TY - JOUR A1 - Zerbst, Uwe A1 - S., Romano A1 - D., Manenti A1 - S., Beretta T1 - Semi-probabilistic method for residual lifetime of aluminothermic welded rails with foot cracks JF - Theoretical and Applied Fracture Mechanics N2 - One of the most frequent and dangerous failure modes in continuous welded rails is fatigue crack Propagation terminated by brittle fracture. Due to the brittleness of the weld material and HAZ and the scatter in its mechanical properties, a statistical approach is necessary. The paper deals with surface cracks at the foot base of aluminothermic welded rails, developing a probabilistic methodology for determining the day by day prospective failure probability. The investigations presented here comprise weld material characterization, simulation of fatigue crack propagation and finally the determination of the failure probability using the Monte Carlo method. The effect of various parameters, such as axle weight, Initial crack size, residual stresses, fatigue crack propagation threshold and date of inspection were analyzed. The results show that, independent of the date of the last inspection, almost any failure event happens in wintertime. This is in accordance with practical experience. However, from the proposed analysis it is evident that the main parameter controlling rail fracture is not only the minimum local temperature, but the temperature range over the whole year. Finally, the results are compared to the standard rail classification method. KW - Railway rails KW - Foot crack KW - Fatigue crack KW - Failure probability KW - Residual lifetime PY - 2016 DO - https://doi.org/10.1016/j.tafmec.2016.05.002 SN - 0167-8442 VL - 85 IS - Part B SP - 398 EP - 411 PB - Elsevier AN - OPUS4-38156 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Bruno, Giovanni A1 - Buffière, J.-Y. A1 - Wegener, T. A1 - Niendorf, T. A1 - Wu, T. A1 - Zhang, X. A1 - Kashaev, N. A1 - Meneghetti, G. A1 - Hrabe, Nik A1 - Madia, Mauro A1 - Werner, Tiago A1 - Hilgenberg, Kai A1 - Koukolikova, M. A1 - Prochazka, R. A1 - Dzugan, J. A1 - Möller, B. A1 - Beretta, S. A1 - Evans, Alexander A1 - Wagener, R. A1 - Schnabel, K. T1 - Damage tolerant design of additively manufactured metallic components subjected to cyclic loading: State of the art and challenges JF - Progress in materials science N2 - This article is an outcome of a workshop on Fatigue of Additive Manufactured Metallic Components jointly organized by the Federal Institute for Materials Research and Testing (BAM) Berlin, Germany and the National Institute of Standards and Technology (NIST) Boulder, CO, U.S.A. The aim of the workshop was a comprehensive discussion of the specific aspects of additively manufactured (AM) components in regard to failure under cyclic loading. Undoubtedly, a better understanding and the further development of approaches for damage tolerant component design of AM parts are among the most significant challenges currently facing the use of these new technologies. This article presents a thorough overview of the workshop discussions. It aims to provide a review of the parameters affecting the damage tolerance of AM parts with special emphasis on the process parameters intrinsic to the AM technologies, the resulting defects and residual stresses. Based on these aspects, concepts for damage tolerant component design for AM are reviewed and critically discussed. KW - Additive manufacturing KW - Fatigue loading KW - Component assessment KW - Damage tolerance KW - Defects KW - Residual stresses PY - 2021 DO - https://doi.org/10.1016/j.pmatsci.2021.100786 SN - 0079-6425 VL - 121 PB - Elsevier CY - Amsterdam AN - OPUS4-51937 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Beretta, S. A1 - Köhler, G. A1 - Lawton, A. A1 - Vormwald, M. A1 - Beier, H.T. A1 - Klinger, Christian A1 - Cerný, I. A1 - Rudlin, J. A1 - Heckel, Thomas A1 - Klingbeil, Dietmar T1 - Safe life and damage tolerance aspects of railway axles - A review JF - Engineering fracture mechanics N2 - The paper gives an overview on safe life and damage tolerance methods applied to railway axles. It describes failure scenarios due to fatigue crack initiation and propagation. Besides common aspects of design, specific features such as corrosion and impact damage from flying ballast are discussed which may reduce the fatigue strength of axles during service. Potential effects of non-metallic inclusions from the steel manufacturing process are addressed in the context of the very high number of loading cycles railway axles are designed for. With respect to damage tolerance general lines of fracture mechanics residual lifetime analyses are introduced. More specific discussion is provided on aspects such as the threshold value of fatigue crack propagation and reliability aspects of non-destructive inspection. KW - Railway axle KW - Safe life design KW - Damage tolerance KW - Fatigue strength KW - Fatigue crack propagation KW - Inspection intervals PY - 2013 DO - https://doi.org/10.1016/j.engfracmech.2012.09.029 SN - 0013-7944 SN - 1873-7315 VL - 98 SP - 214 EP - 271 PB - Elsevier Science CY - Kidlington AN - OPUS4-27779 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Beretta, S. T1 - Failure and damage tolerance aspects of railway components JF - Engineering failure analysis N2 - Railway structures such as rails and axles are safety relevant components since any failure includes the risk of catastrophic derailment. This paper gives a brief overview on the most important potential failure scenarios driven by fatigue crack initiation and propagation and discusses the effects of important influencing factors such as vehicle weight and speed, track quality and environmental conditions. The present paper summarizes earlier work of the authors in this field. KW - Railway rails KW - Railway axles KW - Fatigue crack propagation KW - Damage tolerance KW - Fracture mechanics PY - 2011 DO - https://doi.org/10.1016/j.engfailanal.2010.06.001 SN - 1350-6307 SN - 1873-1961 VL - 18 IS - 2 SP - 534 EP - 542 PB - Elsevier Science Publ. CY - Oxford AN - OPUS4-22639 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scolavino, L. A1 - Beretta, S. A1 - Madia, Mauro A1 - Zerbst, Uwe T1 - Critical speed of flawed rotors: global vs local approach T2 - ASME Turbo Expo 2014 - GT2014 - Turbine technical conference and exposition (Proceedings) N2 - The burst of a disc in rotating machinery can cause catastrophic damage of the equipment and, more importantly, it can represent a mortal threat to anyone in the sphere of influence of the event. In order to minimize the danger associated to a rotating component failure, burst testing is required by the authorities in order to set safety margins to the normal operating speeds. Moreover more accurate predicting tools are required for designing the components. This paper presents the results of a numerical and analytical study on the assessment of the crack driving force for discs containing surface flaws. The aim is to provide a simple, though reliable, tool in order to be able to calculate the possible dangerous in-service speed for a rotating component and, therefore, to set burst margins above the normal operating conditions of the equipment. An R6-like flaw assessment procedure is adopted considering different assumptions in the definition of the critical speed and the analytical predictions are compared with the results of elastic-plastic finite element analysis of disc. In particular, the validity and potentiality of the method is proved for surface flaws in different positions in the disc. T2 - ASME Turbo Expo 2014 - GT2014 CY - Düsseldorf, Germany DA - 16.06.2014 KW - Critical speed KW - Flawed rotors KW - Flaw assessment PY - 2014 SN - 978-0-7918-4576-9 DO - https://doi.org/10.1115/GT2014-26881 VL - 7A SP - 26881, 1 EP - 8 AN - OPUS4-32382 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pourheidar, A. A1 - Patriarca, L. A1 - Madia, Mauro A1 - Werner, Tiago A1 - Beretta, S. T1 - Progress in the measurement of the cyclic R-curve and its application to fatigue assessment JF - Engineering fracture mechanics N2 - The cyclic R-curve describes the resistance of a material to fatigue crack propagation fromthe short to the long crack regimes and it is therefore an essential ingredient in any fracturemechanics-based fatigue assessment procedure. This work presents different testing proceduresemployed in the experimental determination of the cyclic R-curve, especially focusing onthe comparison with long fatigue crack propagation thresholds obtained by means of thecompression precracking load reduction (CPLR) procedure. The tests were performed on theEA4T steel considering different stress ratios. The results show a good reproducibility of thecyclic R-curves at every stress ratio and for any testing procedure. In addition, the cyclicR-curves were used in a fracture mechanics-based assessment to predict the fatigue limits ofspecimens containing micro-notches. KW - Cyclic R-curve KW - Fatigue limit KW - Fatigue propagation threshold KW - EA4T steel KW - Digital image correlation PY - 2022 DO - https://doi.org/10.1016/j.engfracmech.2021.108122 SN - 0013-7944 VL - 260 SP - 1 EP - 17 PB - Elsevier CY - Kidlington AN - OPUS4-54208 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mazzei, S. A1 - Madia, Mauro A1 - Beretta, S. A1 - Mancaleoni, A. A1 - Aparo, S. T1 - Analysis of Cu-wire pull and shear test failure modes under ageing cycles and finite element modelling of Si-crack propagation JF - Microelectronics reliability N2 - In microelectronic packaging, wire bonding is the predominant method for making electrical connections. Copper is increasingly substituting gold as interconnection material since it is a much cheaper alternative and it also offers several physical advantages. Adequate and reliable mechanical integrity of the connection is usually checked by process controls based onto 'wire pull' and 'ball bond shear' tests. In this paper the two methods are compared in terms of sensitiveness in detecting a latent weakness of the bond-pad structure, either induced by inappropriate wire bonding process or cumulated during reliability ageing. The failure modes (in terms of frequency and maximum test load) observed at the ball bond interface have been investigated on two different batches of a same chip, obtained from different wire-bonding recipes and including both unstressed and aged units. Cross-sections of the samples, submitted to pull and shear both in destructive and non-destructive tests, have allowed us to investigate the relationship between the bond morphological characteristics (metal deformation and potential micro-damages induced by copper bonding) and the weak points for fracture propagation inside the bond-pad inner layers and the silicon substrate. Besides the experimental activities, fracture mechanics and the finite element method have been employed to model the pull and shear tests. The aims of the finite element modelling have been to predict the reduction of test maximum load in defective ball bonds and the crack growth angle adopting a mixed-mode criterion. Good results have been obtained by the numerical fracture analysis, which can then support the reliability characterization and mechanical improvement of the bond. KW - Copper wire bonding KW - Mixed-mode crack growth KW - Silicon cratering KW - Stress intensity factor PY - 2014 DO - https://doi.org/10.1016/j.microrel.2014.04.004 SN - 0026-2714 VL - 54 IS - 11 SP - 2501 EP - 2512 PB - Elsevier CY - Amsterdam [u.a.] AN - OPUS4-32381 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Madia, Mauro A1 - Riesch-Oppermann, H. A1 - Zerbst, Uwe A1 - Beretta, S. ED - Klingbeil, D. ED - Vormwald, M. ED - Eulitz, K.-G. T1 - A new full-probabilistic framework for the structural integrity assessment of structures containing cracks T2 - 18th European conference on fracture (ECF 18) - Fracture of materials and structures from micro to macro scale (Proceedings) T2 - 18th European conference on fracture (ECF 18) - Fracture of materials and structures from micro to macro scale CY - Dresden, Germany DA - 2010-08-30 KW - Structural integrity KW - SINTAP KW - FITNET KW - Reliability KW - FORM PY - 2010 SN - 978-3-00-031802-3 IS - C.02.1-3 / #306 SP - 1 EP - 10 AN - OPUS4-22843 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Madia, Mauro A1 - Foletti, S. A1 - Beretta, S. A1 - Cavalleri, E.A. T1 - A tool for the structural integrity assessment of turbine disks: probabilistic and numerical background T2 - ASME Turbo Expo 2013 - GT2013 (Proceedings) N2 - Rotor disks for gas turbines are heavy components and are usually designed following a safe-life approach, where the low-cycle fatigue analysis is carried out referring to design life curves with suitable probabilistic margins. However, in the case of such a heavy component there is the possibility of rare occurrence of undetected defects or, better, the need to identify the defect acceptability for the different rotor regions (considering stress, temperature, mission profile).In order to carry out such calculations for a turbine rotor disk a software named AStrID (Assessment of the Structural Integrity of Disks) has been developed in close cooperation between Politecnico di Milano and Ansaldo Energia (AEN). This paper summarizes its background and some of the relevant features. T2 - ASME Turbo Expo 2013 - GT 2013 CY - San Antonio, TX, USA DA - 03.06.2013 PY - 2013 SP - GT2013-96029, 1-8 AN - OPUS4-29456 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Madia, Mauro A1 - Beretta, S. A1 - Schödel, M. A1 - Zerbst, Uwe A1 - Luke, M. A1 - Varfolomeyev, I. T1 - Stress intensity factor solutions for cracks in railway axles JF - Engineering fracture mechanics N2 - The aim of this paper is a collection of stress intensity factor solutions for cracks in railway axle geometries which the authors of the present special issue developed and/or used for damage tolerance analyses. These solutions comprise closed form analytical as well as tabled geometry functions and they refer to solid as well as hollow axles and various crack sites such as the T- and V-notch and the axle body. KW - Railway axles KW - Stress intensity factor PY - 2011 DO - https://doi.org/10.1016/j.engfracmech.2010.03.019 SN - 0013-7944 SN - 1873-7315 VL - 78 IS - 5 SP - 764 EP - 792 PB - Elsevier Science CY - Kidlington AN - OPUS4-22495 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -