TY - JOUR A1 - Epishin, A. I. A1 - Nolze, Gert A1 - Malakhov, A. Yu. A1 - Pervukhina, O. L. T1 - Investigation of the Structure of Interfaces Between Metals and Alloys Joined by Explosion Welding N2 - The structure of interfaces in Fe20Cr6Al/Cu, titanium/steel and brass/Invar bimetals obtained by explosion welding from sheet components with a thickness of 1 and 4, 25 and 5, 12 and 8 mm, respectively, was studied using analytical methods of scanning electron microscopy. The wave dimensions (length/height) were approximately 200/50 μm for Fe20Cr6Al/Cu, 700/70 μm for titanium/steel and 350/100 μm for brass/Invar. At the micron scale, mutual penetration of the welded components into each other (trans-interface diffusion) was not detected. In the iron-based plate of Fe20Cr6Al/Cu bimetal, a strong texture and cracks, which are a critical defect, were formed as a result of severe plastic deformation. Less pronounced textures were revealed in the components of titanium/steel bimetal. In titanium/steel bimetal, Laves phase particles Fe2Ti were found near the welded interface, while in brass/Invar bimetal, local contact melting was observed. However, the particles Fe2Ti and local melting areas are not critical defects, as they do not cause unacceptable deterioration in the adhesive strength of the welded joints, which was confirmed by a high shear strength of 500-570 MPa for the brass/Invar bimetal. KW - EBSD KW - Welding KW - Interface PY - 2025 DO - https://doi.org/10.1007/s11665-025-12660-x SN - 1059-9495 SP - 1 EP - 11 PB - Springer Science and Business Media LLC AN - OPUS4-64732 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Singh, Shobhit Pratap A1 - Löwe, Peter A1 - Schriever, Sina A1 - Olbricht, Jürgen A1 - Rehmer, Birgit A1 - Nolze, Gert A1 - Skrotzki, Birgit T1 - High-throughput creep evaluation of IN738LC in bending using digital image correlation at 850 °C N2 - High-temperature alloys, when used in structural applications, undergo slow time-dependent deformation known as creep. Assessing creep behavior is critical for estimating the in-service life of these alloys. Conventionally, uniaxial creep tests are widely conducted at elevated temperatures to determine creep rates. In recent years, bending creep of cantilevers, when combined with digital image correlation (DIC), has emerged as a promising high-throughput technique for rapidly estimating creep life. However, the applicability of bending creep above 700 ◦C for high-temperature alloys using DIC has not been fully established. In this work, we compare uniaxial creep rates of the nickel-based superalloy IN738LC with bending creep rates measured at 850 ◦C using high-temperature DIC. The bending creep data show excellent agreement with uniaxial creep results in the stress range of 240–360 MPa. The measured creep xponent, a critical rate-determining parameter, is found to be ~8 for both uniaxial and bending creep, with the rate data scattered within a factor of two. An in-house experimental setup was developed to perform bending creep tests at high temperatures, with strain monitored through DIC. Our results demonstrate that bending creep, combined with DIC, provides a reliable and efficient method for creep testing of high-temperature alloys. Compared to conventional uniaxial creep experiments, this approach requires significantly less time and material, thereby reducing effort, energy, and cost. We anticipate that this technique will serve as a foundation for testing precious high-temperature materials. For instance, in ongoing rapid discoveries of advanced alloys, in-service creep life can be evaluated much faster with reduced material requirements. Moreover, this method holds strong potential for application to high-entropy alloys and additively manufactured alloys designed for demanding high-temperature environments. KW - Digital image correlation KW - Bending creep KW - Nickel-based superalloys KW - High throughput testing KW - High-temperature materials PY - 2025 UR - https://www.sciencedirect.com/science/article/pii/S0921509325017034?via%3Dihub DO - https://doi.org/10.1016/j.msea.2025.149479 VL - 950 SP - 1 EP - 12 PB - Elsevier B.V. AN - OPUS4-64814 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -