TY - JOUR A1 - Xin, L. A1 - Bungartz, M. A1 - Maenz, S. A1 - Horbert, V. A1 - Hennig, M. A1 - Illerhaus, Bernhard A1 - Günster, Jens A1 - Bossert, J. A1 - Bischoff, S. A1 - Borowski, J. A1 - Schubert, H. A1 - Jandt, K. A1 - Kunisch, E. A1 - Kinne, R. A1 - Brinkmann, O. T1 - Decreased extrusion of calcium phosphate cement versus high viscosity PMMA cement into spongious bone marrow—an ex vivo and in vivo study in sheep vertebrae N2 - Vertebroplasty or kyphoplasty of osteoporotic vertebral fractures bears the risk of pulmonary cement embolism (3.5%–23%) caused by leakage of commonly applied acrylic polymethylmethacrylate (PMMA) cement to spongious bone marrow or outside of the vertebrae. Ultraviscous cement and specific augmentation systems have been developed to reduce such adverse effects. Rapidly setting, resorbable, physiological calcium phosphate cement (CPC) may also represent a suitable alternative. PURPOSE: This study aimed to compare the intravertebral extrusion of CPC and PMMA cement in an ex vivo and in vivo study in sheep. STUDY DESIGN/SETTING: A prospective experimental animal study was carried out. METHODS: Defects (diameter 5 mm; 15 mm depth) were created by a ventrolateral percutane-ous approach in lumbar vertebrae of female Merino sheep (2–4 years) either ex vivo (n = 17) or in vivo (n = 6), and injected with: (1) CPC (L3); (2) CPC reinforced with 10% poly(l-lactide-co-glycolide) (PLGA) fibers (L4); or (3) PMMA cement (L5; Kyphon HV-R). Controls were untouched (L1) or empty defects (L2). The effects of the cement injections were assessed in vivo by blood gas analysis and ex vivo by computed tomography (CT), micro-CT (voxel size: 67 µm), histology, and biomechanical testing. KW - Bone marrow extrusion KW - Brushite-forming calcium phosphate cement KW - Cement injection KW - Ex vivo KW - High- viscosity PMMA cement KW - In vivo KW - Large animal model KW - Sheep KW - Vertebroplasty PY - 2016 DO - https://doi.org/10.1016/j.spinee.2016.07.529 SN - 1529-9430 SN - 1878-1632 VL - 16 IS - 12 SP - 1468 EP - 1477 PB - Elsevier Inc. AN - OPUS4-38058 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Gunella, F. A1 - Kunisch, E. A1 - Maenz, S. A1 - Horbert, V. A1 - Xin, L. A1 - Mika, J. A1 - Borowski, J. A1 - Bischoff, S. A1 - Schubert, H. A1 - Sachse, A. A1 - Illerhaus, Bernhard A1 - Günster, Jens A1 - Bossert, J. A1 - Jandt, K. D. A1 - Plöger, F. A1 - Kinne, R. W. A1 - Brinkmann, O. A1 - Bungartz, M. ED - Carragee, T1 - The GDF5 mutant BB-1 enhances the bone formation induced by an injectable, poly(l-lactide-co-glycolide) acid (PLGA) fiber-reinforced, brushite-forming cement in a sheep defect model of lumbar osteopenia N2 - BACKGROUND CONTEXT: Targeted delivery of osteoinductive bone morphogenetic Proteins (eg, GDF5) in bioresorbable calcium phosphate cement (CPC), potentially suitable for vertebroplasty and kyphoplasty of osteoporotic vertebral fractures, may be required to counteract augmented local bone catabolism and to support complete bone regeneration. The biologically optimized GDF5 Mutant BB-1 may represent an attractive drug candidate for this purpose. PURPOSE: The aim of the current study was to test an injectable, poly (l-lactide-co-glycolide) acid (PLGA) fiber-reinforced, brushite-forming CPC containing low-dose BB-1 in a sheep lumbar osteopenia model. STUDY DESIGN/ SETTING: This is a prospective experimental animal study. METHODS: Bone defects (diameter 5 mm) were generated in aged, osteopenic female sheep and were filled with fiber-reinforced CPC alone (L4; CPC+fibers) or with CPC containing different dosages. KW - Bone morphogenetic protein; KW - Bone regeneration; KW - Micro-Computed-Tomography; KW - Calcium phosphate cement; KW - GDF-5 mutant; KW - Large animal model sheep; KW - Osteoporotic vertebral fracture PY - 2018 DO - https://doi.org/10.1016/j.spinee.2017.10.002 SN - 1529-9430 SN - 1878-1632 VL - 18 IS - 2 SP - 357 EP - 369 PB - Elsevier CY - New York AN - OPUS4-44561 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hoffmann, M. A1 - Schubert, Nils A1 - Günster, Jens A1 - Stawarczyk, B. A1 - Zocca, Andrea T1 - Additive manufacturing of glass-ceramic dental restorations by layerwise slurry deposition (LSD-print) N2 - This study is dedicated to the additive manufacturing of a feldspar glass-ceramic for dental applications by LSD-print (layerwise slurry deposition) technology, a variation of binder jetting using water-based ceramic slurries as feedstock. This technology was investigated for the manufacturing of single tooth restoration demonstrators with good aesthetic properties, and to compare the additively manufactured material with a commercial reference. Model restorations with > 99 % relative density were processed with a debinding and firing cycle of 45 min, however the whole process chain accounts for up to 30 hours. Significant differences between LSD-printed and reference materials were found for fracture strength, fracture toughness and Martens parameters. Printing orientation affected shrinkage and fracture strength, but not fracture toughness and Martens parameters. Nevertheless, the results suggest that the LSD-print technology processing the developed slurry is a promising option for manufacturing dental restorations meeting class 1a requirements according to DIN EN ISO 6871:2019–01. KW - Additive Manufacturing KW - 3D-printing KW - LSD-print KW - Dental ceramics KW - Glass-ceramic KW - Debinding KW - Firing KW - Sinter-crystallization PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-624768 DO - https://doi.org/10.1016/j.jeurceramsoc.2025.117235 VL - 45 IS - 7 SP - 1 EP - 13 PB - Elsevier Ltd. AN - OPUS4-62476 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bungartz, M. A1 - Maenz, S. A1 - Kunisch, E. A1 - Horbert, V. A1 - Xin, L. A1 - Gunella, F. A1 - Mika, J. A1 - Borowski, J. A1 - Bischoff, S. A1 - Schubert, H. A1 - Sachse, A. A1 - Günster, Jens A1 - Illerhaus, Bernhard A1 - Bossert, J. A1 - Jandt, K. D. A1 - Kinne, R. W. A1 - Brinkmann, O. T1 - First-time systematic postoperative clinical assessment of a minimally invasive approach for lumbar ventrolateral vertebroplasty in the large animal model sheep N2 - Large animal models are highly recommended for meaningful preclinical studies, including the optimization of cement augmentation for vertebral body defects by vertebroplasty/kyphoplasty. The aim of this study was to perform a systematic characterization of a strictly minimally invasive in vivo large animal model for lumbar ventrolateral vertebroplasty. This is a prospective experimental animal study. Lumbar defects (diameter 5 mm; depth approximately 14 mm) were created by a ventrolateral percutaneous approach in aged, osteopenic, female sheep (40 Merino sheep; 6–9 years; 68–110 kg). L1 remained untouched, L2 was left with an empty defect, and L3 carried a defect injected with a brushite-forming calcium phosphate cement (CPC). Trauma/functional impairment, surgical techniques (including drill sleeve and working canula with stop), reproducibility, bone defects, cement filling, and functional cement augmentation were documented by intraoperative incision-to-suture time and X-ray, postoperative trauma/impairment scores, and ex vivo osteodensitometry, microcomputed tomography (CT), histology, static/fluorescence histomorphometry, and biomechanical testing. Minimally invasive vertebroplasty resulted in short operation times (28±2 minutes; mean±standard error of the mean) and X-ray exposure (1.59±0.12 minutes), very limited local trauma (score 0.00±0.00 at 24 hours), short postoperative recovery (2.95±0.29 hours), and rapid decrease of the postoperative impairment score to 0 (3.28±0.36 hours). Reproducible defect creation and cement filling were documented by intraoperative X-ray and ex vivo conventional/micro-CT. Vertebral cement augmentation and osteoconductivity of the CPC was verified by osteodensitometry (CPC>control), micro-CT (CPC>control and empty defect), histology/static histomorphometry (CPC>control and empty defect), fluorescence histomorphometry (CPC>control; all p<.05 for 3 and 9 months), and compressive strength measurements (CPC numerically higher than control; 102% for 3 months and 110% for 9 months). This first-time systematic clinical assessment of a minimally invasive, ventrolateral, lumbar vertebroplasty model in aged, osteopenic sheep resulted in short operation times, rapid postoperative recovery, and high experimental reproducibility. This model represents an optimal basis for standardized evaluation of future studies on vertebral augmentation with resorbable and osteoconductive CPC. KW - Computed tomography KW - Calcium phosphate cement KW - Large animal model KW - Minimal-invasive KW - Vertebroplasty KW - Void defect PY - 2016 UR - http://www.sciencedirect.com/science/article/pii/S152994301630273X DO - https://doi.org/10.1016/j.spinee.2016.06.015 VL - 16 IS - 10 SP - 1263 EP - 1275 PB - Elsevier Inc. AN - OPUS4-38429 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Maenz, S. A1 - Brinkmann, O. A1 - Kunisch, E. A1 - Horbert, V. A1 - Gunella, F. A1 - Bischoff, S. A1 - Schubert, H. A1 - Sachse, A. A1 - Xin, L. A1 - Günster, Jens A1 - Illerhaus, Bernhard A1 - Jandt, K. D. A1 - Bossert, J. A1 - Kinne, R. W. A1 - Bungartz, M. T1 - Enhanced bone formation in sheep vertebral bodies after minimally invasive treatment with a novel, PLGA fiber-reinforced brushite cement. N2 - Injectable, brushite-forming calcium phosphate cements (CPC) show potential for bone replacement, but they exhibit low mechanical strength. This study tested a CPC reinforced with poly(l-lactide-co-glycolide) acid (PLGA) fibers in a minimally invasive, sheep lumbar vertebroplasty model. The study aimed to test the in vivo biocompatibility and osteogenic potential of a PLGA fiber-reinforced, brushite-forming CPC in a sheep large animal model. KW - µCT KW - Vertebral KW - PLGA cement PY - 2017 UR - http://www.sciencedirect.com/science/article/pii/S152994301631066X DO - https://doi.org/10.1016/j.spinee.2016.11.006 SN - 1529-9430 SN - 1878-1632 VL - 17 IS - 5 SP - 709 EP - 719 PB - Elsevier Science direct AN - OPUS4-40462 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gunella, F. A1 - Kunisch, E. A1 - Bungartz, M. A1 - Maenz, S. A1 - Horbert, V. A1 - Xin, L. A1 - Mika, J. A1 - Borowski, J. A1 - Bischoff, S. A1 - Schubert, H. A1 - Hortschansky, P. A1 - Sachse, A. A1 - Illerhaus, Bernhard A1 - Günster, Jens A1 - Bossert, J. A1 - Jandt, K. D. A1 - Plöger, F. A1 - Kinne, R. W. A1 - Brinkmann, O. T1 - Low-dose BMP-2 is sufficient to enhance the bone formation induced by an injectable, PLGA fiber-reinforced, brushite-forming cement in a sheep defect model of lumbar osteopenia N2 - BACKGROUND CONTEXT: Bioresorbable calcium phosphate cement (CPC) may be suitable for vertebroplasty/kyphoplasty of osteoporotic vertebral fractures. However, additional targeted de- livery of osteoinductive bone morphogenetic Proteins (BMPs) in the CPC may be required to counteract the augmented local bone catabolism and support complete bone regeneration. PURPOSE: This study aimed at testing an injectable, poly (l-lactide-co-glycolide) acid (PLGA) fiber-reinforced, brushite-forming cement (CPC) containing low-dose bone morphogenetic Protein BMP-2 in a sheep lumbar osteopenia model. STUDY DESIGN/ SETTING: This is a prospective experimental animal study. METHODS: Bone defects (diameter 5 mm) were generated in aged, osteopenic female sheep and filled with fiber-reinforced CPC alone (L4; CPC+ fibers) or with CPC containing different dosages of BMP-2 (L5; CPC+ fibers + BMP-2; 1, 5, 100, and 500g BMP-2; n=5 or 6 each). The results were compared with those of untouched controls (L1). Three and 9 months after the operation, structural and functional effects of the CPC (±BMP-2) were analyzed ex vivo by measuring (1) bone Mineral density (BMD); (2) bone structure, that is, bone volume/total volume (assessed by micro-computed tomography [micro-CT] and histomorphometry), trabecular thickness, and trabecular number; (3) bone formation, that is, osteoid volume/bone volume, osteoid surface/bone surface, osteoid thickness, mineralizing surface/bone surface, mineral Apposition rate, and bone formation rate/bone surface; (4) bone resorption, that is, eroded surface/bone surface; and (5) compressive strength. RESULTS: Compared with untouched controls (L1), CPC+ fibers (L4) and/or CPC+ fibers + BMP-2(L5) significantly improved all parameters of bone formation, bone resorption, and bone structure. These effects were observed at 3 and 9 months, but were less pronounced for some parameters at 9 months. Compared with CPC without BMP-2, additional significant effects of BMP-2 were demonstrated for bone structure (bone volume/total volume, trabecular thickness, trabecular number) and formation (osteoid surface/bone surface and mineralizing surface/bone surface), as well as for the compressive strength. The BMP-2 effects on bone Formation at 3 and 9 months were dose-dependent, with 5–100g as the optimal dosage. CONCLUSIONS: BMP-2 significantly enhanced the bone formation induced by a PLGA fiber-reinforced CPC in sheep lumbar osteopenia. A single local dose as low as ≤100g BMP-2 was sufficient to augment middle to long-term bone formation. The novel CPC+ BMP-2 may thus represent an alternative to the bioinert, supraphysiologically stiff polymethylmethacrylate cement presently used to treat osteoporotic vertebral fractures by vertebroplasty/kyphoplasty. KW - Bone regeneration KW - Computed tomography KW - Calcium phosphat cement KW - Large animal model sheep KW - Osteoporotic vertebral fracture PY - 2017 DO - https://doi.org/10.1016/j.spinee.2017.06.005 SN - 1529-9430 SN - 1878-1632 VL - 17 IS - 11 SP - 1699 EP - 1711 PB - Elsevier Inc. AN - OPUS4-43237 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bungartz, M. A1 - Kunisch, E. A1 - Maenz, S. A1 - Horbert, V. A1 - Xin, L. A1 - Gunella, F. A1 - Mika, J. A1 - Borowski, J. A1 - Bischoff, S. A1 - Schubert, H. A1 - Sachse, A. A1 - Illerhaus, Bernhard A1 - Günster, Jens A1 - Bossert, J. A1 - Jandt, K. D. A1 - Plöger, F. A1 - Kinne, R. W. A1 - Brinkmann, O. T1 - GDF5 significantly augments the bone formation induced by an injectable, PLGA fiber-reinforced, brushite-forming cement in a sheep defect model of lumbar osteopenia N2 - BACKGROUND CONTEXT: Biodegradable calcium phosphate cement (CPC) represents a promising option for the surgical treatment of osteoporotic vertebral fractures. Because of augmented local bone catabolism, however, additional targeted delivery of bone morphogenetic proteins with the CPC may be needed to promote rapid and complete bone regeneration. PURPOSE: In the present study, an injectable, poly(l-lactide-co-glycolide) acid (PLGA) fiber-reinforced, brushite-forming cement (CPC) containing the bone morphogenetic Protein GDF5 was tested in a sheep lumbar osteopenia model. STUDY DESIGN/SETTING: This is a prospective experimental animal study METHODS: Defined bone defects (diameter 5 mm) were placed in aged, osteopenic female sheep. Defects were treated with fiber-reinforced CPC alone (L4; CPC+ fibers) or with CPC containing different dosages of GDF5 (L5; CPC+ fibers + GDF5; 1, 5, 100, and 500g GDF5; n = 5 or 6 each). The results were compared with those of untouched controls (L1). Three and 9 months postoperation, structural and functional effects of the CPC (±GDF5) were assessed ex vivo by measuring (1) bone mineral density (BMD); (2) bone structure, that is, bone volume/total volume (assessed by micro-computed tomography and histomorphometry), trabecular thickness, and trabecular number; (3) bone formation, that is, osteoid volume/bone volume, osteoid surface/bone surface, osteoid thickness, mineralized surface/bone surface, mineral apposition rate, and bone formation rate/bone surface; (4) bone resorption, that is, eroded surface/bone surface; and (5) compressive strength. RESULTS: Compared with untouched controls (L1), both CPC+ fibers (L4) and CPC+ fibers + GDF5 (L5) numerically or significantly improved all parameters of bone formation, bone resorption, and bone structure. These significant effects were observed both at 3 and 9 months, but for some parameters they were less pronounced at 9 months. Compared with CPC without GDF5, additional significant effects of CPC with GDF5 were demonstrated for BMD and parameters of bone formation and structure (bone volume/total volume, trabecular thickness, and trabecular number, as well as mineralized surface/bone surface). The GDF5 effects were dose-dependent (predominantly in the 5–100g range) at 3 and 9 months. CONCLUSIONS: GDF5 significantly enhanced the bone formation induced by a PLGA fiber-reinforced CPC in sheep lumbar osteopenia. The results indicated that a local dose as low as ≤100g GDF5 may be sufficient to augment middle to long-term bone formation. The novel CPC+ GDF5 combination may thus qualify as an alternative to the bioinert, supraphysiologically stiff poly-(methyl methacrylate) cement currently applied for vertebroplasty/kyphoplasty of osteoporotic vertebral fractures. KW - Bone regeneration KW - Computed tomography KW - Large animal model sheep KW - Osteoporotic vertebral fracture PY - 2017 DO - https://doi.org/10.1016/j.spinee.2017.06.007 SN - 1529-9430 SN - 1878-1632 VL - 17 IS - 11 SP - 1685 EP - 1698 PB - Elsevier Inc. AN - OPUS4-43239 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ginés-Palomares, J.-C. A1 - Fateri, M. A1 - Schubert, T. A1 - de Peindray d’Ambelle, L. A1 - Simon, Sebastian A1 - Gluth, Gregor A1 - Günster, Jens A1 - Zocca, Andrea T1 - Material aspects of sintering of EAC-1A lunar regolith simulant N2 - Future lunar exploration will be based on in-situ resource utilization (ISRU) techniques. The most abundant raw material on the Moon is lunar regolith, which, however, is very scarce on Earth, making the study of simulants a necessity. The objective of this study is to characterize and investigate the sintering behavior of EAC-1A lunar regolith simulant. The characterization of the simulant included the determination of the phase assemblage, characteristic temperatures determination and water content analysis. The results are discussed in the context of sintering experiments of EAC-1A simulant, which showed that the material can be sintered to a relative density close to 90%, but only within a very narrow range of temperatures (20–30 °C). Sintering experiments were performed for sieved and unsieved, as well as for dried and non-dried specimens of EAC-1A. In addition, an analysis of the densification and mechanical properties of the sintered specimens was done. The sintering experiments at different temperatures showed that the finest fraction of sieved simulant can reach a higher maximum sintering temperature, and consequently a higher densification and biaxial strength. The non-dried powder exhibited higher densification and biaxial strength after sintering compared to the dried specimen. This difference was explained with a higher green density of the non-dried powder during pressing, rather than due to an actual influence on the sintering mechanism. Nevertheless, drying the powder prior to sintering is important to avoid the overestimation of the strength of specimens to be fabricated on the Moon. KW - Lunar regolith KW - Ceramics KW - Microstructure KW - Sintering KW - Softening temperature PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-592668 DO - https://doi.org/10.1038/s41598-023-50391-y SN - 2045-2322 VL - 13 SP - 1 EP - 14 PB - Springer Nature AN - OPUS4-59266 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Geffroy, P.-M. A1 - Schubert, Nils Hendrik A1 - Günster, Jens A1 - Zocca, Andrea T1 - Quantification of in-plane stress development during drying of tape-cast ceramic layers by cantilever deflection method N2 - The control of stress development in cast ceramics during drying is usually one of critical steps in ceramic processes, which is important also for additive manufacturing technologies using a suspension as feedstock. This work introduces a method based on the cantilever deflection method, to simultaneously quantify the kinetics of solvent evaporation, the shrinkage and the intensity of in-plane stresses developed during drying. Particular attention is given here to the experimental limits of the method and to the optimization of the experimental conditions to suitably measure the intensity of in-planar stress in the coating. The optimized method is applied to four alumina slurries for the water-based additive manufacturing technology LSD-print. Four stages of drying are identified and discussed in relation with the granulometry and morphology of the alumina ceramic particles. KW - Additive Manufacturing KW - Tape casting KW - Ceramic layers KW - Drying stress PY - 2025 DO - https://doi.org/10.1016/j.jeurceramsoc.2024.116868 VL - 45 IS - 1 SP - 1 EP - 10 PB - Elsevier B.V. AN - OPUS4-61044 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -