TY - CONF A1 - Sturm, Patrick A1 - Gluth, Gregor A1 - Greiser, Sebastian A1 - Jäger, Christian A1 - Brouwers, H.J.H. A1 - Kühne, Hans-Carsten T1 - Investigations on one-part geopolymers synthesized from different silica sources N2 - One-part geopolymers, synthesized from three different silica sources and sodium aluminate, were investigated regarding their microstructure and the evolution of their compressive strength on curing at slightly elevated temperatures. The effect of thermal treatment was studied up to 1000 °C and for the investigation of the chemical durability specific samples were treated with sulfuric acid (H2SO4, pH = 1). Depending on the silica feedstock, different degrees of reaction were observed. One of the silicas had a significantly higher reactivity. For two of the silicas, significant amounts of zeolites occurred as reaction products besides geopolymeric gel, whereas the more reactive silica source lead to the formation of a rather fully condensed geopolymeric network. The composites indicated promising behavior on heating in so far as no distinct shrinkage step occurred in the temperature range of dehydration. Up to 400 °C the residual strength of those mixes increased. Above 800 °C the samples underwent new phase formation. After exposure to sulfuric acid (pH 1; 70 d) specimens showed a residual compressive strength of about 77 % of the reference, indicating high acid resistance. T2 - 6th International Conference on Non-Traditional Cement & Concrete CY - Brno, Czech Republic DA - 19.06.2017 KW - Geopolymers KW - Zeolites KW - Thermal properties KW - Acid resistance KW - Chemical durability PY - 2017 SN - 978-80-214-5507-8 SP - 299 EP - 306 AN - OPUS4-40774 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Greiser, Sebastian A1 - Sturm, Patrick A1 - Gluth, Gregor A1 - Hunger, M. A1 - Jäger, Christian T1 - Differentiation of the solid-state NMR signals of gel, zeolite phases and water species in geopolymer-zeolite composites N2 - Geopolymer-zeolite composites were synthesized using a silica-rich industrial byproduct from chlorosilane production and sodium aluminate. Pastes were cured at 80 °C and 80% RH, and subsequently dried in two different climates: at 23 °C and 50% RH, and under vacuum. 1H MAS, 23Na MAS and 29Si MAS NMR and XRD measurements were performed after the drying procedures as well as after subsequent aging. Zeolite Na-A was found beside traces of faujasite-type zeolite and zeolite EMT as major crystalline phases in the cured composites; the fraction of geopolymeric gel in the reaction products was determined to be ~18% on a molar basis. Various water species could be distinguished using 1H MAS and 1H-29Si CP MAS NMR, applying rotorsynchronized echo experiments. The largest fraction of the pore water resides in the α-cages of the zeolite Na-A and in the geopolymeric gel; in addition, water exists in the β-cages of the zeolites and adsorbed at sodium ions. The water species in α-cages and in the pores of the geopolymeric gel exhibit slightly different chemical shifts of 4.7 ppm and 4.9 ppm, respectively, in the 1H MAS NMR spectra. Changes of the water content in the geopolymer pores of differently dried samples were observed and led to slightly varied chemical shifts in the 29Si MAS NMR spectra too. Measurements after more than 500 days revealed no significant aging effects of the composites, which confirm their chemical stability. KW - Geopolymers KW - Aluminosilicate inorganic polymers KW - Zeolite Na-A KW - Spectroscopy KW - Drying PY - 2017 DO - https://doi.org/10.1016/j.ceramint.2016.11.004 SN - 0272-8842 VL - 43 IS - 2 SP - 2202 EP - 2208 PB - Elsevier AN - OPUS4-38694 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Watolla, Marie-Bernadette A1 - Gluth, Gregor A1 - Sturm, Patrick A1 - Rickard, W.D.A. A1 - Krüger, Simone A1 - Schartel, Bernhard T1 - Intumescent geopolymer-bound coatings for fire protection of steel N2 - The passive fire protection of steel structures and other load-bearing components will continue to gain importance in future years. In the present contribution, novel intumescent aluminosilicate (geopolymer-bound) composites are proposed as fire-protective coatings on steel. Steel plates coated with these materials were exposed to the standard temperature-time curve as defined in ISO 834 – 1:1999. The coatings partially foamed during curing and expanded further during thermal exposure, demonstrating their intumescent characteristic.Thermogravimetryandoscillatory rheometry determined that the intumescent behavior is attributed to a transition to a viscous state (loss factor > 1) in the temperature range of major water release, differing from conventional geopolymers. XRD and SEM images showed that the coatings had characteristics of ceramic or glass-ceramic foams after fire resistance testing, suggesting superior performance under challenging conditions. The thickness of the coatings influenced their foaming and intumescent behavior and thus the time for the coated steel plates to reach 500 °C. A number of additives were also studied with the best performance obtained from samples containing sodium tetraborate.Acoating of just 6mmwas able to delay the time it takes for a steel substrate to reach 500 °C to more than 30 minutes. KW - Geopolymers KW - Fire protection KW - Intumescence KW - Coatings KW - Fire resistance PY - 2017 UR - https://www.ceramic-science.com/articles/all-articles.html?article_id=100558 DO - https://doi.org/10.4416/JCST2017-00035 VL - 8 IS - 3 (Topical issue: Geopolymers) SP - 351 EP - 364 PB - Göller Verlag CY - Baden-Baden AN - OPUS4-42139 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -