constantly increasing demand for renewable energy sources leads to the necessity of transporting large amounts of hydrogen. Since pipelines enable a cost-effective way for the distribution of gaseous hydrogen, the interaction of hydrogen and the pipeline materials must be carefully investigated as hydrogen can cause a degradation of the mechanical properties under certain conditions. Especially welds, which are assumed to be more susceptible to the degradation enhanced by hydrogen, are of great interest. The aim of this study is to investigate the effect of gaseous hydrogen on the mechanical properties of an X65 pipeline, and the longitudinal submerged arc welding (SAW) welded joint. The tests are conducted using the hollow specimen technique on two types of specimens: one extracted from the base material (BM) and the other extracted as a cross-weld (CW) specimen consisting of BM and weld seam. The specimens are charged in situ under a pressure of 60 bar and tested using slow strain rate (SSR) tensile tests with a nominal strain rate of 10−5 s−1. The properties obtained of specimens tested in hydrogen atmosphere are compared to the properties of comparable specimen in inert argon atmosphere as a reference. The performed tests showed a decrease of the reduction of area (RA) from 72% in inert atmosphere to 52% in hydrogen atmosphere for the CW specimen and a decrease from 73% in inert atmosphere to 51% for the BM. Metallographic analyses showed the crack initiation between fine-grained heat-affected zone (FGHAZ) and BM for the specimens tested in hydrogen atmosphere as well as for the reference specimens. This leads to the conclusion that the location of the crack initiation does not change due to the presence of gaseous hydrogen. KW - Hydrogen KW - Hollow specimen technique KW - Pipeline KW - SSRT KW - Hydrogen embrittlement KW - Cross-weld specimen PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-624658 DO - https://doi.org/10.1007/s40194-025-01953-3 SN - 0043-2288 SN - 1878-6669 VL - 69 IS - 3 SP - 861 EP - 870 PB - Springer CY - Berlin AN - OPUS4-62465 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grimault de Freitas, Tomás T1 - Hollow Specimen Method for Tests in High-Pressure Hydrogen Gas: The Role of Strain-Rate and Surface Quality N2 - The hollow specimen technique is a simple and economical technique that has the potential to make materials qualification with pressurised gaseous hydrogen widely accessible to academia and industry. This contribution focuses on the results obtained from assessing the influence of the specimen production and its response to hydrogen effects. Depending on the production method, different roughness and residual stresses can be expected on the inner hole surface of the specimens. This is relevant because an increase in stress concentration sites, e.g. notches, has been found to be associated with increased severity of hydrogen effects. The presence of strain-induced martensite caused by mechanical stress may also be detrimental and accelerate the embrittlement. To assess this influence, the inner hole of the hollow specimens was manufactured in two different ways: 1) only drilling; 2) EDM followed by honing. A representative steel widely used in hydrogen technologies was assessed, X5CrNi18-10 (AISI 304). Roughness measurements, and electron back-scatter diffraction (EBSD) analysis have been performed previous to mechanical testing to infer on the effect of the different production methods on the surface of the inner hole. Next, the specimens were mechanically tested via slow strain rate tensile tests in argon and in hydrogen, both at 150 bar and room temperature. Here, a strain-rate sensibility analysis was performed to investigate the influence of strain-rate on hydrogen degradation. T2 - International Conference on Hydrogen Safety 2025 CY - Seoul, South Korea DA - 22.09.2025 KW - Tensile Testing KW - Hollow Specimen Technique KW - High-Pressure Hydrogen Gas KW - Hydrogen Embrittlement KW - Surface Condition KW - Strain Rate PY - 2025 AN - OPUS4-64286 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grimault de Freitas, Tomás T1 - Hollow Specimen Method for Tests in High-Pressure Hydrogen Gas: The TransHyDE - H2HohlZug Project N2 - As the world moves towards a decarbonised economy, the demand for sustainable and low-carbon alternatives is growing rapidly. Hydrogen has an important role to play in this transition, but in order to make the most of hydrogen as an energy carrier, a comprehensive understanding of its impact on the integrity of structural materials is necessary. Metallic materials, mainly steels, are the most commonly used structural materials in various components throughout the hydrogen supply chain. Ensuring their sustainable and safe use in hydrogen technologies is a crucial factor in the development of the hydrogen economy. This is particularly important since hydrogen can promote crack formation and ultimately lead to premature failure in these materials when combined with mechanical load. This process is commonly known as Hydrogen Embrittlement and can occur in almost all the steels used for the hydrogen technologies. Extensive materials qualification is required for the rapid implementation of hydrogen technologies, however, most accepted, and standardised test methods for determining the effect of gaseous hydrogen on metallic materials describe complex and costly procedures that are only available to a very limited extent worldwide. The hollow specimen technique is a simple and economical method that has the potential to overcome the limitations of the current methods and complement them for qualifying metallic materials under high-pressure hydrogen gas. Unlike the conventional autoclave technique, this method requires significantly lower amounts of hydrogen, resulting in fewer safety measures and no need for complex equipment or a specialised laboratory. The technique's low investment and testing costs, simple operation, and shorter testing time make it an optimal for widespread use around the world, thereby increasing the output of results. Initial studies have demonstrated the feasibility of assessing hydrogen effects in metallic materials using the hollow specimen technique. This led to the establishment of an ISO committee to standardise the method. However, there are open questions that currently prevent the technique from being standardised for hydrogen testing. These open questions relate to specimen geometry, inner hole surface and gas quality and are being addressed in the H2HohlZug project, of which the overall aim is to systematically close the gaps towards a standard. This contribution presents the structure and milestones of the project, followed by initial results. T2 - TransHyDE Vollversammlung 2025 CY - Leipzig, Germany DA - 26.11.2025 KW - Hydrogen KW - Hydrogen Embrittlement KW - Hollow Specimen Technique KW - High-Pressure Gaseous Hydrogen KW - TransHyDE KW - H2HohlZug KW - Standardisation PY - 2025 AN - OPUS4-64938 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grimault de Freitas, Tomás T1 - Comprehensive Standardisation of the Hollow Specimen Technique for Tests in High-Pressure Hydrogen Gas N2 - The hollow specimen technique is a simple and economical method that has the potential to overcome the limitations and complement the current techniques for qualifying metallic materials under highpressure hydrogen gas. In this technique, an axial hole is manufactured in a tensile specimen, which is then filled with hydrogen gas, sealed, and placed in a standard testing machine. This method requires significantly lower amounts of hydrogen, resulting in fewer safety measures and does not require complex equipment or a specialised laboratory, unlike the conventional autoclave technique. Initial studies have demonstrated the feasibility of assessing hydrogen effects in metallic materials using the hollow specimen technique. This led to the establishment of the committee ISO/TC 164/SC 1/WG 9 to standardise the method, however, there are still open questions that currently prevent the technique from being standardised for hydrogen testing. These open questions are being addressed in the H2HohlZug project, which is presented in this contribution. T2 - Oxford - EPRI Hydrogen Embrittlement Workshop CY - Oxford, United Kingdom DA - 23.06.2024 KW - Hollow Specimen Technique KW - High-pressure Gaseous Hydrogen KW - Hydrogen Embrittlement KW - Tensile Testing PY - 2024 AN - OPUS4-60501 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Grimault de Freitas, Tomás T1 - Hollow Specimen Technique for Tests in High-Pressure Hydrogen Gas: The Path Towards Standardisation and the Case Study of a Pipeline Steel and its Weld N2 - The hollow specimen technique is a simple method that has the potential to make material qualification with gaseous pressurized hydrogen widely applicable for the hydrogen industry at low cost. The feasibility of this method has been demonstrated in several studies, leading to the establishment of an ISO committee for its standardization. Questions have emerged during this process, that currently prevent the method from being standardized for hydrogen testing. These questions relate to specimen geometry, specimen manufacturing and gas quality and are being systematically addressed in the TransHyDE-H2HohlZug project. The aim is to close the identified gaps towards the standardization of this method for hydrogen testing. This contribution presents the structure and milestones of the project, followed by the results regarding the influence of specimen production and its response to hydrogen effects. Depending on the production method, different roughness and residual stresses can be expected on the inner hole surface of the specimens. This is of importance since an increase in stress concentration sites have been found to be associated to a higher severity of hydrogen effects. This influence has been investigated after applying the following machining processes: a) drilled only; b) drilled and reamed; c) drilled and honed; d) electro-discharge machining (EDM) and honed; e) EDM and reamed. Roughness measurements using a profilometer, electron back-scatter diffraction (EBSD) analysis and microhardness tests have been performed previous to mechanical testing to infer on the effect of the different production methods on the surface of the inner hole. Next, the specimens were mechanically tested via slow strain rate tensile tests in a argon and in hydrogen, both at 150 bar and room temperature. Here, a strain-rate sensibility analysis was also performed to identify an optimal strain-rate for the mechanical tests. Based on the results an optimal production method is identified and proposed. T2 - ASTM Conference on Hydrogen Materials CY - La Rochelle, France DA - 03.06.2025 KW - Hydrogen KW - Hydrogen Embrittlement KW - Hollow Specimen Technique KW - High-Pressure Gaseous Hydrogen KW - Austenitic Stainless Steel KW - H2HohlZug KW - TransHyDE KW - Tensile Test KW - Pipeline Steel PY - 2025 AN - OPUS4-63329 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -