TY - JOUR A1 - Emamverdi, Farnaz A1 - Yin, Huajie A1 - Smales, Glen Jacob A1 - Harrison, W. J. A1 - Budd, P. M. A1 - Böhning, Martin A1 - Schönhals, Andreas T1 - Polymers of intrinsic microporosity - Molecular mobility and physical aging revisited by dielectric spectroscopy and X‑ray scattering N2 - Polymers of intrinsic microporosity (PIMs) are promising candidates for the active layer in gas separation membranes due to their high permeability and reasonable permselectivity. These appealing properties originate from a microporous structure as a result of inefficient segment packing in the condensed state due to a combination of a ladder-like rigid backbone and sites of contortion. However, this class of polymers suffers from a significant decrease in the permeability with time due to physical aging, whereby typically, the permselectivity increases. The initial microporous structures approach a denser state via local rearrangements, leading to the reduction of the permeability. Hence, a detailed characterization of the molecular mobility in such materials can provide valuable information on physical aging. In this work, the dielectric behavior of PIM-1 films and their behavior upon heating (aging) were revisited by isothermal frequency scans during different heating/cooling cycles over a broad temperature range between 133 and 523 K (−140 to 250 °C). In addition, the obtained results were compared with data of samples that were annealed at ambient temperatures over different time scales. Multiple dielectric processes were observed: several relaxation processes due to local fluctuations and a Maxwell−Wagner−Sillars polarization effect related to the microporosity. The temperature dependence of the rates of all processes follows the Arrhenius law where the estimated activation energy depends on the nature of the process. The influence of the thermal history (aging) on the processes is discussed in detail. KW - Polymers of intrinsic microporosity PY - 2022 DO - https://doi.org/10.1021/acs.macromol.2c00934 VL - 55 SP - 7340 EP - 7350 PB - American Chemical Society CY - Washington, DC AN - OPUS4-55485 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Konnertz, Nora A1 - Ding, Yi A1 - Harrison, W.J. A1 - Budd, P.M. A1 - Schönhals, Andreas A1 - Böhning, Martin T1 - Molecular mobility and gas transport properties of nanocomposites based on PIM-1 and polyhedral oligomeric phenethyl-silsesquioxanes (POSS) N2 - Polymers with intrinsic microporosity (PIMs) are of great interest in the field of gas separation membranes. Already the first synthesized PIM-1 shows extraordinary permeability and selectivity. Unfortunately, PIM-1 is susceptible to physical aging and thus gradually loses its outstanding properties. In this study a polyhedral oligomeric silsesquioxane with phenethyl substituents (PhenethylPOSS) was used as a nanofiller (0–40 wt%) in the PIM-1 matrix to potentially improve the gas transport properties and prevent physical aging. The molecular mobility of the solution-cast nanocomposite films was analyzed by Broadband Dielectric Spectroscopy (BDS). Furthermore, gas permeability was determined with the time lag method (0–20 bar upstream pressure) at 35 °C for N2, O2, CH4 and CO2. KW - Broadband Dielectric Spectroscopy KW - Gas separation KW - Gas permeation KW - Polymers of intrinsic microporosity KW - Nanocomposite KW - POSS KW - PIM-1 PY - 2017 DO - https://doi.org/10.1016/j.memsci.2017.02.007 SN - 0376-7388 SN - 1873-3123 VL - 529 SP - 274 EP - 285 PB - Elsevier B.V. CY - Amsterdam AN - OPUS4-39169 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zorn, R. A1 - Yin, Huajie A1 - Lohstroh, W. A1 - Harrison, W. A1 - Budd, P.M. A1 - Pauw, Brian Richard A1 - Böhning, Martin A1 - Schönhals, Andreas T1 - Anomalies in the low frequency vibrational density of states for a polymer with intrinsic microporosity - the Boson peak of PIM-1 N2 - Polymers with intrinsic microporosity are promising candidates for the active separation layer in gas separation membranes. Here, the vibrational density of states (VDOS) for PIM-1, the prototypical polymer with intrinsic microporosity, is investigated by means of inelastic neutron scattering. The results are compared to data measured for a more conventional high-performance polyimide used in gas separation membranes (Matrimid). The measured data show the characteristic low frequency excess contribution to VDOS above the Debye sound wave level, generally known as the Boson peak in glass-forming materials. In comparison to the Boson peak of Matrimid, that of PIM-1 is shifted to lower frequencies. This shift is discussed considering the microporous, sponge-like structure of PIM-1 as providing a higher compressibility at the molecular scale than for conventional polymers. For an annealed PIM-1 sample, the Boson peak shifts to higher frequencies in comparison to the un-annealed sample. These changes in the VDOS of the annealed PIM-1 sample are related to changes in the microporous structure as confirmed by X-ray scattering. KW - Polymers KW - Boson peak KW - Neutron scattering KW - Physical aging KW - Polymer of intrinsic microporosity PY - 2018 DO - https://doi.org/10.1039/C7CP07141H SN - 1463-9076 SN - 1463-9084 VL - 20 IS - 3 SP - 1355 EP - 1363 PB - The Royal Society of Chemistry AN - OPUS4-43808 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yin, Huajie A1 - Chua, Y. Z. A1 - Yang, B. A1 - Schick, C. A1 - Harrison, W. A1 - Budd, P. A1 - Böhning, Martin A1 - Schönhals, Andreas T1 - First clear cut experimental evidence for a glass transition in a polymer with intrinsic microporosity: PIM-1 N2 - Polymers with intrinsic microporosity (PIMs) represent a novel, innovative class of materials with great potential in various applications from high-performance gas separation membranes to electronic devices. Here for the first time, for PIM-1, as the archetypal PIM, fast scanning calorimetry provides definitive evidence for a glass transition (Tg=715 K, heating rate 3·10^4 K/s) by decoupling the time-scales responsible for glass transition and decomposition. As the rigid molecular structure of PIM-1 prevents any conformational changes, small-scale bend and flex fluctuations must be considered the origin of its glass transition. This result has strong implications for the fundamental understanding of the glass transition and for the physical aging of PIMs and other complex polymers, both topical problems of materials science. KW - Polymers with intrinsic microporosity KW - Fast Scanning Calorimetry PY - 2018 DO - https://doi.org/10.1021/acs.jpclett.8b00422 SN - 1948-7185 VL - 9 IS - 8 SP - 2003 EP - 2008 PB - ACS AN - OPUS4-44683 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zorn, R. A1 - Lohstroh, W. A1 - Zamponi, M. A1 - Harrison, W. A1 - Budd, P. A1 - Böhning, Martin A1 - Schönhals, Andreas T1 - Molecular mobility of a polymer of intrinsic microporosity revealed by quasielastic neutron scattering N2 - Quasielastic neutron scattering by employing a combination of time-of-flight and backscattering techniques is carried out to explore the molecular mobility of a polymer of intrinsic microporosity (PIM-1) at microscopic time scales in comparison with a high-performance polyimide. Molecular fluctuations can change the structure of the temporary network of micropores and open or close pathways for gas molecules. Therefore, the investigation might help to understand the selectivity of PIMs in gas separation processes. The performed neutron scattering experiments provide evidence for a low-temperature relaxation process, which was assigned to methyl group rotation. This methyl group rotation was analyzed in terms of jump diffusion in a three-fold potential. The analysis results in a fraction of methyl groups which are immobilized. For PIM-1 it was found that the fraction of immobilized methyl groups decreases with increasing temperature up to 350 K. At higher temperatures the number of immobilized methyl group increases gain due to an underlying relaxation process. This motional process on a somewhat larger length scale might lead to a reversible structural rearrangement which partially hinders the strongly localized methyl group rotation. In addition, it was found that the activation energy for the methyl group rotation for PIM-1 and the polyimide is significantly higher than for conventional polymers. KW - Polymer of intrinsic microporosity KW - Quasielastic neutron scattering PY - 2020 DO - https://doi.org/10.1021/acs.macromol.0c00963 SN - 0024-9297 SN - 1520-5835 VL - 53 IS - 15 SP - 6731 EP - 6739 PB - American Chemical Society CY - Washington, DC AN - OPUS4-51147 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Konnertz, Nora A1 - Ding, Yi A1 - Harrison, W.J. A1 - Budd, P.M. A1 - Schönhals, Andreas A1 - Böhning, Martin T1 - Molecular mobility of the high performance membrane polymer PIM-1 as investigated by dielectric spectroscopy N2 - The increasing demand for energy efficient separation processes fosters the development of new high performance polymers as selective separation layers for membranes. PIM-1 is the archetypal representative of the class of polymers of intrinsic microporosity (PIM) which are considered most promising in this sector, especially for gas separations. Since their introduction, PIMs stimulated a vast amount of research in this field and meanwhile evolved to the state of the art in membrane technology for gas separation. The major obstacle for extending the practical membrane application is their strong tendency to physical aging. For the first time, investigations by broadband dielectric spectroscopy (BDS) addressing molecular dynamics and conductivity in PIM 1 are presented. As chain packing during film formation from the casting solution and physical aging are key factors determining the separation performance of PIMs as membrane materials, characterization of the molecular mobility in such materials as revealed by BDS will provide valuable information for further development and optimization. KW - PIM-1 KW - BDS broadband dielectric spectroscopy KW - Relaxation KW - Membrane PY - 2016 DO - https://doi.org/10.1021/acsmacrolett.6b00209 SN - 2161-1653 VL - 5 IS - 4 SP - 528 EP - 532 PB - ACS American Chemical Society CY - Washington, DC, USA AN - OPUS4-35798 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yin, Huajie A1 - B, Yang A1 - Chua, Y. Z. A1 - Szymoniak, Paulina A1 - Carta, M A1 - Malpass-Evans, R A1 - McKeown, N A1 - Harrison, W A1 - Budd, P A1 - Schick, C A1 - Böhning, Martin A1 - Schönhals, Andreas T1 - Effect of backbone rigidity on the glass transition of polymers of in-trinsic microporosity probed by fast scanning calorimetry N2 - Polymers of Intrinsic Microporosity (PIMs) of high performance have developed as materials with a wide application range in gas separation and other energy-related fields. Further optimization and long-term behavior of devices with PIMs require an understanding of the structure-property relationships including physical aging. In this context the glass transi-tion plays a central role, but with conventional thermal analysis a glass transition is usually not detectable for PIMs be-fore their thermal decomposition. Fast scanning calorimetry provides evidence of the glass transition for a series of PIMs, as the time scales responsible for thermal degradation and for the glass transition are decoupled by employing ultrafast heating rates of tens of thousands K s-1. The investigated PIMs were chosen considering the chain rigidity. The estimated glass transition temperatures follow the order of the rigidity of the backbone of the PIMs. KW - Polymers of intrinsic microporosity KW - Fast scanning calormetry PY - 2019 DO - https://doi.org/10.1021/acsmacrolett.9b00482 SN - 2161-1653 VL - 8 IS - 8 SP - 1022 EP - 1028 PB - ACS Publications AN - OPUS4-48617 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Emamverdi, Farnaz A1 - Huang, J. A1 - Mosane Razavi, Negar A1 - Bojdys, M. J. A1 - Forster, A. B. A1 - Budd, P. M. A1 - Böhning, Martin A1 - Schönhals, Andreas T1 - Molecular Mobility and Gas Transport Properties of Mixed Matrix Membranes Based on PIM‑1 and a Phosphinine Containing Covalent Organic Framework N2 - Polymers with intrinsic microporosity (PIMs) are gaining attention as gas separation membranes. Nevertheless, they face limitations due to pronounced physical aging. In this study a covalent organic framework containing λ5-phosphinine moieties, CPSF-EtO were incorporated as a nanofiller (concentration range 0-10 wt%) into a PIM-1 matrix forming dense films with a thickness of ca. 100 μm. The aim of the investigation was to investigate possible enhancements of gas transport properties and mitigating effects on physical aging. The incorporation of the nanofiller occurred on aggregate level with domains up to 100 nm as observed by T-SEM and confirmed by X-ray scattering. Moreover, the X-ray data show that the structure of the microporous network of the PIM-1 matrix is changed by the nanofiller. As the molecular mobility is fundamental for gas transport as well as for physical aging, the study includes dielectric investigations of pure PIM-1 and PIM-1/CPSF-EtO mixed matrix membranes to establish a correlation between the molecular mobility and the gas transport properties. Using the time-lag method the gas permeability and the permselectivity were determined for N2, O2, CH4 and CO2 for samples with variation in filler content. A significant increase in the permeability of CH4 and CO2 (50 % increase compared to pure PIM-1) was observed for a concentration of 5 wt% of the nanofiller. Furthermore, the most pronounced change in the permselectivity was found for the gas pair CO2/N2 at a filler concentration of 7 wt%. KW - Polymers of Intrinsic Microporosity KW - Nanocomposites PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-595031 DO - https://doi.org/10.1021/acs.macromol.3c02419 SN - 0024-9297 VL - 57 IS - 4 SP - 1829 EP - 1845 PB - ACS Publications AN - OPUS4-59503 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -