TY - JOUR A1 - Adel-Khattab, D. A1 - Giacomini, F. A1 - Gildenhaar, R. A1 - Berger, G. A1 - Gomes, Cynthia A1 - Linow, Ulf A1 - Hardt, M. A1 - Peleska, B. A1 - Günster, Jens A1 - Stiller, M. A1 - Houshmand, A. A1 - Ghaffar, K. A1 - Gamal, A. A1 - El-Mofty, M. A1 - Knabe, C. T1 - Development of a synthetic tissue engineered three- dimensional printed bioceramic-based bone graft with homogenously distributed osteoblasts and mineralizing bone matrix in vitro N2 - Over the last decade there have been increasing efforts to develop three-dimensional (3D) scaffolds for bone tissue Engineering from bioactive ceramics with 3D printing emerging as a promising technology. The overall objective of the present study was to generate a tissue engineered synthetic bone graft with homogenously distributed osteoblasts and mineralizing bone Matrix in vitro, thereby mimicking the advantageous properties of autogenous bone grafts and facilitating usage for reconstructing segmental discontinuity defects in vivo . To this end, 3D scaffolds were developed from a silica-containing calcium alkali orthophosphate, using, fi rst, a replica technique – the Schwartzwalder – Somers method – and, second, 3D printing, (i.e. rapid prototyping). The mechanical and physical scaffold properties and their potential to facilitate homogenous colonization by osteogenic cells and extracellular bone matrix formation throughout the porous scaffold architecture were examined. Osteoblastic cells were dynamically cultured for 7 days on both scaffold types with two different concentrations of 1.5 and 3 × 10⁹ cells/l. The amount of cells and bone matrix formed and osteogenic marker expression were evaluated using hard tissue histology, immunohistochemical and histomorphometric analysis. 3D-printed scaffolds (RPS) exhibited more micropores, greater compressive strength and silica release. RPS seeded with 3 × 10⁹ cells/l displayed greatest cell and extracellular Matrix formation, mineralization and osteocalcin expression. In conclusion, RPS displayed superior mechanical and biological properties and facilitated generating a tissue engineered synthetic bone graft in vitro, which mimics the advantageous properties of autogenous bone grafts, by containing homogenously distributed terminally differentiated osteoblasts and mineralizing bone matrix and therefore is suitable for subsequent in vivo implantation for regenerating segmental discontinuity bone defects. KW - Bone tissue engineering KW - Calcium alkali orthophosphate KW - Rapid prototyping KW - Scaffold KW - Mandible PY - 2017 DO - https://doi.org/10.1002/term.2362 SN - 1932-6254 SN - 1932-7005 VL - 12 IS - 1 SP - 44 EP - 58 PB - Wiley Online Library AN - OPUS4-40745 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Knabe, C. A1 - Stiller, M. A1 - Kampschulte, M. A1 - Wilbig, Janka A1 - Peleska, B. A1 - Günster, Jens A1 - Gildenhaar, R. A1 - Berger, G. A1 - Rack, A. A1 - Linow, U. A1 - Heiland, M. A1 - Rendenbach, C. A1 - Koerdt, S. A1 - Steffen, C. A1 - Houshmand, A. A1 - Xiang-Tischhauser, L. A1 - Adel-Khattab, D. T1 - A tissue engineered 3D printed calcium alkali phosphate bioceramic bone graft enables vascularization and regeneration of critical-size discontinuity bony defects in vivo N2 - Recently, efforts towards the development of patient-specific 3D printed scaffolds for bone tissue engineering from bioactive ceramics have continuously intensified. For reconstruction of segmental defects after subtotal mandibulectomy a suitable tissue engineered bioceramic bone graft needs to be endowed with homogenously distributed osteoblasts in order to mimic the advantageous features of vascularized autologous fibula grafts, which represent the standard of care, contain osteogenic cells and are transplanted with the respective blood vessel. Consequently, inducing vascularization early on is pivotal for bone tissue engineering. The current study explored an advanced bone tissue engineering approach combining an advanced 3D printing technique for bioactive resorbable ceramic scaffolds with a perfusion cell culture technique for pre-colonization with mesenchymal stem cells, and with an intrinsic angiogenesis technique for regenerating critical size, segmental discontinuity defects in vivo applying a rat model. To this end, the effect of differing Si-CAOP (silica containing calcium alkali orthophosphate) scaffold microarchitecture arising from 3D powder bed printing (RP) or the Schwarzwalder Somers (SSM) replica fabrication technique on vascularization and bone regeneration was analyzed in vivo. In 80 rats 6-mm segmental discontinuity defects were created in the left femur. KW - Additive Manufacturing KW - Bio active ceramic KW - In-vivo KW - Alcium alkali phosphate PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-584555 DO - https://doi.org/10.3389/fbioe.2023.1221314 SN - 2296-4185 VL - 11 SP - 1 EP - 20 PB - Frontiers SA CY - Lausanne AN - OPUS4-58455 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lopez-Heredia, M.A. A1 - Gildenhaar, Renate A1 - Berger, Georg A1 - Linow, Ulf A1 - Wirth, Cynthia A1 - Günster, Jens A1 - Houshmand, A. A1 - Stiller, M. A1 - Knabe-Ducheyne, C. T1 - Effect of stressed and unstressed cell culture environments on the viability of MC3T3 cells with calcium phosphates T2 - ISACB-6 - International symposium on apatite and correlative biomaterials CY - Nantes, France DA - 2013-06-05 KW - Cell culture media KW - Fetal bovine serum KW - Stressed KW - Unstressed KW - Calcium alkaline orthophosphates PY - 2013 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-299387 DO - https://doi.org/10.4172/2090-5025.S1-002 SN - 2090-5017 SN - 2090-5025 N1 - Geburtsname von Wirth, Cynthia: Gomes, C. M. - Birth name of Wirth, Cynthia: Gomes, C. M. SP - 1 EP - 3(?) PB - Ashdin AN - OPUS4-29938 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller-Mai, C.M. A1 - Berger, Georg A1 - Stiller, M. A1 - Gildenhaar, Renate A1 - Jörn, Daniela A1 - Ploska, Ute A1 - Houshmand, A. A1 - Bednarek, A. A1 - Koch, C. A1 - Knabe, C. T1 - Evaluation of degradable bone cements for percutaneous augmentation of bone defects KW - Bone defect KW - Bioactive bone cement KW - Calcium alkali orthophosphates KW - Histology KW - Histomorphometry KW - Knochendefekt KW - Bioaktiver Knochenzement KW - Calciumalkaliorthophosphat KW - Histologie KW - Histomorphometrie PY - 2010 DO - https://doi.org/10.1002/mawe.201000706 SN - 0933-5137 SN - 1521-4052 VL - 41 IS - 12 SP - 1040 EP - 1047 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-22891 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dombrowski, Felix A1 - Marx, Heidi A1 - Ploska, Ute A1 - Nicolaides, Dagmar A1 - Stiller, M. A1 - Knabe, C. A1 - Berger, Georg T1 - Solubility and ingrowth behaviour of degradable and figuline calcium alkaline phosphate cements N2 - The thrust of the investigations presented here is to point out the degradation behaviour in vitro and the ingrowth behaviour in vivo of four different calcium alkaline phosphate cements. Two of the figuline and mouldable composites consist of the crystalline phase Ca2KNa(PO4)2 and two of the crystalline phase Ca10[K/Na](PO4)2 each containing 2wt% medium gel strength porcine gelatin. Furthermore A-TCP was added to both Ca10[K/Na](PO4)2 cements as a hardening supporting reactant. The testing material groups differ in small amorphous portions containing either silica phosphate (GB9), magnesium potassium phosphate (GB14) or diphosphates (401545 and 401545(70)). The respective composites show a monomodal particle size distribution (d50~7µm; span~4) and an average total porosity around 28vol%.For the solubility studies cylindrical samples (d=6mm; h=12mm) were stored in a 0.1mol TRIS buffer solution and incubated at 37°C for maximum 50 weeks. The storage solution was analysed and renewed every week. The results are plotted cumulative. For the in vivo studies critical size defects were dissected to mandibles in a sheep model in which a 1cm³ area of the bottom of the mandibles was surgically resected and replaced with the figuline cements whereas the mouldability allows the reconstruction of the original outer contour without draining off even when replacing upside down. KW - Calcium alkaline phosphate cement KW - Gelatin KW - Figuline KW - Solubility KW - Ingrowth behavior PY - 2012 DO - https://doi.org/10.4028/www.scientific.net/KEM.493-494.387 SN - 1013-9826 VL - 493-494 SP - 387 EP - 390 PB - Trans Tech Publ. CY - Aedermannsdorf AN - OPUS4-24924 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rack, T. A1 - Zabler, S. A1 - Rack, C. A1 - Stiller, M. A1 - Riesemeier, Heinrich A1 - Cecilia, A. A1 - Nelson, K. T1 - Coherent synchrotron-based micro-imaging employed for studies of micro-gap formation in dental implants N2 - Biocompatible materials such as titanium are regularly applied in oral surgery. Titanium-based implants for the replacement of missing teeth demand a high mechanical precision in order to minimize micro-bacterial leakage, especially when two-piece concepts are used. Synchrotron-based hard x-ray radiography, unlike conventional laboratory radiography, allows high spatial resolution in combination with high contrast even when micro-sized features in such highly attenuating objects are visualized. Therefore, micro-gap formation at interfaces in two-piece dental implants with the sample under different mechanical loads can be studied. We show the existence of micro-gaps in implants with conical connections and study the mechanical behavior of the mating zone of conical implants during loading. The micro-gap is a potential source of implant failure, i.e., bacterial leakage, which can be a stimulus for an inflammatory process. T2 - 10th International conference on X-ray microscopy CY - Chicago, Illinois, USA DA - 15.08.2010 KW - X-ray imaging KW - Dental implants KW - Digital radiography KW - Implant-abutment interface KW - Synchrotron radiation KW - X-ray phase contrast PY - 2011 SN - 978-0-7354-0925-5 DO - https://doi.org/10.1063/1.3625398 N1 - Serientitel: AIP conference proceedings – Series title: AIP conference proceedings VL - 1365 SP - 445 EP - 448 AN - OPUS4-25347 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Knabe, C. A1 - Houshmand, A. A1 - Berger, Georg A1 - Ducheyne, P. A1 - Gildenhaar, Renate A1 - Kranz, I. A1 - Stiller, M. T1 - Effect of rapidly resorbable bone substitute materials on the temporal expression of the osteoblastic phenotype in vitro N2 - Ideally, bioactive ceramics for use in alveolar ridge augmentation should possess the ability to activate bone formation and, thus, cause the differentiation of osteoprogenitor cells into osteoblasts at their surfaces. Therefore, in order to evaluate the osteogenic potential of novel bone substitute materials, it is important to examine their effect on osteoblastic differentiation. This study examines the effect of rapidly resorbable calcium-alkali-orthophosphates on osteoblastic phenotype expression and compares this behavior to that of β-tricalcium phosphate (TCP) and bioactive glass 45S5. Test materials were three materials (denominated GB14, GB9, GB9/25) with a crystalline phase Ca2KNa(PO4)2 and with a small amorphous portion containing either magnesium potassium phosphate (GB14) or silica phosphate (GB9 and GB9/25, which also contains Ca2P2O7); and a material with a novel crystalline phase Ca10[K/Na](PO4)7 (material denominated 352i). SaOS-2 human bone cells were grown on the substrata for 3, 7, 14, and 21 days, counted, and probed for an array of osteogenic markers. GB9 had the greatest stimulatory effect on osteoblastic proliferation and differentiation, suggesting that this material possesses the highest potency to enhance osteogenesis. GB14 and 352i supported osteoblast differentiation to the same or a higher degree than TCP, whereas, similar to bioactive glass 45S5, GB9/25 displayed a greater stimulatory effect on osteoblastic phenotype expression, indicating that GB9/25 is also an excellent material for promoting osteogenesis. KW - Bone substitute materials KW - Calcium-alkali-orthophosphate ceramics KW - SaOS-2 cells KW - Osteoblast differentiation KW - Bioactive glass PY - 2008 DO - https://doi.org/10.1002/jbm.a.31383 SN - 1549-3296 SN - 1552-4965 VL - 84A IS - 4 SP - 856 EP - 868 PB - Wiley CY - Hoboken, NJ AN - OPUS4-16658 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Rack, A. A1 - Zabler, S. A1 - Riesemeier, Heinrich A1 - Weidemann, Gerd A1 - Müller, Bernd R. A1 - Helfen, L. A1 - Stiller, M. A1 - Knabe, C. A1 - Goebbels, Jürgen A1 - Banhart, J. T1 - Nondestructive 3D insights into foamy metals and bioregenerative ceramics KW - X-ray Computed Tomography KW - Metal foams KW - Bioregenerative ceramics PY - 2008 UR - http://www.helmholtz-berlin.de/media/media/oea/web/pr_webseite/druckschriften/infos/bessy/highlights2007.pdf#page=34 SN - 1611-6127 SP - 34 EP - 35 PB - Berliner Elektronenspeicherring-Gesellschaft für Synchrotronstrahlung CY - Berlin AN - OPUS4-17538 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gildenhaar, Renate A1 - Berger, Georg A1 - Lehmann, Erhard A1 - Stiller, M. A1 - Koch, C. A1 - Ducheyne, P. A1 - Rack, A. A1 - Seligmann, H. A1 - Jonscher, S. A1 - Knabe, C. T1 - A comparative study of the biodegradability of calcium-alkali-orthophosphate ceramics in vitro and in vivo KW - Calcium-alkali-orthophosphate KW - Solubility KW - Biodegradability PY - 2007 SN - 1013-9826 VL - 330-332 SP - 63 EP - 66 PB - Trans Tech Publ. CY - Aedermannsdorf AN - OPUS4-14528 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Jörn, Daniela A1 - Gildenhaar, Renate A1 - Berger, Georg A1 - Stiller, M. A1 - Knabe, C. T1 - Behaviour of calcium alkali orthophosphate cements under simulated implantation conditions KW - Calcium alkali orthophosphates KW - Calcium phosphate cement KW - Compressive strength KW - Setting times PY - 2009 SN - 1013-9826 VL - 396-398 SP - 213 EP - 216 PB - Trans Tech Publ. CY - Aedermannsdorf AN - OPUS4-17881 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -