TY - CONF A1 - Raedel, Martina T1 - Research and reconstruction of historic gold mosaics N2 - A research project of reconstructing historical gold mosaics deals with reconstructing weatherproof gold and silver mosaics according to historical models. The gold mosaics examinded originate mainly from germany from 1880 to 1920 and are composed of three parts. They consist of a matching support glass, the gold or silver layer and a cover glass. By examining the morphology and layer thicknesses with the ESEM, and using chemical analysis with the EDX, the relationship of glass composition and damage patterns was established. The glass analysis provided quantitative composition data and made it possible to determine its chemical stability. It supplied the basis for calculating glass characteristics and was referred to when casting suitable historical mosaic glass. The analysis of the qualitative composition of the gold and silver layers also served as a model for reconstruction. After testing selected reconstructed gold mosaics in the climate chamber, the ESEM was used for capturing leaching and other process data and the glass composition was optimized accordingly. Over 100 predominantly historical gold mosaics were analyzed and the results entered into a database which can now be consulted for comparative investigations to determine both origin and date. T2 - What comes to mind when you hear mosaics, conserving mosaics from ancient to modern CY - Barcelona, Spain DA - 15.10.2017 KW - Gold mosaics KW - Leaching process KW - Composition KW - Database PY - 2017 AN - OPUS4-43216 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Raedel, Martina T1 - Untersuchungen zum Alterungsverhalten gefüllter Glasklebstoffe N2 - Die vorliegende Untersuchung befasst sich mit der Frage, inwieweit mit Füllstoff angereicherte Klebstoffe für die Restaurierung von Flachgläsern mit größeren Defekten oder als Ergänzungsmaterial geeignet sind. Hierzu werden verschiedene silikatische Füllstoffe untersucht und in ausgewählte Glasklebstoffe eingearbeitet. Die Zugabe der Füllstoffe ermöglicht eine gezielte Eigenschaftssteuerung von z.B. Viskosität oder Härte. Die eingesetzten Füllstoffe werden hinsichtlich ihrer Zusammensetzung und Korngröße charakterisiert und mikroskopisch betrachtet. Die optimale Dispergierung der Füllstoffe in die Klebstoffe wird ermittelt und in Testreihen überprüft. Die angefertigten gefüllten Klebstoffe werden durch Farb- und UV-VIS Messungen charakterisiert. REM-Aufnahmen geben Aufschluss über die Verteilung der Füllstoffe im Klebstoff. Tests zur Biegefestigkeit sowie die Durchführung dynamisch-mechanischer Analysen (DMA) ermöglichen Aussagen zum Alterungsverhalten der Klebstoffe. Dazu werden die Prüfkörper vor und nach der Alterung im Klimaprüfschrank untersucht. Die Ergebnisse zeigen, dass sich durch die Beimischung von Füllstoffen Eigenschaften wie Festigkeit, Elastizität und auch Vergilbungsbeständigkeit beeinflussen lassen. Im Praxisbetrieb in den Restaurierungswerkstätten ist es jedoch schwierig, eine optimale Mischung der Komponenten zu erreichen. Dies begrenzt die Verwendung der getesteten Füllstoffe als transparentes Ergänzungsmaterial. Im Versuchsverlauf konnten dennoch vielversprechende gefüllte Klebstoffe entwickelt und auch die Transparenz verbessert werden. Die Testergebnisse werden vorgestellt und erläutert. T2 - "Wissen wollen", Stuttgarter Forschungen zur Objektrestaurierung CY - Stuttgart, Germany DA - 09.11.2017 KW - Gefüllte Glasklebstoffe KW - Restaurierung KW - Alterungsverhalten PY - 2017 AN - OPUS4-43220 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Raedel, Martina A1 - Bücker, Michael T1 - Long term corrosion protection - A contradiction in terms? A comparative study of modern and traditional anticorrosion systems N2 - A comparative study tested the performance of modern anti-corrosion Systems against that of traditional red lead Systems. One aim of the research project was to find alternatives for the use of a red lead priming coat, the Standard anti-corrosive primer for iron and Steel in the past but a material which endangers health as well as environment. The investigation aimed to determine whether anti-corrosion Systems developed for industrial use were suitable for the Conservation of historic iron and cast iron objects. Besides coatings containing red lead, several surface tolerant coatings with different anti-corrosion pigments were examined. The modern anti-corrosion Systems examined were suitable for surfaces where Optimum surface preparation is not practical. They were applied to both historical samples and to newly prepared model samples. After uniform pre-corrosion, the model samples were coated and underwent two different ageing procedures: accelerated ageing in a climate chamber and outdoor weathering on a test site with moderate city climate. The specimens were exposed for more than two and a half years. Evaluation of the artificially aged samples was carried out under the aspect coating degradation, tensile strength test, cross-hatch test and Fourier-transform infrared microscope. The results of the research with optical evaluation and test procedures will be presented. The two ageing methods will be discussed, with different results from the naturally and artificially aged samples. The results Show a similar eligibility of modern anti-corrosion Systems as compared with red lead Systems for the use in Conservation. T2 - Metal 2013 - ICOM-CC Interim Meeting of the Metal Working Group CY - Edinburgh, Scotland DA - 16.09.2013 KW - Comparative study KW - Anti-corrosion systems KW - Red lead coating KW - Metal Restaurierung KW - Anti-korrosions Beschichtungssysteme KW - Bleimennige-Überzüge KW - Vergleichende Studie PY - 2013 SN - 978-1-84917-142-7 SP - 79 EP - 86 AN - OPUS4-32552 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Raedel, Martina T1 - Testing the Durability of Modified Corrosion Protection Systems for Monuments Conservation T2 - EuroCorr 2014 CY - Pisa, Italien DA - 2014-09-08 PY - 2014 AN - OPUS4-32623 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Raedel, Martina T1 - One solution with three components - filled adhesives for stained glass window conservation T2 - ICOM-CC Glass and Ceramics Working Group Interim Meeting CY - Amsterdam, Netherlands DA - 2013-10-07 PY - 2013 AN - OPUS4-29891 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Raedel, Martina T1 - Long Term Corrosion Protection- a Contradiction in Terms? T2 - Metal 2013 CY - Edinburgh, Scotland DA - 2013-09-16 PY - 2013 AN - OPUS4-29858 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Raedel, Martina A1 - Torge, Manfred A1 - Bücker, Michael ED - Uwe Peltz, ED - Olivia Zorn, T1 - Restaurierung von Glasmalereien des 19. Jahrhunderts mit modifizierten Glasklebstoffen KW - Glasgemälde des 19. Jahrhunderts KW - Glasrestaurierung KW - Glasmalerei KW - Glasklebstoffe für die Restaurierung KW - Forschungsprojektergebnisse PY - 2009 SN - 978-3-8053-3981-0 SP - 235 EP - 241 PB - Philipp von Zabern AN - OPUS4-19790 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Raedel, Martina T1 - Das Glasgemälde einer Strahlenkranzmadonna aus der Berliner Nikolaikirche - Materialtechnische Untersuchungen und Restaurierung T2 - Kolloquium: Stadt - Museum - Sammlung, Neue Forschung zur Sammlung alter Kunst des Stadtmuseums Berlin, Märkisches Museum CY - Berlin, Germany DA - 2008-05-31 PY - 2008 AN - OPUS4-17682 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Raedel, Martina T1 - Colored Glass Adhesives for the Restoration of Stained Glass Windows T2 - Internationale Tagung "Forum for the Conservation and Restoration of Stained Glass Windows" CY - New York City, NY, USA DA - 2009-06-01 PY - 2009 AN - OPUS4-19984 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Raedel, Martina A1 - Bücker, Michael A1 - Unger, Brita T1 - Historische und moderne Goldmosaike im Vergleich KW - Historische und moderne Goldmosaike KW - Aufbau KW - Besonderheiten KW - Herstellungstechnik KW - Glaszusammensetzung KW - EDX-Analyse KW - Viskositäts-Temperatur-Verhalten KW - Ausdehnungskoeffizient PY - 2010 SN - 0947-6229 IS - 3 SP - 184 EP - 185 PB - Dt. Bergbau-Museum CY - Bochum AN - OPUS4-22707 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -