TY - CONF A1 - Hünert, Daniela A1 - Schulz, Wencke A1 - Nitschke, Heike A1 - Saliwan Neumann, Romeo A1 - Oder, Gabriele A1 - Kranzmann, Axel T1 - Corrosion behaviour of ferritic and martensitic power plant steels under conditions of dual atmospheres N2 - The most efficient construction materials for boiler water walls and superheaters in steam power plants are ferritic and martensitic steels. In practical operation tubes are simultaneously exposed to combustion gas and air/steam on their opposite surfaces. The corrosion behaviour of ferritic-martensitic steels under such dual atmospheres is nondistinctive and has therefore been investigated in a special designed test equipment between 500 and 620°C. The power plant conditions were simulated wi th a flowing and pressurised (80 bar) combustion gas on the inner side of the tube which mainly consists of H2O and/or CO2. On the outer side, the tube material was exposed to air. It was discovered that under similar temperatures the oxides formed on the air side under dual atmosphere conditions were significantly different to the oxide scales formed when the alloy was exposed to air only. It is assumed that the anomalous corrosion behaviour during the dual atmosphere exposure is due to the hydrogen transport through the bulk alloy from the combustion gas side to the air side. T2 - NACE International corrosion conference 2009 CY - Atlanta, Georgia, USA DA - 2009-03-22 KW - High temperature corrosion KW - Dual atmosphere KW - Corrosive gases KW - Mild steels KW - 9-12% Cr-steels KW - Hydrogen transport PY - 2009 SP - 1 EP - 10 (Paper 09263) AN - OPUS4-22335 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz, Wencke A1 - Feigl, Michael A1 - Dörfel, Ilona A1 - Saliwan Neumann, Romeo A1 - Nofz, Marianne A1 - Kranzmann, Axel T1 - Alumina coatings against carburization and oxidation under oxyfuel conditions T2 - 1st International conference on materials for energy CY - Karlsruhe, Germany DA - 2010-07-04 PY - 2010 SN - 978-3-89746-117-8 SP - 1012 AN - OPUS4-24179 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schulz, Wencke A1 - Hünert, Daniela A1 - Nitschke, Heike A1 - Saliwan Neumann, Romeo A1 - Kranzmann, Axel T1 - Comparison of the corrosion behaviour of 9-12 % Cr steels in H2O, H2O-CO2 and H2O-CO2-O2 T2 - NACE International corrosion conference 2009 CY - Atlanta, Georgia, USA DA - 2009-03-22 KW - 9-12%Cr-steels KW - Steam KW - CO2 KW - O2 KW - High-temperature corrosion KW - Evaporation of chromium PY - 2009 SP - 1 EP - 10 (Paper No. 09264) AN - OPUS4-19464 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -