TY - CONF A1 - Höhne, Patrick A1 - Kuchenbecker, Petra A1 - Rabe, Torsten T1 - Superior granule properties by spray drying controlled destabilized slurries with ultrasound N2 - Homogeneous introduction of organic additives is a key of ceramic powder processing. Addition of organics to ceramic slurries holds advantages compared to dry processing like organic content reduction and a more homogeneous additive distribution on the particle surface. Investigations of the alumina slurries were primarily based on zeta potential measurements and sedimentation analysis by optical centrifugation. Both methods were combined to determine a suitable additive type, amount and composition, whereas the spray drying suitability has been ensured by viscosity measurements. Granules, yielded by spray drying of such ideally dispersed alumina slurries, are mostly hollow and possess a hard shell. Those granules cannot easily be processed and can only hardly be destroyed in the following shaping step, leading to sinter bodies with many defects and poor strength and density. The precise slurry destabilization, carried out after ideally dispersing the ceramic powder, shows a strong influence on the drying behavior of the granules and hence on the granule properties. A promising degree of destabilization and partial flocculation was quantified by optical centrifugation and resulted in improved granule properties. Spray drying the destabilized alumina slurries yielded homogeneous “non-hollow” granules without the above mentioned hard shell. Sample bodies produced of these granules exhibited a reduction of defect size and number, leading to better results for sinter body density and strength. The positive effect of the slurry destabilization has been further improved, by exchanging the atomizing unit from a two-fluid one to an ultrasound atomizer with only minor slurry adjustments necessary. The controlled destabilization and ultrasound atomization of the ceramic slurry show excellent transferability for zirconia and even ZTA (zirconia toughened alumina) composite materials. T2 - Partec 2019 CY - Nuremberg, Germany DA - 09.04.2019 KW - Destabilization KW - Slurry KW - Ultrasound KW - Atomization PY - 2019 AN - OPUS4-48291 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Höhne, Patrick A1 - Kuchenbecker, Petra A1 - Lindemann, Franziska A1 - Güther, Wolfgang A1 - Rabe, Torsten T1 - Utilization of an ultra sound atomizer for spray granulation of oxide ceramic fine powder N2 - Spray drying based granulation processes aim for flowable granules neither containing voids nor hard shells thus leading to a homogenous microstructure in the green and sinter bodies without strength reducing large pores. The increase of the specific surface area due to the utilization of finer powders as raw materials makes the production of granules of demanded quality more sophisticated. Innovations regarding additives as well as process engineering are therefore required. While conventional spray granulation processes of ceramic materials are based on rotational, one stream or two stream nozzles for nebulization, the investigations in the ZIM project concentrate on the applicability of an ultra sound atomizer unit. A spray dryer comprised of the aforementioned ultra sound atomization unit implemented in a commercial spray dryer (Niro, Denmark) was used as test system. Potential advantages of the ultra sound nebulization are investigated for model systems of alumina, zirconia and a ZTA composite while focusing on solids content, yield, pressability and granule properties (size, size distribution, flowability, shape and microstructure) as well as the final sinter body properties (density, microstructure and flexural strength). First ultra sound spray drying experiments yielded granules with excellent processability. Spray drying of identical slurries, as before tested and optimized for a two stream nozzle atomization process, resulted in a more suitable size distribution for dry pressing (less particles below 20 µm) and a higher yield. Furthermore, sinter bodies produced of ultra sound granules seem to have less large pores and a more homogenous microstructure T2 - 92. Jahrestagung der deutschen keramischen Gesellschaft CY - Berlin, Germany DA - 20.03.2017 KW - Ceramics KW - Spray drying KW - Ultra sound KW - Atomization KW - Microstructure PY - 2017 AN - OPUS4-39588 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -