TY - JOUR A1 - Musyanovych, A. A1 - Grimmer, Christoph A1 - Sadak, A. E. A1 - Heßling, L. A1 - Lüdicke, M. A1 - Bilsel, M. A1 - Horn, Wolfgang A1 - Richter, Matthias T1 - Polymer Capsules with Volatile Organic Compounds as Reference Materials for Controlled Emission N2 - Encapsulation of volatile organic compounds (VOCs) that could evaporate at a defined rate is of immense interest for application in emission reference materials (ERMs). Polyurethane/polyurea microcapsules with various VOC active ingredients (limonene, pinene, and toluene) were successfully produced by interfacial polymerization with Shirasu porous glass membrane emulsification in a size range between 10 and 50 μm. The effect of surfactant, VOC, monomer(s) type, and ratio has a great effect on the formulation process and morphology of capsules. The type of VOC played a significant role in the encapsulation efficiency. Due to the difference in vapor pressure and VOC/water interfacial tension, the formulation for encapsulation was optimized for each individual VOC. Furthermore, to achieve effective stability of the large droplets/capsules, a combination of ionic and nonionic surfactants was used. Optical and scanning electron microscopy, Fourier transform infrared spectroscopy (FTIR), and thermogravimetric analysis (TGA), were used to characterize the optimized microcapsules. The results showed that the obtained microcapsules exhibited a spherical shape and core–shell morphology and featured characteristic urethane-urea bonds. The amount of encapsulated VOC ranges between 54 and 7 wt %. The emission tests were performed with the help of the emission test chamber procedure (EN 16516). The limonene-loaded polyurethane/polyurea microcapsules show a change in emission rate of less than 10% within 14 days and can be considered as a potential candidate for use as an ERM. KW - Polymer microcapsules KW - Membrane emulsification KW - Polyaddition KW - Volatile organic compound (VOC) KW - Emission testing PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-619227 DO - https://doi.org/10.1021/acsami.4c12826 SN - 1944-8252 VL - 16 IS - 50 SP - 69999 EP - 70009 PB - ACS AN - OPUS4-61922 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Horn, Wolfgang A1 - Wilke, Olaf A1 - Mull, B. A1 - Richter, Matthias A1 - Brödner, Doris A1 - Mölders, N. A1 - Renner, M. T1 - Reproducibly emitting reference material for quality assurance/quality control of emission test chamber measurements N2 - Volatile Organic Compounds (VOC) are ubiquitous in the indoor air, since they emit from materials used indoors. Investigations of these materials are mostly carried out in test chambers under controlled climatic conditions. Quality control of these test chamber measurements is important but there is a lack of commercially available homogenous reference materials as required for round robin tests or quality assurance of laboratories. The approach of the present study is the impregnation of a supporting material with VOC, which are reproducibly released in measurable chamber air concentrations under standardised test conditions. A polymer made of Thermoplastic Polyurethane (TPU) was chosen as carrier material. It was impregnated with the VOC trimethyl pentanediol isobutyrat (texanol). T2 - Healthy Buildings 2017 Europe CY - Lublin, Poland DA - 02.07.2017 KW - Emissions testing KW - Volatile organic compounds KW - Polymeric material KW - CO2 assisted impregnation PY - 2017 SN - 978-83-7947-232-1 SP - Paper 0172, 1 EP - 2 AN - OPUS4-42348 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Richter, Matthias A1 - Mull, Birte A1 - Horn, Wolfgang A1 - Brödner, Doris A1 - Mölders, N. A1 - Renner, M. T1 - Reproducibly emitting reference material on thermoplastic polyurethane basis for quality assurance/quality control of emission test chamber measurements N2 - Volatile Organic Compounds (VOC) are ubiquitous in the indoor air since they are emitted from materials used indoors. Investigations of these materials are mostly carried out in emission test chambers under controlled climatic conditions. Reference materials are an important tool for quality assurance/Quality control of emission test chamber measurements but so far they are not commercially available. In this study, a new approach was tested to develop an appropriate reference material with homogenous and reproducible emission of the VOC with well measurable air concentrations in emission test Chambers larger than 20 L at air change rates of 0.5 - 1 /h. Thermoplastic Polyurethane (TPU) was selected as Matrix material which was impregnated with 2,2,4- trimethyl-1,3-pentanediol monoisobutyrate (texanol) as test VOC using compressed carbon dioxide. An optimization of the impregnation parameters such as temperature, pressure, time, VOC injection volume and TPU sample size was performed until the targeted area specific Emission rate (SERa) value was reached. Further aspects like process control, storage effects and correlation of the sample size to the emission rate were investigated. It was found that the SERa immediately after sample preparation were not reproducible between the batches but became unified 10 days after loading into the test chamber indicating the necessity of aging before use. SERa between 13,000 and 18,000 mg m-2 h-1 were obtained, and the impregnated materials could be well stored in aluminum-coated polyethylene foil for at least seven weeks without significant losses. Furthermore, the impregnation of styrene and the SVOC 2,6-diisopropylnaphthalene was tested. KW - Reference material KW - Emissions testing KW - Volatile organic compounds KW - Polymer material KW - CO2 assisted impregnation PY - 2017 DO - https://doi.org/10.1016/j.buildenv.2017.06.005 SN - 0360-1323 SN - 1873-684X VL - 122 SP - 230 EP - 236 PB - Elsevier AN - OPUS4-40646 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Musyanovych, A. A1 - Grimmer, Christoph A1 - Sadak, A. E. A1 - Heßling, L. A1 - Bilsel, M. A1 - Horn, Wolfgang A1 - Richter, Matthias T1 - Polymeric Capsules with VOCs for Controlled Emission N2 - Micro-(nano-)encapsulation technology involves building of a barrier between the core and the environment and offers a number of benefits to preserve the functional and physicochemical properties of core material. Tremendous progress has been made in synthesizing well-defined capsules to achieve desired properties such as particle size, chemical composition, and controlled release of the payload. Encapsulation of volatile organic compounds (VOCs) that could evaporate with a defined rate is of immense interest for application in emission reference materials (ERM). These are urgently needed for quality assurance and quality control purposes (QA/QC) required by test standards for the determination of chemical emissions of construction and other materials for interior use. As such ERMs are hardly available on the market, the EU-funded EMPIR project MetrIAQ [1] was started to fill this gap by developing a material with temporally constant emission of VOCs typically found in indoor air. Different capsules in a size range between 5 and 50 μm were synthesized through an interfacial polyaddition/polycondensation reaction in direct (water-in-oil) system. As VOC several types of hydrophobic liquid materials were used. After synthesis, the morphology and physicochemical properties of capsules were characterized by electron microscopy, FTIR and DSC/TGA. An encapsulation efficiency up to 90% could be reached. The emission kinetic of volatile agents was studied in emission test chambers at 23 °C and 50% RH for 14 days. First results indicate that variation of the cross-linking grade of the shell material is one important parameter to adjust the desired emission rate. The overall aim is to achieve a consistent emission profile that decreases by less than 10 % over a target period of at least 14 days. T2 - 36th European Colloid & Interface Society Conference CY - Chania, Crete, Greece DA - 04.09.2022 KW - Capsules KW - Volatile organic compound KW - Polymer KW - Material emissions KW - Reference materials PY - 2022 AN - OPUS4-56039 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Horn, Wolfgang A1 - Richter, Matthias A1 - Nohr, M. A1 - Wilke, Olaf A1 - Jann, Oliver T1 - Application of a novel reference material in an international round robin test on material emissions testing N2 - Emission testing of products is currently a rapidly increasing field of measurement activity. Labelling procedures for construction products are based on such emission test chamber measurements and hence measurement performance should be verified. A suited procedure for this purpose is the testing of one unique homogenous material in different laboratories within a Round Robin Test (RRT). Therefore, it is useful to have a reference material which can be used within inter-laboratory studies or as part of the quality management system to ensure comparable results. Several approaches on the development of reproducibly emitting materials have been published. These have in common only to emit a single VOC – toluene. Two further research studies carried out by BAM aimed to develop reference material for emissions testing containing one or more VOC in a single material. The first approach was a doped lacquer with Volatile and Semi-Volatile Organic Compounds (VOC/SVOC) and the second was Thermoplastic Polyurethane (TPU) or a Squalane/Paraffin mixture. Results received with the lacquer based material were presented in more detail. KW - Emission test chamber KW - Reference material KW - Round robin test KW - VOC PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-419412 DO - https://doi.org/10.1111/ina.12421 SN - 1600-0668 SN - 0905-6947 VL - 28 IS - 1 SP - 181 EP - 187 PB - Wiley & Sons, Ltd. AN - OPUS4-41941 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -