TY - JOUR A1 - de Olivera, Paulo A1 - Michalchuk, Adam A1 - de Oliveira Guilherme Buzanich, Ana A1 - Bienert, Ralf A1 - Torresi, R. A1 - Camargo, P. A1 - Emmerling, Franziska T1 - Tandem X-ray absorption spectroscopy and scattering for in situ time-resolved monitoring of gold nanoparticle mechanosynthesis N2 - Current time-resolved in situ approaches limit the scope of mechanochemical investigations possible. Here we develop a new, general approach to simultaneously follow the evolution of bulk atomic and electronic structure during a mechanochemical synthesis. This is achieved by coupling two complementary synchrotron-based X-ray methods: X-ray absorption spectroscopy (XAS) and X-ray diffraction. We apply this method to investigate the bottom-up mechanosynthesis of technologically important Au micro and nanoparticles in the presence of three different reducing agents, hydroquinone, sodium citrate, and NaBH4. Moreover, we show how XAS offers new insight into the early stage generation of growth species (e.g. monomers and clusters), which lead to the subsequent formation of nanoparticles. These processes are beyond the detection capabilities of diffraction methods. This combined X-ray approach paves the way to new directions in mechanochemical research of advanced electronic materials. KW - Mechanochemistry KW - XANES KW - X-ray diffraction KW - Nano particles PY - 2020 DO - https://doi.org/10.1039/d0cc03862h SN - 1364-548X VL - 56 SP - 10329 EP - 10332 PB - Royal Society of Chemistry AN - OPUS4-51760 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Baláž, Matej A1 - Birinci, Mustafa A1 - Şentürk, Kader A1 - Achimovičová, Marcela A1 - Baláž, Peter A1 - Tampubolon, Imelda Octa A1 - Stolar, Tomislav A1 - Bienert, Ralf A1 - Emmerling, Franziska A1 - Erdemoğlu, Sema A1 - Sis, Hikmet A1 - Erdemoğlu, Murat T1 - Utilizing Taguchi method and in situ X-ray powder diffraction monitoring to determine the influence of mechanical activation conditions on the physico-chemical properties and Al leachability of K-feldspar N2 - K-feldspar represents an important natural resource of potassium and aluminum. Within the framework of this study, the K-feldspar was mechanically activated in a planetary ball mill under different conditions planned according to 43 Taguchi orthogonal array experimental design. As outputs, specific surface area (SBET), median particle size (d50), amorphization degree of mineral phases , and Al recovery were used. It was found that the initial d50 value of 293 μm could be reduced to 6.7 μm and the SBET value of 4.7 m2/g could be increased up to 32.5 m2/g upon milling. Both microcline KAl3SiO8, and albite NaAl3SiO8 could be almost completely amorphized, whereas quartz SiO2 still maintained some crystallinity even under the most intensive conditions. Increasing SBET and decreasing the d50 values did not lead to a significant improvement in Al leach recovery, whereas a clear relationship between the amorphization of microcline and the recovered aluminum was found. Analysis of Variance (ANOVA) showed that increasing ball-to-powder ratio is the most beneficial for the improvement in Al recovery. In situ powder X-ray diffraction monitoring performed in an oscillation ball mill under synchrotron irradiation has shown very rapid amorphization of microcline phase at the beginning. However, amorphization of microcline was only partial after two hours of the treatment in this mill, apart from almost complete process in the planetary ball mill. In the end, regressions for the calculation of Al recovery by knowing the values of input parameters were calculated. In general, by just using mechanical activation without the subsequent roasting process that is commonly used to boost metal recoveries, it was possible to quantitatively recover aluminum from K-feldspar. KW - Mechanochemistry KW - Mechanical activation KW - Design of experiments PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-611059 DO - https://doi.org/10.1016/j.jmrt.2024.08.156 SN - 2238-7854 VL - 32 SP - 3886 EP - 3895 PB - Elsevier B.V. AN - OPUS4-61105 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -