TY - JOUR A1 - Bosch, R.-W. A1 - Cottis, R.A. A1 - Csecs, K. A1 - Dorsch, T. A1 - Dunbar, L. A1 - Heyn, Andreas A1 - Huet, F. A1 - Hyökyvirta, O. A1 - Kerner, Z. A1 - Kobzova, A. A1 - Macak, J. A1 - Novotny, R. A1 - Öijerholm, J. A1 - Piippo, J. A1 - Richner, R. A1 - Ritter, S. A1 - Sánchez-Amaya, J.M. A1 - Somogyi, A. A1 - Väisänen, S. A1 - Zhang, W. T1 - Reliability of electrochemical noise measurements: Results of round-robin testing on electrochemical noise N2 - Sixteen laboratories have performed electrochemical noise (EN) measurements based on two systems. The first uses a series of dummy cells consisting of a 'star' arrangement of resistors in order to validate the EN measurement equipment and determine its baseline noise performance, while the second system, based on a previous round-robin in the literature, examines the corrosion of aluminium in three environments. All participants used the same measurement protocol and the data reporting and analysis were performed with automatic procedures to avoid errors. The measurement instruments used in the various laboratories include commercial general-purpose potentiostats and custom-built EN systems. The measurements on dummy cells have demonstrated that few systems are capable of achieving instrument noise levels comparable to the thermal noise of the resistors, because of its low level. However, it is of greater concern that some of the instruments exhibited significant artefacts in the measured data, mostly because of the absence of anti-aliasing filters in the equipment or because the way it is used. The measurements on the aluminium samples involve a much higher source noise level during pitting corrosion, and most (though not all) instruments were able to make reliable measurements. However, during passivation, the low level of noise could be measured by very few systems. The round-robin testing has clearly shown that improvements are necessary in the choice of EN measurement equipment and settings and in the way to validate EN data measured. The results emphasise the need to validate measurement systems by using dummy cells and the need to check systematically that the noise of the electrochemical cell to be measured is significantly higher than the instrument noise measured with dummy cells of similar impedance. KW - Electrochemical noise KW - Round-robin KW - Corrosion PY - 2014 DO - https://doi.org/10.1016/j.electacta.2013.12.093 SN - 0013-4686 SN - 1873-3859 VL - 120 SP - 379 EP - 389 PB - Elsevier Science CY - Kidlington AN - OPUS4-30284 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kiefer, R. A1 - Stilke, R. A1 - Boese, E. A1 - Heyn, Andreas A1 - Engelking, M. A1 - Hillert, R. T1 - Klärung des Schadensmechanismus dekorativ verchromter Kunststoffanbauteile unter verschärfter Streusalzbelastung durch Calcium- und Magnesiumchlorid N2 - Dekorativ verchromte Kunststoffanbauteile werden seit Anfang der 1970er Jahre in der Automobilindustrie eingesetzt, um Fahrzeugen eine optisch höhere Wertigkeit zu geben. Um Chrom auf der Oberfläche vor Korrosion zu schützen, werden Mehrfachschichten auf einem Kunststoffsubstrat (Kupfer und mehrere Nickelüberzüge) abgeschieden. Die verschiedenen Nickelüberzüge erfüllen im Korrosionsschutzsystem spezielle Funktionen und variieren daher in ihrer Zusammensetzung. Die oberen Schichten sind definiert mikroporig bzw. mikrorissig. N2 - Since the 1970‘s, decorative chromium-plated plastic components have been used in the automotive industry to enhance the visual appearance of automobiles. In order to protect an outer layer of chromium from corrosion, multiple layers have to be deposited onto the plastic Substrate (copper and multiple nickel layers). The individual nickel layers each fulfill a special function in the corrosion protection System and thus differ in their composition. The outer layers are characterised by their microporosity and micro cracks. KW - Korrosion KW - Schaden KW - Chrom KW - Nickel KW - Überzug KW - Streusalz KW - Automobil KW - Elektrochemie PY - 2012 SN - 0016-4232 VL - 103 IS - 9 SP - 1904 EP - 1914 PB - Leuze CY - Saulgau, Württ. AN - OPUS4-26839 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kiefer, R. A1 - Boese, E. A1 - Heyn, Andreas A1 - Engelking, M. A1 - Hillert, R. T1 - Korrosion verchromter Kunstoffanbauteile unter verschärfter Streusalzbelastung mit CaCl2 N2 - Dekorativ verchromte Kunststoffanbauteile werden seit Anfang der 1970er Jahre in der Automobilindustrie eingesetzt, um einem Fahrzeug eine optisch höhere Wertigkeit zu geben. Diese mikroporig bzw. mikrorissig galvanisch abgeschiedenen Überzüge auf Kunststoffanbauteilen sind in einer festgelegten Reihenfolge übereinander angeordnet, um die Funktionen Dekorativität und Korrosionsbeständigkeit zu erfüllen. Unter dem Chromüberzug befindet sich u.a. ein Glanznickelüberzug, welcher durch Poren bzw. Risse bei Kontakt mit Streusalzsole gezielt korrodieren soll und somit den Chromüberzug kathodisch schützt. Der Zusatz von Kalziumchlorid in die Streusalzmischungen in Regionen mit extrem niedrigen Temperaturen (z. B. Winter in Moskau) stört diesen Mechanismus. Unter diesen Bedingungen wurden flächenhafte Schäden am Chromüberzug mikroporig verchromter Kunststoffanbauteile beobachtet. Bei Volkswagen erfolgte daraufhin die Umstellung aller verchromten Bauteile im Exterieur auf mikrorissig. Die Ursache für diese Schäden soll in der vorliegenden Arbeit geklärt werden. T2 - 14. Sommerkurs Werkstoffe und Fügen am Institut für Werkstoff- und Fügetechnik CY - Magdeburg, Germany DA - 23.09.2011 KW - Chrom-Nickel-Überzug KW - Streusalz KW - Calziumchlorid KW - Korrosionsschaden KW - Automobilbau KW - Korrosionsprüfung KW - Elektrochemie PY - 2011 SN - 978-3-940961-56-3 SP - 167 EP - 176 AN - OPUS4-24495 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Munsch, Sarah Mandy A1 - Bintz, Thilo A1 - Heyn, R. A1 - Hirsch, H. A1 - Grunewald, J. A1 - Kruschwitz, Sabine T1 - Detailed investigation of capillary active insulation materials by 1H nuclear magnetic resonance (NMR) and thermogravimetric drying N2 - Capillary active interior insulation materials are an important approach to minimize energy losses of historical buildings. A key factor for their performance is a high liquid conductivity, which enables redistribution of liquid moisture within the material. We set up an experiment to investigate the development of moisture profiles within two different interior insulation materials, calcium-silicate (CaSi) and expanded perlite (EP), under constant boundary conditions. The moisture profiles were determined by two different methods: simple destructive sample slicing with subsequent thermogravimetric drying as well as non-destructive NMR measurements with high spatial resolution. The moisture profiles obtained from both methods show good agreement, when compared at the low spatial resolution of sample slicing, which demonstrates the reliability of this method. Moreover, the measured T2-relaxation-time distributions across the sample depth were measured, which may give further insight into the saturation degree of the different pore sizes. In order to explain differences in the moisture profiles between CaSi and EP, we determined their pore-size distribution with different methods: conversion of the NMR T2 relaxationtime distribution at full saturation, mercury intrusion porosimetry and indirect determination from pressure plate measurements. CaSi shows a unimodal distribution at small pore diameters, while in EP, a bi-modal or wider distribution was found. We assume that the smaller pore diameters of CaSi lead to a higher capillary conductivity, which causes a more distributed moisture profile in comparison with that of EP. T2 - NDT-CE CY - Zurich, Switzerland DA - 16.08.2022 KW - Insulation material KW - Nuclear magnetic resonance KW - Capillary conductivity KW - Pore-size distribution PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-579172 DO - https://doi.org/10.58286/27205 SN - 1435-4934 VL - 27 IS - 9 SP - 1 EP - 11 AN - OPUS4-57917 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmigalla, S. A1 - Heyn, Andreas A1 - Wesling, V. A1 - Reiter, R. A1 - Echtermeyer, P. T1 - Investigation of the pitting corrosion behaviour of nickel based alloy claddings by evaluation of electrochemical noise measurements N2 - Claddings of different nickel based alloys were generated on a mild Steel (S235JR) and a stainless steel type 304 by Cold Metal Transfer (CMT). This welding procedure possesses a low degree of mixing between the Substrate and cladding material. Thus it improves the corrosion behaviour of the claddings. The aim of our investigations was to examine the effect of the welding parameters: energy per unit length, shielding gas and finishing surface treatment on the pitting corrosion behaviour of the claddings. However, under Standard test conditions nickel based alloys are often resistant to pitting corrosion. Moreover these test methods are inaccurate and require a large period of time resulting from the iterative progress to determine the critical pitting temperature (CPT). A potentiostatic test method was modified using a high concentrated CaCI2-solution and a conventional three electrode measuring cell. The pitting corrosion behaviour is calculated from current noise charges. During the test the course of corrosion is detected online by the evaluation of electrochemical noise Signals while a continuous increase of temperature by a defined heating rate is realised. Thus a critical pitting temperature can be estimated by only one attempt. Furthermore the deviation of the measured CPT is very low compared to Standard tests using gravimetrical and microscopic evaluation. That enables to figure out the influence of the welding parameters in an exact way. T2 - EUROCORR 2011 - Developing solutions for the global challenge CY - Stockholm, Sweden DA - 04.09.2011 KW - Nickelbasislegierung KW - Plattieren KW - Schweißverfahren KW - Cold metal transfer KW - Korrosionsprüfung KW - Elektrochemie KW - Elektrochemisches Rauschen PY - 2011 SP - 1 EP - 9 AN - OPUS4-24565 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wesling, V. A1 - Reiter, R. A1 - Echtermeyer, P. A1 - Heyn, Andreas A1 - Schmigalla, S. ED - Wielage, B. T1 - Untersuchungen zur Herstellung von aufmischungsarmen Plattierungen aus NiCrMo-Legierungen und deren spezifischen Korrosionseigenschaften N2 - Für viele Anlagenkomponenten der chemischen Industrie, der Offshoretechnik aber auch in der Kraftwerksindustrie stellt die Verwendung von NiCrMo-Legierungen eine bewährte werkstofftechnische Lösung dar, um den Anforderungen hinsichtlich der Korrosionsbeständigkeit gerecht zu werden. Aufgrund gestiegener Werkstoffkosten kommt dem Auftragschweißen dieser Werkstoffe eine zunehmende Bedeutung zu. Die Anwendung des Cold-Metal-Transfer-Prozesses (CMT) zur Verarbeitung von NiCrMo-Legierungen bietet verfahrensspezifische Vorteile, da es mit diesem geregelten Kurzlichtbogenprozess möglich ist, aufmischungsarme Plattierungen mit Aufmischungsgraden < 5 % zu erzeugen und die thermische Beeinflussung des Grundwerkstoffs zu minimieren. Die chemische Zusammensetzung der Plattierungen weist geringe Eisengehalte sowie hohe Nickel-, Chrom- und Molybdängehalte auf, die bei geeigneter Parameterwahl denen der Schweißzusatzwerkstoffe entsprechen. Zur Qualifizierung der Schweißplattierungen sind geeignete Prüfverfahren erforderlich, die den Einfluss der Verfahrensparameter auf das Korrosionsverhalten reproduzierbar darstellen können. Ein Schwerpunkt stellt die Untersuchung der Lochkorrosionsbeständigkeit in chloridhaltigen Medien dar. Dazu wurde am IWF eine Prüfmethode auf Basis des elektrochemischen Rauschens entwickelt. Diese ermöglicht es, die Lochkorrosionsbeständigkeit von NiCrMo-Werkstoffen bei gegenüber Standardprüfverfahren stark verkürzter Prüfdauer exakt und reproduzierbar zu ermitteln. Zudem besitzen selektive Korrosionserscheinungen in schwefelsauren, chloridhaltigen Medien, wie z.B. Nasskondensate in Müllverbrennungsanlagen, bei Schweißplattierungen in der Praxis Relevanz, da es bei der Erstarrung nach dem Plattiervorgang zur Seigerung von für die Korrosionsbeständigkeit wichtigen Legierungselementen kommt. Durch Bestimmung von Passivierungsstromdichten in einem geeigneten Prüfmedium lassen sich Aussagen über die Neigung zur selektiven Korrosion der Plattierungen in Abhängigkeit der Parameter treffen. T2 - 15. Werkstofftechnisches Kolloquium CY - Chemnitz, Germany DA - 20.09.2012 KW - Plattierung KW - Schweißplattierung KW - Nickellegierung KW - CMT KW - Korrosionsschutz KW - Korrosionsprüfung PY - 2012 SN - 978-3-00-039358-7 SN - 1439-1597 N1 - Serientitel: Werkstoffe und werkstofftechnische Anwendungen – Series title: Werkstoffe und werkstofftechnische Anwendungen VL - 47 SP - 235 EP - 245 AN - OPUS4-27487 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -