TY - CONF A1 - Bakir, Nasim T1 - Influence of the weld pool geometry on solidification cracking in partial penetration high power laser beam welding N2 - Solidification cracking is still a serious problem in laser beam welding, especially in the welding of thick-walled plates. The influence of weld pool geometry on solidification cracking in partial penetration welding of thick plates is investigated within scope of this study. Therefore, a specific experimental setup of steel and quartz glass in butt configuration and on the side with high-speed camera were used to record the weld pool shape. In addition, the influence of laser inclination angle on the weld pool geometry and on solidification crack formation was investigated. The results show a bulge in the weld pool root, which is separated from an upper region by a necking region. This leads to a case where there are three different longitudinal region lengths with different solidification zones. This temporal sequence of solidification strongly promotes the formation of solidification cracks in the weld root. T2 - LANE 2022: 12th CIRP Conference on Photonic Technologies CY - Fürth, Germany DA - 04.09.2022 KW - Laser beam welding KW - Weld pool shape KW - Solidification craking PY - 2022 AN - OPUS4-56395 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bakir, Nasim T1 - About the origin of solidification cracking in laser welded thick-walled structures N2 - In this study, a three-dimensional CFD-simulation model was developed to simulate the fluid flow in the weld pool. The CFD-model showed a bulging region in the middle of the depth, which is separated from the top surface and bottom surface by two narrowing regions. It can be concluded that the interaction of the movement of the laser source with the Marangoni vortex leads to a teardrop shape at the upper and bottom surface of the workpiece. Additionally, it shows that the bulging in the weld is a result of the backflows on the upper and lower sides due to the thermo-capillary-driven flows. The weld pool shape was used as a heat source in a two-dimensional thermomechanical model, which allows a highly accurate transformation of the weld pool dimensions obtained from the CFD model. This developed technique allows the consideration of physical aspects, which cannot be considered when using traditional heat sources. The mechanical model has shown that the chronological order of the solidification of the weld has a significant influence on the nature and distribution of the stresses in the weld. High tensile stress has been observed in the bulging region, i.e. in the susceptible region for solidification cracking, when compared to the other narrowing regions, which show compressive stress. T2 - 4th International Conference on Welding and Failure Analysis of Engineering Materials CY - Aswan, Egypt DA - 18.11.2018 KW - Laser beam welding KW - Numerical simulation KW - CFD-model KW - FE-model KW - Weld pool geometry PY - 2018 AN - OPUS4-46725 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bakir, Nasim T1 - Anwendung der digitalen Bildkorrelation (DIC) Technik zur Untersuchung der Heißrissanfälligkeit laserstrahlgeschweißter Verbindungen mit dem CTW-Test T2 - Assistentenseminar CY - Magdeburg, Germany DA - 2014-12-01 PY - 2014 AN - OPUS4-33158 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bakir, Nasim T1 - Anwendung der digitalen Bildkorrelation (DIC) zur Ermittlung der kritischen lokalen Dehnungen bei der Erstarrungsrissentstehung und deren numerische Analyse T2 - BAM Alumni Colloquium - Division V.5 - 5.5 - 5.7 - 9.3 - 9.4 CY - Berlin, Germany DA - 2014-09-11 PY - 2014 AN - OPUS4-31472 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Numerical simulation of solidification crack formation during laser beam welding of austenitic stainless steels under external load N2 - Solidification cracking phenomena taking place under controlled tensile weldability (CTW) test conditions have already been investigated both experimentally and numerically via FEA in order to get a better understanding of the mechanisms of hot crack formation during laser beam welding of austenitic steel grades. This paper develops a threedimensional finite element model employing the contact element technique to simulate the formation and propagation of solidification cracks during laser full penetration welding of fully austenitic stainless steel 1.4376. During the experimental procedure, the resulting strain and displacement directed to the laser beam in the close vicinity of the weld pool was measured at the surface of the workpiece using a digital image correlation (DIC) technique with an external diode laser as an illuminating source. Local strain fields, global loads and crack lengths predicted by the model are in good agreement with those observed in experiments. KW - Solidification cracking KW - Finite element analysis KW - Imaging KW - Laser welding KW - Austenitic stainless steels PY - 2016 DO - https://doi.org/10.1007/s40194-016-0357-1 SN - 0043-2288 SN - 1878-6669 VL - 60 IS - 5 SP - 1001 EP - 1008 PB - Springer CY - Berlin, Heidelberg AN - OPUS4-37287 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bakir, Nasim T1 - Investigation of solidification cracking susceptibility of laser welded joints of austenitic stainless steels T2 - 3rd INTERNATIONAL CONFERENCE IN AFRICA AND ASIA, Welding and Failure Analysis of Engineering Materials CY - Luxor, Egypt DA - 2015-11-02 PY - 2015 AN - OPUS4-35018 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bakir, Nasim T1 - Using optical measuring to investigate the hot cracking susceptibility of laser welded joints T2 - Lasers in Manufacturing 2015 CY - Munich, Germany DA - 2015-06-22 PY - 2015 AN - OPUS4-34399 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bakir, Nasim T1 - Investigation of solidification cracking susceptibility of type 316L stainless steel during laser beam welding using an in-situ observation technique N2 - This technique is the first to provide a measurement of the full strain field locally in the immediate vicinity of the solidification front. Automatic identification of the cases that can be critical for the solidification crack formation the described procedure of the optical measurement allows the real material-dependent values of critical strain characterising the transition to hot cracking during laser welding processes to be determined. The local critical strain in vicinity of the solidification front has observed between 3.6 and 4.2%. T2 - Lasers in Manufacturing Conference 2017 CY - Munich, Germany DA - 26.06.2017 KW - Optical measurment technique KW - Critical strain KW - Solidification cracking KW - Laser beam Welding PY - 2017 AN - OPUS4-41242 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael A1 - Bakir, Nasim T1 - Comparative study of hot cracking susceptibility for laser welded joints by means of a self- restraint and an externally loaded hot cracking tests N2 - Over the past decade, laser beam welding has significantly evolved and established itself as an efficient tool in the industry. Solidification cracking and the weldability of materials have been highly contentious issues for many years. Today, there are many self and externally loaded tests to investigate the hot cracking resistance of steels. The purpose of this paper is to compare the susceptibility of three stainless steel grades to hot cracking by using an externally loaded hot cracking test (CTW) and a self-restraint test in accordance with SEP-220-3. The repeatability and effectiveness of the results are discussed. The experimental results are widely dispersed, implying a low predictive value for the self-restraint test. On the other hand, the results from the externally loaded test exhibit excellent repeatability and provide a quantitative characterization of the susceptibility of steels to hot cracking. T2 - The 5th International Conference on Steels in Cars and Trucks CY - Amsterdam-Schiphol, Netherlands DA - 19.06.2017 KW - Externally loaded test KW - Hot cracking test KW - SEP-1220-3 KW - CTW test KW - Self-restraint test PY - 2017 SP - 1 EP - 8 AN - OPUS4-41174 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Üstündag, Ömer A1 - Bakir, Nasim A1 - Gook, S. A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael T1 - Hybrid laser‑arc welding of laser‑ and plasma‑cut 20‑mm‑thick structural steels N2 - It is already known that the laser beam welding (LBW) or hybrid laser-arc welding (HLAW) processes are sensitive to manufacturing tolerances such as gaps and misalignment of the edges, especially at welding of thick-walled steels due to its narrow beam diameter. Therefore, the joining parts preferably have to be milled. The study deals with the influence of the edge quality, the gap and the misalignment of edges on the weld seam quality of hybrid laser-arc welded 20-mm-thick structural steel plates which were prepared by laser and plasma cutting. Single-pass welds were conducted in butt joint configuration. An AC magnet was used as a contactless backing. It was positioned under the workpiece during the welding process to prevent sagging. The profile of the edges and the gap between the workpieces were measured before welding by a profile scanner or a digital camera, respectively. With a laser beam power of just 13.7 kW, the single-pass welds could be performed. A gap bridgeability up to 1 mm at laser-cut and 2 mm at plasma-cut samples could be reached respectively. Furthermore, a misalignment of the edges up to 2 mm could be welded in a single pass. The new findings may eliminate the need for cost and time-consuming preparation of the edges. KW - Hybrid laser-arc welding KW - Thick-walled steel KW - Edge quality KW - Gap bridgeability KW - Laser cutting KW - Plasma cutting PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-552013 DO - https://doi.org/10.1007/s40194-022-01255-y SN - 0043-2288 VL - 66 SP - 507 EP - 514 PB - Springer AN - OPUS4-55201 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Straße, Anne A1 - Bakir, Nasim A1 - Gumenyuk, Andrey A1 - Rethmeier, Michael ED - Schmidt, M. ED - Vollertsen, F. ED - Schmidt, B. M. T1 - Preliminary study to investigate the applicability of optical strain measurement technique for the detection of hot cracks in laser metal deposited layers N2 - Laser metal deposition (LMD) as an additive manufacturing technique became increasingly important in recent years and thus the demand for component safety. This is the reason, for the need for reliable in-situ defect detection techniques. For laser beam weld seams an optical measurement technique based on an optical flow algorithm was successfully used to define the critical straining conditions that lead to hot cracking. This algorithm was adapted for bead-on-plate weld seams on LMD deposited layers of IN718 alloy while performing external strain on the specimen in an externally loaded hot cacking test facility. The resulting transversal hot cracks along the weld seam were localized via X-Ray inspection and the type of cracking confirmed by Scanning Electron Microscopy (SEM). The strain distribution was measured in the vicinity of the solidification front and correlated to the detected hot cracks. Based on the results this technique could be adopted for LMD experiments. T2 - 12th CIRP Conference on Photonic Technologies [LANE 2022] CY - Fürth, Germany DA - 04.09.2022 KW - Laser Metal Deposition (LMD) KW - Strain measurement KW - Optical flow KW - Critical strain PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-556445 DO - https://doi.org/10.1016/j.procir.2022.08.034 VL - 111 SP - 335 EP - 339 PB - Elsevier B.V. CY - Amsterdam AN - OPUS4-55644 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -