TY - JOUR A1 - Schasse, R. A1 - Kannengießer, Thomas A1 - Kromm, Arne A1 - Mente, Tobias T1 - Residual stresses in repair welds of high-strength low-alloy steels N2 - Residual stresses are often the cause for cracks in weld constructions. That is why the residual stress level, induced by manufacturing process, plays a crucial role. The present study aims on the effect of multiple repair weld procedures on a high-strength structural steel S690QL. The widespread technology of carbon arc-air gouging was applied. The weld zone and the heat-affected zone (HAZ) were subjected to multiple thermal cycles by gouging and subsequent repair welding. The investigations were focused on the change of the residuals stresses, the impact on the microstructure and the changes for the mechanical properties of the repair welded joint. The residual stresses were determined by X-ray diffraction. The results have shown a significant dependence for the residual stress levels from the repair cycle. In addition, distinctive changes in microstructures and hence mechanical properties occurred. The fusion line of the repair weld and the adjacent HAZ are the most critical areas. This is where the loss of ductility is most pronounced. KW - Residual stresses KW - High-strength steels KW - Brittle fracture PY - 2015 DO - https://doi.org/10.1007/s40194-015-0257-9 SN - 0043-2288 SN - 1878-6669 VL - 59 IS - 6 SP - 757 EP - 765 PB - Springer CY - Oxford AN - OPUS4-34974 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mente, Tobias T1 - Schweißeignung höherfester Feinkornbaustähle mit Streckgrenzen über 1000 MPa T2 - Konzerforschungsseminar - voestalpine "welding of high strength steels" CY - Linz, Austria DA - 2011-03-24 PY - 2011 AN - OPUS4-25033 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schröpfer, Dirk A1 - Mente, Tobias A1 - Kannengießer, Thomas T1 - Kaltrissbildung in Baustählen im Lichte der Regelwerke N2 - Der verstärkte Einsatz höherfester Stähle und Zusatzwerkstoffe erfordert ein vertieftes Verständnis der Zusammenhänge zwischen Schweißverfahren, Wärmeeinbringung, Abkühlbedingungen sowie den daraus resultierenden metallurgischen Vorgängen in der Schweißnaht und deren Umgebung. Nur aus dem Zusammenwirken aller Einflussfaktoren lassen sich Strategien ableiten, mit deren Hilfe die Festigkeitseigenschaften bzw. die Lebensdauer von Schweißkonstruktionen in einem Maße verbessert werden können, die den Einsatz höherfester Werkstoffe rechtfertigen und somit deren Leichtbaupotenzial voll ausgenutzt werden kann. Vorgestellt werden einige beispielhafte Untersuchungen an Schweißverbindungen aus höherfesten Feinkornbaustählen zu Interaktionen der Haupteinflussgrößen auf die Kaltrissbildung. T2 - 17. Tagung Schweißen in der maritimen Technik und im Ingenieurbau CY - Hamburg, Germany DA - 19.04.2017 KW - Kaltrisse KW - hochfeste Feinkornbaustähle KW - Eigenspannungen KW - Wasserstoffbedingte Eigenschaftsdegradation KW - Regelwerke KW - Schweißen KW - Wärmeführung PY - 2017 VL - 2017 SP - 54 EP - 67 AN - OPUS4-41068 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rhode, Michael A1 - Nietzke, Jonathan A1 - Mente, Tobias A1 - Richter, Tim A1 - Kannengießer, Thomas T1 - Characterization of Hydrogen Diffusion in Offshore Steel S420G2+M Multi-layer Submerged Arc Welded Joint N2 - As onshore installation capacity is limited, the increase in the number of offshore wind turbines (OWT) is a major goal. In that connection, the OWTs continuously increase in size and weight and demand adequate foundations concepts like monopiles or tripods. These components are typically manufactured from welded mild steel plates with thickness up to 200 mm. The predominant welding technique is submerged arc welding (SAW). In accordance with the standards, the occurrence of hydrogen-assisted cracking is anticipated by either a minimum waiting time (MWT, before non-destructive testing of the welded joint is allowed) at ambient or a hydrogen removal heat treatment (HRHT) at elevated temperatures. The effectiveness of both can be estimated by calculation of the diffusion time, i.e., diffusion coefficients. In this study, these coefficients are obtained for the first time for a thick-walled S420G2+M offshore steel grade and its multi-layer SAW joint. The electrochemical permeation technique at ambient temperature is used for the determination of diffusion coefficients for both the base material and the weld metal. The coefficients are within a range of 1025 to 1024 mm2/s (whereas the weld metal had the lowest) and are used for an analytical and numerical calculation of the hydrogen diffusion and the related MWT. The results showed that long MWT can occur, which would be necessary to significantly decrease the hydrogen concentration. Weld metal diffusion coefficients at elevated temperatures were calculated from hydrogen desorption experiments by carrier gas hot extraction. They are within a range of 1023 mm2/s and used for the characterization of a HRHT dwell-time. The analytical calculation shows the same tendency of long necessary times also at elevated temperatures. That means the necessary time is strongly influenced by the considered plate thickness and the estimation of any MWT/HRHT via diffusion coefficients should be critically discussed. T2 - European Congress and Exhibition on Advanced Materials and Process - Euromat 2021 CY - Online meeting DA - 13.09.2021 KW - Thick-walled KW - Hydrogen diffusion KW - Offshore KW - Steel KW - Submerged arc welding PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-544127 DO - https://doi.org/10.1007/s11665-022-06679-7 SN - 1059-9495 SP - 1 EP - 13 PB - Springer Nature AN - OPUS4-54412 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rhode, Michael A1 - Mente, Tobias A1 - Kannengießer, Thomas T1 - Parameters and challenges for reliable hydrogen determination in welded joints by carrier gas hot extraction N2 - For the hydrogen-based energy economy of tomorrow, the construction of the necessary infrastructure will play a central role. Most materials used to date, such as welded steels, can be prone to hydrogen embrittlement under certain conditions. This includes the classic delayed cold cracking during welding as well as degradation phenomena during service of components in hydrogen-containing environment. For the evaluation of any hydrogen effect, for example, on the mechanical properties of a welded metallic material, the hydrogen content must be precisely determined. In the case of weld seams, the carrier gas hot extraction (CGHE) according to ISO 3690 is meanwhile state-of-the-art. CGHE is based on accelerated hydrogen degassing due to the thermal activation of hydrogen at elevated temperatures. In addition to the quantification of hydrogen, thermal desorption analysis (TDA) with varying heating rates can be used to determine and evaluate the hydrogen trapping at microstructural defects in the material. For both techniques, experimental and metrological influences must be considered, which have a major effect on the result. For example, ISO 3690 suggests different sample geometries and minimum extraction times for CGHE. This study summarizes the results and experiences of numerous investigations at the Federal Institute for Materials Research and Testing (BAM) with different sample temperatures and geometries (ISO 3690 type B and cylindrical TDA samples) regarding the influence of the sample surface (polished/welded), measurement accuracy depending on the sample volume and the insufficient monitoring of the effect of PI control on the extraction temperature. A deviating extraction temperature from the target temperature can significantly falsify the measurement results. Based on the results, methods are shown which allow the desired extraction temperature to be reached quickly without physically interfering with the measuring equipment. This serves to significantly improve the reliability of the hydrogen measurement through increased signal stability and accelerated hydrogen desorption. In general, an independent temperature measurement with dummy samples is recommended for the heating procedure of choice to exclude possible undesired temperature influences before the measurement. The methods described can be transferred directly to industrial applications KW - Welding KW - Hydrogen measurement KW - ISO 3690 KW - Carrier gas hot extraction PY - 2024 DO - https://doi.org/10.37434/tpwj2024.04.01 SN - 0957-798X VL - 4 SP - 3 EP - 10 PB - International Association Welding AN - OPUS4-60071 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kromm, Arne A1 - Schasse, R. A1 - Xu, Ping A1 - Mente, Tobias A1 - Kannengießer, Thomas ED - Olden, T.-M. ED - Muransky, O. ED - Edwards, L. T1 - Influence of weld repair by gouging on the residual stresses in high strength steels N2 - Carbon arc-air gouging is a common technology when repairing defects in welded structures. Often this technique is applied in repeated cycles even on the same location of the joint. Due to the multiple heat input by gouging and subsequent re-welding, the residual stresses are strongly influenced. This can become crucial when microstructure and mechanical properties are adversely affected by multiple weld reparations. Knowledge about the relation of gouging and residual stresses is scarce but important when high strength steels, which are sensitive to residual stresses, are processed. The present study shows the effect of repair welding on a high strength steel structural element. The weld and the heat affected zone were subjected to multiple thermal cycles by gouging and subsequent repair welding. The residual stresses were determined by X-ray diffraction at different positions along the joint. The results showed that the residual stress level has increased by the repair cycles. This is most pronounced for the heat affected zone. Adapted welding procedures may prevent detrimental residual stress distributions. T2 - ICRS 2016 - 10th International Conference on Residual Stresses CY - Sydney, Australia DA - 03.07.2016 KW - Repair welding KW - Weld residual stress KW - Carbon arc-air gouging PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-389242 SN - 978-1-94529117-6 SN - 978-1-94529117-3 DO - https://doi.org/10.21741/9781945291173-29 SN - 2474-395X VL - 2 SP - 169 EP - 174 PB - Materials Research Forum LLC CY - Millersville, PA, USA AN - OPUS4-38924 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Rhode, Michael A1 - Mente, Tobias A1 - Kannengießer, Thomas A1 - Czeskleba, Denis T1 - Simulation of hydrogen distribution in submerged arc welded heavy plates as tool for evaluating cold cracking sensitivity for offshore structures N2 - Foundation structures for offshore wind turbines are typically made of heavy plate struc-tural steels, such as S420ML, welded by submerged arc welding. Due to the welding process conditions, higher amounts of hydrogen can be introduced. In this context, large plate thicknesses result in long diffusion paths and a prolonged diffusion time for hydrogen at ambient temperature and possible delayed hydrogen-assisted cold cracking. As a result, hydrogen can accumulate in areas of high mechanical stress and strain. Due to the delayed diffusion, a minimum waiting time of up to 48 h must be observed before non-destructive testing can be performed. In addition, the assessment of possible cold crack locations is very complex. For this reason, a numerical model of a component-like weld test was developed to simulate the temperature field during welding and subsequent cooling. A hydrogen diffusion model based on the temporal-local temperature distribution was established. It was applied to simulate the change of hydrogen distribution as a function of temperature cycle during multi-layer welding and further for the entire waiting time interval ≤ 48 h. As a result, crack critical areas could be evaluated in terms of accu-mulated hydrogen. An advantage of the diffusion model is the simulation of a normalized concentration, i.e. between "0" (no hydrogen) and "1" (max. concentration), which can be scaled to experimentally determined hydrogen concentrations. Finally, selected results for increased real hydrogen ingress are presented, which confirm the relatively high crack resistance of the S420 submerged arc welded joint. KW - Hydrogen assisted cracking KW - Diffusion KW - Numerical simulation KW - Offshore steel PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-632416 DO - https://doi.org/10.21268/20250507-6 SP - 1 EP - 12 PB - Technische Universität Clausthal CY - Clausthal-Zellerfeld, Deutschland AN - OPUS4-63241 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rhode, Michael A1 - Nietzke, Jonathan A1 - Mente, Tobias T1 - Trapping and diffusion in high-pressure hydrogen charged CoCrFeMnNi high entropy alloy compared to austenitic steel 316L N2 - High entropy alloys (HEAs) have attracted considerable research attention as potential substitute materials for austenitic steels in high-pressure hydrogen environments. The corresponding hydrogen absorption, diffusion and trapping has received less scientific attention. Therefore, the CoCrFeMnNi-HEA was investigated and compared to an austenitic steel AISI 316L. Both were subjected to high-pressure hydrogen charging at 200 bar and 1000 bar. Thermal Desorption Analysis (TDA) was used to clarify the specific desorption behavior and hydrogen trapping. For this purpose, the underlying TDA spectra were analyzed in terms of a reasonable peak deconvolution into a defined number of peaks and the activation energies for the respective and predominant hydrogen trapping sites were then calculated. Both materials show comparable hydrogen diffusivity. However, there were significant differences in the absorbed hydrogen concentrations at both charging pressures. The calculated activation energies suggest strong hydrogen trapping in the CoCrFeMnNi-HEA. KW - High-entropy alloy KW - Hydrogen diffusion KW - Trapping KW - High-pressure charging KW - Thermal desorption analysis PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-611901 DO - https://doi.org/10.1016/j.ijhydene.2024.09.393 SN - 0360-3199 VL - 89 IS - 89 SP - 772 EP - 782 PB - Elsevier B.V. CY - Amsterdam, Netherlands AN - OPUS4-61190 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rhode, Michael A1 - Richter, Tim A1 - Mente, Tobias A1 - Mayr, P. A1 - Nitsche, A. T1 - Thickness and microstructure effect on hydrogen diffusion in creep‑resistant 9% Cr P92 steel and P91 weld metal N2 - Martensitic 9% Cr steels like P91 and P92 show susceptibility to delayed hydrogen assisted cracking depending on their microstructure. In that connection, effective hydrogen diffusion coefficients are used to assess the possible time-delay. Limited data on room temperature diffusion coefficients reported in literature vary widely by several orders of magnitude (mostly attributed to variation in microstructure). Especially P91 weld metal diffusion coefficients are rare so far. For that reason, electrochemical permeation experiments had been conducted using P92 base metal and P91 weld metal (in as-welded and heat-treated condition) with different thicknesses. From the results obtained, diffusion coefficients were calculated using to different methods, time-lag, and inflection point. Results show that, despite microstructural effects, the sample thickness must be considered as it influences the calculated diffusion coefficients. Finally, the comparison of calculated and measured hydrogen concentrations (determined by carrier gas hot extraction) enables the identification of realistic diffusion coefficients. KW - Creep-resistant steel KW - Diffusion KW - Hydrogen assisted cracking KW - Welding KW - Electrochemical permeation PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-540645 DO - https://doi.org/10.1007/s40194-021-01218-9 SN - 0043-2288 SP - 1 EP - 16 PB - Springer Nature Switzerland AG AN - OPUS4-54064 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rhode, Michael A1 - Nietzke, Jonathan A1 - Richter, Tim A1 - Mente, Tobias A1 - Mayr, P A1 - Nitsche, A T1 - Hydrogen effect on mechanical properties and cracking of creep‑resistant 9% Cr P92 steel and P91 weld metal N2 - Martensitic 9% Cr steels like P91 and P92 can show an increased susceptibility to delayed hydrogen-assisted cracking. The focus of this study was the microstructure and heat treatment efect on the mechanical properties of P92 base material and P91 multi-layer weld metal in both as-welded and post weld heat treated (PWHT) condition. Tensile tests with hydrogen free reference samples and electrochemically hydrogen charged samples were carried out; the mechanical properties were assessed and supported by detailed fractographic analysis. Finally, a hydrogen and microstructure-dependent fracture criterion is established. All investigated microstructures showed a hydrogen-infuenced degradation of the mechanical properties compared to the hydrogen-free reference samples. The as-welded martensitic P91 weld metal had the highest degree of degradation in the presence of hydrogen. The P91 PWHT weld metal and the P92 base material had comparable properties. From that point of view, a signifcantly increased risk for hydrogen-assisted cold cracking during welding fabrication of P91 weld joints must be considered before any heat treatment is conducted. T2 - IIW Annual Assembly, Meeting of Commission IX-C CY - Tokyo, Japan DA - 16.07.2022 KW - Creep-resisting materials KW - Welding KW - Hydrogen assisted cracking KW - Hydrogen embrittlement KW - Mechanical properties PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-564070 DO - https://doi.org/10.1007/s40194-022-01410-5 SN - 0043-2288 SP - 1 EP - 12 PB - Springer Nature CY - Basel (CH) AN - OPUS4-56407 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rhode, Michael A1 - Mente, Tobias A1 - Steppan, E. A1 - Kannengießer, Thomas A1 - Steger, J. T1 - Hydrogen trapping in T24 Cr-Mo-V steel weld joints - microstructure effect vs. experimental influence on activation energy for diffusion N2 - Hydrogen-assisted cracking is a critical combination of local microstructure, mechanical load and hydrogen concentration. Welded microstructures of low-alloyed creep-resistant Cr-Mo-V steels show different hydrogen trapping kinetics. This influences the adsorbed hydrogen concentration as well as the diffusion by moderate or strong trapping. A common approach to describe hydrogen traps is by their activation energy that is necessary to release hydrogen from the trap. In the present study, Cr-Mo-V steel T24 (7CrMoVTiB10-10) base material and TIG weld metal were investigated. Electrochemically hydrogen charged specimens were analyzed by thermal desorption analysis (TDA) with different linear heating rates. The results show two different effects. At first, the microstructure effect on trapping is evident in terms of higher hydrogen concentrations in the weld metal and increased activation energy for hydrogen release. Secondly, it is necessary to monitor the real specimen temperature. A comparison between the adjusted heating rate and the real specimen temperature shows that the calculated activation energy varies by factor two. Thus, the trap character in case of the base material changes to irreversible at decreased temperature. Hence, the effect of the experimental procedure must be considered as well if evaluating TDA results. Finally, realistic temperature assessment is mandatory for calculation of activation energy via TDA. KW - Creep-resistant steel KW - Hydrogen assisted cracking KW - Thermal desorption analysis KW - Welding KW - Microstructure KW - Diffusion PY - 2018 DO - https://doi.org/10.1007/s40194-017-0546-6 SN - 0043-2288 SN - 1878-6669 VL - 62 IS - 2 SP - 277 EP - 287 PB - Springer CY - Berlin, Heidelberg AN - OPUS4-44505 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mente, Tobias T1 - Numerische Simulation wasserstoffunterstützter Kaltrisse in hochfesten Stählen T2 - Konzernforschungsseminar - voestapline "welding of high strength steels" CY - Linz, Austria DA - 2011-03-24 PY - 2011 AN - OPUS4-25034 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Nietzke, Jonathan A1 - Mente, Tobias A1 - Kannengießer, Thomas T1 - Diffusionsmessungen in UP-Mehrlagenschweißgut als effektives Tool gegen verzögerte Kaltrissbildung in Dickblechschweißungen N2 - Offshore-Windenergieanlagen bilden einen zentralen Bestandteil der zukünftigen Energieerzeugung. Hierzu notwendige Gründungs- und Turmstrukturen werden vorrangig aus UP-geschweißten Blechen aus hochfesten niedriglegierten Stählen mit Dicken bis zu 200 mm hergestellt. Die großen Blechdicken begünstigen hohe Schweißeigenspannungen und lange Diffusionswege für z. B. über den Schweißprozess eingebrachten Wasserstoff. Damit steigt das Risiko für eine wasserstoffunterstützte Kaltrissbildung (WKB) an. Zum sichereren Ausschluss von WKB in den geschweißten Komponenten wird in Abhängigkeit der Nahtgröße, Wärmeeinbringung und Stahlsorte eine Mindestwartezeit (MWZ) von bis zu 48 h empfohlen, bevor die zerstörungsfreie Prüfung durchgeführt wird. Es ist allerdings offen, ob die empfohlene MWZ zu konservativ ist. Einflüsse sind hier bspw. die schwierige Bewertung des Wasserstoffdiffusionsverhaltens im heterogenen UP-Mehrlagen-Schweißgut (SG) im Vergleich zum Grundwerkstoff (GW). Zudem sind nur sehr begrenzt H-Diffusionskoeffizienten für UP-Mehrlagen-SG als Grundlage zur Abschätzung des Zeitintervalls einer möglichen verzögerten Kaltrissbildung (somit MWZ) oder auch für Nachwärmprozeduren zur Wasserstoffreduktion (keine MWZ) verfügbar. Verlässliche H-Diffusionskoeffizienten sind daher ein adäquates Tool zur Bewertung des Risikos einer verzögerten WKB. Dieser Beitrag beschreibt Untersuchungen zur Charakterisierung der Wasserstoffdiffusionsverhalten in UP-Mehrlagen-SG eines 60 mm dicken Bleches einer Offshore-Stahlgüte. Dazu wurden Proben unterschiedlicher Dicke aus dem reinen Schweißgut extrahiert und über elektrochemische Permeation und Trägergasheißextraktion im Temperaturbereich bis 400 °C sehr interessante Ergebnisse zu den korrespondierenden Diffusionskoeffizienten erarbeitet. T2 - DVS Congress 2021 CY - Online meeting DA - 14.09.2021 KW - UP-Schweißen KW - Wasserstoff KW - Kaltriss KW - Permeation KW - Diffusion PY - 2021 SN - 978-3-96144-146-4 VL - 371 SP - 448 EP - 459 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-53369 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Kromm, Arne A1 - Mente, Tobias A1 - Czeskleba, Denis A1 - Brackrock, Daniel A1 - Kannengießer, Thomas T1 - Bauteilversuch zur Bewertung der wasserstoffunterstützten Rissanfälligkeit geschweißter, dickwandiger Offshore-Gründungsstrukturen N2 - Offshore-Windenergieanlagen erfordern Gründungskonzepte aus unterpulver-(UP-)geschweißten Dickblechen (bspw. der Güte S420ML). Während der Schweißfertigung kann eine zeitverzögerte wasserstoffunterstützte Kaltrissbildung auftreten, deren Bewertung aufgrund der Bauteilgröße von Offshore-Strukturen sehr komplex ist. Deswegen wurde eine bauteilähnliche Geometrie (Mock-Up) entwickelt, um reale Steifigkeitsverhältnisse auf den Labormaßstab zu übertragen. Zusätzliche Versteifungen simulieren die Wirkung einer Einspannung bzw. Schrumpfbehinderung der Schweißnaht. Über die Verwendung von Schweißpulvern mit definierter Feuchte wurden zudem ein Extremszenario der Wasserstoffaufnahme simuliert. Entsprechend der vorgegebenen Mindestwartezeit für die ZfP von bis zu 48 h wurde die Schweißnaht zerstörungsfrei mit Phased-Array-Ultraschall-Prüfung (PAUT) geprüft und die Eigenspannungen über Röntgendiffraktometrie (XRD) bestimmt. Zusätzlich wurde die Wasserstoffverteilung in der Schweißverbindung numerisch simuliert. Außer zulässigen Defekten (wie Poren), wurde keine verzögerte Kaltrissbildung in den Mock-Ups festgestellt, was auf hohe Rissbeständigkeit hindeutet. T2 - Tagung Werkstoffprüfung 2023 CY - Berlin, Germany DA - 23.11.2023 KW - Kaltrissbildung KW - Wasserstoff KW - Offshore KW - Schweißen KW - Bauteiltest PY - 2023 DO - https://doi.org/10.48447/WP-2023-219 SP - 316 EP - 321 CY - Berlin AN - OPUS4-58908 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mente, Tobias T1 - Gasflaschenzerknall in einer Löschanlage: Ursachen – Schadensanalyse – Prävention N2 - Schadensanalyse an einer mit Inergen gefüllten Gasflasche aus einer Löschanlage aus dem vergütetem Stahl 34CrMo4. Die Durchführung der Schadensanalyse erfolgte nach VDI 3822. Schadensursache war Spannungsrisskorrosion durch Wasserreste in Verbindung mit dem Gasbestandteil Kohlendioxid des eingefüllten Inergen. Die Wasserreste verblieben nach der hydraulischen Druckprüfung unentdeckt in der 1996 hergestellten Gasflasche. Auch bei der Erstbefüllung mit Inergen im Jahr 2003 blieben die Wasserreste unentdeckt. Nach Installation der befüllten Gasflasche in der Löschanlage im Jahr 2004 verblieb diese dort bis zum Schadensereignis im Jahr 2021. T2 - 51. VDI-Jahrestagung Schadensanalyse - Produktverbesserung durch Schadensprävention CY - Würzburg, Germany DA - 21.10.2025 KW - Gasflasche KW - Inergen-Löschanlage KW - Schadensanalyse PY - 2025 AN - OPUS4-64652 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Mente, Tobias A1 - Böllinghaus, Thomas T1 - Modeling of hydrogen-assisted cracking (HAC) in duplex stainless steels (DSS) N2 - Modeling of Hydrogen-Assisted Cracking (HAC) in Duplex Stainless Steels (DSS): - Hydrogen causes significant degradation in DSS and consequently HAC - Mechanisms of HAC have not been fully understood in two-phase microstructures - Mesoscale numerical modeling for HAC in DSS was created, coupled to the macroscale, enabling simulation of HAC in both phases independent from predefined crack paths T2 - International Hydrogen Conference - Material Performance in Hydrogen Environments CY - Jackson Lake Lodge, Moran, Wyoming, USA DA - 11.09.2016 KW - Hydrogen KW - Numerical modeling KW - Duplex stainless steel KW - Hydrogen assisted cracking PY - 2016 AN - OPUS4-37404 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mente, Tobias T1 - Mesoscale Model for Hydrogen Assisted Cracking in Two-Phase Microstuctures T2 - 10th International Seminar Numerical Analysis of Weldability CY - Seggauberg, Austria DA - 2012-09-23 PY - 2012 AN - OPUS4-26781 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Böllinghaus, Thomas A1 - Mente, Tobias A1 - Wongpanya, Pornwasa A1 - Viyanit, Ekkarut A1 - Steppan, Enrico ED - Böllinghaus, Thomas ED - Lippold, J. C. ED - Cross, C. E. T1 - Numerical modelling of hydrogen assisted cracking in steel welds N2 - Hydrogen assisted stress corrosion and cold cracking represent still a major topic regarding the safety of welded steel components against failure in many industrial branches. Hydrogen might be introduced during fabrication welding or might be taken up from an environment during sour service or at cathodic protection. Additionally, understanding and avoidance of hydrogen entry into weld microstructures from gaseous pressurized environments becomes increasingly important for renewable energy components. There are two types of metallurgical mechanisms associated with hydrogen assisted cracking, i.e. the cracking as well as hydrogen transport and trapping mechanisms. For numerical modelling, it has to be considered that both types are not independent of each other, that the mechanisms are not yet completely clarified and that validation of such models strongly depends on implementation of the correct hydrogen related materials properties. However, quite significant achievements have been made in modelling of hydrogen assisted cracking by indirect coupling of thermal, stress-strain as well as hydrogen uptake and diffusion analyses. After a brief introduction into the subject and by revisiting various proposed cracking mechanisms, the present contribution focuses on recent developments of a numerical model based on a comparison of actual hydrogen concentrations and mechanical loads with respective hydrogen dependent material properties as crack initiation and propagation criteria. The basic procedure for numerical simulation of crack initiation and propagation is outlined and it is shown how such numerical simulations can be validated experimentally. Furthermore, it is highlighted how such a procedure has been extended to a comprehensive model for life time prediction of welded steel pipeline components and experimentally verified. Finally, it is outlined how the model can be extended to simulate cracking in heterogeneous steel microstructures on the different scales. KW - hydrogen assisted cracking KW - numerical simulation KW - supermartensitic stainless steel KW - high strength low alloyed structural steel KW - duplex stainless steel PY - 2016 UR - http://link.springer.com/chapter/10.1007%2F978-3-319-28434-7_18 UR - http://www.springer.com/us/book/9783319284323 SN - 978-3-319-28432-3 SN - 978-3-319-28434-7 DO - https://doi.org/10.1007/978-3-319-28434-7_18 SP - Part VI, 383 EP - 439 PB - Springer International Publishing CY - Switzerland ET - 1 AN - OPUS4-35593 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mente, Tobias T1 - Kaltrissbildung in Baustählen im Lichte der Regelwerke - Kaltrissvermeidung in geschweißten Bauteilen aus hochfestem Stahl N2 - Herausforderungen bei der schweißtechnischen Verarbeitung / Welche Rolle spielt der Wasserstoff beim Schweißen? / Vorgewärmt und doch ein Kaltriss? - Wärmeführung beim Schweißen / Abbildung bauteilspezifischer Beanspruchungen im Labormaßstab / Maßnahmen zur Kaltrissvermeidung / Moderne Lichtbogenschweißverfahren T2 - 29. Schweißtechnisches Kolloquium des DVS Bezirksverbandes Hamburg CY - Hochschule für Angewandte Wissenschaften Hamburg, Germany DA - 06.02.2018 KW - Wasserstoffunterstützte Kaltrissbildung KW - Hochfester Feinkornbaustahl KW - Eigenspannungen KW - Einspanngrad KW - Modifizierter Sprühlichtbogen KW - Numerische Simulation PY - 2018 AN - OPUS4-44028 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mente, Tobias A1 - Grimault de Freitas, Tomás A1 - Nietzke, Jonathan A1 - Konert, Florian A1 - Sobol, Oded A1 - Wackermann, Ken A1 - Ruchti, Peter A1 - Elsen-Humberg, Stefan A1 - Systermans, Thomas ED - Zimmermann, Martina T1 - Hohlzugprüfung als kostengünstige Methode zur Werkstoffcharakterisierung für die Wasserstoffwirtschaft N2 - Wasserstoff ist ein notwendiger Baustein zur Erreichung zukünftiger Klimaziele. Für eine schnell hochlaufende Wasserstoffwirtschaft ist es daher notwendig sowohl bestehende Infrastruktur als auch neue Werkstoffe für den sicheren und nachhaltigen Einsatz in Wasserstofftechnologien zu qualifizieren. Die akzeptierten und standardisierten Prüfverfahren zur Ermittlung des Einflusses gasförmigen Wasserstoffs auf die mechanischen Eigenschaften metallischer Werkstoffe sind meist sehr komplex, mit hohem technologischem und finanziellem Aufwand verbunden und stehen nur Wenigen Instituten weltweit zur Verfügung. Die Hohlzugprüftechnik bietet hier eine kostengünstige und einfach zu realisierende Alternative. Mit der im Jahr 2024 erstmals veröffentlichten ISO 7039 wurde diese Prüftechnik auch für die Wirtschaft anwendbar gemacht. Der Standard gilt allgemein für die Prüfung mit gasförmigen Medien, weist jedoch in Bezug auf die Prüfung mit gasförmigem Wasserstoff noch einige Wissenslücken auf. Im Teilvorhaben H2HohlZug des Leitprojekt TransHyDE werden die Lücken zum Einfluss der Geometrie, Oberflächenqualität sowie Gasreinheit in einzelnen Arbeitspaketen geschlossen und die Erkenntnisse in einen Standard überführt. T2 - 43. Vortrags- und Diskussionstagung Werkstoffprüfung 2025 - Werkstoffe und Bauteile auf dem Prüfstand CY - Dresden, Germany DA - 27.11.2025 KW - Hohlzugprüfung KW - Druckwasserstoff KW - ISO 7039 KW - H2HohlZug - TransHyDE PY - 2025 SN - 978-3-88355-454-9 SP - 11 EP - 17 PB - Deutsche Gesellschaft für Materialkunde e.V. (DGM) CY - Dresden AN - OPUS4-64937 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -