TY - JOUR A1 - Rhode, Michael A1 - Schaupp, Thomas A1 - Münster, C. A1 - Mente, Tobias A1 - Kannengießer, Thomas A1 - Böllinghaus, Thomas T1 - Hydrogen determination in welded specimens by carrier gas hot extraction - a review on the main parameters and their effects on hydrogen measurement N2 - Carrier gas hot extraction (CGHE) is a commonly applied technique for determination of hydrogen in weld joints using a thermal conductivity detector (TCD) for hydrogen measurement. The CGHE is based on the accelerated hydrogen effusion due to thermal activation at elevated temperatures. The ISO 3690 standard suggests different specimen geometries as well as necessary minimum extraction time vs. temperature. They have the biggest influence on precise hydrogen determination. The present study summarizes the results and experience of numerous test runs with different specimen temperatures, geometries (ISO 3690 type B and small cylindrical samples), and factors that additionally influence hydrogen determination. They are namely specimen surface (polished/as-welded), limited TCD sensitivity vs. specimen volume, temperature measurement vs. effects of PI-furnace controller, as well as errors due to insufficient data assessment. Summarized, the temperature is the driving force of the CGHE. Two different methods are suggested to increase the heating rate up to the desired extraction temperature without changing the experimental equipment. Suggestions are made to improve the reliability of hydrogen determination depended on the hydrogen signal stability during extraction accompanied by Evaluation of the recorded data. Generally, independent temperature measurement with dummy specimens is useful for further data analysis, especially if this data is used for calculation of trapping kinetics by thermal desorption analysis (TDA). KW - Hydrogen KW - Carrier gas hot extraction KW - Experimental design KW - Thermal conductivity device PY - 2019 DO - https://doi.org/10.1007/s40194-018-0664-9 SN - 0043-2288 VL - 63 IS - 2 SP - 511 EP - 526 PB - Springer CY - Berlin, Heidelberg AN - OPUS4-47603 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaupp, Thomas A1 - Kannengießer, Thomas T1 - Heißriss-Forschung an der BAM - Ein kleiner Überblick N2 - Die Vermeidung von Heißrissen beim Schweißen ist für die Sicherheit geschweißter Komponenten unerlässlich. Die Entstehung von Heißrissen wird durch die komplexe Interaktion von Schweißprozess, Metallurgie und der konstruktiven Umgebung beschrieben. Bislang wurden mehr als 140 Heißrisstests entwickelt, um die Neigung gegenüber einer Rissbildung festzulegen. Grundsätzlich werden diese in selbstbeanspruchende und fremdbeanspruchte Heißrisstests eingeteilt. Der Vortrag gibt einen Überblick über Forschungsthemen der BAM, welche sich in den letzten Jahren hauptsächlich mit den metallurgischen als auch mit den konstruktiven Einflüssen auf die Rissbildung beschäftigt haben. Von austenitischen und ferritischen Werkstoffen, über neuentwickelte LTT-Legierungen bis hin zur in-situ Radiographie zur Überwachung des Risswachstums während des Schweißens wird ein breites Forschungsspektrum aufgezeigt. Zum Abschluss ist ein Ausblick für zukünftige Forschungsfelder gegeben. Diese Arbeiten konzentrieren sich auf die zwei- und dreidimensionale bildliche Charakterisierung von (Mikro-)Heißrissen in innovativen Werkstoffen zur Erweiterung bestehender Modellvorstellungen zum Rissphänomen. T2 - Forschungsseminar CY - Technische Universität Clausthal, Clausthal, Germany DA - 31.01.2018 KW - Heißriss KW - Austenit KW - Ferrit KW - LTT-Legierung KW - Prüfverfahren PY - 2018 AN - OPUS4-44019 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaupp, Thomas A1 - Schröpfer, Dirk A1 - Kannengießer, Thomas T1 - Kaltrissbildung in Mehrlagenschweißungen - Einflussanalyse von Nahtgeometrie und Wärmeführung beim Einsatz modifizierter Sprühlichtbögen N2 - Ausgehend vom derzeit vorrangigen Einsatz in Mobilkranen, kommen höherfeste Feinkornbaustähle mit Streckgrenzen ab 960 MPa zunehmend auch in anderen modernen Stahlkonstruktionen zur Anwendung. Dies ist aufgrund aktueller Forderungen nach Energie- und Ressourceneffizienz im Sinne des konstruktiven Leichtbaus vielfach notwendig. Die Verwendung höherfester Stähle sowie deren schweißtechnische Verarbeitung, insbesondere in sicherheitsrelevanten Tragstrukturen, erfordert ein tiefgreifendes Verständnis der Zusammenhänge zwischen Schweißverfahren, Wärmeeinbringung, Abkühlbedingungen sowie den daraus resultierenden metallurgischen Vorgängen in der Schweißnaht und den nahtnahen Bereichen. Vorwiegend werden höherfeste Güten mittels MAG-Prozess geschweißt. Bedeutende Fortschritte in der Regelungstechnik führten unter den Herstellern von Schweißstromquellen in den letzten Jahren zur Entwicklung zahlreicher modifizierter Sprühlichtbogenprozesse (mod. SLB). Diese Prozesse ähneln sich in ihren Eigenschaften und ermöglichen die bekannten positiven Aspekte, wie Einsparung an Schweißzusatz sowie Schweiß- und Rüstzeit aufgrund der Möglichkeit reduzierter Nahtöffnungswinkel. Der mod. SLB bedingt zusammen mit einer anderen Nahtgeometrie veränderte Naht- und Schweißraupenquerschnitte sowie einen abweichenden Lagenaufbau. Diese wirtschaftlich-technisch attraktive Möglichkeit reduzierter Nahtöffnungswinkel findet in den Regelwerken zur schweißtechnischen Verarbeitung höherfester Feinkornbaustähle unter Vermeidung von Kaltrissbildung bisher keine Berücksichtigung. Dabei gilt es, gerade die Interaktion der Haupteinflussgrößen auf die Kaltrissbildung unter reduziertem Nahtöffnungswinkel zu betrachten. Im Rahmen zweier AiF-Forschungsvorhaben (IGF-Nr. 17.978 N, 18.596 BR) wurde daher der Einfluss der Wärmeführung anhand vergleichender Mehrlagenschweißungen mittels konventionellem Übergangslichtbogen und mod. SLB mit angepasster Nahtkonfiguration auf schweißbedingte Beanspruchungen sowie auf die Wasserstoffkonzentration im Schweißgut untersucht. T2 - DVS Congress 2018 - Große Schweißtechnische Tagung CY - Friedrichshafen, Germany DA - 17.09.2018 KW - Kaltriss KW - Hochfester Feinkornbaustahl KW - MAG-Schweißen PY - 2018 SN - 978-3-96144-036-8 VL - 344 SP - 73 EP - 78 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-45977 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Kannengießer, Thomas A1 - Schaupp, Thomas ED - Brockmann, S. ED - Krupp, U. T1 - Wasserstoffunterstützte Kaltrissbildung in Schweißnähten hochfester Stahlgüten - Anforderungen an die Prüfung N2 - Wasserstoff kann eine Rissbildung u.U. auch noch nach Tagen in der Schweißnaht bewirken. Dabei stellen höherfeste Stähle etablierte Kaltrissprüftests vor Herausforderungen. Generell nimmt die zur Rissvermeidung tolerierbare Wasserstoffkonzentration mit zunehmender Festigkeit der Werkstoffe ab. Zudem verändern weiterentwickelte Schweißverfahren die Nahtgeometrie und Wärmeeinbringung und die Ausbildung risskritischer Mikrostrukturen (z.B. Wärmeeinflusszone). Am Beispiel des Implant- und Tekken-Tests werden die Einsatz- u. Anwendungsgrenzen bewertet. Zu berücksichtigen ist, dass beim Schweißen eine äußere mechan. Beanspruchung durch bauteilspezifische Steifigkeitsverhältnisse wirksam ist. Zusätzlich werden weiterführende Prüfverfahren zur Bestimmung der Wasserstoffkonzentration und -diffusion in Schweißnähten vorgestellt, wie die Trägergasheißextraktion (TGHE) für die Ermittlung der Wasserstoffkonzentration (ISO 3690) oder Hochtemperaturdiffusionskoeffizienten. Diese Werte sind für die schweißtechnische Praxis von großer Bedeutung, um Haltezeiten z.B. für das Wasserstoffarmglühen abzuleiten. T2 - Tagung Werkstoffprüfung 2021 CY - Online meeting DA - 02.12.2021 KW - Wasserstoff KW - Kaltrissprüfung KW - Schweißen KW - Stahl KW - Hochfest PY - 2021 SN - 978-3-941269-98-9 SP - 15 EP - 20 PB - Stahlinstitut VDEh CY - Düsseldorf AN - OPUS4-53900 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rhode, Michael A1 - Mente, Tobias A1 - Kannengießer, Thomas A1 - Schaupp, Thomas A1 - Zavdoveev, Anatoly T1 - Challenges for testing hydrogen-assisted cold cracking in weld seams of high-strength steel grades N2 - Hydrogen can cause weld cold cracking even days after fabrication. In this respect, higher strength steels present a challenge to established cold crack testing. In general, the tolerable hydrogen concentration for crack prevention decreases with increasing material strength. In addition, advanced welding processes require changes in weld geometry and heat input. This directly influences the formation of crack-critical microstructures, e.g. in hardened areas of the heat-affected zone. The limits of use and application of modern cold cracking tests are evaluated by (1) the externally loaded Implant-test and (2) the self-restraint Tekken-test. In particular, external mechanical stresses, which cause additional mechanical loads on the components during welding, must be considered due to the component-specific stiffness of high-strength steels. Accompanying test methods for determining hydrogen concentration and diffusion in welds are presented, such as carrier gas hot extraction for determining hydrogen concentration (ISO 3690) or temperature-dependent diffusion coefficients. These values are of great importance for a holistic approach to the evaluation of the cold cracking sensitivity of high strength steels. KW - Hydrogen KW - Welding KW - Cold cracking test KW - High-strength steel PY - 2024 DO - https://doi.org/10.37434/tpwj2024.08.01 SN - 0957-798X VL - 2024 IS - 8 SP - 3 EP - 9 PB - International Association "Welding" CY - Kyiv, Ukraine AN - OPUS4-60946 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schaupp, Thomas A1 - Schröpfer, Dirk A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Welding residual stresses in 960 MPa grade QT and TMCP high-strength steels N2 - High-strength steels with yield strengths ≥ 690 MPa are becoming increasingly significant for modern steel constructions. Both quenched and tempered (QT) high-strength steels and steels produced by the thermo-mechanically controlled process (TMCP) are currently available. TMCP-steels are usually provided with a typical mill scale. Apart from the manufacturing process these steels differ also in their chemical composition. The influence of these differences are investigated here with focus on the residual stresses formed during TIG welding. Bead on plate welds have shown characteristic residual stress distributions depending on the type of steel as well as on the heat input and preheat temperature. The following work demonstrates that the fluid flow, induced by the elements present in the mill scale, leads to a deeper penetration of the material. This can also lead to increased residual stresses in the surface of the weld and the HAZ. Furthermore, higher heat input and preheat temperature can induce higher tensile residual stresses − which are evident in the present study. KW - Residual stresses KW - High-strength steel KW - Welding KW - Mill scale KW - Phase transformation PY - 2017 DO - https://doi.org/10.1016/j.jmapro.2017.05.006 SN - 1526-6125 VL - 27 SP - 226 EP - 232 PB - ELSEVIER AN - OPUS4-40312 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Griesche, Axel A1 - Pfretzschner, Beate A1 - Schaupp, Thomas A1 - Kannengießer, Thomas A1 - Kardjilov, N. ED - Somerday, B. P. ED - Sofronis, P. T1 - Measurement of hydrogen distributions in metals by neutron radiography and tomography N2 - Neutron imaging has become a valuable tool for measuring hydrogen distributions qualitatively and quantitatively in metals. Hydrogen mass flow can be measured inside cm thick Steel samples with 10 s temporal resolution. Hydrogen accumulations around craclcs in embrittled iron samples can be visualized three-dimensionally. The gas pressure of hydrogen in crack cavities has been measured to be in the ränge of 5 MPa to 15 MPa. This quality of information allows new insights for the analysis of damage mechanisms on a micrometer scale, e.g., of hydrogen blistering. Further, this method is nondestructive and provides local information in situ and in three dimensions with a spatial resolution of 20 µm - 30 µm. T2 - International Hydrogen Conference 2016 CY - Jackson Lake Lodge, Wyoming, USA DA - 11.09.2017 KW - Hydrogen KW - Neutron imaging KW - Neutron radiography KW - Neutron tomography PY - 2017 SN - 978-0-7918-6138-7 DO - https://doi.org/10.1115/1.861387_ch46 SP - 416 EP - 422 AN - OPUS4-42505 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schaupp, Thomas A1 - Schröpfer, Dirk A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Welding residual stress distribution of quenched and tempered and thermo-mechanically hot rolled high strength steels N2 - Beside quenched and tempered (QT) high strength steels advanced technologies in steel manufacturing provide steels produced by the thermo-mechanical controlled process (TMCP) with yield strength of 960 MPa. These steels differ in the carbon and micro-alloying element content. With variation of heat control TIG-welded dummy seams on both steel types were performed. Analyses concerning microstructure and residual stress evolution due to welding showed typical stress distributions according to common concepts. Yet, the TMCP-steel shows higher residual stresses than the QT-steel. KW - Mill Scale KW - Quenched KW - Residual Stress KW - Tempered High Strength Steel KW - Thermo-Mechanical Controlled Process KW - Welding PY - 2014 DO - https://doi.org/10.4028/www.scientific.net/AMR.996.457 SN - 1022-6680 SN - 1662-8985 VL - 996 SP - 457 EP - 462 PB - Trans Tech Publ. CY - Zurich AN - OPUS4-31443 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schaupp, Thomas A1 - Ernst, W. A1 - Spindler, H. A1 - Kannengießer, Thomas T1 - Hydrogen-assisted cracking of GMA welded 960 MPa grade high-strength steels N2 - High-strength steels with yield strength of 960 MPa are susceptible to hydrogen-assisted cracking (HAC) during welding processing. In the present paper, the implant test is used to study HAC in a quenched and tempered steel S960QL and a high-strength steel produced by thermo-mechanical controlled process S960MC. Welding is performed using the gas metal arc welding process. Furthermore, diffusible hydrogen concentration (HD) in arc weld metal is determined. Based on the implant test results, lower critical stress (LCS) for complete fracture, critical implant stress for crack initiation, and embrittlement index (EI) are determined. At HD of 1.66 ml/100 g, LCS is 605 MPa and 817 MPa for S960QL and S960MC, respectively. EI is 0.30 and 0.46 for S960QL and S960MC, respectively. Fracture surfaces of S960QL show higher degradation with reduced deformation. Both, higher EI of S960MC and fractography show better resistance to HAC in the HAZ of S960MC compared to S960QL. KW - High-strength steel KW - Welding KW - Diffusible hydrogen KW - Hydrogen-assisted cracking KW - Heat-affected zone KW - Implant test PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-510307 DO - https://doi.org/10.1016/j.ijhydene.2020.05.077 SN - 0360-3199 VL - 45 IS - 38 SP - 20080 EP - 20093 PB - Elsevier Ltd CY - Amsterdam, NL AN - OPUS4-51030 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaupp, Thomas A1 - Schröpfer, Dirk A1 - Schröder, Nina A1 - Kannengießer, Thomas T1 - Einfluss von Konstruktion und Wasserstoff auf die Kaltrissbildung hochfester Feinkornbaustähle N2 - Der konstruktive Leichtbau erfordert den zunehmenden Einsatz hochfester Feinkornbaustähle mit Streckgrenzen ≥ 690 MPa. Neben den durch die Wandstärkenreduzierung erreichbaren Einsparungen an Ressourcen und Fertigungszeit lässt sich eine weitere Minimierung der Schweißzeit und -kosten mittels abgesenkter Schweißnahtvolumina erreichen. Hierzu wurden moderne Lichtbogenprozesse, wie bspw. der modifizierte Sprühlichtbogen (Mod.SLB), mit erhöhter Abschmelzleistung entwickelt, mit denen auch enge Nahtspalte bzw. Nahtöffnungswinkel geschweißt werden können. Hochfeste Verbindungen unterliegen zunehmend erhöhten Anforderungen in Bezug auf die schweißtechnische Verarbeitung und der resultierenden Bauteilperformance und sicherheit. Dies gilt insbesondere beim Bauteilschweißen mittels solcher Hochleistungsverfahren in Verbindung mit engen Nahtspalten. In der vorliegenden Arbeit soll dieser Herausforderung durch Klärung der Einflüsse auf die Kaltrissbildung bei einem hochfesten Feinkornbau-stahl S960QL Rechnung getragen werden. Für die Kaltrissprüfung werden entsprechende adaptierte Proben analog dem selbstbeanspruchenden TEKKEN-Test verwendet und hinsichtlich Rissbildung, Gefüge, Gehalt an diffusiblem Wasserstoff und Eigenspannungen analysiert. Die Variation der Nahtöffnungswinkel der Prüfnähte erfolgt zwischen 30° und 60°. Zur Vermeidung wasserstoffunterstützter Kaltrissbildung wird die Wirksamkeit einer Nachwärmprozedur aus der Schweißwärme heraus untersucht. Als Ergebnis zeigen die Schweißgüter, die an reduziertem Nahtöffnungswinkel erzeugt wurden, im Mittel etwas höhere Wasserstoffkonzentrationen. Zudem ist an diesen Schweißgütern eine vermehrte Mikro- als auch Makrorissbildung festzustellen. An allen Proben, die nicht nachgewärmt wurden, treten Kerbrisse aufgrund von Kaltrissbildung auf, deren Vermeidung sich durch ein Nachwärmen unmittelbar nach dem Schweißen als besonders effektiv darstellte. T2 - DVS Congress 2020 - Große Schweißtechnische Tagung CY - Online meeting DA - 14.09.2020 KW - Hochfester Feinkornbaustahl KW - MAG-Schweißen KW - Kaltriss KW - Wasserstoff KW - TEKKEN PY - 2020 SN - 978-3-96144-098-6 VL - 365 SP - 564 EP - 570 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-51259 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schaupp, Thomas A1 - Kannengießer, Thomas A1 - Burger, S. A1 - Zinke, M. A1 - Jüttner, S. T1 - Einfluss der Wärmeführung auf die Wasserstoffkonzentration in geschweißten höherfesten Feinkornbaustählen beim Einsatz modifizierter Sprühlichtbogenprozesse N2 - Um den wachsenden Anforderungen an den stofflichen und konstruktiven Leichtbau sowie den Forderungen nach Ressourceneffizienz Rechnung zu tragen, werden in vielen Industriebranchen zunehmend höherfeste Feinkornbaustähle mit Streckgrenzen über 690 MPa eingesetzt. Allerdings werden mit zunehmender Festigkeit deutlich höhere Anforderungen an deren schweißtechnische Verarbeitung gestellt, da die Sensibilität gegenüber einer Herabsetzung der mechanischen Eigenschaften durch den beim Schweißen aufgenommenen diffusiblen Wasserstoff mit steigender Festigkeit zunehmen kann. In den vergleichenden Untersuchungen von konventionellem Übergangslichtbogen und modifiziertem Sprühlichtbogen bei reduziertem Nahtöffnungswinkel konnte gezeigt werden, dass die Schweißprozessparameter die in das Schweißgut eingebrachte Wasserstoffkonzentration beeinflussen. Grundsätzlich ist den erarbeiteten Ergebnissen zu entnehmen, dass im Schweißgut von Stumpfstoßverbindungen mit reduziertem Nahtöffnungswinkel erhöhte mittlere Wasserstoffkonzentrationen vorliegen. Diese können mit geeigneten Wärmeführungen signifikant reduziert werden. Dabei erwies sich eine Nachwärmprozedur aus der Schweißwärme heraus als zielführend. KW - Hochfester Stahl KW - Schutzgasschweißen KW - Wärmeführung KW - Wasserstoff KW - Rissbildung PY - 2018 VL - 70 IS - 5 SP - 290 EP - 297 PB - DVS Media GmbH CY - Düsseldorf AN - OPUS4-45109 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schaupp, Thomas A1 - Rhode, Michael A1 - Yahyaoui, Hamza A1 - Kannengießer, Thomas ED - Duprez, Lode T1 - Hydrogen distribution in multi-layer welds of steel S960QL N2 - High-strength low-alloyed (HSLA) steels with yield strength ≥ 690 MPa have increasing importance in steel construction and civil engineering. However, weld processing of those steels is a major challenge. The susceptibility for degradation of mechanical properties of weld joints significantly increases in presence of hydrogen and can result in hydrogen assisted cracking (HAC). Generally, risk for HAC increases with increasing yield strength of HSLA steels. To minimize the incidence of HAC, it is essential to gain knowledge about both the (1) absorbed hydrogen amount and its distribution in the weld seam and (2) options to lower the amount of introduced hydrogen. Existing standards recommend heat treatment procedures (interpass temperature or post weld heat treatment) to reduce the diffusible hydrogen concentration in weldments. In this context, different weld seam geometries should be considered. For HSLA steel fabrication weld processing with seam opening angles of 45° to 60° is typical. Modern weld technologies allow welding with seam opening angles of 30° - reduced welding time and costs. In the present study, the hydrogen distribution in multi-layer welds of a 960 MPa HSLA steel was analysed. Influence of different seam opening angles as well as heat input, interpass temperature and post weld heat treatments were investigated. The welded samples were quenched in ice water immediately after welding and subsequently stored in liquid nitrogen. After defined warming up, small specimens were machined from the weld seam by water jet cutting. The diffusible hydrogen concentration was measured by carrier gas hot extraction with coupled mass spectrometer. The results showed, that low heat input and post weld heat treatment procedures can lower hydrogen concentrations in welds. Furthermore, a gradient of the hydrogen concentration was identified with increasing weld pool depth. By varying the seam opening angles different hydrogen concentrations were measured. T2 - Third International Conference on Metals & Hydrogen CY - Ghent, Belgium DA - 29.05.2018 KW - Hydrogen concentration KW - Welding KW - High-strength steel KW - Heat treatment KW - carrier gas hot extraction PY - 2018 SN - 978-9-08179-422-0 SP - P44 AN - OPUS4-45358 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schaupp, Thomas A1 - Rhode, Michael A1 - Kannengießer, Thomas ED - Lippold, J. ED - Böllinghaus, Thomas ED - Richardson, I. T1 - Influence of welding parameters on diffusible hydrogen content in high-strength steel welds using modified spray arc process N2 - In order to satisfy the growing requirements towards lightweight design and resource efficiency in modern steel constructions, e.g., mobile cranes and bridges, high-strength steels with typical yield strength ≥ 690 MPa are coming into use to an increasing extent. However, these steels require special treatment in welding. The susceptibility for degradation of the mechanical properties in the presence of hydrogen increases significantly with increasing yield strength. In case of missing knowledge about how and the amount of hydrogen that is uptaken during welding, hydrogen-assisted cracking (HAC) can be a negative consequence. Moreover, modern weld technology like the modified spray arc process enables welding of narrower weld seams. In this context, a reduced number of weld beads, volume, and total heat input are technical and economical benefits. This work presents the influence of welding parameters on the diffusible hydrogen content in both (1) single-pass and (2) multi-layer welds. Different hydrogen concentrations were detected by varied contact tube distance, wire feed speed, arc length, and varied arc type (transitional arc and modified spray arc). The results show that all welding parameters have significant influence on the diffusible hydrogen concentration in the single-pass welds. By increasing the number of weld beads in case of multi-layer welding, the hydrogen concentration has been reduced. Whereby, differences in hydrogen concentrations between both arc types are present. KW - Hydrogen KW - MAG welding KW - High-strength steels KW - Process parameters PY - 2018 DO - https://doi.org/10.1007/s40194-017-0535-9 SN - 0043-2288 SN - 1878-6669 VL - 62 IS - 1 SP - 9 EP - 18 PB - Springer CY - Berlin Heidelberg AN - OPUS4-43864 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schröpfer, Dirk A1 - Kromm, Arne A1 - Schaupp, Thomas A1 - Kannengießer, Thomas T1 - Welding stress control in high-strength steel components using adapted heat control concepts N2 - High-strength steels are increasingly applied in modern steel constructions to meet today’s lightweight requirements. Welding of these steels demands a profound knowledge of the interactions between the welding process, cooling conditions, heat input, and the resulting metallurgical occurrences in the weld and its vicinity. Additionally, welding stresses may be detrimental for the safety and performance of high-strength steel component welds during fabrication and service, especially due to the high yield ratio. For a development of strategies to adjust welding heat control, all these effects should be considered, to reach a complete exploitation of the high-strength steel potential. In recent researches at BAM, multilayer GMAW experiments were performed with high-strength steels, in which cooling conditions and resulting microstructure were analyzed for varied heat control parameters. The application of a unique 3d-operating testing facility and X-ray diffraction measurements allowed the analysis of local stresses in the weld while welding and cooling under component relevant shrinkage restraints. As a result, correlations between material behavior, welding, and cooling condition and the arising multi-axial stresses and forces were found. Based on this study, statements for the development of adapted heat control concepts were derived, which are presented by means of specific analysis examples. KW - Residual stresses KW - GMA welding KW - Restraint KW - High-strength steels KW - Process parameters PY - 2019 DO - https://doi.org/10.1007/s40194-018-00691-z SN - 0043-2288 VL - 63 IS - 3 SP - 647 EP - 661 PB - Springer AN - OPUS4-48006 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Laquai, René A1 - Schaupp, Thomas A1 - Müller, Bernd R. A1 - Griesche, Axel A1 - Kupsch, Andreas A1 - Lange, Axel A1 - Kannengießer, Thomas A1 - Bruno, Giovanni T1 - 3D Crack analysis in hydrogen charged lean duplex stainless steel with synchrotron refraction CT N2 - Hydrogen in metals can cause a degradation of the mechanical properties, the so-called hydrogen embrittlement. In combination with internal stresses, hydrogen assisted cracking (HAC) can occur. This phenomenon is not completely understood yet. To better characterise the cracking behaviour, it is important to gain information about the evolution of the 3D crack network. For this purpose samples of lean duplex stainless steel were loaded with hydrogen by means of electrochemical charging and investigated by means of synchrotron refraction CT and SEM fractography after uniaxial tensile loading. Synchrotron refraction CT is an analyser-based imaging (ABI) technique. It uses a Si (111) single crystal as analyser, which is placed into the beam path between sample and detector. According to Bragg’s law only incident x-rays within a narrow range around the Bragg-angle are diffracted from the analyser into the detector. Hence, the analyser acts as an angular filter for the transmitted beam. This filtering allows to turn the refraction and scattering of x-rays into image contrast. Refraction occurs at all interfaces, where the density of the material changes and is more sensitive to density changes than the attenuation. Therefore, it is possible to detect smaller cracks than with classical x-ray imaging techniques, like CT, with comparable spacial resolution. It also visualises the 3D structure of the cracks and gains quantitative information about their morphology and distribution. Since cracks introduced by HAC are usually very small and have a small opening displacement, synchrotron refraction CT is expected to be well suited for imaging this cracking mechanism and can be a valuable tool to characterise the formation and the evolution of a 3D crack network. T2 - WCNDT 2016 CY - München, Germany DA - 13.06.2016 KW - X-ray refraction KW - Computed tomography KW - Hydrogen assisted cracking KW - Duplex stainless steel PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-366481 SN - 978-3-940283-78-8 VL - BB 158 SP - Tu.4.B.3, 1 EP - 9 AN - OPUS4-36648 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -