TY - JOUR A1 - Epishin, A.I. A1 - Nolze, Gert A1 - Alymov, M.I. T1 - Pore Morphology in Single Crystals of a Nickel-Based Superalloy After Hot Isostatic Pressing N2 - The morphology of pores partially shrunk during a half-hour HIP at temperature of 1288 °C and pressure of 103 MPa has been investigated in nickel-based superalloy CMSX-4. The investigation resulted in the following findings: surrounding the shrinking pores by a c¢-shell (Ni3Al), faceting of the pores surface by {023} and {011} planes, and formation the submicroscopic satellite pores connected by channels with the neighboring larger pores. It is assumed that the formation of the c¢-shell around the pores and the faceting of the pore surface is due to diffusion processes occurring during pore shrinkage, and therefore these findings can be considered as arguments supporting the vacancy model of pore annihilation. The submicroscopic satellite pores are expected to be the result of dividing the casting pores of a complex initial shape during their shrinking. The connecting channels are probably required for the gas to escape from the rapidly shrinking small satellite pores into the slowly shrinking large pore. Thus, it is reasonable to assume that the casting pores may contain some amount of gas. KW - HIP KW - Superalloy KW - Porosity KW - Faceting KW - negative crystal growth PY - 2022 DO - https://doi.org/10.1007/s11661-022-06893-x SN - 1073-5623 SP - 1 EP - 9 PB - Springer Nature AN - OPUS4-56409 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Cios, G. A1 - Winkelmann, A. A1 - Nolze, Gert A1 - Tokarski, T. A1 - Jany, B. R. A1 - Bala, P. T1 - EBSD and TKD analyses using inverted contrast Kikuchi diffraction patterns and alternative measurement geometries N2 - Electron backscatter diffraction (EBSD) patterns can exhibit Kikuchi bands with inverted contrast due to anomalous absorption. This can be observed, for example, on samples with nanoscale topography, in case of a low tilt backscattering geometry, or for transmission Kikuchi diffraction (TKD) on thicker samples. Three examples are discussed where contrast-inverted physics-based simulated master patterns have been applied to find the correct crystal orientation. As first EBSD example, self-assembled gold nanostructures made of Au fcc and Au hcp phases on single-crystal germanium were investigated. Gold covered about 12% of the mapped area, with only two thirds being successfully interpreted using standard Hough-based indexing. The remaining third was solved by brute force indexing using a contrast-inverted master pattern. The second EBSD example deals with maps collected at a non-tilted surface instead of the commonly used 70◦ tilted one. As TKD example, a jet-polished foil made of duplex stainless steel 2205 was examined. The thin part close to the hole edge producing normal-contrast patterns were standard indexed. The areas of the foil that become thicker with increasing distance from the edge of the hole produce contrast-inverted patterns. They covered three times the evaluable area and were successfully processed using the contrast-inverted master pattern. In the last example, inverted patterns collected at a non-tiled sample were mathematically inverted to normal contrast, and Hough/Radon-based indexing was successfully applied. KW - EBSD KW - TKD KW - Contrast inversion KW - Topography KW - Kikuchi diffraction PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-613862 VL - 267 SP - 1 EP - 8 PB - Elsevier CY - Amsterdam AN - OPUS4-61386 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Heide, K. A1 - Nolze, Gert A1 - Völksch, G. A1 - Heide, G. T1 - Boracite Mg3[B7O13Cl] from the Zechstein salt deposits N2 - Among the borates in the Middle European Zechstein Salt Succession boracite Mg3[B7O13Cl] is the most common mineral in quantity and local distribution. An exceptional enrichment is observed in Stassfurt Serie Z2) in the Stassfurth seam K2H. Boracite is to be found in two varieties: individual crystals in cubic, tetrahedral or dodecahedral habit on the one hand and fibrous crystals so-called “stassfurtite” on the other hand. The formation conditions such widely spread borates in the salt succession are ambiguous in two respects. First of all the synthetic formation of boracites is to be made by hydrothermal or melt conditions. Both processes can be suspended for the salt succession. Furthermore the cubic modification is stable above 265°C for the Mg-boracite. The cubic, tetrahedral or dodecahedral habit could be used as a geothermometer, but such conditions can be exclude by the paragenetic minerals, esp. carnallite (MgKCl3 x 6H2O). The chemical composition of orthorhombic, pseudo-cubic boracite depends on the location. Pure Mg-boracite in hexahedral habit and in fibrous habit, so-called “stassfurtite”, occurs in the North Harz region, whereas the Fe-, Mn-, Mg-boracite appears in the South Harz region. Until now the source of boron, the time of formation of crystals, but also the reasons for the differences in habit of the single hexahedral crystals are still unclear. The formation during a diagenetic/metamorphic process is evident. However, the preferred formation in Stassfurt seam could be an indication for the boron enrichment in an early diagenetic process. Furthermore permit the determination of the thermal stability and the volatile content of crystals conclusions to the chemical composition of the fluid. The observed variation suggests that the condition of crystal growth as well as the chemical composition of fluid repeatedly changed over the time. Randomly occuring xenomorpheous anhydrite and magnesite inclusions within single boracite crystals have been interpreted as an indication to factors of chemical milieu during the formation of crystals. The reversible phase transition temperature of the boracite is a linearly function of the iron and manganese content and varies from 265°C for Mg-boracite to 330°C for Fe(Mn)-boracite. The thermal decomposition of boracite is determined by two processes. The decomposition started with a boron-chlorine release (BOCl?), having a maximum rate at 1050°C. Additionally to this release one observes a simultaneous emission of H2O, HCl, HF, CO2 , N2 , SO2 , H2 , and hydro carbons. The results give evidence for the aged approach of a secondary formation of boracite within the complete Stassfurt seam, possibly in connection with the formation of salt diapirs in the Jura and Cretaceous period. The wider environmental distribution of borates is an indication of chemical transport processes within the salt succession. This should be a more important issue in the discussion about the utilisation of salt diapirs for the storage of nuclear waste. KW - Borate KW - Boracite KW - Thermal behaviour KW - Electron backscatter diffraction KW - Energy-dispersive x-ray spectroscopy PY - 2013 DO - https://doi.org/10.1524/zkri.2013.1633 VL - 228 SP - 467 EP - 475 PB - Oldenbourg Wissenschaftsverlag, München AN - OPUS4-37982 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nolze, Gert A1 - Payton, E. A1 - Winkelmann, Aimo T1 - Advanced EBSD Pattern Interpretation through Iterative Post-Processing N2 - Since the BSE signal depends on many factors, like the chemistry of the phase and the acceleration voltage, the size and position of the detector array is (slightly) different from phase to phase so that an (iterative) post-processing of the stored patterns is highly recommended. The derived BSE signal can be used for phase assignment in high resolution and high speed maps when EBSD fails and/or EDS (energy dispersive spectroscopy) needs too much time for a suitable and parallel signal acquisition. KW - Electron backscatter diffraction KW - Phase identification KW - Microstructure KW - SEM PY - 2013 DO - https://doi.org/10.1017/S1431927613005631 VL - 19 IS - Suppl. 2 SP - 728 EP - 729 AN - OPUS4-37986 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nolze, Gert T1 - Combination of colored patterns and cubes for crystallographic point group visualization N2 - A concept based on the application of a cube as a general polyhedron is presented for the visualization of point group symmetry. The cube is used to represent both the highest and lowest crystal symmetries, with differences observable as patterns characteristic to each point group. Patterns are generated using direction-specific color keys, which enable the recognition of point group-specific distribution of vectors in an external reference frame. For the visualization of the incoherent hexagonal crystal classes, two twinned cubes are applied in order to generate symmetry operators that would otherwise be missing. The resulting hexagonal dipyramid is described in the frame of a cube, reducing the number of used symmetry operators from 72 to 60. The complete set of 32 polyhedra are suitable, for example, as a visual aid for understanding the crystal symmetry and/or sub- and supergroup relationships. KW - Subgroup KW - Crystal class KW - Color key KW - Fundamental zone KW - Teaching PY - 2013 DO - https://doi.org/10.1002/crat.201300134 VL - 48 IS - 7 SP - 476 EP - 489 PB - WILEY-VCH AN - OPUS4-37988 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nolze, Gert T1 - Azimuthal Projections: Data Rotation and Projection Switching in Real Time N2 - Pole figures are often used to present crystal orientation data. The huge number of single orientation measurements acquired by electron backscatter diffraction (EBSD) poses a challenge for pole figure representation due to the large number of calculations required. This significantly reduces the speed at which the data may be rotated and affects the ability to switch between different projection types. In the present work, it will be shown that satisfactory representation of orientation data in different projection types can generally be achieved by an imaging of a spherical projection. With this approach, explicit calculation of the projections is no longer required, allowing for both real-time dataset rotation and real-time switching between all projection types relevant to materials science. The technique can be applied to any other directional property distribution, for example, not only for EBSD orientation presentation. KW - Stereographic projection KW - Equal area projection KW - Gnomonic projection KW - Azimuthal projection KW - Crystal orientation KW - Projection imaging KW - Coordinate transformation KW - Real-time rotation PY - 2013 DO - https://doi.org/10.1017/S1431927613001414 VL - 19 SP - 950 EP - 958 PB - Microscopy Society of America AN - OPUS4-37989 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Reith, F. A1 - Fairbrother, L. A1 - Nolze, Gert A1 - Wilhelmi, O. A1 - Clode, P. L. A1 - Gregg, A. O. A1 - Parsons, J. E. A1 - Wakelin, S. A. A1 - Pring, A. A1 - Hough, R. A1 - Southam, G. A1 - Brugger, J. T1 - Nanoparticle factories: Biofilms hold the key to gold dispersion and nugget formation N2 - Biofilms living on gold (Au) grains play a key role in the biogeochemical cycle of Au by promoting the dispersion of Au via the formation of Au nanoparticles as well as the formation of secondary biomorphic Au. Gold grains from Queensland, Australia, are covered by a polymorphic, organic-inorganic layer that is up to 40 μm thick. It consists of a bacterial biofilm containing Au nanoparticles associated with extracellular polymeric substances as well as bacterioform Au. Focused ion beam (FIB) sectioning through the biofilm revealed that aggregates of nanoparticulate Au line open spaces beneath the active biofilm layer. These aggregates (bacterioform Au type 1) resulted from the reprecipitation of dissolved Au, and their internal growth structures provide direct evidence for coarsening of the Au grains. At the contact between the polymorphic layer and the primary Au, bacterioform Au type 2 is present. It consists of solid rounded forms into which crystal boundaries of underlying primary Au extend, and is the result of dealloying and Ag dissolution from the primary Au. This study demonstrates that (1) microbially driven dissolution, precipitation, and aggregation lead to the formation of bacterioform Au and contribute to the growth of Au grains under supergene conditions, and (2) the microbially driven mobilization of coarse Au into nanoparticles plays a key role in mediating the mobility of Au in surface environments, because the release of nanoparticulate Au upon biofilm disintegration greatly enhances environmental mobility compared to Au complexes only. KW - Nanomaterial KW - Gold KW - Electron backscatter diffraction PY - 2010 DO - https://doi.org/10.1130/G31052.1 VL - 38 IS - 9 SP - 843 EP - 846 PB - Geological Society of America AN - OPUS4-37995 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Winkelmann, Aimo A1 - Nolze, Gert T1 - Channeling-enhanced EDX for polarity resolved crystal orientation determination N2 - Using channeling-enhanced energy-dispersive X-ray spectroscopy (EDX), we demonstrate polarity sensitive orientation determination of a non-centrosymmetric crystal in the scanning electron microscope. The authors observe a characteristic asymmetry in the channeling-enhanced, angle-dependent EDX data of a GaAs sample, which is in good agreement to simulations using the dynamical theory of diffraction for the incident electron beam. This allows us to assign the orientation of the GaAs crystal according to the non-centrosymmetric point group. The method shown here overcomes the limitation of a reduced point-group sensitivity of electron backscatter diffraction Patterns and electron channeling patterns for crystalline phases that contain atoms of approximately equal electron scattering cross sections. KW - Channeling KW - EDX KW - EDS KW - Composition KW - GaAs KW - GaP PY - 2016 DO - https://doi.org/10.1002/crat.201600258 SN - 0232-1300 SN - 0023-4753 VL - 51 IS - 12 SP - 752 EP - 756 AN - OPUS4-38098 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nolze, Gert T1 - Interphase boundary characterization in duplex steel and iron meteorites using EBSD technique N2 - The properties of materials are mainly described by the orientation distribution of the crystalline phases in a material. Beside the so considered anisotropy also the grain as well as phase boundaries are of extreme importance for a whole string of properties, e.g. the strength of a material. On the example of the interface between fcc and bcc iron the discovered and derived models are discussed. Although the common models are based on the crystal lattice description, the atomic configuration on the interface is analysed. Since experimentally a wide spread of orientations data appears the consideration of the frequency distribution is proposed to find at least the main orientation relationship between fcc and bcc. High-indexed pole figures as well as the Euler subspace are introduced in order to increase the accuracy and to compare different measurements. For the sake of simplicity EBSD measurements on iron meteorites are used since they commonly consist of large fcc single crystals which transformed to a low and very specific number of bcc grains. In special cases the described procedure could also be used for steels. KW - Orientation relationships KW - Electron backscatter diffraction KW - Steel KW - Iron meteorites KW - Kurdjumov-Sachs KW - Nishiyama-Wassermann PY - 2006 SN - 1733-3490 SN - 0004-0770 SN - 0860-7052 VL - 51 IS - 1 SP - 15 EP - 22 AN - OPUS4-38030 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Glowacka, A. A1 - Wozniak, M. J. A1 - Nolze, Gert A1 - Swiatnicki, W. A. T1 - Hydrogen induced phase transformations in austenitic-ferritic steel N2 - The hydrogen influence on the microstructure of the austenitic-ferritic Cr22-Ni5-Mo3 stainless steel was investigated. Cathodic hydrogen charging was performed electrochemically from aqueous solution of 0.1M H2SO4 with hydrogen entry promoter addition. The aim of this study was to reveal microstructural changes appearing during the hydrogen charging and particularly to clarify the occurrence of phase transformations induced by hydrogen. The specific changes in both phases of steel were observed. In the ferritic phase, strong increase of dislocation density was noticed. Longer time of hydrogen charging leaded also to the strips and twin plates formation in ferrite phase. In the austenitic phase, the generation of stacking faults, followed by the formation of α' martensite was remarked. KW - Steel KW - Hydrogen KW - Embrittlement KW - Electron backscatter diffraction KW - SEM PY - 2006 DO - https://doi.org/10.4028/www.scientific.net/SSP.112.133 SN - 1662-9779 VL - 112 SP - 133 EP - 140 AN - OPUS4-38031 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nolze, Gert A1 - Geist, V. T1 - A new method for the investigation of orientation relationships in meteoritic plessite N2 - The orientation relationship (OR) between the bcc and fcc phase in the plessite microstructure of the iron meteorites Watson, Agpalilik and Gibeon has been analysed in a scanning electron microscope using electron back-scattered diffraction (EBSD). A very strong OR exists, independently on the analysed plessite type and the observed spreading of single orientation data. The agreement between the experimental orientation distribution and existing models varies for each meteorite. The black plessite in the Agpalilik corresponds to the Nishiyama-Wassermann model whereas the Duplex plessite of the Gibeon meteorite shows an OR close to the Kurdjumov-Sachs model. The Watson meteorite is strongly deformed so that a general OR is difficult to determine due to the blurred experimental orientation distribution. KW - Meteorite KW - Orientation relationship KW - Steel KW - Electron backscatter diffraction KW - Kurdjumov-Sachs KW - Nishiyama-Wassermann PY - 2004 DO - https://doi.org/10.1002/crat.200310193 SN - 0023-4753 SN - 0232-1300 VL - 39 IS - 4 SP - 343 EP - 352 AN - OPUS4-38032 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kraus, Werner A1 - Nolze, Gert T1 - POWDER CELL-A Program for the representation and manipulation of crystal structure and calculation of the resulting X-ray powder pattern N2 - The main component of this program is a simultaneous representation of the unit cell and the calculated powder pattern. It allows the manipulation of the Crystal structure by moving selected atoms of the asymmetric unit. The resulting powder pattern can be directly compared to experimental data in order to obtain reliable starting values for further computations in refinement programs. KW - XRD KW - Simulation KW - PowderCell KW - Programming KW - Crystal structure KW - Refinement PY - 1996 SN - 0021-8898 VL - 29 SP - 301 EP - 303 AN - OPUS4-38033 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Nolze, Gert ED - Sen Gupta, S. P. ED - Chatterjee, P. T1 - PowderCell : a mixture between crystal structure visualizer, simulation and refinement tool N2 - The program PowderCell is a crystallographic tool for visualization of Crystal structures. However, it offers also non-conventional features like the fulautomatical generation of subgroups or the consideration of non-standard settings of space-group types. On the one Hand the program is very useful for non-crystallographers who like to get an impression of the atomic arrangement within the unit cell. But also for crystallographers it is recommendable because it contains a lot of additional information which can be extracted and used like data given in the International Tables for Crystallography, Vol. A. However, the most important advantage of the program is the simultaneous calculation of the X-ray or neutron diffraction powder patterns for a mixture of up to 10 crystalline phases. Between more than 7 different characteristic radiations can be chosen and their influence on the resulting powder pattern can be studied. Furthermore, experimental diffractograms can be analysed using a refinement procedure. The implemented LeBail-algorithm allows the investigation of unknown phases. In combination with the refinement algorithm an interface to Shelx offers the possibility for a step by step ab initio structure analysis. Certainly, the user-friendly shell is one reason that especially users who are not so familar with space-group symmetry, crystal structure data or diffractometry use this powerful tool for the solution of scientific or analytical problems as well as in teaching. KW - XRD KW - Simulation KW - Crystal structure KW - Neutron diffraction PY - 2002 SN - 8177642626 SN - 9788177642629 SP - 146 EP - 155 PB - Allied Publishers CY - Kolkata, India AN - OPUS4-38035 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Nolze, Gert ED - Sen Gupta, S. P. ED - Chatterjee, P. T1 - The determination of residual stress N2 - X-ray stress analysis on crystalline materials is based on the determination of elastic lattice strains. The strains described by the shift of peak positions are converted to stresses by the means of theory of elasticity. The development of the sin2ψ-method of X-ray stress analysis introduced an enormous progress in X-ray stress analysis during the last decades. This report outlines some important elements of X-ray physics and fundamentals of theory of elasticity. The Standard measuring procedure are described and special experimental differences to the common powder diffractometry are outlined. KW - XRD KW - Residual stress PY - 2002 SN - 81-7764-262-6 SN - 9788177642629 SP - 77 EP - 83 PB - Allied Publishers CY - Kolkata, India AN - OPUS4-38036 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nolze, Gert A1 - Kraus, Werner T1 - PowderCell 2.0 for Windows N2 - PowderCell contains a comfortable, user friendly visualization and modification tool for crystal structures. It provides on-line calculation of the corresponding powder diffraction patterns simulating a variety of experimental conditions. The common ICSD and Shelx file formats are supported for importing crystal structure information. It has control of automatic cell transformation and also derivation of subgroups. More than 740 different settings of the 230 space-group types are supported. Up to ten crystal structures can be considered simultaneously. A full pattern refinement enables the direct comparison with experimental diffractograms for quantitative phase analysis, lattice parameter refinement, polynomial background estimation, etc. KW - XRD KW - Simulation KW - Powdercell KW - Software KW - Programming KW - Phase mixtures KW - Crystal structure KW - Subgroup PY - 1998 SN - 0885-7156 VL - 13 IS - 4 SP - 256 EP - 259 PB - Cambridge University Press AN - OPUS4-38037 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lühr, T. A1 - Winkelmann, Aimo A1 - Nolze, Gert A1 - Krull, D. A1 - Westphal, C. T1 - Direct Atom Imaging by Chemical-Sensitive Holography N2 - In order to understand the physical and chemical properties of advanced materials, functional molecular adsorbates, and protein structures, a detailed knowledge of the atomic arrangement is essential. Up to now, if subsurface structures are under investigation, only indirect methods revealed reliable results of the atoms’ spatial arrangement. An alternative and direct method is three-dimensional imaging by means of holography. Holography was in fact proposed for electron waves, because of the electrons’ short wavelength at easily accessible energies. Further, electron waves are ideal structure probes on an atomic length scale, because electrons have a high scattering probability even for light elements. However, holographic reconstructions of electron diffraction patterns have in the past contained severe image artifacts and were limited to at most a few tens of atoms. Here, we present a general reconstruction algorithm that leads to high-quality atomic images showing thousands of atoms. Additionally, we show that different elements can be identified by electron holography for the example of FeS₂ . KW - holography KW - electron diffraction KW - atomic imaging KW - photoemission KW - electron backscattering PY - 2016 DO - https://doi.org/10.1021/acs.nanolett.6b00524 VL - 16 IS - 5 SP - 3195 EP - 3201 PB - American Chemical Society AN - OPUS4-37739 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dietrich, D. A1 - Nolze, Gert A1 - Mehner, T. A1 - Nickel, D. A1 - Lampke, T. T1 - EDS/EBSD studies and HR-EBSD pattern analysis on pre-Inca ceramic fragments recovered during San José de Moro Archaeology Program N2 - Pre-Inca civilizations like the coastal cultures Moche and Nazca (Early Intermediate) and the inland culture Wari (Middle Horizon) were agrarian societies which supported indigenous elites of impressive wealth, power, and organization. With the expansion of the Wari Empire, the polychrome style and technique of Nazca propagated to the other cultures. High status burials, most of the Late Moche Fine Line ceramics and a large corpus of ceramics with Wari-derived decoration have been recovered in San José de Moro since 1991. The degree of transfer of procedures in this highly interactive scenario is of special interest: is there a limitation to decoration or is it adopted by the local potters also regarding the formulation of the ceramic bodies? In this context the relative amount, size and type of incorporated non-plastic inclusions as temper are important. T2 - The 16th European Microscopy Congress 2016 CY - Lyon, France DA - 28.08.2016 KW - EBSD KW - EDX KW - Ceramic KW - Phase distribution KW - Microstructure KW - Texture KW - Phase identification KW - SEM PY - 2016 DO - https://doi.org/10.1002/9783527808465.EMC2016.4462 SP - 4462 PB - John Wiley & Sons AN - OPUS4-37740 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nolze, Gert A1 - Hielscher, R. ED - Hielscher, Ralf T1 - Orientations - perfectly colored N2 - The inverse pole figure (IPF) coloring for a suitable evaluation of crystal orientation data is discussed. The major goal is a high correlation between encoding color and crystal orientation. Revised color distributions of the fundamental sectors are introduced which have the advantages of (1) being applicable for all point groups, (2) not causing color discontinuities within grains, (3) featuring carefully balanced regions for red, cyan, blue, magenta, green and yellow, and (4) an enlarged gray center in opposition to a tiny white center. A new set of IPF color keys is proposed which is the result of a thorough analysis of the colorization problem. The discussion considers several topics: (a) the majority of presently applied IPF color keys generate color discontinuities for specifically oriented grains; (b) if a unique correlation between crystal direction and color is requested, discontinuity-preventing keys are possible for all point groups, except for 4, 3 and 1; (c) for a specific symmetry group several IPF color keys are available, visualizing different features of a microstructure; and (d) for higher symmetries a simultaneous IPF mapping of two or three standard reference directions is insufficient for an unequivocal orientation assignment. All color keys are available in MTEX, a freely available MATLAB toolbox. KW - Electron backscatter diffraction KW - Color coding KW - Symmetry groups KW - Orientation description PY - 2016 DO - https://doi.org/10.1107/S1600576716012942 SN - 0021-8898 SN - 1600-5767 VL - 49 IS - 5 SP - 1786 EP - 1802 AN - OPUS4-37741 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Li, L. A1 - Han, M. A1 - Nolze, Gert T1 - The determination of lattice parameters using single EBSD patterns N2 - A typical electron backscatter diffraction (EBSD) pattern usually contains more than a hundred of Kikuchi poles that formed by intersecting dozens of visible Kikuchi bands. The poles correspond to zone axes in real space or lattice planes in reciprocal space. The band widths are inversely proportional to the interplanar spacings of diffracting lattice planes, and the angle formed by the beam source and two band center-lines approximately corresponds to angle between two lattice planes. However, EBSD patterns always suffer from gnomic distortions. In addition, the band width measurement has a relative error of 5-20% due to the complex profile. Thus, an EBSD pattern always provides abundant crystallographic information but disappointingly low accuracy. T2 - Microscopy & MicroAnalysis 2016 CY - Columbus, Ohio, USA DA - 24.07.2016 KW - Electron backscatter diffraction KW - Lattice parameter determination PY - 2016 UR - https://www.cambridge.org/core/services/aop-cambridge-core/content/view/S1431927616004025 SN - 1431-9276 SN - 1435-8115 VL - 22 SP - Suppl. 3, 634 EP - 635 AN - OPUS4-37742 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Winkelmann, Aimo A1 - Nolze, Gert T1 - Orientation analysis of non-centrosymmetric crystal structures using electron backscatter diffraction N2 - Crystal structures that show a broken symmetry in their cubic and hexagonal modifications are of great relevance for optoelectronic and photonic applications. This is why methods which are sensitive to non-centrosymmetric structures are important for analysis of these materials in technological applications. T2 - 24th Annual Conference of the german Crystallographic Society CY - Stuttgart, Germany DA - 14.03.2016 KW - Electron backscatter diffraction KW - Non-centrosymmetry KW - Friedel's rule KW - Pattern matching KW - GaN KW - GaP PY - 2016 VL - 36 Supplement SP - 22 PB - Walter de Gruyter GmbH & Co KG AN - OPUS4-37743 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nolze, Gert T1 - Introduction to PowderCell N2 - The presentation give a short introduction into the free-available software PowderCell (BAM)for the simulation of X-ray diffraction patterns of polycrystalline materials. T2 - PowderCell Users meeting CY - Joinville, Brazil DA - 19.10.2015 KW - X-ray diffraction KW - Simulation KW - Structure viewer KW - Subgroup relationships PY - 2015 AN - OPUS4-37791 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nolze, Gert T1 - EBSD: more reliable and accurate N2 - The presentation discusses numerous new approaches in order to increase precision and accuracy of electrom backscatter diffraction measurements. T2 - 1st EBSD Workshop CY - Belo Horizonte, Brazil DA - 17.09.2015 KW - Orientation mapping KW - Electron backscatter diffraction KW - Lattice parameter determination KW - Orientation precision KW - Orientation noise PY - 2015 AN - OPUS4-37797 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Epishin, A. I. A1 - Petrushin, N. V. A1 - Link, T. A1 - Nolze, Gert A1 - Loshchinin, Yu. V. A1 - Gerstein, G. T1 - Thermal stability of the structure of a heat-resistant cobalt alloy hardened with intermetallic γ'-phase precipitates N2 - The thermal stability of the microstructure of a heat-resistant cobalt alloy, which consists of a γ solid solution strengthened with γ'-phase precipitates, has been studied. The temperature behavior of the dissolution of the hardening γ' phase and the kinetics of its coarsening at 700 and 800°C have been determined. It is found that, during prolonged annealing at 800°C, the γ' → β phase transformation occurs. KW - Superalloy KW - Microstructure KW - Hardening KW - Electron backscatter diffraction KW - TEM PY - 2016 DO - https://doi.org/10.1134/S0036029516040078 SN - 0036-0295 VL - 2016 IS - 4 SP - 286 EP - 291 PB - Pleiades Publishing AN - OPUS4-37768 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nolze, Gert T1 - Microstructure characterization of the Treysa meteorite N2 - Microstructure descripton of heat-affected zone, fusion crust and main metal of the Treysa iron using scanning electron microscopy, EBSD and EDS. T2 - 8. Deutsches Meteoriten Kolloquium, CY - Zella Willingshausen, Germany DA - 02.04.2016 KW - Electron backscatter diffraction KW - EDX KW - Light microscopy KW - Microstructure KW - Oxidation PY - 2016 DO - https://doi.org/10.13140/RG.2.1.3387.8161 AN - OPUS4-37769 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -