TY - JOUR A1 - Wegner, Karl David A1 - Pouget, S. A1 - Ling, W. L. A1 - Carriere, M. A1 - Reiss, P. T1 - Gallium – a versatile element for tuning the photoluminescence properties of InP quantum dots N2 - With the goal to tune the emission properties of colloidal InP quantum dots, the incorporation of Ga was explored. Unexpectedly, depending on the nature of the gallium precursor, the photoluminescence shifted either to the red (gallium oleate) or to the blue (gallium acetylacetonate). In the first case, larger-sized InP/GaP core/shell nanocrystals were formed, while in the second case the formation of an InGaP alloy structure enabled the blue range of emission (475 nm) to be accessed. KW - Indium phosphide KW - Quantum dots KW - Gallium doping PY - 2019 DO - https://doi.org/10.1039/C8CC09740B VL - 55 IS - 11 SP - 1663 EP - 1666 PB - Royal Society of Chemistry AN - OPUS4-48306 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Alam, F. A1 - Wegner, Karl David A1 - Pouget, S. A1 - Amidani, L. A1 - Kvashnina, K. A1 - Aldakov, D. A1 - Reiss, P. T1 - Eu2+: A suitable substituent for Pb2+ in CsPbX3 perovskite nanocrystals? N2 - Eu2+ is used to replace toxic Pb2+ in metal halide perovskite nanocrystals (NCs). The synthesis implies injection of cesium oleate into a solution of europium (II) bromide at an experimentally determined optimum temperature of 130 ○C and a reaction time of 60 s. Structural analysis indicates the formation of spherical CsEuBr3 nanoparticles with a mean size of 43 ± 7 nm. Using EuI2 instead of EuBr2 leads to the formation of 18-nm CsI nanoparticles, while EuCl2 does not show any reaction with cesium oleate forming 80-nm EuCl2 nanoparticles. The obtained CsEuBr3 NCs exhibit bright blue emission at 413 nm (FWHM 30 nm) with a room temperature photoluminescence quantum yield of 39%. The emission originates from the Laporte-allowed 4f7–4f65d1 transition of Eu2+ and shows a PL decay time of 263 ns. The long-term stability of the optical properties is observed, making inorganic lead-free CsEuBr3 NCs promising deep blue emitters for optoelectronics. KW - Perovskite KW - Lead-free KW - fluorescence KW - anion-exchange PY - 2019 DO - https://doi.org/10.1063/1.5126473 SN - 0021-9606 VL - 151 SP - 231101-1 EP - 231101-7 PB - AIP Publishing AN - OPUS4-50696 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -