TY - CONF A1 - Maack, Stefan A1 - Küttenbaum, Stefan A1 - Torrent, R. A1 - Ebell, Gino A1 - Völker, Tobias T1 - Testing to reasses - Corrosion activity assessment based on NDT using a prestressed concrete bridge as case study N2 - Corrosion of concrete reinforcement is one of the major damage mechanisms affecting both the load-bearing capacity and the serviceability of reinforced concrete structures significantly. The challenge of detecting corrosion is that the corrosion process in its various forms is not immediately visible, especially in the corrosion initiation phase inside the concrete. When externally discernible damages are observed during visual inspections on the structure, the extent of the damage inside the concrete is often already significant. Corrosion caused by carbonation often leads to severe discoloration of the surface or even large-area spalling of the concrete cover. In contrast, chloride-induced corrosion is usually difficult to observe visually, but can cause much more serious damage in less time. The effect occurs locally and can lead to weakening of the cross-section of the reinforcement. This, in turn, can cause sudden structural collapses without prior notice. Therefore, it is important to investigate whether there is protection against corrosion of the reinforcement in the concrete and to detect active corrosion in the structure at an early stage. In the meanwhile, various non-destructive and minimally invasive testing methods are available to evaluate the resistance to penetration of corrosion-promoting pollutants and to detect active corrosion. In this paper, a bridge crossing the river Regen (Germany) is used as a case-study to demonstrate how the information obtained applying different testing methods can be combined and evaluated in the context of structural reassessments. Both the results of the permeability testing (Torrent tester) and the electrical resistance measurement (Wenner probe) are considered, as well as active corrosion areas are localized using the half-cell potential mapping combined with the concrete cover measurement with the eddy current method and ground penetrating radar (GPR). The results are evaluated using drill cores and in addition laser-induced breakdown spectroscopy (LIBS) was applied to obtain information about possible ion transport in the concrete. T2 - EUROSTRUCT 2021 - 1st Conference of the European Association on Quality Control of Bridges and Structures - EUROSTRUCT CY - Padova, Italy DA - 30.08.2021 KW - Nondestructive testing KW - Corrosion KW - Bridge KW - Durability assessment KW - Civil engineering PY - 2021 AN - OPUS4-53222 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -