TY - CONF A1 - Dalichow, Dirk A1 - Wilsch, Gerd A1 - Völker, Tobias T1 - Laser Induced Breakdown Spectroscopy for the Chemical Investigation of Concrete—Status of Practical Application N2 - The assessment and maintenance of reinforced concrete structures depends largely on knowledge of the chloride content and chloride ingress. Common methods are the wet chemical analysis of drill dust or powder from ground drill core segments. However, due to the homogenization process, this approach often fails to detect locally elevated chloride levels. A state-of-the-art alternative method is laser-induced breakdown spectroscopy (LIBS), which offers rapid analysis and the possibility of detecting several chemical elements simultaneously. This method is particularly characterized by its ability to measure light elements such as hydrogen, carbon or sodium. The spatial resolution of LIBS is usually 0.25 mm but can be increased to 0.1 mm or less if required. BARG, is the first commercial building materials laboratory in Germany to use LIBS in practice. The current LIBS setup enables rapid, spatial quantification of the chlorine content and at the same time the creation of element maps that visually represent the distribution of essential elements in the concrete. This method can be used to localize areas of elevated chlorine content, particularly in cracks or near reinforcing bars. With the ability to analyze several elements simultaneously, LIBS can determine measurement points associated with the cement phase and, taking into account the water content, relate the measured contents directly to the cement mass. The detailed ingress profiles determined by LIBS provide essential data for the estimation of accurate chlorine diffusion coefficients, which are crucial for probabilistic lifetime predictions. The estimation of the carbon distribution enables the localization of carbonated regions and their effect on the chloride distribution. The possibility of quantitatively determining the sulfur distribution also indicates areas that are affected by a possible sulfate attack. The presentation uses practical examples to demonstrate the possibilities and advantages of the LIBS method. In addition, the newly published leaflet B14 of the German Society for Non-Destructive Testing (DGZfP) will be presented, which describes the use of LIBS for the quantitative determination of chloride content in concrete. T2 - ICCRRR 2024 CY - Cape Town, South Africa DA - 04.11.2024 KW - Concrete KW - Chloride KW - Corrosion KW - Repair KW - Maintenance PY - 2024 DO - https://doi.org/10.1007/978-3-031-75507-1_40 VL - 59 SP - 411 EP - 420 AN - OPUS4-62480 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Maack, Stefan A1 - Torrent, R. A1 - Ebell, Gino A1 - Völker, Tobias A1 - Küttenbaum, Stefan T1 - Testing to reassess – Corrosion activity assessment based on NDT using a prestressed concrete bridge as case-study N2 - Corrosion of concrete reinforcement is one of the major damage mechanisms affecting both the load-bearing capacity and the serviceability of re-inforced concrete structures significantly. When externally discernible damages are observed during visual inspections on the structure, the extent of the damage inside the concrete is often already significant. Corrosion caused by carbonation often leads to severe discoloration of the surface or even large-area spalling of the concrete cover. In contrast, chloride-induced corrosion is usually difficult to observe visually but can cause much more serious damage in less time. The effect occurs locally and can lead to weakening of the cross-section of the reinforce-ment. This, in turn, can cause sudden structural collapses without prior notice. In the meanwhile, various non-destructive and minimally invasive testing methods are available to evaluate the resistance to penetration of corrosion-pro-moting pollutants and to detect active corrosion. In this paper, a bridge crossing the river Regen is used as a case-study to demonstrate how the information ob-tained applying different testing methods can be combined and evaluated in the context of structural reassessments. Both the results of the permeability testing and the electrical resistance measurement are considered, as well as active corro-sion areas are localized using the half-cell potential mapping combined with the concrete cover measurement with the eddy current method and ground penetrat-ing radar. The results are evaluated using drill cores and in addition laser-induced breakdown spectroscopy was applied to obtain information about possible chlo-ride ion transport into the concrete. T2 - EUROSTRUCT 2021 – 1ST conference of the european association on quality control of bridges and structures - Eurostruct CY - Padova, Italy DA - 30.08.2021 KW - Nondestructive testing KW - Corrosion KW - Bridge KW - Durability assessment KW - Civil engineering PY - 2022 SN - 978-3-030-91876-7 SP - 1 EP - 9 PB - Springer International Publishing AN - OPUS4-54006 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schwarz, W. A1 - Wilsch, Gerd A1 - Katsumi, N. A1 - Ebell, Gino A1 - Völker, Tobias T1 - Ion distribution in concrete overlay, mapped by laser induced breakdown spectroscopy (LIBS), modified by an embedded zinc anode N2 - Galvanic corrosion protection by embedded zinc anodes is an accepted technique for the corrosion protection of reinforcing steel in concrete. Galvanic currents flow between the zinc anode and the steel reinforcement due to the potential difference that is in the range of a few hundred mV. The ion distribution was studied on two steel reinforced concrete specimens admixed with 3 wt.% chloride/wt. cement and galvanically protected by a surface applied EZ-anode. On both specimens, a zinc anode was embedded and glued to the concrete surface by a geo-polymer-based chloride-free binder. At one specimen, the EZ-anode was operated for 2,5 years, the EZ-anode at the other specimen was not electrically connected to the reinforcement, this specimen serves as a reference. Both specimens have been stored under identical conditions. The ion distribution between the anode (EZ-anode) and cathode (steel reinforcement) was studied by laser-induced breakdown spectroscopy (LIBS) after 7 months, 12 months, and 2,5 years. Results of the LIBS studies on the specimen with activated EZ-anode after 7 months, 12 months, and 2,5 years and of the reference specimen after 2,5 years are reported. Results show that diffusion of ions contributes to the changes in the ion distribution but migration, especially of chlorides towards the EZ-anode is significant despite the weak electric field – several hundred millivolts - generated by the galvanic current. Results show that chloride ions accumulate near the zinc-anode as in water-insoluble zinc-hydroxy chlorides - Simonkolleit. T2 - ICCRRR 2022 CY - Capetown, South Africa DA - 03.10.2022 KW - Korrosion KW - Corrosion KW - LIBS KW - Zinc PY - 2022 AN - OPUS4-55948 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schwarz, W. A1 - Wilsch, Gerd A1 - Katsumi, N. A1 - Ebell, Gino A1 - Völker, Tobias T1 - Ion distribution in concrete overlay, mapped by laser induced breakdown spectroscopy (LIBS), modified by an embedded zinc anode N2 - Galvanic corrosion protection by embedded zinc anodes is an accepted technique for the corrosion protection of reinforcing steel in concrete. Galvanic currents flow between the zinc anode and the steel reinforcement due to the potential difference that is in the range of a few hundred mV. The ion distribution was studied on two steel reinforced concrete specimens admixed with 3 wt.% chloride/wt. cement and galvanically protected by a surface applied EZ-anode. On both specimens, a zinc anode was embedded and glued to the concrete surface by a geo-polymer-based chloride-free binder. At one specimen, the EZ-anode was operated for 2,5 years, the EZ-anode at the other specimen was not electrically connected to the reinforcement, this specimen serves as a reference. Both specimens have been stored under identical conditions. The ion distribution between the anode (EZ-ANODE) and cathode (steel reinforcement) was studied by laser-induced breakdown spectroscopy (LIBS) after 7 months, 12 months, and 2,5 years. Results of the LIBS studies on the specimen with activated EZ-anode after 7 months, 12 months, and 2,5 years and of the reference specimen after 2,5 years are reported. Results show that diffusion of ions contributes to the changes in the ion distribution but migration, especially of chlorides towards the EZ-anode is significant despite the weak electric field – several hundred millivolts - generated by the galvanic current. Results show that chloride ions accumulate near the zinc-anode as in water-insoluble zinc-hydroxy chlorides - Simonkollite. T2 - ICCRRR 2022 CY - Capetown, South Africa KW - Corrosion KW - LIBS KW - Zinc KW - Anode PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-560576 DO - https://doi.org/10.1051/matecconf/202236404023 SN - 2261-236X VL - 364 SP - 1 EP - 7 PB - EDP Sciences CY - Les Ulis AN - OPUS4-56057 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schwarz, W. A1 - Wilsch, Gerd A1 - Pichelhöfer, A. A1 - Ebell, Gino A1 - Völker, Tobias T1 - Galvanic chloride extraction by an embedded zinc anode: Ion distribution mapped by laser induced breakdown spectroscopy (LIBS) N2 - An important aspect with regard to the service life of zinc based galvanic anodes and the durability of the corrosion protection of steel in concrete is the “galvanic chloride extraction”. Chloride ions move in the electric field generated by the current, flowing between the galvanic anode and the cathodic steel. Migration leads to an accumulation of anions, e.g. chloride ions, at the anode and depletion of chlorides near the steel rebar surface. The ion migration was studied on steel reinforced concrete specimens admixed with 3 wt.% chloride/wt. cement and galvanically protected by a surface applied embedded zinc anode (EZA). The zinc anode was embedded and glued to the concrete surface by a geo-polymer based chloride free binder. The EZA was operated over a period of 1 year and the ion distribution between anode (EZA) and cathode (steel reinforcement) was studied by laser induced breakdown spectroscopy (LIBS) after 5 months, 7 months and 12 months. The results show that chloride ions efficiently migrate in the direction of the zinc-anode and accumulate there. Chloride distribution in the EZA correlates with the distribution of zinc ions generated by the anodic dissolution of the zinc anode in the binder matrix. The microstructure of the binder matrix and its interface to the zinc-anode are studied by REM/EDX – preliminary results will be reported. T2 - Concrete Solutions 2019 CY - Cluj Napoca, Romania DA - 30.09.2019 KW - Galvanic corrosion KW - Corrosion KW - Chloride extraction PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-488189 DO - https://doi.org/10.1051/matecconf/201928903010 VL - 289 SP - 03010, 1 EP - 5 PB - MATEC Web of Conferences AN - OPUS4-48818 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -