TY - JOUR A1 - Müllner, S. A1 - Held, T. A1 - Tichter, Tim A1 - Rank, P. A1 - Leykam, D. A1 - Jiang, W. A1 - Lunkenbein, T. A1 - Gerdes, T. A1 - Roth, C. T1 - Impact of Functional Groups in Reduced Graphene Oxide Matrices for High Energy Anodes in Lithium-Ion Batteries N2 - Most high capacity anode materials for lithium-ion batteries (LiB) require a carbonaceous matrix. In this context one promising material is reduced graphene oxide (rGO). Herein, we present the influence of different reduction degrees of rGO on its physico-chemical properties, such as crystallinity, specific surface area, electrical conductivity and electrochemical lithiation/delithiation behavior. It is found that a heat treatment under inert and reducing atmospheres increases the long-range order of rGO up to a temperature of 700 °C. At temperatures around 1000 °C, the crystallinity decreases. With decreasing oxygen content, a linear decrease in irreversible capacity during cycle 1 can be observed, along with a significant increase in electrical conductivity. This decrease in irreversible capacity can be observed despite an increase in specific surface area indicating the more significant influence of the oxygen content on the capacity loss. Consequently, the reversible capacity increases continuously up to a carbon content of 84.4 at% due to the thermal reduction. Contrary to expectations, the capacity decreases with further reduction. This can be explained by the loss of functional groups that will be lithiated reversibly, and a simultaneous reduction of long-range order, as concluded from dq/dU analysis in combination with XRD analysis. KW - Batteries KW - Functional Materials KW - Graphene Oxide PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-606852 DO - https://doi.org/10.1149/1945-7111/ace70a SN - 0013-4651 VL - 170 IS - 7 SP - 1 EP - 12 PB - The Electrochemical Society AN - OPUS4-60685 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Akhmetova, Irina A1 - Beyer, Sebastian A1 - Schutjajew, K. A1 - Tichter, T. A1 - Wilke, Manuel A1 - Prinz, Carsten A1 - B. Martins, Inês C. A1 - Al-Sabbagh, Dominik A1 - Roth, C. A1 - Emmerling, Franziska T1 - Cadmium benzylphosphonates - the close relationship between structure and properties N2 - Cadmium benzylphosphonate Cd(O3PBn)·H2O and its fluorinated derivates Cd(O3PBn-3F)·H2O, Cd(O3PBn-4F)·H2O, and Cd(O3PBn-F5)·H2O were synthesized mechanochemically. The Crystal structures of the compounds were determined based on powder X-ray diffraction (PXRD) data. The influence of the ligand substitution on the crystal structure of the metal phosphonate was determined. The hydrophobicity as a function of degree of fluorination was investigated using dynamic vapor sorption. KW - Mechanochemistry KW - Metal phosphonates KW - PXRD KW - DVS PY - 2019 DO - https://doi.org/10.1039/c9ce00776h VL - 21 SP - 5958 EP - 5964 PB - RSC Royal Society of Chemistry AN - OPUS4-49930 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -