TY - JOUR A1 - Wetzel, Annica A1 - Hans, Ann-Kathrin A1 - von der Au, Marcus A1 - Brand, Izabella A1 - Wittstock, Gunther A1 - Özcan Sandikcioglu, Özlem A1 - Witt, Julia T1 - Long-term corrosion studies of CrCoNi and CrMnFeCoNi in sulfuric acid N2 - This study investigates the long-term corrosion behavior of CrCoNi and CrMnFeCoNi MPEAs over 28 d in 1 M H2SO4. Corrosion progression and passive film evolution were analyzed using open circuit potential measurements, electrochemical impedance spectroscopy, X-ray photoelectron spectroscopy, and scanning electron microscopy. Unlike short-term polarization tests, where CrCoNi exhibited intergranular corrosion, long-term immersion resulted in a stable, Cr-rich passive oxide layer. In contrast, CrMnFeCoNi formed a porous mixed oxide layer, increasing its susceptibility to degradation and revealing a distinct corrosion mechanism. X-ray photoelectron spectroscopy tracking at weekly intervals showed that prolonged immersion led to the transformation of sulfide/sulfite species into a sulfate-containing surface film. This effect was only detectable in long-term corrosion studies. These findings provide new insights into the time-dependent degradation mechanisms of MPEAs and demonstrate that corrosion mechanisms differ significantly from short-term polarization tests. This highlights the need for long-term studies to properly assess material stability in practical applications. KW - Long-term corrosion KW - Multi-principal element alloys (MPEAs) KW - X-ray photoelectron spectroscopy (XPS) PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-636895 DO - https://doi.org/10.1038/s41529-025-00637-z SN - 2397-2106 VL - 9 IS - 1 SP - 1 EP - 13 PB - Springer Science and Business Media LLC AN - OPUS4-63689 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sobetkii, Arcadii A1 - Mosinoiu, Laurentiu-Florin A1 - Caramarin, Stefania A1 - Mitrica, Dumitru A1 - Cursaru, Laura-Madalina A1 - Matei, Alexandru-Cristian A1 - Tudor, Ioan-Albert A1 - Serban, Beatrice-Adriana A1 - Ghita, Mihai A1 - Vitan, Nicoleta A1 - Witt, Julia A1 - Özcan Sandikcioglu, Özlem A1 - Postolnyi, Bogdan A1 - Pogrebnjak, Alexander T1 - Deposition and Characterization of Cu-Enhanced High-Entropy Alloy Coatings via DC Magnetron Sputtering N2 - Protection against microbiologically influenced corrosion (MIC) is critical for materials used in aquatic environments, as MIC accelerates material degradation and leads to faster structural failure. Copper (Cu) has the potential to substantially improve the MIC resistance in alloys. In this study, high-entropy alloy (HEA) coatings containing Cu were deposited using DC (Direct Current) magnetron sputtering to enhance the corrosion resistance and mechanical properties of various substrates. Two CuCrFeMnNi HEA compositions in the form of bulk alloys and PVD (Physical Vapor Deposition) coatings, with 5% and 10% Cu, were analyzed for their microstructural, mechanical, and anticorrosive characteristics. Deposition parameters were varied to select the optimal values. Microstructural evaluations using SEM-EDS (scanning electron microscopy and energy dispersive X-ray spectroscopy), XRD (X-ray diffraction), and AFM (atomic force microscopy) revealed uniform, dense coatings with good adhesion composed of dendritic and interdendritic BCC (body-centered cubic) and FCC (face centered cubic) structures, respectively. Microhardness tests indicated improved mechanical properties for the samples coated with developed HEAs. The coatings exhibited improved corrosion resistance in NaCl solution, the 10% Cu composition displaying the highest polarization resistance and lowest corrosion rate. These findings suggest that Cu-containing HEA coatings are promising candidates for applications requiring enhanced corrosion protection. KW - High-entropy alloys (HEAs) KW - DC magnetron sputtering KW - Cu-enhanced coatings KW - Corrosion resistance KW - Microstructural characterization PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-625561 DO - https://doi.org/10.3390/app15041917 SN - 2076-3417 VL - 15 IS - 4 SP - 1 EP - 14 PB - MDPI AN - OPUS4-62556 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -