TY - JOUR A1 - Kricheldorf, H. R. A1 - Weidner, Steffen T1 - About the crystallization of cyclic and linear poly(L-lactide)s in alcohol-initiated and Sn(II)2-ethylhexanoate- catalyzed ROPs of L-lactide conducted in solution N2 - 1-Hydroxymethylnaphtalene (HMN) or 11-bromoundecanol (BUND) were used as initiators and Sn(II) 2-ethylhexanoate (SnOct2) as catalyst for ROPs of L-Lactide (LA) at 115 °C in bulk or in 4 M and 2M solutions in toluene. The LA/In ratio, the LA/Cat ratio and the time were varied. The matrix-assisted laser desorption/ionization time-of-flight (MALDI TOF) mass spectra exclusively displayed peaks of linear chains, when the ROPs were conducted in bulk. But in contrast to reports in the literature, mixtures of linear and cyclic poly(L-lactide) (PLA), were obtained, when the ROPs were performed in solution. The intensity distribution of the mass peaks of cyclic PLAs displayed a “saw-tooth pattern” after annealing in contrast to the mass peak distribution of the liner chains. This new phenomenon indicated that cyclic PLAs and linear PLAs crystallized in separate crystals from the same reaction mixture. This conclusion was confirmed by fractionated crystallization from 2 M solution, which confirmed that the cyclic PLAs nucleate and crystallize faster than the linear chains. KW - Polylactide KW - MALDI-TOF MS KW - Ring opening polymerization KW - Crystallization PY - 2023 DO - https://doi.org/10.1016/j.polymer.2023.125946 SN - 0032-3861 VL - 276 SP - 1 EP - 11 PB - Elsevier Ltd. AN - OPUS4-57308 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Cappella, Brunero A1 - Sturm, Heinz A1 - Weidner, Steffen T1 - Breaking polymer chains by dynamic plowing lithography N2 - The adhesion of poly(methyl methacrylate) (PMMA) and polystyrene (PS) films, whose surface has been previously structured by dynamic plowing lithography (DPL), has been measured by means of force–displacement curves. The different adhesion of modified and unmodified PS leads to the assumption that polymer chains are broken during DPL. After measuring the energy dissipated by the tip during DPL, in order to check that the transferred energy is sufficient to break covalent bonds, the polymer chain scission caused by the lithographic process has been definitely confirmed by size exclusion chromatography measurements of the lithographed films. KW - AFM KW - Nanolithography KW - Chain scission PY - 2002 DO - https://doi.org/10.1016/S0032-3861(02)00285-9 SN - 0032-3861 SN - 1873-2291 VL - 43 IS - 16 SP - 4461 EP - 4466 PB - Springer CY - Berlin AN - OPUS4-1608 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kricheldorf, H. R. A1 - Weidner, Steffen T1 - Alcohol-Initiated and SnOct2-Catalyzed Ring-Opening Polymerization (ROP) of L-Lactide in Solution: A Re-investigation N2 - Alcohol-initiated ring-opening polymerizations (ROP) of L-lactide (LA) were studied in solution at 70 °C, whereupon the nature of the alcohol, the LA/initiator ratio, the LA/SnOct2 ratio and the time were varied. In contrast to literature, neat SnOct2 is catalytically active in THF and several aromatic but donor solvents, such as 1,3-dioxolane, dimethylformamide (DMF) or N-methyl pyrrolidone (NMP), strongly reduce the activity of SnOct2. In agreement with literature, no cycles were formed by neat SnOct2 at 70 °C in toluene, whereas almost complete cyclization occurs at 115 °C. This finding is attributed to strongly reduced mobility of the initially formed linear chains having one Sn-O-CH and one anhydride end group. Due to better solvation and enhanced mobility cyclization occurs in THF at 70 °C. KW - Polylactide KW - Ring-opening polymerization KW - MALDI-TOF MS KW - Transesterification PY - 2023 DO - https://doi.org/10.1016/j.eurpolymj.2023.111822 SN - 0014-3057 SP - 1 EP - 18 PB - Elsevier CY - New York, NY [u.a.] AN - OPUS4-56818 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Weidner, Steffen T1 - Rezension: Kompakte Zusammenfassung - MALDI-TOF Mass Spectrometry of Synthetic Polymers. Von H. Pasch, W. Schrepp. Springer, Heidelberg 2003, 298 Seiten. geb., 79,95 Euro. ISBN 3-540-44259-6 PY - 2003 DO - https://doi.org/10.1002/nadc.20030511123 SN - 1439-9598 SN - 1521-3854 VL - 51 IS - 11 SP - 1173 PB - Wiley-VCH CY - Weinheim AN - OPUS4-4678 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gross, J.H. A1 - Weidner, Steffen T1 - Influence of Electric Field Strength and Emitter Temperature on Field Desorption Mass Spectra of Polyethylene Oligomers N2 - The influence of electric field strength and emitter temperature on dehydrogenation and C–C cleavage in field desorption (FD) mass spectrometry of polyethylene (PE) oligomers of average molecular weights ranging from 500 to 2000 is examined. Low mass oligomers yield molecular weight (MW) distributions that are basically in accordance with results from gel-permeation chromatography. For these materials, dehydrogenation can be greatly reduced by reduction of the emitter potential. Furthermore, the influence of emitter potential on MW distributions indicates the occurrence of field-induced C–C cleavages. Reliable MW distributions are more difficult to obtain from higher mass oligomers by FD-MS because of the need for higher field strength and higher emitter temperatures to effect their desorption/ionization. Experiments reveal that the application of FD-MS to PE oligomers is limited not only by field-induced but also by thermally-induced fragmentations. Even then, FD mass spectra contain valuable information on mass range and homogeneity of PE samples up to about m/z 3600. PY - 2000 DO - https://doi.org/10.1255/ejms.300 SN - 1469-0667 SN - 1356-1049 SN - 1365-0718 IS - 6 SP - 11 EP - 17 PB - IM Publications CY - Chichester AN - OPUS4-11098 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weidner, Steffen T1 - MALDI von geregelten und ungeregelten Polyamiden nach kritischer Chromatographie T2 - VII. Anwendertreffen MALDI-TOF-MS zur Charakterisierung von synthetischen Polymeren CY - Berlin, Germany DA - 2002-05-14 PY - 2002 AN - OPUS4-11136 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weidner, Steffen T1 - Mechanism of homogeneously catalyzed polymerization of liquid-crystalline sidegroup monomers investigated by means of MALDI-TOF-MS (No. 433) T2 - 219th ACS National Meeting CY - San Francisco, CA, USA DA - 2000-03-26 PY - 2000 AN - OPUS4-11314 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weidner, Steffen T1 - Beispiele für zweidimensionale Kopplungen von Chromatographie und MALDI-TOF-Massenspektrometrie zur Analyse von Polymeren T2 - BAM-Abt. VI-Seminar CY - Berlin, Germany DA - 2003-09-25 PY - 2003 AN - OPUS4-11139 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weidner, Steffen T1 - SFC of new liquid-crystalline cholesteryl esters T2 - InCom '96, International Symposium on Instrumentalized Analytical Chemistry and Computer Technology CY - Düsseldorf, Germany DA - 1996-03-25 PY - 1996 AN - OPUS4-11194 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - You, Zengchao A1 - Jakubowski, Norbert A1 - Panne, Ulrich A1 - Weidner, Steffen T1 - Separation of polystyrene nanoparticles with different coatings using two-dimensional off-line coupling of asymmetrical flow field flow fractionation and capillary electrophoresis N2 - The successful off-line coupling of asymmetrical flow field flow fractionation (AF4) and capillary electrophoresis (CE) for separation of nanoparticles (NPs) with different surface coatings was shown. We could successfully demonstrate that, in a certain NP size range, hyphenation of both techniques significantly improved the separation of differently coated NPs. Three mixtures of polystyrene nanoparticles (PS-NPs) with comparable core sizes but different coatings (no coating/carboxyl-coated) were studied. Separation in either method resulted in non-baseline resolved or non-separated peaks. In contrast, two-dimensional off-line coupling of AF4 and CE resulted in clearly separated regions in their 2 D plots in case of 20 and 50 nm particle mixtures, whereas the 100 nm NP mixture could not be separated at all. Various factors affecting the separation like hydrodynamic diameter or SDS concentration were discussed. KW - Capillary electrophoresis (CE) KW - Nanoparticles with same nominal diameter KW - Surface coating KW - Two-dimensional off-line coupling KW - Asymmetrical flow field flow fractionation (AF4) PY - 2019 DO - https://doi.org/10.1016/j.chroma.2019.01.056 VL - 1593 SP - 119 EP - 126 PB - Elsevier AN - OPUS4-47363 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - El Malah, T. A1 - Rolf, Simone A1 - Weidner, Steffen A1 - Thünemann, Andreas A1 - Hecht, S. T1 - Amphiphilic folded dendrimer discs and their thermosensitive self-assembly in water N2 - Folded dendrimers with peripheral ether side chains show a thermally induced hierarchical aggregation process, in which the transition temperature and the dimensions of the aggregates can readily be tuned via the generation number (see figure). KW - Click chemistry KW - Cotton effect KW - Dendrimers KW - Hierarchical self-assembly KW - Thermochemistry PY - 2012 DO - https://doi.org/10.1002/chem.201200414 SN - 0947-6539 SN - 1521-3765 VL - 18 IS - 19 SP - 5837 EP - 5842 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-25822 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weidner, Steffen T1 - Polymer characterization using sophisticated liquid chromatographic techniques combined with MALDI- and ESI-TOF mass spectrometry T2 - 55th ASMS conference on Mass Spectrometry CY - Indianapolis, IN, USA DA - 2007-06-03 PY - 2007 AN - OPUS4-14745 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -