TY - JOUR A1 - Deubener, J. A1 - Behrens, H. A1 - Müller, Ralf A1 - Zietka, S. A1 - Reinsch, Stefan T1 - Kinetic fragility of hydrous soda-lime-silica glasses N2 - The effect of hydration on the kinetic fragility of soda-lime-silica glasses was investigated by viscometry in the glass transition range. Water-bearing glasses were prepared from industrial float glass (FG) and a ternary model glass (NCS = 16Na2O 10CaO 74SiO2 in mol%) by bubbling steam through the melt at 1480 °C and up to 7 bar. Additionally, a sodium borosilicate glass (NBS = 16Na2O 10B2O3 74SiO2 in mol%) was hydrated under equal conditions. As detected by infrared spectroscopy water dissolves in the glasses exclusively as OH-groups. The hydration resulted in a total water content CW up to ~ 0.2 wt% for FG, NCS and NBS glasses. Kinetic fragility, expressed by the steepness index m, was determined from the temperature dependence of η at the glass transition. Viscosity data from previous studies on hydrous float glasses (CW > 1 wt%) were surveyed together with literature data on the (H2O)–Na2O–CaO–SiO2, (H2O)–Na2O–SiO2 and (H2O)–SiO2 systems to expand the range of water concentration and bulk composition. We could demonstrate that m decreases for all glasses although water is dissolved as OH and should depolymerize the network. An empirical equation of the general type m = a - b logCW where a, b are fitting parameters, enables m to be predicted, for each glass series as function of the water content CW. The enlarged data base shows that the parameter B of the Arrhenius viscosity-temperature relation decreases much stronger than the isokom temperature at the glass transition. KW - Soda-lime-silica KW - Fragility KW - Viscosity KW - Water in glass PY - 2008 DO - https://doi.org/10.1016/j.jnoncrysol.2008.04.021 SN - 0022-3093 VL - 354 IS - 42-44 SP - 4713 EP - 4718 PB - North-Holland Publ. Co. CY - Amsterdam AN - OPUS4-18187 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zietka, S. A1 - Deubener, J. A1 - Behrens, H. A1 - Müller, Ralf T1 - Glass transition and viscosity of hydrated silica glasses N2 - The viscosity of silica glasses with different water contents was measured by penetration of sapphire microspheres in the range from 1012-1014·7 Pas at ambient pressure. Commercial silica glasses were used together with hydrous silica glasses, which were prepared by melting glass powder plus water in an internally heated pressure vessel at 2-3 kbar and 1350-1450°C. The temperature dependence of the viscosity of silica glasses with total water contents Cw of 5·4×10-4, 7·0×10-4, 1·00×10-2, and 1·55×10-2(Cw in mass fractions) can be described by Arrhenius equations. From the results, the linear dependence of the T12 isokom (K) with the logarithm of the water content was determined as T12=192-409 logCw. The analysis of the compositional dependence of the T12 isokom in the H2O-Na2O-SiO2 system reveals a temperature depression of up to 200 K for mixed water- and sodium-bearing glasses compared to H2O-SiO2 and Na2O-SiO2 glasses with same molar silica content. From these findings we conclude that protons may contribute significantly to the mixed alkali effect in glasses. KW - Wassergehalt KW - Silicatgläser KW - Viskosität PY - 2007 SN - 1753-3562 SN - 0017-1050 SN - 0031-9090 SN - 1750-6697 VL - 48 IS - 6 SP - 380 EP - 387 PB - Society of Glass Technology CY - Sheffield AN - OPUS4-18396 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Saathoff, F. A1 - Cantré, S. A1 - Müller, Werner ED - Ziegler, M. ED - Bräu, G. ED - Heerten, G. ED - Laackmann, K. T1 - Modified filtration criteria for non-woven geotextiles in landfill construction N2 - The German landfill ordinance includes a certification requirement for geosynthetics used in landfill liner and capping systems. The certification guidelines describe the basis for the design of geosynthetics used in landfill construction. According to the rules which are usually applied, the thickness of the filter geotextile has to be at least 30 times the characteristic opening size O90. Filter geotextiles which are often used in geocomposite drains have a mass per area of 200 g/m² and do not fulfill this requirement. In this paper modified filter criteria for geosynthetics are presented with a particular focus on These geotextile filters in geocomposite drains. T2 - 10th International conference on geosynthetics CY - Berlin, Germany DA - 21.09.2014 KW - Filtration criteria KW - Drainage KW - Geotextile KW - Non-woven KW - Landfill KW - Certification guidelines PY - 2014 SN - 978-3-9813953-9-6 SP - 1 EP - 7 AN - OPUS4-31578 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Meyerhofer, F. A1 - Dissinger, F. A1 - Weigert, Florian A1 - Jungclaus, J. A1 - Müller-Caspary, K. A1 - Waldvogel, S. R. A1 - Resch-Genger, Ute A1 - Voss, T. T1 - Citric Acid Based Carbon Dots with Amine Type Stabilizers: pHSpecific N2 - We report the synthesis and spectroscopic characteristics of two different sets of carbon dots (CDs) formed by hydrothermal reaction between citric acid and polyethylenimine (PEI) or 2,3-diaminopyridine (DAP). Although the formation of amide-based species and the presence of citrazinic acid type derivates assumed to be responsible for a blue emission is confirmed for both CDs by elemental analysis, infrared spectroscopy, and mass spectrometry, a higher abundance of sp2-hybridized nitrogen is observed for DAP-based CDs, which causes a red-shift of the n-π* absorption band relative to the one of PEI-based CDs. These CD Systems possess high photoluminescence quantum yields (QY) of ∼40% and ∼48% at neutral pH, demonstrating a possible tuning of the optical properties by the amine precursor. pH-Dependent spectroscopic studies revealed a drop in QY to < 9% (pH ∼ 1) and < 21% (pH ∼ 12) for both types of CDs under acidic and basic conditions. In contrast, significant differences in the pHdependency of the n-π* transitions are found for both CD types which are ascribed to different (de)protonation sequences of the CD-specific fluorophores and functional groups using Zeta potential analysis. KW - Fluorescence KW - Particle KW - Nano KW - Surface group analysis KW - Carbon dot KW - C-dot KW - Fluorescent probe KW - Quantum yield KW - Synthesis KW - IR KW - MS KW - Polymer KW - Ligand PY - 2020 DO - https://doi.org/10.1021/acs.jpcc.9b11732 VL - 124 IS - 16 SP - 8894 EP - 8904 PB - American Chemical Society AN - OPUS4-50813 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Rack, A. A1 - Zabler, S. A1 - Riesemeier, Heinrich A1 - Weidemann, Gerd A1 - Müller, Bernd R. A1 - Helfen, L. A1 - Stiller, M. A1 - Knabe, C. A1 - Goebbels, Jürgen A1 - Banhart, J. T1 - Nondestructive 3D insights into foamy metals and bioregenerative ceramics KW - X-ray Computed Tomography KW - Metal foams KW - Bioregenerative ceramics PY - 2008 UR - http://www.helmholtz-berlin.de/media/media/oea/web/pr_webseite/druckschriften/infos/bessy/highlights2007.pdf#page=34 SN - 1611-6127 SP - 34 EP - 35 PB - Berliner Elektronenspeicherring-Gesellschaft für Synchrotronstrahlung CY - Berlin AN - OPUS4-17538 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rack, A. A1 - Riesemeier, Heinrich A1 - Zabler, S. A1 - Weitkamp, T. A1 - Müller, Bernd R. A1 - Weidemann, Gerd A1 - Modregger, P. A1 - Banhart, J. A1 - Helfen, L. A1 - Danilewsky, A.N. A1 - Gräber, H.G. A1 - Heldele, R. A1 - Mayzel, B. A1 - Goebbels, Jürgen A1 - Baumbach, T. ED - Stuart R. Stock, T1 - The high-resolution synchrotron-based imaging stations at the BAMline (BESSY) and TopoTomo (ANKA) N2 - The BAMline at the BESSY light source in Berlin and the TopoTomo beamline at the ANKA synchrotron facility in Karlsruhe (both Germany) operate in the hard X-ray regime (above 6 keV) with similiar photon flux density. For typical imaging applications, a double multilayer monochromator or a filtered white beam is used. In order to optimise the field of view and the resolution of the available indirect pixel detectors, different optical systems have been installed, adapted, respectively, to a large field of view (macroscope) and to high spatial resolution (microscope). They can be combined with different camera systems, ranging from 16-bit dynamic range slow-scan CCDs to fast CMOS cameras. The spatial resolution can be brought substantially beyond the micrometer limit by using a Bragg magnifier. The moderate flux of both beamlines compared to other 3rd generation light sources is compensated by a dedicated scintillator concept. For selected applications, X-ray beam collimation has proven to be a reliable approach to increase the available photon flux density. Absorption contrast, phase contrast, holotomography and refraction-enhanced imaging are used depending on the application. Additionally, at the TopoTomo beamline digital white beam synchrotron topography is performed, using the digital X-ray pixel detectors installed. KW - Microtomography KW - Non-destructive evaluation KW - Coherent imaging KW - X-ray refraction KW - X-ray phase contrast KW - Synchrotron-CT KW - Synchrotron instrumentation KW - Scintillator KW - Bragg magnification KW - Holotomography KW - X-ray topography PY - 2008 DO - https://doi.org/10.1117/12.793721 SN - 0277-786X VL - 7078 SP - 70780X-1 - 70780X-9 AN - OPUS4-18296 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hakim, I. A1 - Laquai, René A1 - Schumacher, David A1 - Müller, Bernd R. A1 - Graja, P. A1 - Meyendorf, N. A1 - Donaldson, S. T1 - The Effect of Manufacturing Conditions on Discontinuity Population and Fatigue Fracture Behavior in Carbon/Epoxy Composites N2 - Carbon fiber composites have been increasingly used in aerospace, military, sports, automotive and other fields due to their excellent properties, including high specific strength, high specific modulus, corrosion resistance, fatigue resistance, and low thermal expansion coefficient. Interlaminar fracture is a serious failure mode leading to a loss in composite stiffness and strength. Iscontinuities formed during manufacturing process degrade the fatigue life and interlaminar fracture resistance of the composite. In his study, three approaches were implemented and their results were correlated to quantify discontinuities effecting static and fatigue interlaminar fracture behavior of carbon fiber composites. Samples were fabricated by hand layup vacuum bagging manufacturing process under three different vacuum levels, indicated High (-686 mmHg), Moderate (-330 mmHg) and Poor (0 mmHg). Discontinuity content was quantified throughthickness by destructive and nondestructive techniques. Eight different NDE methods were conducted including imaging NDE methods: X-Ray laminography, ultrasonic, high frequency eddy current, pulse thermography, pulse phase thermography and lock-in-thermography, and averaging NDE techniques: X-Ray refraction and thermal conductivity measurements. Samples were subsequently destructively serial sectioned through-thickness into several layers. Both static and fatigue interlaminar fracture behavior under Mode I were conducted. The results of several imaging NDE methods revealed the trend in percentages of discontinuity. However, the results of averaging NDE methods showed a clear correlation since they gave specific values of discontinuity through-thickness. Serial sectioning exposed the composite’s internal structure and provided a very clear idea about the type, shape, size, distribution and location of most discontinuities included. The results of mechanical testing showed that discontinuities lead to a decrease in Mode I static interlaminar fracture toughness and a decrease in Mode I cyclic strain energy release rates fatigue life. Finally, all approaches were correlated: the resulted NDE percentages and parameters were correlated with the features revealed by the destructive test of serial sectioning and static and fatigue values in order to quantify discontinuities such as delamination and voids. T2 - QNDE 2016 CY - Atlanta, GA, USA DA - 17.07.2016 KW - Carbon Fber Reinforced Polymers KW - Nondestructive Testing KW - X-ray Imaging KW - Ultrasound KW - Thermography PY - 2017 SN - 978-0-7354-1474-7 DO - https://doi.org/10.1063/1.4974661 SN - 0094-243X N1 - Geburtsname von Schumacher, David: Walter, D. - Birth name of Schumacher, David: Walter, D. VL - 1806 SP - UNSP 090017, 1 EP - 11 PB - AIP Publishing CY - Melville, NY, USA AN - OPUS4-39716 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ast, S. A1 - Fischer, Tobias A1 - Müller, H. A1 - Mickler, W. A1 - Schwichtenberg, M. A1 - Rurack, Knut A1 - Holdt, H.-J. T1 - Integration of the 1,2,3-triazole 'click' motif as a potent signalling element in metal ion responsive fluorescent probes N2 - In a systematic approach we synthesized a new series of fluorescent probes incorporating donor–acceptor (D-A) substituted 1,2,3-triazoles as conjugative π-linkers between the alkali metal ion receptor N-phenylaza-[18]crown-6 and different fluorophoric groups with different electron-acceptor properties (4-naphthalimide, meso-phenyl-BODIPY and 9-anthracene) and investigated their performance in organic and aqueous environments (physiological conditions). In the charge-transfer (CT) type probes 1, 2 and 7, the fluorescence is almost completely quenched by intramolecular CT (ICT) processes involving charge-separated states. In the presence of Na+ and K+ ICT is interrupted, which resulted in a lighting-up of the fluorescence in acetonitrile. Among the investigated fluoroionophores, compound 7, which contains a 9-anthracenyl moiety as the electron-accepting fluorophore, is the only probe which retains light-up features in water and works as a highly K+/Na+-selective probe under simulated physiological conditions. Virtually decoupled BODIPY-based 6 and photoinduced electron transfer (PET) type probes 3–5, where the 10-substituted anthracen-9-yl fluorophores are connected to the 1,2,3-triazole through a methylene spacer, show strong ion-induced fluorescence enhancement in acetonitrile, but not under physiological conditions. Electrochemical studies and theoretical calculations were used to assess and support the underlying mechanisms for the new ICT and PET 1,2,3-triazole fluoroionophores. KW - Charge transfer KW - Click chemistry KW - Electron transfer KW - Fluorescent probes KW - Metal ions PY - 2013 DO - https://doi.org/10.1002/chem.201201575 SN - 0947-6539 SN - 1521-3765 VL - 19 IS - 9 SP - 2990 EP - 3005 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-27742 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rack, A. A1 - Zabler, S. A1 - Müller, Bernd R. A1 - Riesemeier, Heinrich A1 - Weidemann, Gerd A1 - Lange, Axel A1 - Goebbels, Jürgen A1 - Hentschel, Manfred P. A1 - Görner, Wolf T1 - High resolution synchrotron-based radiography and tomography using hard X-rays at the BAMline (BESSY II) N2 - The use of high brilliance and partial coherent synchrotron light for radiography and computed tomography (CT) allows to image micro-structured, multi-component specimens with different contrast modes and resolutions up to submicrometer range. This is of high interest for materials research, life science and non-destructive evaluation applications. An imaging setup for microtomography and radiography installed at BESSY II (a third generation synchrotron light source located in Berlin, Germany) as part of its first hard X-ray beamline (BAMline) can now be used for absorption, refraction as well as phase contrast — dedicated to inhouse research and applications by external users. Monochromatic synchrotron light between 6 keV and 80 keV is attained via a fully automated double multilayer monochromator. For imaging applications the synchrotron beam transmitted by the sample is converted with a scintillator into visible light. By use of microscope optics this luminescence image is then projected onto, e.g., a CCD chip. Several scintillating materials are used in order to optimise the performance of the detector system. Different optical systems are available for imaging ranging from a larger field of view and moderate resolutions (macroscope — up to 14 mm x 14 mm field of view) to high resolution (microscope — down to 0.35 μm pixel size), offering magnifications from 1.8× to 40×. Additionally asymmetric cut Bragg crystals in front of the scintillator can be used for a further magnification in one dimension by a factor of about 20. Slow and fast cameras are available, with up to 16 bit dynamic range. We show the suitability of the setup for numerous applications from materials research and life science. KW - Microtomography KW - Non-destructive evaluation KW - Synchrotron instrumentation KW - Coherent imaging KW - X-ray refraction KW - Phase contrast KW - Holotomography KW - Synchrotron-CT KW - Scintillator KW - Bragg magnification PY - 2008 DO - https://doi.org/10.1016/j.nima.2007.11.020 SN - 0168-9002 SN - 0167-5087 VL - 586 IS - 2 SP - 327 EP - 344 PB - North-Holland CY - Amsterdam AN - OPUS4-17738 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mühler, T. A1 - Helsch, G. A1 - Heinrich, J.G. A1 - Yao, Dongxu A1 - Gräf, S. A1 - Müller, F.A. A1 - Günster, Jens T1 - Strategies for the selective volume sintering of ceramics N2 - The present study is dealing with the basic physics for a novel way to generate a free-formed ceramic body, not like common layer by layer, but directly by Selective Volume Sintering (SVS) in a compact block of ceramic powder. To penetrate with laser light into the volume of a ceramic powder compact it is necessary to investigate the light scattering properties of ceramic powders. Compared with polymers and metals, ceramic materials are unique as they offer a wide optical window of transparency. The optical window typically ranges from below 0.3 up to 5 µm wave length. In the present study thin layers of quartz glass (SiO2) particles have been prepared. As a function of layer thickness and the particle size, transmission and reflection spectra in a wave length range between 0.5 and 2.5 µm have been recorded. Depending on the respective particle size and by choosing a proper relation between particle size and wave length of the incident laser radiation, it is found that light can penetrate a powder compact up to a depth of a few millimeters. With an adjustment of the light absorption properties of the compact the initiation of sintering in the volume of the compact is possible. KW - Additive Manufacturing PY - 2014 DO - https://doi.org/10.1557/jmr.2014.174 SN - 0884-2914 VL - 29 IS - 17 SP - 2095 EP - 2099 PB - Materials Research Society CY - Warrendale, Pa. AN - OPUS4-32544 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rahner, E. A1 - Thiele, T. A1 - Voss, Heike A1 - Müller, F.A. A1 - Bonse, Jörn A1 - Gräf, S. T1 - Objective, high-throughput regularity quantification of laser-induced periodic surface structures (LIPSS) N2 - The growing demand for precise surface functionalization through laser-generated periodic surface structures highlights the necessity for efficient, reproducible, and objective evaluation methods to evaluate their structural regularity. We introduce ReguΛarity (v.1.2.7), a freely available, Python-based software with a graphical user interface for the automated, quantitative assessment of the regularity of laser-induced periodic surfaces structures (LIPSS), obtained from optical microscopy, SEM, or AFM. The software integrates image segmentation, one- and two-dimensional Fourier analyses, and gradient-based orientation determination to facilitate a comprehensive regularity analysis of grating-like (quasi-)periodic surface patterns with spatial periods Λ. This is achieved through the proposed regularity tuple R, composed of five key parameters: the normalized spread of the spatial period RΛ,2D (from 2D-FT), the normalized variation of the most frequent spatial period RΛ (from 1D-FT), the Gini coefficient G, the Dispersion of the LIPSS Orientation Angle δθ (DLOA), and the mean phase deviation . To demonstrate its applicability, we compare ideal sinusoidal patterns with SEM images obtained from LIPSS on stainless steel (AISI 316L) and aluminum alloy (AlMg5) surfaces, confirming the software’s ability to objectively distinguish between varying levels of structural regularity. ReguΛarity facilitates high-throughput analysis and data-driven process optimization in surface engineering and laser materials processing. KW - Laser-induced periodic surface structures (LIPSS) KW - Image processing KW - Regularity quantification KW - Fourier analysis KW - Structural homogeneity PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-654070 DO - https://doi.org/10.1016/j.apsusc.2026.165919 SN - 0169-4332 VL - 726 SP - 1 EP - 12 PB - Elsevier B.V. AN - OPUS4-65407 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, S. T1 - Langzeitlagerung von Klärschlammaschen ab 2029? Erste Erfahrungen zur Phosphorrückgewinnung aus deponierten Klärschlammverbrennungsaschen N2 - Das Institut für Siedlungswasserwirtschaft (ISA) der RWTH Aachen University sowie die Bundesanstalt für Materialforschung und -prüfung (BAM) untersuchen gemeinsam fünf deponierte KSA, die von drei Deponiebetreibern ausgebaut und zur Verfügung gestellt wurden sind. Im Fokus der Untersuchungen stehen die physikalische und chemische Charakterisierung der deponierten KSA sowie deren P-Rückgewinnungspotenzial bei der Behandlung in thermochemischen sowie nasschemischen Verfahren. Diese Ergebnisse werden im Vergleich mit „frischen“, also nicht deponierten KSA-Proben vergleichbarer Herkunft bewertet, um so den Einfluss der Lagerung auf die KSA zu erfassen. T2 - Berliner Klärschlamm Konferenz CY - Berlin, Germany DA - 11.11.2025 KW - Phosphor KW - Langzeitlagerung KW - Deponie KW - Rückgewinnung KW - Klärschlammasche PY - 2025 AN - OPUS4-64832 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, S. A1 - Herzel, Hannes A1 - Adam, Christian A1 - Montag, D. ED - Holm, O. ED - Thomé-Kozmiensky, E. ED - Quicker, P. ED - Kopp-Assenmacher, S. T1 - Langzeitlagerung von Klärschlammaschen ab 2029? Erste Erfahrungen zur Phosphorrückgewinnung aus deponierten Klärschlammverbrennungsaschen N2 - Das Institut für Siedlungswasserwirtschaft (ISA) der RWTH Aachen University sowie die Bundesanstalt für Materialforschung und -prüfung (BAM) untersuchen gemeinsam fünf deponierte KSA, die von drei Deponiebetreibern ausgebaut und zur Verfügung gestellt wurden sind. Im Fokus der Untersuchungen stehen die physikalische und chemische Charakterisierung der deponierten KSA sowie deren P-Rückgewinnungspotenzial bei der Behandlung in thermochemischen sowie nasschemischen Verfahren. Diese Ergebnisse werden im Vergleich mit „frischen“, also nicht deponierten KSA-Proben vergleichbarer Herkunft bewertet, um so den Einfluss der Lagerung auf die KSA zu erfassen. T2 - Berliner Klärschlamm Konferenz CY - Berlin, Germany DA - 11.11.2025 KW - Klärschlammasche KW - Recycling KW - Deponie KW - Monoverbrennung PY - 2025 SN - 978-3-911006-63-7 VL - 8 SP - 192 EP - 202 PB - Thomé-Kozmiensky Verlag GmbH CY - Neuruppin AN - OPUS4-65017 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lackmann, C. A1 - Velki, M. A1 - Šimić, A. A1 - Müller, Axel A1 - Braun, U. A1 - Ečimović, S. A1 - Hollert, H. T1 - Two types of microplastics (polystyrene-HBCD and car tire abrasion) affect oxidative stress-related biomarkers in earthworm Eisenia andrei in a time-dependent manner N2 - Microplastics are small plastic fragments that are widely distributed in marine and terrestrial environments. While the soil ecosystem represents a large reservoir for plastic, research so far has focused mainly on the impact on aquatic ecosystems and there is a lack of information on the potentially adverse effects of microplastics on soil biota. Earthworms are key organisms of the soil ecosystem and are due to their crucial role in soil quality and fertility a suitable and popular model organism in soil ecotoxicology. Therefore, the aim of this study was to gain insight into the effects of environmentally relevant concentrations of microplastics on the earthworm Eisenia andrei on multiple levels of biological organization after different exposure periods. Earthworms were exposed to two types of microplastics: (1) polystyrene-HBCD and (2) car tire abrasion in natural soil for 2, 7, 14 and 28 d. Acute and chronic toxicity and all subcellular investigations were conducted for all exposure times, avoidance behavior assessed after 48 h and reproduction after 28 d. Subcellular endpoints included enzymatic biomarker responses, namely, carboxylesterase, glutathione peroxidase, acetylcholinesterase, glutathione reductase, glutathione S-transferase and catalase activities, as well as fluorescence-based measurements of oxidative stress-related markers and multixenobiotic resistance activity. Multiple biomarkers showed significant changes in activity, but a recovery of most enzymatic activities could be observed after 28 d. Overall, only minor effects could be observed on a subcellular level, showing that in this exposure scenario with environmentally relevant concentrations based on German pollution levels the threat to soil biota is minimal. However, in areas with higher concentrations of microplastics in the environment, these results can be interpreted as an early warning signal for more adverse effects. In conclusion, these findings provide new insights regarding the ecotoxicological effects of environmentally relevant concentrations of microplastics on soil organisms. KW - Microplastics KW - Earthworms KW - Toxicity KW - Biomarker KW - oxidative stress PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-545423 DO - https://doi.org/10.1016/j.envint.2022.107190 VL - 163 SP - 1 EP - 12 PB - Elsevier Ltd. AN - OPUS4-54542 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Liens, A. A1 - Reveron, H. A1 - Douillard, T. A1 - Blanchard, N. A1 - Lughi, V. A1 - Sergo, V. A1 - Laquai, René A1 - Müller, Bernd R. A1 - Bruno, Giovanni A1 - Schomer, S. A1 - Fürderer, T. A1 - Adolfsson, E. A1 - Courtois, N. A1 - Swain, M. A1 - Chevalier, J. T1 - Phase transformation induces plasticity with negligible damage in ceria-stabilized zirconia-based ceramics N2 - Ceramics and their composites are in general brittle materials because they are predominantly made up of ionic and covalent bonds that avoid dislocation motion at room temperature. However, a remarkable ductile behavior has been observed on newly developed 11 mol.% ceria-stabilized zirconia (11Ce-TZP) composite containing fine alumina (8 vol.% Al2O3) and elongated strontium hexa-aluminate (8 vol.% SrAl12O19) grains. The as-synthesized composite also has shown full resistance to Low Temperature Degradation (LTD), relatively high strength and exceptionally high Weibull modulus, allowing its use in a broader range of biomedical applications. In this study, to deepen the understanding of plastic deformation in Ce-TZP based composites that could soon be used for manufacturing dental implants, different mechanical tests were applied on the material, followed by complete microstructural characterization. Distinct from pure Ce-TZP material or other zirconia-based ceramics developed in the past, the material here studied can be permanently strained without affecting the Young modulus, indicating that the ductile response of tested samples cannot be associated to damage occurrence. This ductility is related to the stress-induced tetragonal to monoclinic (t-m) zirconia phase transformation, analogue to Transformation-Induced Plasticity (TRIP) steels, where retained austenite is transformed to martensite. The aim of this study is to corroborate if the observed plasticity can be associated exclusively to the zirconia t-m phase transformation, or also to microcraking induced by the transformation. The t-m transformed-zones produced after bending and biaxial tests were examined by X-ray refraction and SEM/TEM coupled with Raman. The results revealed that the observed elastic-plastic behavior occurs without extensive microcracking, confirming a purely elastic-plastic behavior driven by the phase transformation (absence of damage). KW - Zirconia KW - Ceria KW - Ceramic matrix composite KW - Plasticity KW - Phase transformation KW - X-Ray Refraction PY - 2020 UR - http://www.sciencedirect.com/science/article/pii/S1359645419307177 DO - https://doi.org/10.1016/j.actamat.2019.10.046 SN - 1359-6454 VL - 183 SP - 261 EP - 273 PB - Elsevier Ltd. AN - OPUS4-49740 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mielke, Johannes A1 - Dohányosová, P. A1 - Müller, P. A1 - López-Vidal, S. A1 - Hodoroaba, Vasile-Dan T1 - Evaluation of electrospray as a sample preparation tool for electron microscopic investigations: Toward quantitative evaluation of nanoparticles N2 - The potential of electrospray deposition, for the controlled preparation of particles for imaging in electron microscopes, is evaluated on various materials: from mono-modal suspensions of spherical particles to multimodal suspensions and to real-world industrial materials. It is shown that agglomeration is reduced substantially on the sample carrier, compared with conventional sample preparation techniques. For the first time, it is possible to assess the number concentration of a tri-modal polystyrene suspension by electron microscopy, due to the high Deposition efficiency of the electrospray. We discovered that some suspension stabilizing surfactants form artifact particles during electrospraying. These can be avoided by optimizing the sprayed suspension. KW - Electrospary KW - Nanoparticles KW - Sample preparation KW - TEM grid KW - SEM PY - 2017 DO - https://doi.org/10.1017/S1431927616012587 SN - 1431-9276 SN - 1435-8115 VL - 23 IS - 1 SP - 163 EP - 172 PB - Cambridge University Press AN - OPUS4-39244 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Cant, D. J. H. A1 - Minelli, C. A1 - Sparnacci, K. A1 - Müller, Anja A1 - Kalbe, H. A1 - Stoger-Pollach, M. A1 - Unger, Wolfgang A1 - Werner, W. S. M. A1 - Shard, A. G. T1 - Surface-Energy Control and Characterization of Nanoparticle Coatings N2 - Accurate and reproducible measurement of the structure and properties of high-value nanoparticles is extremely important for their commercialization. A significant proportion of engineered nanoparticle systems consist of some form of nominally core-shell structure, whether by design or unintentionally. Often, these do not form an ideal core-shell structure, with typical deviations including polydispersity of the core or shell, uneven or incomplete shells, noncentral cores, and others. Such systems may be created with or without intent, and in either case an understanding of the conditions for formation of such particles is desirable. Precise determination of the structure, composition, size, and shell thickness of such particles can prove challenging without the use of a suitable range of characterization techniques. Here, the authors present two such polymer core-shell nanoparticle systems, consisting of polytetrafluoroethylene cores coated with a range of thicknesses of either polymethylmethacrylate or polystyrene. By consideration of surface energy, it is shown that these particles are expected to possess distinctly differing coating structures, with the polystyrene coating being incomplete. A comprehensive characterization of these systems is demonstrated, using a selection of complementary techniques including scanning electron microscopy, scanning transmission electron microscopy, thermogravimetric analysis, dynamic light scattering, differential centrifugal sedimentation, and X-ray photoelectron spectroscopy. By combining the results provided by these techniques, it is possible to achieve superior characterization and understanding of the particle structure than could be obtained by considering results separately. KW - Nanoparticles KW - Core-shell KW - XPS KW - Size KW - Thickness KW - Damage PY - 2020 DO - https://doi.org/10.1021/acs.jpcc.0c02161 VL - 124 IS - 20 SP - 11200 EP - 11211 PB - ACS CY - Washington DC AN - OPUS4-50899 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, Anja A1 - Sparnacci, K. A1 - Unger, Wolfgang A1 - Tougaard, S. T1 - Determining nonuniformities of core-shell nanoparticle coatings by analysis of the inelastic background of X-ray photoelectron spectroscopy survey spectra N2 - Most real core-shell nanoparticle (CSNP) samples deviate from an ideal core-shell structure potentially having significant impact on the particle properties. An ideal structure displays a spherical core fully encapsulated by a shell of homogeneous thickness, and all particles in the sample exhibit the same shell thickness. Therefore, analytical techniques are required that can identify and characterize such deviations. This study demonstrates that by analysis of the inelastic background in X-ray photoelectron spectroscopy (XPS) survey spectra, the following types of deviations can be identified and quantified: the nonuniformity of the shell thickness within a nanoparticle sample and the incomplete encapsulation of the cores by the shell material. Furthermore, CSNP shell thicknesses and relative coverages can be obtained. These results allow for a quick and straightforward comparison between several batches of a specific CSNP, different coating approaches, and so forth. The presented XPS methodology requires a submonolayer distribution of CSNPs on a substrate. Poly(tetrafluoroethylene)-poly(methyl methacrylate) and poly(tetrafluoroethylene)-polystyrene polymer CSNPs serve as model systems to demonstrate the applicability of the approach. KW - Core-shell KW - Nanoparticles KW - Inelastic background KW - Polymers KW - QUASES KW - XPS PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-511315 DO - https://doi.org/10.1002/sia.6865 SN - 0142-2421 SN - 1096-9918 VL - 52 SP - 1 EP - 8 PB - Wiley CY - Chichester AN - OPUS4-51131 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Brüngel, R. A1 - Rückert, J. A1 - Müller, P. A1 - Babick, F. A1 - Friedrich, C. M. A1 - Ghanem, A. A1 - Hodoroaba, Vasile-Dan A1 - Mech, A. A1 - Weigel, S. A1 - Wohlleben, W. A1 - Rauscher, H. T1 - NanoDefiner Framework and e-Tool Revisited According to the European Commission’s Nanomaterial Definition 2022/C 229/01 N2 - The new recommended definition of a nanomaterial, 2022/C 229/01, adopted by the European Commission in 2022, will have a considerable impact on European Union legislation addressing chemicals, and therefore tools to implement this new definition are urgently needed. The updated NanoDefiner framework and its e-tool implementation presented here are such instruments, which help stakeholders to find out in a straightforward way whether a material is a nanomaterial or not. They are two major outcomes of the NanoDefine project, which is explicitly referred to in the new definition. This work revisits the framework and e-tool, and elaborates necessary adjustments to make these outcomes applicable for the updated recommendation. A broad set of case studies on representative materials confirms the validity of these adjustments. To further foster the sustainability and applicability of the framework and e-tool, measures for the FAIRification of expert knowledge within the e-tool’s knowledge base are elaborated as well. The updated framework and e-tool are now ready to be used in line with the updated recommendation. The presented approach may serve as an example for reviewing existing guidance and tools developed for the previous definition 2011/696/EU, particularly those adopting NanoDefine project outcomes. KW - Nanomaterial definition KW - Nanomaterial categorisation KW - Nanomaterial regulation KW - Nanomaterial legislation KW - Decision support KW - FAIRification PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-571618 DO - https://doi.org/10.3390/nano13060990 SN - 2079-4991 VL - 13 IS - 6 - Special Issue "Identification and Quantification of Nanomaterials" SP - 1 EP - 16 PB - MDPI CY - Basel, CH AN - OPUS4-57161 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Baer, D. R. A1 - Cant, D. J. H. A1 - Castner, D. G. A1 - Ceccone, G. A1 - Engelhard, M. H. A1 - Karakoti, A. S. A1 - Müller, Anja ED - Hodoroaba, Vasile-Dan ED - Unger, Wolfgang ED - Shard, A. G. T1 - Preparation of nanoparticles for surface analysis N2 - A variety of methods used to prepare nano-objects for surface analysis are described along with information about when they might be best applied. Intrinsic properties of NPs which complicate their characterization and need to be considered when planning for surface or other analyses of NPs are identified, including challenges associated with reproducible synthesis and functionalization of the particles as well as their dynamic nature. The relevant information about the sample preparation processes, along with analysis details and data that need to be added to the collection of material provenance information is identified. Examples of protocols that have been successfully used for preparation of nano-objects for surface analysis are included in an annex. KW - Sample preparation KW - Nanoparticles KW - Surface chemistry KW - XPS KW - Dynamic behavior KW - Nano-object KW - Surface analysis PY - 2020 SN - 978-0-12-814182-3 DO - https://doi.org/10.1016/B978-0-12-814182-3.00018-3 SP - 295 EP - 347 PB - Elsevier CY - Amsterdam AN - OPUS4-50186 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Heinrich, Thomas A1 - Darlatt, Erik A1 - Lippitz, Andreas A1 - Müller, S. A1 - Schalley, C. A1 - Unger, Wolfgang T1 - Systematic XP and NEXAFS spectroscopy studies of (ter-)pyridineterminated self-assembled monolayers and their addressability for functional molecules N2 - The chemical composition of surfaces functionalized with self-assembled monolayers (SAMs) is an important parameter that determines their performance in a broad range of applications, from immobilizing molecular machines to initiation and growth control of MOFs (Metal-Organic Frameworks). In this article, a critical Survey of XPS (X-ray photoelectron spectroscopy) and NEXAFS (near edge X-ray absorption fine structure) spectroscopy data for pyridine-functionalized monolayers on gold surfaces is presented to compile correlations that have been indiscernible before. Monolayers with aromatic backbones are compared to monolayers with aliphatic backbones. Monolayers with pyridine end-groups are compared to mixed monolayers formed terpyridine-functionalized by molecules end-groups and non-functionalized molecules. Thiol-oxidation during ageing of the SAMs in air is addressed. And finally, the addressability of the SAMs for the deposition of metal-ions and organic molecules is investigated and compared. This work consequently delivers a comprehensive set of spectroscopic data of (ter-)pyridine-terminated SAMs and their performance as template for the preparation of functional multilayers of macrocycles exhibiting a preferential orientation. KW - (ter-)pyridineterminated self-assembled monolayer KW - X-ray Photoelectron Spectroscopy (XPS) KW - NEXAFS PY - 2019 DO - https://doi.org/10.1016/j.elspec.2019.03.011 VL - 233 SP - 28 EP - 37 PB - Elsevier B.V. AN - OPUS4-48018 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Horn, Wolfgang A1 - Jann, Oliver A1 - Brosig, L. A1 - Müller, B. A1 - Mertes, A. A1 - de Lima Vasconcelos, S. T1 - Emissions- und geruchsarme Bauprodukte für energieeffiziente Gebäude – Entwicklung von Anforderungen und Konzepten für den Blauen Engel aus Klimaschutzsicht N2 - Menschen, die in der gemäßigten Klimazone leben, verbringen bis zu 90% ihres Lebens in Innenräumen. Deshalb hat das Innenraumklima eine sehr große Bedeutung für deren Wohlergehen, Gesundheit und Leistungsfähigkeit. In Deutschland wird ca. 40% der eingesetzten Primärenergie für das Heizen, Kühlen und Klimatisieren der Innenräume verwendet. Das Forschungsvorhaben hat eine Laufzeit vom Oktober 2013 bis März 2017. Es wird in Kooperation mit der Bundesanstalt für Materialforschung und –prüfung (BAM) und der Hochschule für Technik und Wirtschaft Berlin (HTW Berlin) durchgeführt. Die HTW Berlin koordiniert das Projekt. Die Rheinisch-Westfälische Technische Hochschule Aachen (RWTH) wird teilweise über einen Auftrag in das Projekt integriert. Ziel des Projektes ist es Baustoffe auf ihre Geruchsemissionen zu untersuchen, um Bauprodukte mit niedrigen Emissionen und Gerüchen identifizieren zu können. Den Verbraucherinnen und Verbrauchern wird somit die Möglichkeit gegeben emissions- und geruchsarme Baustoffe zu wählen. Die Aufgabenstellung des Projektes ist nachfolgend aufgeführt: Arbeitspaket 1: Geruchsmessung bei Produkten mit dem Blauen Engel (siehe Kapitel 4 und 5); Arbeitspaket 2: Untersuchung von Vergleichsmaßstäben (siehe Kapitel 6); Arbeitspaket 3: Untersuchung der Linearität der Acetonskala (siehe Kapitel 7); Arbeitspaket 4: Erstellung einer Produktdatenbank (siehe Kapitel 8). Die Geruchsuntersuchung ist in den Vergabekriterien für den „Blauen Engel“ für textile Bodenbeläge (RAL UZ-128) eingebunden worden. Aus den weiteren Untersuchungen sind für die Normung wichtige Erkenntnisse erarbeitet worden. KW - VOC Emissionen KW - Geruch KW - Bewertung KW - Innenraumluftqualtität KW - Bodenbeläge PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-487223 UR - https://www.umweltbundesamt.de/publikationen/emissions-geruchsarme-bauprodukte-fuer UR - https://www.umweltbundesamt.de/sites/default/files/medien/1410/publikationen/2019-08-20-texte_92-2019_emissionsarme-bauprodukte.pdf SN - 1862-4804 VL - 92 SP - 1 EP - 106 PB - Umweltbundesamt CY - Dessau-Roßlau AN - OPUS4-48722 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - de Lima Vasconcelos, S. A1 - Sattler, M. A1 - Müller, B. A1 - Plehn, W. A1 - Horn, Wolfgang T1 - The Influence of textile floor coverings on the indoor air quality N2 - Textile floor coverings are often used in offices and residential buildings. Large areas like meeting rooms, cinemas, theaters and hotels are often equipped with such coverings. They contribute to the comfort of the users as they provide high pedaling comfort and sound absorption. The weakness of these building materials is due to the odor emission that is released from the floor covering, which affects the comfort of the users. A bad air quality and the resulting dissatisfaction can lead to lower employee productivity. The research project of the Hochschule für Technik und Wirtschaft Berlin (HTW-Berlin) is promoted by the German Environment Agency (UBA). The project has the following title: Low-emission and low-odor building products for energy-efficient buildings - Development of requirements and concepts for the Blue Angel from a climate protection perspective; investigates the emission and odor behavior of textile floor coverings (Emissions- und geruchsarme Bauprodukte für energieeffiziente Gebäude - Entwicklung von Anforderungen und Konzepten für den Blauen Engel aus Klimaschutzsicht; untersucht das Emissions- und Geruchsverhalten textiler Bodenbeläge). T2 - Clima 2019 Congress CY - Bucharest, Romania DA - 26.05.2019 KW - VOC Emissionen KW - Geruch KW - Bodenbelag KW - AgBB Bewertung PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-487341 DO - https://doi.org/10.1051/e3sconf/201911102051 SN - 2267-1242 VL - 111 SP - 02051-1 EP - 02051-6 PB - EDP Sciences AN - OPUS4-48734 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Balzer, R. A1 - Behrens, H. A1 - Schuth, S. A1 - Waurischk, Tina A1 - Reinsch, Stefan A1 - Müller, Ralf A1 - Fechtelkord, M. A1 - Deubener, J. T1 - The influence of H2O and SiO2 on the structure of silicoborate glasses N2 - To understand the impact of dissolved water on structure and properties, four boron-rich glasses of molar compositions 15-x Na2O x CaO 15 SiO2 70 B2O3 (with x=0, 7.5, 10) and 10 Na2O 15 SiO2 75 B2O3 were prepared and subsequently hydrated (up to 8 wt% H2O). Density measurements show a non-linear trend upon hydration implying large structural changes in particular at water contents<2 wt%. Near-infrared spectroscopy shows hydroxyl groups are the dominant species in all glasses upon the entire range of water content. Molecular H2O is detectable only at total water contents>2 wt%. 11B MAS NMR spectra show that the abundance of BO4 species is mainly controlled by ratio of (Na2O+CaO)/B2O3 while incorporation of water plays a minor role. Compared to borate glasses, the efficiency of formation of BO4 tetrahedra is favored by crosslinking of the network by SiO4-units. The glass transition temperatures, determined by differential thermal analysis, decreases continuously with water content due to breakage of B-O-B bonds by hydrolysis. However, compared to Silicates and aluminosilicates, the effect of dissolved water is less pronounced which can be explained by weaker B-O-B bonds in comparison to Si-O-Si bonds. KW - High pressure KW - Water speciation KW - Silicoborate glasses KW - Infrared spectroscopy KW - NMR spectroscopy PY - 2019 DO - https://doi.org/10.1016/j.jnoncrysol.2019.05.030 VL - 519 SP - 38 EP - 51 PB - Elsevier B.V. AN - OPUS4-48748 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Akatsuka, C. A1 - Honma, T. A1 - Müller, Ralf A1 - Reinsch, Stefan A1 - Tanaka, S. A1 - Komatsu, T. T1 - Surface crystallization and gas bubble formation during conventional heat treatment in Na2MnP2O7 glass N2 - The crystallization behavior of sodium ion conductive Na2MnP2O7 glass was examined to clarify the crystallization mechanism. The formation of thermodynamically metastable phase, layered Na2MnP2O7, at the surface of the glass occurred. Heat treatment at 430 °C for 3 h lead to surface crystals of Na2MnP2O7 oriented with the (101) direction perpendicular to the sample surface. As the heat treatment temperature increased, the glass-ceramic samples deformed, and the presence numerous micro bubbles due to dissolved water was detected. KW - Glass-ceramic KW - Crystallization KW - Sodium ion batteries KW - Bubble formation KW - Phosphate PY - 2019 DO - https://doi.org/10.1016/j.jnoncrysol.2019.01.030 VL - 510 SP - 36 EP - 41 PB - Elsevier B.V. AN - OPUS4-49618 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Blaeß, Carsten A1 - Müller, Ralf A1 - Poologasundarampilai, G. A1 - Brauer, D. S. T1 - Sintering and concomitant crystallization of bioactive glasses N2 - The sintering of bioactive glasses allows for the preparation of complex structures, such as three‐dimensional porous scaffolds. Such 3D constructs are particularly interesting for clinical applications of bioactive glasses in bone regeneration, as the scaffolds can act as a guide for in‐growing bone cells, allowing for good Integration with existing and newly formed tissue while the scaffold slowly degrades. Owing to the pronounced tendency of many bioactive glasses to crystallize upon heat treatment, 3D scaffolds have not been much exploited commercially. Here, we investigate the influence of crystallization on the sintering behavior of several bioactive glasses. In a series of mixed‐alkali glasses an increased CaO/alkali metal oxide Ratio improved sintering compared to Bioglass 45S5, where dense sintering was inhibited. Addition of small amounts of calcium fluoride helped to keep melting and sintering temperatures low. Unlike glass 13‐93, these new glasses crystallized during sintering but this did not prevent densification. Variation in bioactive glass particle size allowed for fine‐tuning the microporosity resulting from the sintering process. KW - Bioactive glass KW - Crystallization KW - Scaffolds KW - Sintering PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-485458 DO - https://doi.org/10.1111/ijag.13477 SN - 2041-1286 VL - 10 IS - 4 SP - 449 EP - 462 PB - Wiley AN - OPUS4-48545 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kupsch, Andreas A1 - Laquai, René A1 - Müller, Bernd R. A1 - Paciornik, S. A1 - Horvath, J. A1 - Tushtev, K. A1 - Rezwan, K. A1 - Bruno, Giovanni T1 - Evolution of Damage in All-Oxide Ceramic Matrix Composite After Cyclic Loading N2 - While structural ceramics usually display a brittle mechanical behavior, their composites may show nonlinearities, mostly due to microcracking. Herein, the stiffness evolution of a sandwich-like laminate of an Al2O3 15%vol. ZrO2 matrix reinforced with Nextel 610 fibers is studied as a function of number of cycles N in tension. The stiffness of the composite degrades with increasing N, indicating microcracking. However, synchrotron X-ray refraction radiography shows that the internal specific surface of such cracks varies differently. A modeling strategy is developed for the calculation of the equivalent stiffness of mixtures (first the matrix and then the sandwich), based on the Voigt and Reuß schemes. The Bruno–Kachanov model is then used to estimate the initial microcrack density in the matrix (due to the thermal expansion mismatch) and the amount of microcracking increase upon cyclic loading. The stiffness in the composite degrades dramatically already after 20 000 cycles but then remains nearly constant. The combination of mechanical testing, quantitative imaging analysis, and modeling provides insights into the damage mechanisms acting: microcrack propagation is more active than microcrack initiation upon cyclic loading, but the second also occurs. This scenario is similar but not equal to previous results on porous and microcracked ceramics. KW - Ceramic matrix composites KW - Homogenization schemes KW - Microcracking KW - Nonlinear behavior KW - Synchrotron X-ray refraction radiography PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-534541 DO - https://doi.org/10.1002/adem.202100763 SN - 1527-2648 SN - 1438-1656 VL - 24 IS - 6 SP - 2100763 -1 EP - 2100763 -13 PB - VCH GmbH CY - Weinheim AN - OPUS4-53454 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mielke, Johannes A1 - Dohányosová, P. A1 - Müller, P. A1 - Lopez, S. A1 - Hodoroaba, Vasile-Dan T1 - Electrospray as a sample preparation tool for electron microscopic investigations: Toward quantitative evaluation of nanoparticles N2 - The potential of electrospray deposition, for the controlled preparation of particles for imaging in electron microscopes, is evaluated on various materials: from mono-modal suspensions of spherical particles to multimodal suspensions and to real-world industrial materials. It is shown that agglomeration is reduced substantially on the sample carrier, compared with conventional sample preparation techniques. For the first time, it is possible to assess the number concentration of a tri-modal polystyrene suspension by electron microscopy, due to the high deposition efficiency of the electrospray. We discovered that some suspension stabilizing surfactants form artifact particles during electrospraying. These can be avoided by optimizing the sprayed suspension. KW - Electrospray deposition KW - Nanoparticles KW - SEM KW - TEM KW - Sample preparation PY - 2017 UR - https://www.cambridge.org/core/journals/microscopy-and-microanalysis/article/electrospray-as-a-sample-preparation-tool-for-electron-microscopic-investigations-toward-quantitative-evaluation-of-nanoparticles/483B212FF290B7EC001A212A19E4E72A DO - https://doi.org/10.1017/S1431927617010145 SN - 1435-8115 SN - 1431-9276 VL - 23 IS - S1 (July) SP - 1896 EP - 1897 PB - Cambridge University Press CY - New York, NY, U.S.A. AN - OPUS4-42453 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Saathoff, F. A1 - Cantré, S. A1 - Müller, Werner T1 - The new German filtration criteria for geosynthetics in landfill construction N2 - The recent German landfill ordinance includes a certification requirement for geosynthetics used in landfill liner and capping systems. The certification guidelines describe the basis for the design of geosynthetics used in landfill construction. In this paper the new German filter criteria for geosynthetics are presented with a particular focus on geotextile filters in geocomposite drains. T2 - Euro GEO 5 - 5th European geosynthetics congress CY - Valencia, Spain DA - 16.09.2012 KW - Filtration KW - Geosynthetics KW - Landfill PY - 2012 SN - 978-0415-64340-5 VL - 5 IS - Topic: Transport SP - 264 EP - 268 AN - OPUS4-26934 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wonneberger, R. A1 - Gräf, S. A1 - Bonse, Jörn A1 - Wisniewski, W. A1 - Freiberg, K. A1 - Hafermann, M. A1 - Ronning, C. A1 - Müller, F. A. A1 - Undisz, A. T1 - Tracing the Formation of Femtosecond Laser-Induced Periodic Surface Structures (LIPSS) by Implanted Markers N2 - The generation of laser-induced periodic surface structures (LIPSS) using femtosecond lasers facilitates the engineering of material surfaces with tailored functional properties. Numerous aspects of their complex formation process are still under debate, despite intensive theoretical and experimental research in recent decades. This particularly concerns the challenge of verifying approaches based on electromagnetic effects or hydrodynamic processes by experiment. In the present study, a marker experiment is designed to conclude on the formation of LIPSS. Well-defined concentration depth profiles of 55Mn+- and 14N+-ions were generated below the polished surface of a cast Mn- and Si-free stainless steel AISI 316L using ion implantation. Before and after LIPSS generation, marker concentration depth profiles and the sample microstructure were evaluated by using transmission electron microscopy techniques. It is shown that LIPSS predominantly formed by material removal through locally varying ablation. Local melting and resolidification with the redistribution of the material occurred to a lesser extent. The experimental design gives quantitative access to the modulation depth with a nanometer resolution and is a promising approach for broader studies of the interactions of laser beams and material surfaces. Tracing LIPSS formation enables to unambiguously identify governing aspects, consequently guiding the path to improved processing regarding reproducibility, periodicity, and alignment. KW - Laser-induced periodic surface structures (LIPSS) KW - Femtosecond laser processing KW - Ion implantation KW - Transmission Electron Microscopy (TEM) KW - Stainless steel PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-623990 DO - https://doi.org/10.1021/acsami.4c14777 SN - 1944-8244 (Print) SN - 1944-8252 (Online) VL - 17 IS - 1 SP - 2462 EP - 2468 PB - ACS Publications AN - OPUS4-62399 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Onyenso, Gabriel A1 - AI-Zawity, Jiwar A1 - Farahbakhsh, Nastaran A1 - Schardt, Annika A1 - Yadigarli, Aydan A1 - Vakamulla Raghu, Swathi Naidu A1 - Engelhard, Carsten A1 - Müller, Mareike A1 - Schönherr, Holger A1 - Killian, Manuela S. T1 - Novel Ag-modified zirconia nanomaterials with antibacterial activity N2 - The outcome of an implant procedure largely depends on the implant's surface properties. Biomaterials are now designed to have surfaces with multifunctionality, such as favorable tissue integration and the ability to combat bacterial adhesion and colonization. Herein, we report on a simple approach to improve the antibacterial properties of zirconia nanotubes (ZrNTs) coatings by decorating with silver nanoparticles (AgNP), achieved through electrochemical anodization of a zirconium–silver alloy (Zr–Ag). The AgNPs were shown to partially consist of Ag2O, potentially enhancing the availability of Ag+ ions for antibacterial activity. The modified ZrNTs were characterized using SEM, EDS, ToF-SIMS, and XPS to determine their structural morphology and chemical composition, and were further subjected to antibacterial testing. The silver and zirconium ion release behavior was monitored via ICP-MS. ZrNTs decorated with AgNP exhibit strong antimicrobial activity (>99% bacterial killing) against both S. aureus and E. coli. Antimicrobial tests indicate that the antibacterial activity against the Gram-positive pathogen S. aureus was improved by a factor of 100 compared to unmodified ZrNTs, while unmodified ZrNTs already showed a comparable reduction of viable Gram-negative E. coli. This strategy illustrates a straightforward and effective modification that optimizes the interface between the host environment and the biomaterial surface to meet the very important criteria of biocompatibility and active antibacterial response. KW - Mass Spectrometry KW - Nanoparticles KW - Advanced Materials KW - ICP-MS KW - Antimicrobial material KW - ToF-SIMS PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-653990 DO - https://doi.org/10.1039/d5ra07099f SN - 2046-2069 VL - 16 IS - 3 SP - 2286 EP - 2297 PB - Royal Society of Chemistry (RSC) AN - OPUS4-65399 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Götschel, S. A1 - Maierhofer, Christiane A1 - Müller, Jan P. A1 - Rothbart, Nick A1 - Weiser, M. T1 - Quantitative defect reconstruction in active thermography for fiber-reinforced composites N2 - Carbon-fiber reinforced composites are becoming more and more important in the production of light-weight structures, e.g., in the automotive and aerospace industry. Thermography is often used for non-destructive testing of These products, especially to detect delaminations between different layers of the composite. In this presentation, we aim at methods for defect reconstruction from thermographic measurements of such carbon-fiber reinforced composites. The reconstruction results shall not only allow to locate defects, but also give a quantitative characterization of the defect properties. We discuss the simulation of the measurement process using finite element methods, as well as the experimental validation on flat bottom holes. Especially in pulse thermography, thin boundary layers with steep temperature gradients occurring at the heated surface need to be resolved. Here we use the combination of a 1D analytical solution combined with numerical solution of the remaining defect equation. We use the simulations to identify material Parameters from the measurements. Finally, fast heuristics for reconstructing defect geometries are applied to the acquired data, and compared for their accuracy and utility in detecting different defects like back surface defects or delaminations. T2 - 19th World Conference on Non-Destructive Testing 2016 CY - München, Germany DA - 13.06.2016 KW - Active thermography KW - Numerical simulation KW - Time-resolved thermogram KW - Thermal wave PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-366644 UR - https://www.wcndt2016.com/Programme/show/Th-4-C-4 VL - 2016 SP - Th.4.C.4-1 EP - Th.4.C.4-10 AN - OPUS4-36664 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kreutzbruck, Marc A1 - Bauer, P. A1 - Caspers, F. A1 - Heck, S. A1 - Müller, F. A1 - Pohl, Rainer A1 - Scheuerlein, C. A1 - Sickert, Roland A1 - Maierhofer, Christiane A1 - Brackrock, Daniel T1 - Sensoren für Verbunddrähte aus Niob-Titan und Kupfer N2 - Der Large Hadron Collider (LHC) des europäischen Kernforschungszentrums CERN ist einer der weltweit größten und leistungsfähigsten Teilchenbeschleuniger. Um den Teilchenstrahl auf seiner Kreisbahn zu halten, werden mit Hilfe supraleitender Spulen sehr starke Magnetfelder erzeugt. Die hierzu benötigten hohen Ströme werden über Verbunddrähte aus Niob-Titan und Kupfer geleitet. Die Drähte werden u.a. durch Ultraschallschweißungen miteinander verbunden. Eine mangelhafte Verbindung kann zur Erwärmung der Kontaktstelle und in Folge davon zum Zusammenbruch der Supraleitung führen. Auf Anfrage des CERN wurden an der BAM Untersuchungen zur Prüfbarkeit solcher Verbindungen bei Umgebungstemperatur durchgeführt. Es gelang, für einen Verbindungstypen einen Wirbelstromsensor für eine manuelle Prüfung zu entwickeln. Ein Prototyp des Sensors befindet sich beim CERN in der praktischen Erprobung. Das Sensorprinzip sowie Prüfergebnisse aus Labor und Praxis werden vorgestellt. T2 - DGZfP-Jahrestagung 2014 CY - Potsdam, Germany DA - 26.05.2014 KW - Ultraschallprüfung mit Matrix-Sensoren KW - Aktive Thermografie KW - Gabelsensor PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-319785 SN - 978-3-940283-61-0 VL - 148 SP - 1 EP - 12 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-31978 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wiedensohler, A. A1 - Wiesner, A. A1 - Weinhold, K. A1 - Birmili, W. A1 - Herrmann, M. A1 - Merkel, M. A1 - Müller, T. A1 - Pfeifer, S. A1 - Schmidt, A. A1 - Tuch, T. A1 - Velarde, F. A1 - Quincey, P. A1 - Seeger, Stefan A1 - Nowak, A. T1 - Mobility particle size spectrometers: Calibration procedures and measurement uncertainties N2 - Mobility particle size spectrometers (MPSS) belong to the essential instruments in aerosol science that determine the particle number size distribution (PNSD)in the submicrometer size range. Following calibration procedures and target uncertainties against standards and reference instruments are suggested for a complete MPSS quality assurance program: a) calibration of the CPC counting efficiency curve (within 5% for the plateau counting efficiency; within 1 nm for the 50% detection efficiency diameter), b) sizing calibration of the MPSS, using a certified polystyrene latex (PSL) particle size standard at 203 nm (within 3%), c) intercomparison of the PNSD of the MPSS (within 10% and 20% of the dN/dlogDP concentration for the particle size range 20 – 200 nm and 200 to 800 nm, respectively), and d) intercomparison of the integral PNC of the MPSS (within 10%). Furthermore, following measurement uncertainties have been investigated: a) PSL particle size standards in the range from 100-500nm match within 1% after sizing calibration at 203 nm. b) Bipolar diffusion chargers based on the radioactive nuclides Kr85, Am241 and Ni63 and a new ionizer based on corona discharge follow the recommended bipolar charge distribution, while soft X-ray-based charges may alter faster than expected. c) The use of a positive high voltage supply show a 10% better performance than a negative one. d) The intercomparison of the integral PNC of an MPSS against the total number concentration is still within the target uncertainty at an ambient pressure of approximately 500 hPa. KW - Measurement uncertainties KW - Mobility particle size spectrometer (MPPS) KW - Condensation particle counter (CPC) KW - Calibration PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-425060 DO - https://doi.org/10.1080/02786826.2017.1387229 SN - 1521-7388 VL - 52 IS - 2 SP - 146 EP - 164 PB - Tailor & Francis CY - USA AN - OPUS4-42506 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, R.H. A1 - Runge, S. A1 - Ravelli, V. A1 - Mehnert, W. A1 - Thünemann, Andreas A1 - Souto, E.B. T1 - Oral bioavailability of cyclosporine: Solid lipid nanoparticles (SLN®) versus drug nanocrystals N2 - For the development of an optimized oral formulation for cyclosporine A, 2% of this drug has been formulated in solid lipid nanoparticles (SLN™, mean size 157 nm) and as nanocrystals (mean size 962 nm). The encapsulation rate of SLN was found to be 96.1%. Nanocrystals are composed of 100% of drug. For the assessment of the pharmacokinetic parameters the developed formulations have been administered via oral route to three young pigs. Comparison studies with a commercial Sandimmun Neoral/Optoral® used as reference have been performed. The blood profiles observed after oral administration of the commercial microemulsion Sandimmun® revealed a fast absorption of drug leading to the observation of a plasma peak above 1000 ng/ml within the first 2 h. For drug nanocrystals most of the blood concentrations were in the range between 30 and 70 ng/ml over a period of 14 h. These values were very low, showing huge differences between the measuring time points and between the tested animals. On the contrary, administration of cyclosporine-loaded SLN led to a mean plasma profile with almost similarly low variations in comparison to the reference microemulsion, however with no initial blood peak as observed with the Sandimmun Neoral/Optoral®. Comparing the area under the curves (AUC) obtained with the tested animals it could be stated that the SLN™ formulation avoids side effects by lacking blood concentrations higher than 1000 ng/ml. In this study it has been proved that using SLN™ as a drug carrier for oral administration of cyclosporine A a low variation in bioavailability of the drug and simultaneously avoiding the plasma peak typical of the first Sandimmun® formulation can be achieved. KW - Solid lipid nanoparticles KW - SLN KW - Drug nanocrystals KW - Sandimmun Neoral/Optoral KW - Oral administration PY - 2006 DO - https://doi.org/10.1016/j.ijpharm.2006.02.045 SN - 0378-5173 SN - 1873-3476 VL - 317 IS - 1 SP - 82 EP - 89 PB - Elsevier CY - Amsterdam AN - OPUS4-12464 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, Anja A1 - Krahl, T. A1 - Radnik, Jörg A1 - Wagner, Andreas A1 - Werner, W. S. M. A1 - Ritter, B. A1 - Kemnitz, E. A1 - Unger, Wolfgang T1 - Chemical in-depth analysis of (Ca/Sr)F2 core–shell like nanoparticles by X-ray photoelectron spectroscopy with tunable excitation energy N2 - The fluorolytic sol–gel synthesis is applied with the intention to obtain two different types of core–shell nanoparticles, namely, SrF2–CaF2 and CaF2–SrF2. In two separate fluorination steps for core and shell formation, the corresponding metal lactates are reacted with anhydrous HF in ethylene glycol. Scanning transmission electron microscopy (STEM) and dynamic light scattering (DLS) confirm the formation of particles with mean dimensions between 6.4 and 11.5 nm. The overall chemical composition of the particles during the different reaction steps is monitored by quantitative Al Kα excitation X-ray photoelectron spectroscopy (XPS). Here, the formation of stoichiometric metal fluorides (MF2) is confirmed, both for the core and the final core–shell particles. Furthermore, an in-depth analysis by synchrotron radiation XPS (SR-XPS) with tunable excitation energy is performed to confirm the core–Shell character of the nanoparticles. Additionally, Ca2p/Sr3d XPS intensity ratio in-Depth profiles are simulated using the software Simulation of Electron Spectra for Surface Analysis (SESSA). In principle, core–shell like particle morphologies are formed but without a sharp interface between calcium and strontium containing phases. Surprisingly, the in-depth chemical distribution of the two types of nanoparticles is equal within the error of the experiment. Both comprise a SrF2-rich core domain and CaF2-rich shell domain with an intermixing zone between them. Consequently, the internal morphology of the final nanoparticles seems to be independent from the synthesis chronology. KW - Metal fluorides KW - Sol-gel synthesis KW - Synchrotron radiation KW - X-ray photoelectron spectroscopy PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-522284 DO - https://doi.org/10.1002/sia.6937 SN - 0142-2421 VL - 53 IS - 5 SP - 494 EP - 508 PB - Wiley VCH AN - OPUS4-52228 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wolf, S. E. A1 - Müller, L. A1 - Barrea, R. A1 - Kampf, C.J. A1 - Leiterer, Jork A1 - Panne, Ulrich A1 - Hoffmann, T. A1 - Emmerling, Franziska A1 - Tremel, W. T1 - Carbonate-coordinated metal complexes precede the formation of liquid amorphous mineral emulsions of divalent metal carbonates N2 - During the mineralisation of metal carbonates MCO3 (M = Ca, Sr, Ba, Mn, Cd, Pb) liquid-like amorphous intermediates emerge. These intermediates that form via a liquid/liquid phase separation behave like a classical emulsion and are stabilized electrostatically. The occurrence of these intermediates is attributed to the formation of highly hydrated networks whose stability is mainly based on weak interactions and the variability of the metal-containing pre-critical clusters. Their existence and compositional freedom are evidenced by electrospray ionization mass spectrometry (ESI-MS). Liquid intermediates in non-classical crystallisation pathways seem to be more common than assumed. PY - 2011 DO - https://doi.org/10.1039/c0nr00761g SN - 2040-3364 SN - 2040-3372 IS - 3 SP - 1158 EP - 1165 PB - RSC Publ. CY - Cambridge AN - OPUS4-23355 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Gardei, André A1 - Garcia, O. A1 - Riedl, Martin A1 - Vanhellemond, I. A1 - Suput, J.S. A1 - Santarelli, M.-L. A1 - Rodríguez-Maribona, I. A1 - Müller, Urs ED - Jadwiga W. Lukaszewicz, ED - Piotr Niemcewicz, T1 - Performance and durability of a new antigraffiti system for cultural heritage - the EC project GRAFFITAGE T2 - 11th International Congress on Deterioration and Conservation of Stone CY - Torun, Poland DA - 2008-09-15 KW - Cultural heritage KW - Antigraffiti system KW - Sandstone KW - Limestone KW - Brick KW - Monument KW - Cleaning KW - Historische Baustoffe PY - 2008 SN - 978-83-231-2237-1 VL - II SP - 889 EP - 897 PB - Nicolaus Copernicus University Press CY - Torun, Poland AN - OPUS4-18844 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wisniewski, W. A1 - Thieme, C. A1 - Müller, Ralf A1 - Reinsch, Stefan A1 - Groß-Barsnick, S.-M. A1 - Rüssel, C. T1 - Oriented surface nucleation and crystal growth in a 18BaO·22CaO·60SiO2 mol% glass used for SOFC seals N2 - A glass of the composition 37BaO·16CaO·47SiO2 wt% produced on an industrial scale is crystallized at 970 °C for times ranging from 15 min to 2 h. The crystallization at the immediate surface as well as the crystal growth into the bulk are analyzed using scanning electron microscopy (SEM) including energy dispersive X-ray spectroscopy (EDXS) and electron backscatter diffraction (EBSD) as well as X-ray diffraction in the Θ–2Θ setup (XRD). The immediate surface shows the oriented nucleation of walstromite as well as the formation of wollastonite and an unknown phase of the composition BaCaSi3O8. All three phases also grow into the bulk where walstromite ultimately dominates the kinetic selection and grows throughout the bulk due to a lack of bulk nucleation. Walstromite shows systematic orientation changes as well as twinning during growth. A critical analysis of the XRD-patterns acquired from various crystallized samples indicates that their evaluation is problematic and that phases detected by XRD in this system should be verified by another method such as EDXS. KW - Glass KW - Surface nucleation KW - Orientation KW - EBSD PY - 2018 DO - https://doi.org/10.1039/c7ce02008b VL - 20 IS - 6 SP - 787 EP - 795 PB - Royal Society of Chemistry AN - OPUS4-44405 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Kurtenbach, Dirk A1 - Ade, M. A1 - Müller, E. A1 - Mitchell, B.S. ED - Klimanek, P. T1 - Keimbildungs- und Kristallisationskinetik amorpher SiC-Strukturen T2 - Winterschule "Simulationstechniken in der Materialwissenschaft" CY - Cämmerswalde, Deutschland DA - 1999-02-22 KW - Keimbildungskinetik KW - Kristallisationskinetik KW - Siliciumorganische Polymere PY - 1999 SN - 3-86012-078-6 N1 - Serientitel: Freiberger Forschungshefte / B – Series title: Freiberger Forschungshefte / B IS - 295 SP - 293 EP - 300 PB - Techn. Univ. Bergakad. CY - Freiberg AN - OPUS4-759 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, A. A1 - Goecke, S.-F. A1 - Sievi, P. A1 - Albert, F. A1 - Rethmeier, Michael T1 - Laser beam oscillation strategies for fillet welds in lap joints N2 - Laser beam oscillation opens up new possibilities of influencing the welding process in terms of compensation of tolerances and reduction of process emissions that occur in industrial applications, such as in body-in-white manufacturing. The approaches are to adapt the melt pool width in order to generate sufficient melt volume or to influence melt pool dynamics, e.g. for a better degassing. Welding results are highly dependent on the natural frequency of the melt pool, the used spot diameter and the oscillation speed of the laser beam. The conducted investigations with an oscillated 300 µm laser spot show that oscillation strategies, which are adjusted to the joining situation improve welding result for zero-gap welding as well as for bridging gaps to approximately 0.8 mm. However, a complex set of parameters has to be considered in order to generate proper welding results. This work puts emphasize on introducing them. KW - Laser beam welding KW - Gap compensation KW - Process monitoring and control KW - System technology KW - Automotive application PY - 2014 DO - https://doi.org/10.1016/j.phpro.2014.08.149 SN - 1875-3892 VL - 56 SP - 458 EP - 466 PB - Elsevier CY - Amsterdam [u.a.] AN - OPUS4-31437 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, A. A1 - Goecke, S.F. A1 - Rethmeier, Michael T1 - Laser beam oscillation welding for automotive applications N2 - Laser beam oscillation, applied one- or two-dimensional to the actual welding process, influences the welding process in terms of compensation of tolerances and reduction of process emissions like spatter and melt ejections that occur in industrial applications, such as in body-in-white manufacturing. If the welding process could be adapted to these tolerances by the momentarily demanded melt pool width to generate sufficient melt volume or to influence melt pool dynamics, e.g. for a better degassing, laser welding would become more robust. However, beam oscillation results are highly dependent on the natural frequency of the melt pool, the used spot diameter and the oscillation speed of the laser beam. The conducted investigations with an oscillated 300 μm laser spot show that oscillation strategies which are adjusted to the joining situation can bridge gaps to approximately 0.6 mm at metal sheet thickness of 0.8 mm. However, the complex behaviour of the melt pool has to be considered to generate proper welding results. This work puts emphasis on showing aspects of beam oscillation in fillet welding in lap joints. KW - Automotive application KW - Melt pool dynamics KW - Adaptive welding beam oscillation KW - Laser welding KW - Gap bridging PY - 2018 DO - https://doi.org/10.1007/s40194-018-0625-3 SN - 0043-2288 SN - 1878-6669 VL - 62 IS - 5 SP - 1039 EP - 1047 PB - Springer AN - OPUS4-45774 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, A. A1 - Goecke, S.F. A1 - Rethmeier, Michael T1 - Laser beam oscillation for fillet welding N2 - In today’s automotive frame-and-body construction, laser welds are typically carried out as square butt welds in lap joints. These welds are increasingly produced by remote laser welding optics with working distances of 500 mm and more. This enables simple path programming because clamping devices are traversed over and therefore low cycle times with improved productivity is achieved. However, workpiece tolerances lead to part displacements and varying joint positions over time. These displacements have to be acted against by appropriate flange length that contain for positioning deviations. Using this concept, aspired light-weight optimisations, e.g. reducing flange length, are difficult to achieve. By using seam tracking sensors, part tolerances are automatically detected and counteracted for. In addition, joint edge detection allows constructive changes on the type of weld. Fillet welds reduce flange lengths', improve force flow and open up possibilities for visual quality monitoring. Apart from that, vertical displacements in the form of height tolerances still occur. This needs consideration by adapting the set of welding parameter to the current welding situation. In this respect, one main welding parameter is the lateral beam offset to the upper sheet. Since body-in-white welding applications mainly comprise of zinc-coated steel sheets, special requirements for the welding process are given. Especially zero-gap-welding and welding of joints with gaps larger than 0.2 mm are critical. Using a laser beam oscillation process can stabilise these situations. Approaches to finding parameter sets are presented in this paper. KW - Laser beams KW - Welding KW - Fillet welds KW - Gap KW - Process procedures KW - Monitoring systems PY - 2014 DO - https://doi.org/10.1007/s40194-014-0165-4 SN - 0043-2288 SN - 1878-6669 VL - 58 IS - 6 SP - 865 EP - 872 PB - Springer CY - Oxford AN - OPUS4-32075 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, Werner A1 - Jakob, Ines A1 - Li, C.S. A1 - Tatzky-Gerth, Renate T1 - Durability of polyolefin geosynthetic drains N2 - The German Federal Institute for Materials Research and Testing (BAM) has established a testing guideline to assess the suitability of geosynthetic or geocomposite drain (GCD) elements for final landfill cover systems. In an earlier paper the uniform procedure according to the BAM guideline for determining long-term water flow capacity was described, and the structural stability of drain cores under creep was investigated. The extrapolation of creep curves is permissible only when it can be shown, over the extrapolated period (at least 100 years), that oxidative aging does not invoke any relevant changes in the polyolefin material. This can be shown by measuring antioxidant depletion and mechanical degradation of the drain cores and filter/protection geotextiles in oven aging and water immersion tests. In this paper the results of such aging studies on three different GCD products are reported. Degradation of the tensile strength of HALS-stabilized polypropylene needle-punched nonwoven geotextiles (PP NWGTs) starts right from the beginning of the oven aging. This has to be taken into account for lifetime predictions based on residual tensile strength. The rate of oxidative degradation of NWGTs decreases significantly with increasing mass per area. Therefore the expected service life sets a limit on acceptable geotextile grammage. Antioxidant depletion in the drain cores, which are made of relatively thick PP strands or HDPE ribs, is about an order of magnitude slower than in filter and protection NWGTs, which are made of thin fibers. Service life values in excess of 100 years may be obtained for the products when the geotextiles and drain cores are properly stabilized and designed. KW - Geosynthetics KW - Geosynthetic drain elements KW - Long-term behavior KW - Oxidative degradation PY - 2009 DO - https://doi.org/10.1680/gein.2009.16.1.28 SN - 1072-6349 VL - 16 IS - 1 SP - 28 EP - 42 PB - Telford CY - London, UK AN - OPUS4-18999 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmelzer, J.W.P. A1 - Müller, Ralf A1 - Möller, J. A1 - Gutzow, I.S. T1 - Elastic stresses, stress relaxation and crystallisation: theory of nucleation PY - 2002 SN - 0031-9090 VL - 43C SP - 291 EP - 300 PB - Thornton CY - Sheffield AN - OPUS4-3116 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmelzer, J.W.P. A1 - Müller, Ralf A1 - Möller, J. A1 - Gutzow, I.S. T1 - Theory of nucleation in viscoelastic media: application to phase formation in glassforming melts N2 - Glassforming melts behave, in the vicinity of the temperature of vitrification Tg, as viscoelastic bodies. A general theory of nucleation in a viscoelastic body developed elsewhere is applicable to the description of phase formation processes in such systems. The present contribution is directed to the demonstration of the relevance of this proposed general theory to describing phase transformation processes in glassforming melts. The application of the theory is shown to explain a number of experimental results on crystallization of glassforming melts, which have not found a satisfactory interpretation so far. PY - 2003 DO - https://doi.org/10.1016/S0022-3093(02)01428-X SN - 0022-3093 VL - 315 SP - 144 EP - 160 PB - North-Holland Publ. Co. CY - Amsterdam AN - OPUS4-2078 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bauer, L.J. A1 - Wieder, Frank A1 - Truong, V. A1 - Förste, F. A1 - Wagener, Y. A1 - Jonas, A. A1 - Praetz, S: A1 - Schlesiger, C. A1 - Kupsch, Andreas A1 - Müller, Bernd R. A1 - Kanngießer, B. A1 - Zaslansky, P. A1 - Mantouvalou, I. T1 - Absorption Correction for 3D Elemental Distributions of Dental Composite Materials Using Laboratory Confocal Micro-X-ray Fluorescence Spectroscopy N2 - Confocal micro-X-ray fluorescence (micro-XRF) spectroscopy facilitates three-dimensional (3D) elemental imaging of heterogeneous samples in the micrometer range. Laboratory setups using X-ray tube excitation render the method accessible for diverse research fields but interpretation of results and quantification remain challenging. The attenuation of X-rays in composites depends on the photon energy as well as on the composition and density of the material. For confocal micro-XRF, attenuation severely impacts elemental distribution information, as the signal from deeper layers is distorted by superficial layers. Absorption correction and quantification of fluorescence measurements in heterogeneous composite samples have so far not been reported. Here, an absorption correction approach for confocal micro-XRF combining density information from microcomputed tomography (micro-CT) data with laboratory X-ray absorption spectroscopy (XAS) and synchrotron transmission measurements is presented. The energy dependency of the probing volume is considered during the correction. The methodology is demonstrated on a model composite sample consisting of a bovine tooth with a clinically used restoration material. KW - Micro X-ray fluorescence spectroscopy KW - Dental composite materials KW - Computed tomography KW - Absorption correction PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-601630 DO - https://doi.org/10.1021/acs.analchem.4c00116 SN - 0003-2700 SN - 1520-6882 VL - 96 IS - 21 SP - 8441 EP - 8449 PB - American Chemical Society Publications CY - Washington, DC AN - OPUS4-60163 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Müller, Bernd R. A1 - Lange, Axel A1 - Harwardt, Michael A1 - Hentschel, Manfred P. A1 - Hamm, B. A1 - Rogalla, P. A1 - Diederichs, G. A1 - Issever, A.S. T1 - First Synchrotron Refraction CT of Cartilage KW - X-ray Refraction KW - Computed Tomography KW - DEI KW - Cartilage PY - 2008 UR - http://www.helmholtz-berlin.de/media/media/oea/web/pr_webseite/druckschriften/berichte/bessy/annual_report_2007-v2.pdf#page=292 SN - 0179-4159 SP - 292 EP - 296 PB - Berliner Elektronenspeicherring-Gesellschaft für Synchrotronstrahlung CY - Berlin AN - OPUS4-17661 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Müller, R.H. A1 - Runge, S.A. A1 - Ravelli, V. A1 - Thünemann, Andreas A1 - Mehnert, W. A1 - Souto, E.B. T1 - Cyclosporine-loaded solid lipid nanoparticles (SLN): Drug-lipid physicochemical interactions and characterization of drug incorporation N2 - Solid lipid nanoparticles (SLN) were produced loaded with cyclosporine A in order to develop an improved oral formulation. In this study, the particles were characterized with regard to the structure of the lipid particle matrix, being a determining factor for mode of drug incorporation and drug release. Differential scanning calorimetry (DSC) and wide-angle X-ray scattering (WAXS) measurements were employed for the analysis of the polymorphic modifications and mode of drug incorporation. Particles were produced using Imwitor®900 as lipid matrix (the suspension consisted of 10% particles, 8% Imwitor®900, 2% cyclosporine A), 2.5% Tagat S, 0.5% sodium cholate and 87% water. DSC and WAXS were used to analyse bulk lipid, bulk drug, drug incorporated in the bulk and unloaded and drug-loaded SLN dispersions. The processing of the bulk lipid into nanoparticles was accompanied by a polymorphic transformation from the ß to the α-modification. After production, the drug-free SLN dispersions converted back to ß-modification, while the drug-loaded SLN stayed primarily in α-modification. After incorporation of cyclosporine A into SLN, the peptide lost its crystalline character. Based on WAXS data, it could be concluded that cyclosporine is molecularly dispersed in between the fatty acid chains of the liquid-crystalline α-modification fraction of the loaded SLN. KW - Solid lipid nanoparticles KW - Cyclosporine A KW - Characterization KW - Oral bioavailability KW - Lipid polymorphism PY - 2008 DO - https://doi.org/10.1016/j.ejpb.2007.07.006 SN - 0939-6411 SN - 1873-3441 VL - 68 IS - 3 SP - 535 EP - 544 PB - Elsevier CY - Amsterdam AN - OPUS4-17534 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -