TY - JOUR A1 - Dabah, Eitan A1 - Pfretzschner, Beate A1 - Schaupp, Thomas A1 - Kardjilov, N. A1 - Manke, I. A1 - Boin, M. A1 - Woracek, R. A1 - Griesche, Axel T1 - Time-resolved Bragg-edge neutron radiography for observing martensitic phase transformation from austenitized super martensitic steel N2 - Neutron Bragg-edge imaging was applied for the visualization of a γ-Austenite to α'-martensite phase transformation. In the present study, a super martensitic stainless steel sample was heated until complete austenitization and was subsequently cooled down to room temperature. The martensitic phase Transformation started at Ms = 190 °C. Using a monochromatic neutron beam with λ = 0.390 nm, the transmitted intensity was significantly reduced during cooling below Ms, since the emerging martensitic phase has a higher attenuation coefficient than the austenitic phase at this wavelength. The phase Transformation process was visualized by filming the transmission images from a scintillator screen with a CCD camera with a temporal resolution of 30 s and a spatial resolution of 100 µm. KW - Neutron imaging KW - Bragg-edge imaging KW - Phase transformation PY - 2017 DO - https://doi.org/10.1007/s10853-016-0642-9 SN - 0022-2461 SN - 1573-4803 VL - 52 IS - 6 SP - 3490 EP - 3496 AN - OPUS4-38574 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Griesche, Axel A1 - Pfretzschner, Beate A1 - Schaupp, Thomas A1 - Schulz, M. A1 - Kardjilov, N. ED - Duprez, Lode T1 - Hydrogen in steel visualized by neutron imaging N2 - Neutron cameras allow visualizing hydrogen distributions with radiographic or tomographic imaging methods in iron and steel. The necessary contrast between hydrogen and iron stems from the high difference in the total neutron cross section of both elements. This allows e.g. the in situ measurement of hydrogen mass flow inside cm thick steel samples with a temporal resolution of 20 s using neutron radiography as well as the quantitative measurement of hydrogen accumulations at the crack’s inner surfaces in hydrogen embrittled iron samples with neutron tomography. We could detect directly gaseous hydrogen in the crack cavities and we measured the gas pressure. This new quality of the information on a micrometer scale allows new insights for the analysis of hydrogen-induced damage mechanisms. Further, this method is non-destructive and provides local information in situ and in three dimensions with a spatial resolution of 20-30 µm. In this contribution, we show examples that demonstrate the spatial and temporal resolution of the neutron radiography and tomography methods in order to visualize and quantify hydrogen accumulations at cracks. The measurements were performed at the research reactor BER II of the HZB in Berlin and at the FRM II reactor of the neutron source Heinz Maier-Leibnitz in Garching. T2 - Third International Conference on Metals & Hydrogen CY - Ghent, Belgium DA - 29.05.2018 KW - Hydrogen KW - Steel KW - Neutron imaging PY - 2018 SN - 978-9-08179-422-0 SP - J01 AN - OPUS4-45359 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Griesche, Axel A1 - Schaupp, Thomas T1 - Hydrogen in steel visualized by neutron imaging N2 - Neutron cameras allow visualizing hydrogen distributions with radiographic or tomographic imaging methods in iron and steel. The necessary contrast between hydrogen and iron stems from the high difference in the total neutron cross section of both elements. This allows e.g. the in situ measurement of hydrogen mass flow inside cm thick steel samples with a temporal resolution of 20 s using neutron radiography as well as the quantitative measurement of hydrogen accumulations at the crack’s inner surfaces in hydrogen embrittled iron samples with neutron tomography. We could detect directly gaseous hydrogen in the crack cavities and we measured the gas pressure. This new quality of the information on a micrometer scale allows new insights for the analysis of hydrogen-induced damage mechanisms. Further, this method is non-destructive and provides local information in situ and in three dimensions with a spatial resolution of 20-30 μm. In this contribution, we show examples that demonstrate the spatial and temporal resolution of the neutron radiography and tomography methods in order to visualize and quantify hydrogen accumulations at cracks. The measurements were performed at the research reactor BER II of the HZB in Berlin and at the FRM II reactor of the neutron source Heinz Maier-Leibnitz in Garching. T2 - 3rd international conference on metals & hydrogen CY - Ghent, Belgium DA - 29.05.2018 KW - Hydrogen KW - Neutron KW - Radiography KW - Tomography KW - Steel PY - 2018 AN - OPUS4-45074 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pfretzschner, Beate A1 - Schaupp, Thomas A1 - Hannemann, Andreas A1 - Schultz, Michael A1 - Griesche, Axel T1 - On the Genesis of Artifacts in Neutron Transmission Imaging of Hydrogenous Steel Specimens N2 - Hydrogen-charged supermartensitic steel samples were used to systematically investigate imaging artifacts in neutron radiography. Cadmium stencils were placed around the samples to shield the scintillator from excessive neutron radiation and to investigate the influence of the backlight effect. The contribution of scattered neutrons to the total detected intensity was investigated by additionally varying the sample-detector distance and applying a functional correlation between distance and intensity. Furthermore, the influence of the surface roughness on the edge effect due to refraction was investigated. KW - Refraction KW - Neutron imaging KW - Hydrogen KW - Supermartensitic steel KW - Backlight KW - Scattering PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-506587 DO - https://doi.org/10.3390/jimaging6040022 VL - 6 IS - 22 SP - 1 EP - 10 PB - MDPI CY - Basel, Switzerland AN - OPUS4-50658 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaupp, Thomas T1 - Einfluss von Schweißprozessparametern auf den Wasserstoffeintrag in Schweißverbindungen aus hochfestem Feinkornbaustahl N2 - Um den wachsenden Anforderungen nach Leichtbau und Ressourceneffizienz im Kran-, Nutzfahrzeug- und Brückenbau gerecht zu werden, kommen in diesen Industriebranchen vermehrt hochfeste Feinkornbaustähle mit Streckgrenzen von mehr als 690 MPa zum Einsatz. Allerdings erfordern diese Stähle bei der schweißtechnischen Verarbeitung äußerste Sorgfalt, weil gerade die Sensibilität gegenüber einer Degradation der mechanischen Eigenschaften, durch den im Lichtbogen aufgenommenen Wasserstoff, mit steigender Festigkeit signifikant zunimmt und zur wasserstoffunterstützten Kaltrissbildung führen kann. In diesem Vortrag werden Ergebnisse vorgestellt, die den Einfluss von Kontaktrohrabstand, Drahtvorschub sowie Schweißspannung auf den Wasserstoffeintrag in Ein- und Mehrlagenschweißungen aus hochfestem Feinkornbaustahl zeigen. Dabei wird der konventionelle Lichtbogen mit dem modernen modifizierten Sprühlichtbogen verglichen. T2 - Sitzung des NA 092-00-05 GA „Gemeinschaftsarbeitsausschuss NAS/NMP: Zerstörungsfreie Prüfung von Schweißverbindungen (DVS AG Q 4/Q 4.1)“ CY - Berlin, Germany DA - 08.03.2017 KW - Wasserstoffkonzentration KW - MAG-Schweißen KW - Hochfester Feinkornbaustahl KW - Schweißparameter PY - 2017 AN - OPUS4-39395 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaupp, Thomas T1 - Einfluss von Konstruktion und Wasserstoff auf die Kaltrissbildung hochfester Feinkornbaustähle N2 - Der konstruktive Leichtbau erfordert den zunehmenden Einsatz hochfester Feinkornbaustähle mit Streckgrenzen ≥ 690 MPa. Neben den durch die Wandstärkenreduzierung erreichbaren Einsparungen an Ressourcen und Fertigungszeit lässt sich eine weitere Minimierung der Schweißzeit und -kosten mittels abgesenkter Schweißnahtvolumina erreichen. Hierzu wurden moderne Lichtbogenprozesse, wie bspw. der modifizierte Sprühlichtbogen (Mod.SLB), mit erhöhter Abschmelzleistung entwickelt, mit denen auch enge Nahtspalte bzw. Nahtöffnungswinkel geschweißt werden können. Hochfeste Verbindungen unterliegen zunehmend erhöhten Anforderungen in Bezug auf die schweißtechnische Verarbeitung und der resultierenden Bauteilperformance und sicherheit. Dies gilt insbesondere beim Bauteil-schweißen mittels solcher Hochleistungsverfahren in Verbindung mit engen Nahtspalten. In der vorliegenden Arbeit soll dieser Herausforderung durch Klärung der Einflüsse auf die Kaltrissbildung bei einem hochfesten Feinkornbaustahl S960QL Rechnung getragen werden. Für die Kaltrissprüfung werden entsprechende adaptierte Proben analog dem selbstbeanspruchenden TEKKEN-Test verwendet und hinsichtlich Rissbildung, Gefüge, Gehalt an diffusiblem Wasserstoff und Eigenspannungen analysiert. Die Variation der Nahtöffnungswinkel der Prüfnähte erfolgt zwischen 30° und 60°. Zur Vermeidung wasserstoffunterstützter Kaltrissbildung wird die Wirksamkeit einer Nachwärmprozedur aus der Schweißwärme heraus untersucht. Als Ergebnis zeigen die Schweißgüter, die an reduziertem Nahtöffnungs-winkel erzeugt wurden, im Mittel etwas höhere Wasserstoffkonzentrationen. Zudem ist an diesen Schweißgütern eine vermehrte Mikro- als auch Makrorissbildung festzustellen. An allen Proben, die nicht nachgewärmt wurden, treten Kerbrisse aufgrund von Kaltrissbildung auf, deren Vermeidung sich durch ein Nachwärmen unmittelbar nach dem Schweißen als besonders effektiv darstellte. T2 - DVS Congress - Große Schweißtechnische Tagung CY - Online meeting DA - 14.09.2020 KW - Hochfester Feinkornbaustahl KW - MAG-Schweißen KW - Kaltriss KW - TEKKEN PY - 2020 AN - OPUS4-51258 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaupp, Thomas T1 - Einfluss von Schweißprozessparametern auf den Wasserstoffeintrag in Ein- und Mehrlagenschweißungen aus hochfestem Feinkornbaustahl N2 - Um den wachsenden Anforderungen nach Leichtbau und Ressourceneffizienz im Kran-, Nutzfahrzeug- und Brückenbau gerecht zu werden, kommen in diesen Industriebranchen vermehrt hochfeste Feinkornbaustähle mit Streckgrenzen von mehr als 690 MPa zum Einsatz. Allerdings erfordern diese Stähle bei der schweißtechnischen Verarbeitung äußerste Sorgfalt, weil gerade die Sensibilität gegenüber einer Degradation der mechanischen Eigenschaften, durch den im Lichtbogen aufgenommenen Wasserstoff, mit steigender Festigkeit signifikant zunimmt und zur wasserstoffunterstützten Kaltrissbildung führen kann. In diesem Vortrag werden Ergebnisse vorgestellt, die den Einfluss von Kontaktrohrabstand, Drahtvorschub sowie Schweißspannung auf den Wasserstoffeintrag in Ein- und Mehrlagenschweißungen aus hochfestem Feinkornbaustahl zeigen. Dabei wird der konventionelle Lichtbogen mit dem modernen modifizierten Sprühlichtbogen verglichen. Ziel ist es, durch geeignete Wärmeführungen die Wasserstoffkonzentration in Schweißverbindungen zu reduzieren, um somit die Gefahr einer wasserstoffunterstützten Kaltrissbildung zu minimieren. T2 - MDDK – Master-, Diplomanden- und Doktorandenkolloquium CY - Universität Magdeburg, Germany DA - 26.01.2017 KW - Hochfeste Feinkornbaustähle KW - Wasserstoffeintrag KW - MAG-Schweißen KW - Modifizierter Sprühlichtbogen KW - Schweißprozessparameter PY - 2017 AN - OPUS4-39051 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaupp, Thomas T1 - Einfluss der Wärmeführung auf die Wasserstoffverteilung in Schweißverbindungen aus hochfestem Feinkornbaustahl N2 - In vielen Industriebranchen werden zunehmend hochfeste Feinkornbaustähle mit Streckgrenzen ≥ 690 MPa eingesetzt. Allerdings werden mit zunehmender Festigkeit deutlich höhere Anforderungen an deren schweißtechnische Verarbeitung gestellt, da gerade die Sensibilität gegenüber einer Degradation der mechanischen Eigenschaften, durch den beim Schweißen aufgenommenen Wasserstoff, mit steigender Festigkeit stark zunimmt. In der vorliegenden Präsentation sind Ergebnisse aus vergleichenden Untersuchungen mit konventionellem Übergangslichtbogen und modifiziertem Sprühlichtbogen mit reduziertem Nahtöffnungswinkel hinsichtlich der Wasserstoffaufnahme beim Schweißen unter Variation von Streckenenergie, Arbeitstemperatur und Nachwärmprozedur dargestellt. Grundsätzlich ist den erarbeiteten Ergebnissen zu entnehmen, dass im Schweißgut von Stumpfstoßverbindungen mit reduziertem Nahtöffnungswinkel erhöhte mittlere Wasserstoffkonzentrationen vorliegen. Geeignete Wärmeführungen führten zu einer signifikanten Reduzierung der Wasserstoffkonzentration beim Einsatz der Nahtkonfiguration mit abgesenktem Nahtöffnungswinkel. Dabei erwies sich eine Nachwärmprozedur aus der Schweißwärme heraus als zielführend. Des weiteren sind Gradienten der Wasserstoffkonzentration in Blechdickenrichtung aufgezeigt. T2 - Forschungsseminar CY - Otto-von-Guericke-Universität, Magdeburg, Germany DA - 17.01.2018 KW - Hochfester Feinkornbaustahl KW - Wasserstoff KW - Wärmeführung KW - MAG-Schweißen KW - Nachwärmung KW - Wasserstoffgradient PY - 2018 AN - OPUS4-43807 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaupp, Thomas T1 - Zur Bewertung der Kaltrissempfindlichkeit moderner hochfester Feinkornbaustähle mit dem Implant-Test N2 - Der Implant-Test nach ISO 17642-3 gehört zur Gruppe der fremdbeanspruchten Kaltrisstests, bei dem eine äußere Beanspruchung auf einen zylindrischen Stab (Implant-Probe) definiert aufgebracht wird. Mit dieser Kaltrissprüfung wurden vergleichende Analysen zur Kaltrissempfindlichkeit der modernen hochfesten Feinkornbaustähle S960MC und S960QL durchgeführt. Zudem kamen sowohl Massiv- als auch Metallpulverfülldraht zur Variation der Wasserstoffkonzentration zum Einsatz. Der Einsatz des modernen modifizierten Sprühlichtbogens ermöglichte außerdem die Untersuchung des Einbrandprofils auf die Kaltrissbildung. T2 - Sitzung des NA 092-00-05 GA „Gemeinschaftsarbeitsausschuss NAS/NMP: Zerstörende Prüfung von Schweißverbindungen (DVS AG Q 4/Q 4.1)“ CY - Hamm, Germany DA - 04.03.2020 KW - Hochfester Feinkornbaustahl KW - MAG-Schweißen KW - Wasserstoff KW - Kaltriss KW - Implant-Test PY - 2020 AN - OPUS4-50506 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaupp, Thomas A1 - Rhode, Michael T1 - Influence of welding parameters on diffusible hydrogen content in high-strength steels using modified spray arc process N2 - In order to satisfy the growing requirements towards lightweight design and resource efficiency in modern steel constructions, e.g. mobile cranes and bridges, high-strength steels with typical yield strength ≥ 690 MPa are coming into use to an increasing extent. However, these steels require special treatment in welding. The susceptibility for degradation of the mechanical properties in presence of hydrogen increases significantly with increasing yield strength. In case of missing knowledge about how and which amount of hydrogen is uptaken during welding, hydrogen assisted cracking can be a negative consequence. Moreover, modern weld technology like the modified spray arc process enables welding of narrower weld seams. In this context, a reduced number of weld beads, volume and total heat input are technical and economic benefits. This work presents the influence of welding parameters on the diffusible hydrogen content in both (1) single-pass and (2) multi-layer welds. Different hydrogen concentrations were detected by varied contact tube distance, wire feed speed, arc length as well as varied arc type (transitional arc and modified spray arc). The results showed, that all welding parameters had significant influence on the diffusible hydrogen concentration in the single-pass welds. By increasing the number of weld beads in case of multi-layer welding, the hydrogen concentration have been substantially reduced. Whereby, differences in hydrogen concentrations between both arc types are present. T2 - IIW Intermediate Meeting: Commission II-A CY - Trollhättan, Sweden DA - 06.03.2017 KW - Hydrogen concentration KW - MAG Welding KW - High-strength steel KW - Welding parameters PY - 2017 AN - OPUS4-39396 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaupp, Thomas T1 - Einfluss der Wärmeführung auf die Wasserstoffkonzentration im Schweißgut hochfester Feinkornbaustähle beim Einsatz des modifizierten Sprühlichtbogens N2 - Um den wachsenden Anforderungen an den stofflichen und konstruktiven Leichtbau sowie den Forderungen nach Ressourceneffizienz Rechnung zu tragen, werden in vielen Industriebranchen zunehmend höherfeste Feinkornbaustähle mit Streckgrenzen ≥ 690 MPa eingesetzt. Allerdings werden mit zunehmender Festigkeit deutlich höhere Anforderungen an deren schweißtechnische Verarbeitung gestellt, da gerade die Sensibilität gegenüber einer Degradation der mechanischen Eigenschaften, durch den beim Schweißen aufgenommenen Wasserstoff, mit steigender Festigkeit stark zunimmt. In der vorliegenden Arbeit erfolgten vergleichende Untersuchungen mit konventionellem Übergangslichtbogen und modifiziertem Sprühlichtbogen mit reduziertem Nahtöffnungswinkel hinsichtlich der Wasserstoffaufnahme beim Schweißen unter Variation von Streckenenergie, Arbeitstemperatur und Nachwärmprozedur. Grundsätzlich ist den erarbeiteten Ergebnissen zu entnehmen, dass im Schweißgut von Stumpfstoßverbindungen mit reduziertem Nahtöffnungswinkel erhöhte mittlere Wasserstoffkonzentrationen vorliegen. Geeignete Wärmeführungen führten zu einer signifikanten Reduzierung der Wasserstoffkonzentration beim Einsatz der Nahtkonfiguration mit abgesenktem Nahtöffnungswinkel. Dabei erwies sich eine Nachwärmprozedur aus der Schweißwärme heraus als zielführend. T2 - 10. Rostocker Schweißtage, Moderne Fügetechnologien - Erfahrungen und aktuelle Entwicklungen CY - Rostock, Germany DA - 21.11.2017 KW - Hochfester Feinkornbaustahl KW - MAG-Schweißen KW - Wasserstoffkonzentration KW - Wärmeführung KW - Nachwärmung PY - 2017 AN - OPUS4-43046 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaupp, Thomas T1 - Determination of hydrogen distributions in iron and steel using neutron radiography and tomography T2 - 79. DPG-Jahrestagung und DPG-Frühjahrstagung CY - Berlin, Germany DA - 2015-03-15 PY - 2015 AN - OPUS4-32880 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaupp, Thomas T1 - In-situ load analysis in multi-run welding using LTT filler materials T2 - 68th IIW Annual Assembly and International Conference: Commission II-A and Commission X CY - Helsinki, Finland DA - 2015-06-28 PY - 2015 AN - OPUS4-33675 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaupp, Thomas T1 - Vergleich von Schweißeigenspannungen bei vergüteten und thermomechanisch gewalzten hochfesten Feinkornbaustählen T2 - BAM Alumni Kolloquium CY - Berlin, Germany DA - 2014-09-11 PY - 2014 AN - OPUS4-31416 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaupp, Thomas T1 - Einfluss der Wärmeführung auf die Wasserstoffverteilung im Schweißgut hochfester Feinkornbaustähle N2 - In vielen Industriebranchen werden zunehmend hochfeste Feinkornbaustähle mit Streckgrenzen ≥ 690 MPa eingesetzt. Allerdings werden mit zunehmender Festigkeit deutlich höhere Anforderungen an deren schweißtechnische Verarbeitung gestellt, da gerade die Sensibilität gegenüber einer Degradation der mechanischen Eigenschaften, durch den beim Schweißen aufgenommenen Wasserstoff, mit steigender Festigkeit stark zunimmt. In der vorliegenden Präsentation sind Ergebnisse aus vergleichenden Untersuchungen mit konventionellem Übergangslichtbogen und modifiziertem Sprühlichtbogen mit reduziertem Nahtöffnungswinkel hinsichtlich der Wasserstoffaufnahme beim Schweißen unter Variation von Streckenenergie, Arbeitstemperatur und Nachwärmprozedur dargestellt. Grundsätzlich ist den erarbeiteten Ergebnissen zu entnehmen, dass im Schweißgut von Stumpfstoßverbindungen mit reduziertem Nahtöffnungswinkel erhöhte mittlere Wasserstoffkonzentrationen vorliegen. Geeignete Wärmeführungen führten zu einer signifikanten Reduzierung der Wasserstoffkonzentration beim Einsatz der Nahtkonfiguration mit abgesenktem Nahtöffnungswinkel. Dabei erwies sich eine Nachwärmprozedur aus der Schweißwärme heraus als zielführend. Des weiteren sind Gradienten der Wasserstoffkonzentration in Blechdickenrichtung aufgezeigt. T2 - Sitzung des NA 092-00-05 GA „Gemeinschaftsarbeitsausschuss NAS/NMP: Zerstörende Prüfung von Schweißverbindungen (DVS AG Q 4/Q 4.1)“ CY - Halle (Saale), Germany DA - 14.03.2018 KW - Hochfester Feinkornbaustahl KW - MAG-Schweißen KW - Wasserstoffkonzentration KW - Nachwärmung KW - Wärmeführung PY - 2018 AN - OPUS4-44899 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaupp, Thomas T1 - Vergleich von Schweißeigenspannungen bei vergüteten und thermomechanisch gewalzten hochfesten Feinkornbaustählen T2 - MDDK-, Master-, Diplomanden- und Doktorandenkolloguium CY - Magdeburg, Germany DA - 2013-07-04 PY - 2013 AN - OPUS4-28807 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaupp, Thomas T1 - Hydrogen distribution in multi-layer welds of steel S960QL N2 - High-strength low-alloyed (HSLA) steels with yield strength ≥ 690 MPa have increasing im-portance in steel construction and civil engineering. However, weld processing of those steels is a major challenge. The susceptibility for degradation of mechanical properties of weld joints sig-nificantly increases in presence of hydrogen and can result in hydrogen assisted cracking (HAC). Generally, risk for HAC increases with increasing yield strength of HSLA steels. To min-imize the incidence of HAC, it is essential to gain knowledge about both the (1) absorbed hydro-gen amount and its distribution in the weld seam and (2) options to lower the amount of intro-duced hydrogen. Existing standards recommend heat treatment procedures (interpass tempera-ture or post weld heat treatment) to reduce the diffusible hydrogen concentration in weldments. In this context, different weld seam geometries should be considered. For HSLA steel fabrication weld processing with seam opening angles of 45° to 60° is typical. Modern weld technologies allow welding with seam opening angles of 30° - reduced welding time and costs. In the present study, the hydrogen distribution in multi-layer welds of a 960 MPa HSLA steel was analysed. Influence of different seam opening angles as well as heat input, interpass temperature and post weld heat treatments were investigated. The welded samples were quenched in ice water imme-diately after welding and subsequently stored in liquid nitrogen. After defined warming up, small specimens were machined from the weld seam by water jet cutting. The diffusible hydrogen concentration was measured by carrier gas hot extraction with coupled mass spectrometer. The results showed, that low heat input and post weld heat treatment procedures can lower hydrogen concentrations in welds. Furthermore, a gradient of the hydrogen concentration was identified with increasing weld pool depth. By varying the seam opening angles different hydrogen concen-trations were measured. T2 - 3rd International Conference on Metals & Hydrogen CY - Ghent, Belgium DA - 29.05.2018 KW - Hydrogen KW - Welding KW - High-strength steels KW - Heat treatment KW - Carrier gas hot extraction PY - 2018 AN - OPUS4-45076 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaupp, Thomas T1 - Bewertung der Kaltrissempfindlichkeit beim Schweißen höherfester Feinkornbaustähle mittels Implant-Test N2 - Höherfester Feinkornbaustahl mit Streckgrenzen von 960 MPa findet in vielen Industriebranchen zunehmend Einsatz. Allerdings werden mit zunehmender Festigkeit deutlich höhere Anforderungen an deren schweißtechnische Verarbeitung gestellt. Die Sensibilität gegenüber einer Degradation der mechanischen Eigenschaften kann durch den beim Schweißen aufgenommenen diffusiblen Wasserstoff zunehmen. Eine mögliche wasserstoffunterstützte Kaltrissbildung ist die Folge. In dem Vortrag werden vergleichende Untersuchungen von konventionellem Übergangslichtbogen und modifiziertem Sprühlichtbogen mittels Implant-Test vorgestellt. Der Einsatz beider Lichtbögen führt zu ähnlichen kritischen Implantspannungen. Jedoch kommt es beim modifiziertem Sprühlichtbogen zu einer zeitverzögerten Rissbildung. Zudem unterscheidet sich die Bruchtopographie der beiden Fälle. T2 - Forschungsseminar CY - Otto-von-Guericke-Universität Magdeburg, Gemany DA - 27.06.2018 KW - Höherfester Stahl KW - Wasserstoff KW - Implant-Test KW - MAG-Schweißen KW - Spannung PY - 2018 AN - OPUS4-45309 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaupp, Thomas T1 - Modified TEKKEN test for studying hydrogen-assisted cracking in high-strength structural steels N2 - In the present work, the complex interactions of the influences of material, welding process and seam configuration and the restraint of shrinkage on the residual stresses and the influence of diffusible hydrogen on hydrogen-assisted cracking (HAC) in the high-strength steel S960QL were investigated. For this purpose, self-restraint specimens were selected using the TEKKEN test with correspondingly adapted seam opening angles and a restraint intensity of approx. RFy = 17 kN/(mm·mm). The variation of the seam opening angle of the test seams was between 30° and 60°. Due to the comparatively high restraint of shrinkage in the transverse direction of the weld, high tensile residual stresses in the weld metal were expected for both weld seam configurations. In addition, a dehydrogenation heat treatment (DHT) for HAC prevention under restraint of shrinkage was verified. In order to keep distortion and heat input as low as possible, the seam geometries were manufactured from the solid material by means of electric discharge machining (EDM). Both, solid wire and metal cored wire were used. In addition, hydrogen was added to the shielding gas in solid wire welding to increase diffusible hydrogen concentration. Moreover, welding residual stresses at the weld seam surface, which were measured by using mobile X-ray diffraction, were taken into account to evaluate the HAC behavior. DHT was carried out at 250 °C for 4 h in an external furnace. T2 - 73rd IIW Annual Assembly: Commission II-A CY - Online meeting DA - 15.07.2020 KW - High-strength steel KW - Gas metal arc welding KW - Hydrogen-assisted cracking KW - TEKKEN test KW - Residual stresses KW - Dehydrogenation heat treatment PY - 2020 AN - OPUS4-51035 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaupp, Thomas A1 - Burger, S. T1 - Abschlussbericht zum Projekt: „Ermittlung geeigneter Wärmeführungen zur Wasserstoffreduktion beim Schweißen höherfester Feinkornbaustähle mit modifiziertem Sprühlichtbogen“ N2 - Dieses Dokument fasst die Ergebnisse des BAM-Projektes "Ermittlung geeigneter Wärmeführungen zur Wasserstoffreduktion beim Schweißen höherfester Feinkornbaustähle mit modifiziertem Sprühlichtbogen" im Rahmen des Fachausschusses 1 "Schweißmetallurgie & Werkstoffverhalten" des DVS e. V. zusammen. T2 - Sitzung des Fachausschusses 01 "Schweißmetallurgie & Werkstoffverhalten" der Forschungsvereinigung Schweißen und verwandte Verfahren des DVS e. V. CY - Magdeburg, Germany DA - 19.10.2017 KW - Hochfester Feinkornbaustahl KW - Wasserstoff KW - MAG-Schweißen PY - 2017 AN - OPUS4-53674 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaupp, Thomas T1 - Kaltrissbildung in Mehrlagenschweißungen - Einflussanalyse von Nahtgeometrie und Wärmeführung beim Einsatz modifizierter Sprühlichtbögen N2 - Ausgehend vom derzeit vorrangigen Einsatz in Mobilkranen, kommen höherfeste Feinkornbaustähle mit Streck-grenzen ab 960 MPa zunehmend auch in anderen modernen Stahlkonstruktionen zur Anwendung. Dies ist auf-grund aktueller Forderungen nach Energie- und Ressourceneffizienz im Sinne des konstruktiven Leichtbaus viel-fach notwendig. Die Verwendung höherfester Stähle sowie deren schweißtechnische Verarbeitung, insbesondere in sicherheitsrelevanten Tragstrukturen, erfordert ein tiefgreifendes Verständnis der Zusammenhänge zwischen Schweißverfahren, Wärmeeinbringung, Abkühlbedingungen sowie den daraus resultierenden metallurgischen Vor-gängen in der Schweißnaht und den nahtnahen Bereichen. Vorwiegend werden höherfeste Güten mittels MAG-Prozess geschweißt. Bedeutende Fortschritte in der Regelungstechnik führten unter den Herstellern von Schweiß-stromquellen in den letzten Jahren zur Entwicklung zahlreicher modifizierter Sprühlichtbogenprozesse (mod. SLB). Diese Prozesse ähneln sich in ihren Eigenschaften und ermöglichen die bekannten positiven Aspekte, wie Einspa-rung an Schweißzusatz sowie Schweiß- und Rüstzeit aufgrund der Möglichkeit reduzierter Nahtöffnungswinkel. Der mod. SLB bedingt zusammen mit einer anderen Nahtgeometrie veränderte Naht- und Schweißraupenquerschnitte sowie einen abweichenden Lagenaufbau. Diese wirtschaftlich-technisch attraktive Möglichkeit reduzierter Nahtöff-nungswinkel findet in den Regelwerken zur schweißtechnischen Verarbeitung höherfester Feinkornbaustähle unter Vermeidung von Kaltrissbildung bisher keine Berücksichtigung. Dabei gilt es, gerade die Interaktion der Hauptein-flussgrößen auf die Kaltrissbildung unter reduziertem Nahtöffnungswinkel zu betrachten. Im Rahmen zweier AiF-Forschungsvorhaben (IGF-Nr. 17.978 N, 18.596 BR) wurde daher der Einfluss der Wärmeführung anhand verglei-chender Mehrlagenschweißungen mittels konventionellem Übergangslichtbogen und mod. SLB mit angepasster Nahtkonfiguration auf schweißbedingte Beanspruchungen sowie auf die Wasserstoffkonzentration im Schweißgut untersucht. T2 - DVS Congress 2018 - Große Schweißtechnische Tagung CY - Friedrichshafen, Germany DA - 17.09.2018 KW - Kaltriss KW - Hochfester Feinkornbaustahl KW - MAG-Schweißen PY - 2018 AN - OPUS4-45976 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -