TY - JOUR A1 - Rudić, O. A1 - Mittermayr, F. A1 - Gluth, Gregor A1 - Simon, Sebastian A1 - Ukrainczyk, N. A1 - Seyrek, Y. A1 - Freytag, B. A1 - Juhart, J. A1 - Grengg, C. T1 - On the benefits of vegetable oil addition for the pore structure and acid resistance of alkali-activated systems N2 - The impact of high additions of vegetable oil (12 vol%) on the mechanical and microstructural properties of metakaolin-slag-based alkali-activated materials (AAMs) was studied. The addition of oil resulted in a slight decrease in initial polymerization kinetics but did not affect the final degree of reaction. AAM-oil-composite-mortars exhibited approximately ∼30% lower compressive strength primarily due to the entrainment of air voids. Newly formed soap phases significantly reduced the volume of small capillary and gel pores (pore radii <15 nm), leading to a decrease in specific inner surface area by a factor of up to 15. The porosity modification induced by the oil addition greatly enhanced the resistance of AAMs against sulfuric acid attack, shifting the dominant processes from diffusion and cracks to framework-dissolution controlled by the inherent phase stabilities. Following the immersion in sulfuric acid (pHstat = 2) for 8 weeks, the depth of corroded layer decreased by 70% and no cracks due to expansive phases were observed. These promising findings suggest that the incorporation of vegetable oil in AAMs has the potential to address durability concerns associated with diffusion-based corrosion processes, thereby expanding the range of future applications. KW - Alkali-activated materials KW - Acid resistance KW - Pore structure PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-581719 DO - https://doi.org/10.1016/j.ceramint.2023.08.036 VL - 49 IS - 20 SP - 33275 EP - 33290 PB - Elsevier Ltd. AN - OPUS4-58171 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Grengg, C. A1 - Koraimann, G. A1 - Ukrainczyk, N. A1 - Rudic, O. A1 - Luschnig, S. A1 - Gluth, Gregor A1 - Radtke, Martin A1 - Dietzel, M. A1 - Mittermayr, F. T1 - Cu- and Zn-doped alkali activated mortar – Properties and durability in (bio)chemically aggressive wastewater environments N2 - Metakaolin-based alkali activated mortars (AAM) - with and without CuSO4·5H2O and ZnO addition (mass ratio Mn+/solid binder 0.08% to 1.7%) - were casted and exposed within an extensive long-term field campaign over the period of 20 months to a sewer basin, strongly affected by biogenic acid corrosion. (Un-)exposed AAM were tested regarding their physicochemical and microstructural properties, bioreceptivity and overall durability. Metal addition led to a retarding effect during alkali-activation reaction, as well as to an increase in open porosity of up to 3.0% and corresponding lower compressive strength of up to 10.9%. Reduced microbial colonization and diversity were observed on AAM with Cu, while Zn addition led to increased biodiversity. We propose that the observed higher durability of Cu-doped AAM is due to antibacterial effects and associated reduction of biogenic acid production, superseding overall negative effects of metal-dosage on physical material properties. Observed lower durability of Zn-doped AAM was related to combined negative physicochemical and microbial effects. KW - Microbially induced corrosion KW - Alkali-activated materials KW - Biogenic acid corrosion KW - Biogene Schwefelsäurekorrosion KW - MIC PY - 2021 DO - https://doi.org/10.1016/j.cemconres.2021.106541 SN - 0008-8846 VL - 149 SP - 1 EP - 15 PB - Elsevier CY - Oxford AN - OPUS4-53070 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -