TY - JOUR A1 - Salari, Farid A1 - Zocca, Andrea A1 - Bosetti, Paolo A1 - Hlaváček, Petr A1 - Italiano, Antonino A1 - Gobbin, Filippo A1 - Colombo, Paolo A1 - Kühne, Hans-Carsten A1 - Sglavo, Vincenzo M. T1 - Powder-bed 3D printing by selective activation of magnesium phosphate cement: Determining significant processing parameters and their effect on mechanical strength N2 - The present work addresses powder bed binder jetting additive manufacturing by selective magnesium phosphate cement activation. Despite the potential of this technology to aid the digitalization of the construction industry, the effect of processing parameters on the mechanical performance of printed materials has not yet been studied to generate a guideline for the further development of the technology. Statistical methodologies were used to screen the effect of four printing process parameters (printing speed, layer thickness, raster angle, and build direction on flexural and compressive strength). As the exploited technology works with constant fluid pressure, the physical interpretation of the effect of each factor can be considered taking into account the interactions between the binder materials in the powder bed. Analysis of variance (ANOVA) indicated that printing speed and layer thickness significantly affect mechanical performances. Furthermore, the layout of samples for the printing process is preferable to be parallel the printhead movement. An anisotropic behavior was observed, and the samples subjected to compressive forces parallel to the layer plane possessed lower strength values. This effect can be interpreted as a result of a weak area of low density in between layers, leading to a pronounced delamination under compression. Even though the strength of the printed material is not suitable for a structural concrete, it can be marginally improved by design of experiment and optimized for non-structural applications, such as for porous artificial stone. Design of experiment coupled with ANOVA methods can be used in the future to support the development of novel material mixtures, thus expanding the fields of application of this novel additive manufacturing technology. KW - Concrete 3D-printing KW - Particle-bed binder jetting KW - Design of experiment PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-601654 DO - https://doi.org/10.1016/j.oceram.2024.100609 VL - 18 SP - 1 EP - 11 PB - Elsevier B.V. AN - OPUS4-60165 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zocca, Andrea A1 - Franchin, Giorgia A1 - Elsayed, Hamada A1 - Gioffredi, Emilia A1 - Bernardo, Enrico A1 - Colombo, Paolo T1 - Direct Ink Writing of a Preceramic Polymer and Fillers to Produce Hardystonite (Ca2ZnSi2O7) Bioceramic Scaffolds N2 - The direct ink writing of an ink composed of a preceramic polymer and fillers was used to produce hardystonite (Ca2Zn-Si2O7) bioceramic scaffolds. Suitable formulations were developed for the extrusion of fine filaments (350 µm diameter) through a nozzle. The preceramic polymer was employed with the double purpose of contributing to the rheology of the ink by increasing its viscosity and of forming the hardystonite phase upon heat treatment by reacting with the fillers. A control of the rheology is essential when spanning features have to be produced, and therefore the main rheological characteristics of the inks were measured (flow curves, dynamic oscillation tests, viscosity recovery tests) and compared to models reported in the literature. Highly porous scaffolds (up to 80% total porosity) were produced and heat treated in air or in nitrogen atmosphere. The influence of the heat-treatment atmosphere on the morphology, crystalline phase assemblage, and compressive strength of the scaffolds was investigated. KW - Porous materials KW - Bioceramics KW - Polymer precursor KW - Processing PY - 2016 DO - https://doi.org/10.1111/jace.14213 VL - 6 IS - 99 SP - 1960 EP - 1967 PB - Wiley-Blackwell AN - OPUS4-38114 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -