TY - CONF A1 - Beck, Matthias A1 - Goebbels, Jürgen A1 - Isecke, Bernd A1 - Burkert, Andreas A1 - Mietz, Jürgen T1 - Investigations of corrosion on small cathodes in reinforced concrete - observations and suggestions N2 - Corrosion of steel reinforcement in concrete exposed to chloride containing environments is a serious problem in civil engineering practice. The standards and guidelines contain only minimum requirements regarding concrete quality and concrete cover. In very critical cases, for example the ingress of chlorides, the application of different coatings is currently the only possibility to protect the reinforced concrete structures. In this case the modelling of reinforcement corrosion would be more practical. One sub-project of a DFG-research project (FOR 537) is currently performed at the Federal Institute for Materials Research and Testing (BAM). Aim of the sub-project is the description of corrosion propagation and the characterization of the corrosion on specimens with small cathodes by electrochemical parameters. The electrochemical parameters are determined by suitable electrochemical measurements, considering concrete parameters as well as different environmental conditions. T2 - EUROCORR 2009 CY - Nice, France DA - 2009-09-06 KW - Self-corrosion KW - Steel reinforcement KW - Concrete parameters KW - X-ray tomography PY - 2009 IS - Paper 7976 SP - 1 EP - 13 AN - OPUS4-20063 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mietz, Jürgen A1 - Burkert, Andreas T1 - Selection and Durability of Stainless Steels for Civil Engineering N2 - Due to the large number of stainless steels with different chemical composition and different microstructure the selection of the suitable material represents a huge challenge. In order to facilitate the appropriate grade selection, in the current European standard EN 1993-1-4 a procedure is defined based on the use of a look-up table considering the key variables that influence the selection of stainless steels. The table uses descriptions that competent designers should be able to readily understand or define without prior knowledge. The output from the look-up table is used to select alloys based on a Corrosion Resistance Class (CRC) from I to V. The advantage of this approach is that the designer simply specifies the relevant CRC and does not need to consider in detail which of the many (very similar) alloys to specify. KW - Corrosion resistance KW - Stainless steel KW - Civil engineering KW - Atmospheric corrosion PY - 2020 DO - https://doi.org/10.4028/www.scientific.net/KEM.843 SN - 1662-9795 VL - 843 SP - 125 EP - 131 PB - Trans Tech Publications Ltd, CY - Switzerland AN - OPUS4-50831 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Raupach, M. A1 - Mietz, Jürgen A1 - Nürnberger, U. A1 - Wolff, L. A1 - Bruns, M. A1 - Burkert, Andreas A1 - Eich, Gerd A1 - Menzel, K. T1 - Entwicklung eines kombinierten Schutzsystems für chloridbelastete Betonflächen aus Spritzverzinkung mit abdichtender Beschichtung (Abschlussbericht, AiF 12 818 N/2) N2 - Die Zielsetzung dieses Projektes war es, ein kombiniertes Schutzsystem aus Spritzverzinkung und abdichtendem Oberflächenschutzsystem für die Instandsetzung chloridbelasteter und korrosionsgeschädigter Stahlbetonbauteile zu entwickeln. Dabei soll die Spritzverzinkung der Betonoberfläche in den ersten Jahren nach der Instandsetzung einen kathodischen Korrosionsschutz der Bewehrung bewirken, bis der Beton infolge des Oberflächenschutzsystems soweit ausgetrocknet ist, dass auch ohne kathodischen Schutz praktisch keine Korrosion der Bewehrung mehr stattfinden kann. Anhand von Untersuchungen zur Haftung zwischen Beton, Zinkschicht und verschiedenen Oberflächenschutzsystemen wurde der Aufbau des kombinierten Schutzsystems entwickelt. Es wurden verschiedene OS-11a-Systeme ein OS-13-System sowie zwei Systeme nach ZTV-ING, Teil 7 vor und nach künstlicher Bewitterung untersucht. Anhand der Ergebnisse wurde für das kombinierte System ein OS-11a-System ausgewählt und im weiteren hinsichtlich der Wirksamkeit des kathodischen Schutzes sowie hinsichtlich der Austrocknung des Betons untersucht. Es zeigte sich sowohl an ausgelagerten Prüfköpfen sowie auf einer angelegten Versuchsfläche auf Freideck eines Parkhauses, dass ein wirksamer galvanischer kathodischer Korrosionsschutz der Bewehrung nur bei sehr hohen Chloridgehalten (4 M.-% bezogen auf den Zementgehalt) erreicht werden kann. Bei geringeren untersuchten Chloridgehalten kam es vermutlich infolge der Austrocknung der Zink/Beton-Kontaktzone nach relativ kurzer Zeit zu einer Inaktivierung des Zinks. Bei Chloridgehalten von 4 M.-% bildeten sich zwischen der Zinkschicht und dem ausgewählten OS-System gasgefüllte Blasen. Diese Problematik, sowie die Tatsache dass die Wirksamkeit des Prinzips W (Austrocknung des Betons) bei derart hohen Chloridgehalten bezweifelt werden muss, grenzt die Anwendbarkeit des Kombinationssystems mit der Zinkschicht als Opferanode deutlich ein. An neun Jahre alten, ausgelagerten Prüfköpfen durchgeführte Untersuchungen zeigten jedoch, dass mittels Fremdstrombeaufschlagung zwischen Zinkschicht und Bewehrung ein wirksamer kathodischer Schutz auch bei geringeren Chloridgehalten erreicht werden kann. Der Einsatz des entwickelten Kombinationssystems mit Fremdstrombeaufschlagung erscheint somit durchaus durchführbar. Dabei sollte der Fremdstrom jedoch vorsichtig dosiert werden, um den Haftverbund zum Zink nicht zu sehr zu schwächen. Das Ziel des Vorhabens wurde somit erreicht. KW - Chlorinduzierte Korrosion KW - Kathodischer Korrosionsschutz KW - Oberflächenschutzsystem KW - Stahlbeton KW - Thermische Spritzverzinkung PY - 2004 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-355176 SP - 1 EP - 122 PB - IBAC Institut für Bauforschung CY - Aachen AN - OPUS4-35517 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lehmann, Jens A1 - Burkert, Andreas A1 - Mietz, Jürgen T1 - Investigations proofing the passive layer stability of stainless steels N2 - The presented investigations have proved the principal suitability of the KorroPad method to assess the passive layer stability of stainless steels. The electrochemical mode of action could be described in detail and limitations of the applicability have been demonstrated. The influence of different surface finishes has been investigated and verified by known methods for describing corrosion resistances. As a result, the increased corrosion susceptibility of two ground surfaces has been detected, but also the corrosion resistance of further surface finishes could be confirmed. KW - Stainless steel KW - KorroPad KW - Passive layer PY - 2016 DO - https://doi.org/10.1002/maco.201408202 VL - 1 IS - 67 SP - 84 EP - 91 PB - WILEY-VCH Verlag GmbH & Co. KGaA CY - Weinheim AN - OPUS4-35545 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burkert, Andreas A1 - Müller, Thoralf A1 - Lehmann, Jens A1 - Mietz, Jürgen T1 - Long-term corrosion behaviour of stainless steels in marine atmosphere N2 - Nine different stainless steel alloys were exposed for 5 years under marine environment and their corrosion behaviour was compared and assessed. The investigation of four different surface finishes for all alloys tested further enabled to consider industry-specific features of the surface finish for the material comparison. The results of the exposure tests yield conclusions regarding the influence of alloy composition, surface finish and exposure duration under marine environment. The three duplex stainless steels revealed excellent corrosion resistance even in case of crevices during the 5 years of exposure under the given exposure conditions. Also the molybdenum-alloyed ferritic steel 1.4521 showed good corrosion resistance comparable to the classical austenitic materials 1.4301 and 1.4404. KW - Corrosion KW - Free weathering KW - Marine atmosphere KW - Stainless steels PY - 2018 DO - https://doi.org/10.1002/maco.201709636 SN - 0947-5117 SN - 1521-4176 VL - 69 IS - 1 SP - 20 EP - 28 PB - Wiley-VCH Verlag GmbH & Co KGaA CY - Weinheim AN - OPUS4-43625 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Babutzka, Martin A1 - Mietz, Jürgen A1 - Burkert, Andreas T1 - Investigation of the salinization of steel surfaces in marine environment N2 - The salinization and contamination of metal surfaces by chloride-containing aerosols is of great importance with regard to corrosion phenomena of damaged coated metal surfaces and stainless steels in the maritime sector and in offshore applications. Detailed questions have to be answered to clarify whether and to what extent salinization of the surface has an influence on the adhesion and durability of coatings in repairing applications and on pitting occurrence on stainless steels under atmospheric conditions. The questions arise which degree of salinization is reached after which period of time and how a defined and reproducible salinization can be simulated in the laboratory for further systematic investigations. The article is dedicated to these questions. Results of a field trial on the Island of Heligoland are presented and a simple procedure for a defined loading of metal surfaces with chlorides at a laboratory scale using a design of experiments (DoE) approach is introduced. KW - Maritime Atmosphäre KW - Versalzung KW - Maritime atmosphere KW - Salinization PY - 2018 DO - https://doi.org/10.1002/maco.201810636 SN - 0947-5117 SN - 1521-4176 VL - 70 IS - 6 SP - 1016 EP - 1025 PB - Wiley-VCH Verlag CY - Weinheim AN - OPUS4-47727 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Burkert, Andreas A1 - Ebell, Gino A1 - Eichler, T. A1 - Hariri, K. A1 - Harnisch, J. A1 - Keßler, S. A1 - Mayer, T.F. A1 - Meier, J. A1 - Mietz, Jürgen A1 - Reichling, K. A1 - Sodeikat, C. T1 - Merkblatt für Elektrochemische Potentialmessungen zur Detektion von Bewehrungsstahlkorrosion KW - Stahlbeton KW - Korrosion KW - Bewehrung KW - Potentialmessung KW - Zerstörungsfreie Prüfung PY - 2014 SN - 978-3-940283-10-8 VL - B 03 SP - 1 EP - 19 CY - Berlin AN - OPUS4-31077 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Mietz, Jürgen A1 - Fischer, Joachim T1 - Spannungsrisskorrosion an Spannstahl - Ringversuch zur Prüfung der Spannungsrisskorrosion an Spannstählen N2 - Für Spannstähle muss im Rahmen der Überwachung die Beständigkeit gegenüber Spannungsrisskorrosion nach DIN EN ISO 15630-3 nachgewiesen werden. Die Stähle werden hierbei entweder einer konzentrierten Ammoniumthiocyanatlösung oder einer verdünnten Lösung, die eher die Verhältnisse in der Baupraxis wiedergibt, ausgesetzt. In den vergangenen Jahren gab es an Spannstäben der Festigkeitsklasse St 950/1050 immer wieder Probleme mit dem Erreichen der erforderlichen Standzeiten in der konzentrierten Lösung. Der Ringversuch sollte nun klären, inwieweit Unsicherheiten hinsichtlich der Zuverlässigkeit und Aussagekraft der Ergebnisse von Spannungsrisskorrosionsprüfungen bestehen. Außerdem sollten die Prüfanweisungen, die Prüfeinrichtungen sowie die Vor-Ort-Inspektion der Prüfstände kritisch beurteilt werden, um eventuell vorhandene versuchstechnische Probleme zu identifizieren und ggf. zu beheben. PY - 2015 SP - T 3306, 1 EP - 29 PB - Fraunhofer IRB Verl. AN - OPUS4-32461 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burkert, Andreas A1 - Lehmann, Jens A1 - Burkert, Annette A1 - Mietz, Jürgen A1 - Gümpel, P. T1 - Technical and economical stainless steel alternatives for civil engineering applications N2 - Systematic laboratory and field exposure tests allow to compare nine different stainless steels (three ferritic, three austenitic, and three duplex grades) for civil engineering applications. The influence of surface finish was also taken into account by choosing five different industry-specific features. The three duplex stainless steels revealed excellent corrosion resistance under most of the test conditions. Especially for applications in civil engineering the lean duplex steels offer distinct advantages. The manganese-alloyed 1.4376 and the ferritic steel 1.4509 cannot be recommended as alternative materials as they did not perform satisfactorily. KW - Atmospheric corrosion KW - Duplex stainless steels KW - Exposure tests KW - Surface finish PY - 2014 DO - https://doi.org/10.1002/maco.201307057 SN - 0947-5117 SN - 1521-4176 VL - 65 IS - 11 SP - 1080 EP - 1095 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-32350 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mietz, Jürgen T1 - Stand der Überarbeitung zur EN 1993-1-4 - Werkstoffauswahl und Dauerhaftigkeit T2 - Arbeitskreissitzung Korrosion im Bauwesen CY - Heligoland, Germany DA - 2014-06-02 PY - 2014 AN - OPUS4-30911 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mietz, Jürgen A1 - Burkert, Andreas T1 - Regelwerke für die Werkstoffauswahl und Dauerhaftigkeit von nichtrostenden Stählen für Stahlbauten – Entwicklung und aktueller Stand T1 - Technical regulations for the selection of materials and durability for steel structures - Development and current status N2 - Eine der wesentlichsten Veränderungen der im Oktober 2015 erschienenen Neufassung der DIN EN 1993-1-4 findet sich im Anhang A „Werkstoffauswahl und Dauerhaftigkeit“. Im Gegensatz zur Vorgängerversion ist dieser Anhang jetzt normativ. Mit Hilfe eines Punktesystems, das die wichtigsten Einwirkungsparameter der relevanten Expositionsbedingungen berücksichtigt, wird eine Korrosionsbeständigkeitsklasse ermittelt, mit deren Hilfe man eine geeignete Legierung auswählen kann. Dieses Verfahren bietet eine zuverlässige Methode für Planer auch ohne spezielle Kenntnisse auf dem Gebiet der Korrosion bzw. der nichtrostenden Stähle. Die Arbeit geht auch auf Unterschiede sowie Gemeinsamkeiten mit der bisher in Deutschland gültigen allgemeinen bauaufsichtlichen Zulassung Z-30.3.6 ein. KW - Korrosionsschutz KW - Werkstoffauswahl KW - Exposition PY - 2017 DO - https://doi.org/10.1002/stab.201710466 SN - 0038-9145 SN - 1437-1049 VL - 86 IS - 3 SP - 279 EP - 286 PB - Ernst & Sohn CY - Berlin AN - OPUS4-39570 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lehmann, Jens A1 - Fischer, Joachim A1 - Burkert, Andreas A1 - Mietz, Jürgen T1 - Langzeiterfahrungen an einer Gabionenkonstruktion T1 - Long term experiences with a gabion construction N2 - Anhand der hier vorgestellten Untersuchungsergebnisse kann eine umfassende Einschätzung des Korrosionszustands einer Gabionenkonstruktion aus Drähten mit Zink-Aluminium-Überzug nach 20 Jahren Einsatzzeit in Abhängigkeit von unterschiedlichen Expositionsbedingungen vorgenommen werden. Die festgestellten Massenverluste der Zink-Aluminium-Überzüge waren an den Untersuchungspositionen, insbesondere hinsichtlich der verschiedenen Expositionsbedingungen der Probenentnahmestellen, unterschiedlich ausgeprägt. Gabionendrähte, die im direkten Bodenkontakt standen, wiesen dabei die geringsten Restauflagen auf. Atmosphärisch beanspruchte sowie durch Vlies vor direktem Bodenkontakt geschützte Gabionendrähte zeigten dagegen etwas größere Restauflagen. Über den Drahtumfang wurden bei allen untersuchten Drahtproben stark variierende Schichtdicken festgestellt, was offensichtlich herstellungsbedingte Ursachen hat. Die Untersuchungen an der Gabionenkonstruktion haben gezeigt, dass die Annahme einer mittleren linearen Abtragsrate des metallischen Überzugs von 1 mm/a unter den hier untersuchten Bedingungen ein realistischer Wert ist. An Positionen mit direktem Bodenkontakt kann dieser Wert aber deutlich größer ausfallen, sobald sich die Aggressivität des Bodens erhöht. Eine Rotrostbildung war an den Drahtproben nicht feststellbar. KW - Korrosionsschutz KW - Zink-Aluminium-Überzug KW - Gabionen KW - Boden PY - 2017 DO - https://doi.org/10.1002/bate.201600030 SN - 0932-8351 VL - 94 IS - 1 SP - 37 EP - 48 PB - Ernst & Sohn CY - Weinheim AN - OPUS4-38950 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burkert, Andreas A1 - Lehmann, Jens A1 - Burkert, Annette A1 - Mietz, Jürgen A1 - Eich, Gerd T1 - Verzinkte Bauteile im Kontakt mit Spanngliedern N2 - Um zu klären, unter welchen Umständen eine potentielle Gefährdung von Spannstählen beim Kontakt mit verzinkten Bauteilen gegeben ist, wurden Laborversuche in alkalischen Lösungen und Beton sowie Zeitstandversuche an Spannbetonprobekörpern durchgeführt. Abstandsvariationen im Nahbereich haben nur einen geringen Einfluss auf die Polarisation des Stahls. Ein praxisrelevanter, unkritischer Abstand für den indirekten Kontakt, z. B. über die schlaffe Bewehrung, kann nicht definiert werden. Hinsichtlich des Flächenverhältnisses Stahl : Zink wurde ein signifikanter Einfluss festgestellt. Flächenverhältnisse über 10 : 1 führen nicht zu einer Polarisation in den Bereich der Wasserstoffentwicklung. Die Ergebnisse wurden durch Untersuchungen an realen Spannbetonfertigteilen verifiziert. Zeitstandversuche unter Wasserstoffbeladung führten an zugelassenen Spannstählen nicht zu Brüchen während der Versuchszeit. Die anschließend ermittelten mechanischen Kennwerte zeigten keine signifikanten Änderungen. Ein indirekter Kontakt von Spannstählen zu verzinkten Einbauteilen ist deshalb als unkritisch zu bewerten. Der direkte Kontakt ist durch Einhaltung des in der DIN 1045-1 geforderten Mindestabstands von 2 cm sicher auszuschließen. KW - Spannstahl KW - Korrosion KW - Stahlbeton PY - 2008 DO - https://doi.org/10.1002/best.200800619 SN - 0005-9900 SN - 1437-1006 VL - 103 IS - 6 SP - 413 EP - 421 PB - Ernst CY - Berlin AN - OPUS4-17626 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burkert, Andreas A1 - Lehmann, Jens A1 - Burkert, Annette A1 - Mietz, Jürgen T1 - Korrosionsschäden an nichtrostenden Stählen unter atmosphärischen Einsatzbedingungen N2 - Neben konstruktiven Anforderungen werden an nichtrostende Stähle im Bauwesen häufig hohe optische Ansprüche gestellt. Unerwartete Beeinträchtigungen des optischen Erscheinungsbildes nichtrostender Stähle unter wenig korrosiven Bedingungen sind in der Zwischenzeit ein weit verbreitetes Problemfeld und Gegenstand zahlreicher Streitfälle. Vielfach wird die Vermutung geäußert, dass eine veränderte Legierungszusammensetzung, veränderte Umweltbedingungen oder auch die unsachgemäße Verarbeitung die Ursache für diese Erscheinungen sind. Durch eine systematische Untersuchung zahlreicher Schadensfälle an Stabmaterial in den vergangenen zwei Jahren im Rahmen eines Forschungsvorhabens konnte gezeigt werden, dass die Ursachen in bekannten Werkstofffehlern zu finden sind. Hierzu gehören chemische Inhomogenitäten, wie zum Beispiel Ausscheidungen und örtliche Aufkohlung, sowie geometrische Fehler, wie zum Beispiel Hinterschnitte, Walzfehler und Schalenbildung. Die Fehler konnten damit eindeutig als Herstellungsfehler der jeweiligen Halbzeuge identifiziert werden. KW - Korrosion KW - Nichtrostende Stähle KW - Atmosphäre KW - Interkristalline Korrosion KW - Schäden PY - 2010 DO - https://doi.org/10.1002/stab.201001288 SN - 0038-9145 SN - 1437-1049 SN - 0932-6375 VL - 79 IS - 5 SP - 389 EP - 395 PB - Ernst CY - Berlin AN - OPUS4-21242 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Fischer, Joachim A1 - Burkert, Andreas A1 - Mietz, Jürgen T1 - Case studies of stainless steel corrsoion in indoor swimming pool environments N2 - In indoor swimming pools stainless steels are used not only due to structural and economic reasons but also due to aesthetic considerations. And therefore not only safety relevant load bearing components have to fulfil their tasks but also the visual appearance should be free of any staining. In a lot of cases basic requirements (e.g. design criteria, material selection and maintenance) being essential parts of technical regulations were not taken into account. Typical case studies with explanation of the cause of the corrosion problems and possibilities to prevent them are shown in the present paper. KW - Stainless steel KW - Atmospheric corrosion KW - Indoor swimming pools PY - 2011 DO - https://doi.org/10.1179/174327809X409150 SN - 1478-422X VL - 46 IS - 1 SP - 76 EP - 79 PB - Maney Publishing CY - London, UK AN - OPUS4-23287 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mietz, Jürgen A1 - Burkert, Andreas A1 - Lehmann, Jens A1 - Eich, G. ED - Castro-Borges, P. ED - Moreno, E.I. ED - Sakai, K. ED - Gjorv, O.E. ED - Banthia, N. T1 - Risk of stress corrosion cracking of prestressing steels in contact with galvanized components T2 - CONSEC`10 - 6th International conference on concrete under severe conditions CY - Mérida, Yucatán, Mexico DA - 2010-06-07 KW - Prestressing steel KW - Galvanized elements KW - Galvanic corrosion KW - Hydrogen evolution KW - Hydrogen-induced stress corrosion cracking PY - 2010 SN - 978-0-415-59316-8 VL - 1 SP - 239 EP - 246 PB - Taylor & Francis CY - London, UK AN - OPUS4-22037 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burkert, Andreas A1 - Mietz, Jürgen T1 - Korrosionsschäden an Lagertanks für Salzlake N2 - An einem Tankbehälter aus dem Werkstoff X2CrNiMo17-12-2, der zur Zwischenlagerung von Salzlake für die Käseherstellung dient, wurden trotz langjähriger positiver Erfahrungen an vergleichbaren Anlagen bereits kurze Zeit nach der Inbetriebnahme Lochkorrosionserscheinungen festgestellt. Durch entsprechende elektrochemische Laboruntersuchungen konnte gezeigt werden, dass die vorgefundene Lochkorrosion durch den Einsatz eines Oxidationsmittels zu Desinfektionszwecken verursacht wurde. Translated Abstract Corrosion damage at storage tanks for salt brine A tank made of stainless steel type X2CrNiMo17-12-2 for intermediate storage of salt brine for cheese production revealed significant pitting corrosion effects shortly after commissioning although comparable units have shown positive long-term behaviour. By means of electrochemical laboratory tests it could be demonstrated that the observed pitting corrosion was caused by the use of an oxidizing agent for desinfection purposes. PY - 2003 SN - 0947-5117 SN - 1521-4176 VL - 54 IS - 2 SP - 113 EP - 118 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-2378 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Burkert, Andreas A1 - Eich, Gerd A1 - Mietz, Jürgen T1 - Entwicklung eines kombinierten Schutzsystems für chloridbelastete Betonflächen aus Spritzverzinkung mit abdichtender Beschichtung T2 - 2. Kolloquium Gemeinsame Forschung im Korrosionsschutz, Neue Entwicklungen bei Fügeverfahren und Oberflächenschutz CY - Frankfurt am Main, Deutschland DA - 2004-03-02 KW - Stahlbeton KW - Chlorinduzierte Korrosion KW - Thermische Spritzverzinkung KW - Kathodischer Korrosionsschutz KW - Oberflächenschutzsystem PY - 2004 SN - 3-935406-12-6 SP - 72 EP - 83 PB - GfKORR CY - Frankfurt am Main AN - OPUS4-3371 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mietz, Jürgen T1 - Analyse von Spannbetonschäden und Strategien zu deren Vermeidung T2 - Tagung Werkstoffprüfung 2001 - Schadensanalyse und Schadensvermeidung CY - Bad Nauheim, Germany DA - 2001-12-06 PY - 2001 AN - OPUS4-3343 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Eich, Gerd A1 - Burkert, Andreas A1 - Mietz, Jürgen T1 - Entwicklung eines kombinierten Schutzsystems für chloridbelastete Betonflächen aus Spritzverzinkung mit abdichtender Beschichtung (Kurzfassung, AiF 12 818 N) KW - Stahlbeton KW - Chlorinduzierte Korrosion KW - Thermische Spritzverzinkung KW - Kathodischer Korrosionsschutz KW - Oberflächenschutzsystem PY - 2004 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-44201 SP - 1 EP - 4 PB - Bundesanstalt für Materialforschung und -prüfung CY - Berlin AN - OPUS4-4420 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mietz, Jürgen A1 - Burkert, Andreas A1 - Eich, Gerd A1 - Raupach, M. T1 - Development of a new combined corrosion protection system for chloride-contaminated reinforced concrete structures N2 - Chloride-induced damage of reinforcing steel is especially for parking garages and bridges often very severe as large amounts of chlorides act on horizontal surfaces which could lead to fast ingress of these detrimental ions up to the level of the reinforcement and subsequently to high rates of corrosion. In order to avoid the disadvantages of conventional rehabilitation (unreliable prognosis with patch repair or high costs and regular maintenance with cathodic protection using impressed current) a new combined protection system was developed where the principle of drying out the concrete (by means of a surface protection system) is combined with a temporary cathodic protection (by means of a sprayed zinc layer) during the transitional period of the drying out process. This new system was tested both in the laboratory and on-site at a pilot application. Based on the results obtained the possibilities and limitations of the new system are discussed in this paper. KW - Chlorid-induced corrosion KW - Reinforcing steel KW - Cathodic protection KW - Sprayed zinc layer KW - Surface protection system PY - 2005 DO - https://doi.org/10.1002/maco.200403836 SN - 0947-5117 SN - 1521-4176 VL - 56 IS - 2 SP - 104 EP - 110 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-7157 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mietz, Jürgen A1 - Burkert, Andreas ED - Cziesielski, E. T1 - Elektrochemische Verfahren zur Detektion von Bewehrungsstahlkorrosion KW - Potentialfeldmessungen KW - Galvanostatische Pulsmessungen KW - Bewehrungsstahlkorrosion PY - 2004 SN - 3-433-01705-0 SP - 379 EP - 385 PB - Ernst CY - Berlin AN - OPUS4-3519 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Isecke, Bernd A1 - Mietz, Jürgen T1 - Bau- und Instandsetzungsmethoden - Elektrochemische Schutzverfahren zur Beseitigung von Korrosionsrisiken an Stahlbetonbauwerken PY - 2003 SN - 3-935243-14-6 N1 - Serientitel: Schriftenreihe des Verbandes Deutscher Architekten- und Ingenieurvereine – Series title: Schriftenreihe des Verbandes Deutscher Architekten- und Ingenieurvereine IS - 2 SP - 149 EP - 157 PB - Verl. Das Beispiel CY - Darmstadt AN - OPUS4-2789 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Isecke, Bernd A1 - Mietz, Jürgen A1 - Schütt, K. T1 - Temporärer Korrosionsschutz von Spannstählen in unverpressten Hüllrohren PY - 2003 DO - https://doi.org/10.1002/maco.200390091 SN - 0947-5117 SN - 1521-4176 VL - 54 SP - 1 EP - 7 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-2489 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mietz, Jürgen A1 - Burkert, Andreas A1 - Burkert, Annette A1 - Eich, Gerd T1 - Long-term Behaviour of Corrosion Protection Materials for Prestressed Systems T2 - 2nd International fib Congress CY - Naples, Italy DA - 2006-06-05 KW - Prestressed systems KW - Corrosion protection KW - Wax KW - Grease KW - Electrochemical tests PY - 2006 SN - 0-912053-94-1 SP - 12 pages PB - Society for Experimental Mechanics CY - St. Lous AN - OPUS4-12513 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Mietz, Jürgen A1 - Burkert, Annette A1 - Burkert, Andreas A1 - Jonas, Bernhard A1 - Eich, Gerd A1 - Baszynski, Joachim T1 - Korrosionsschutzwirkung von Korrosionsschutzmassen für Spannglieder ohne Verbund KW - Spannstahl KW - Korrosion KW - Korrosionsschutzmittel KW - Wasseraufnahme KW - Schutzwirkung KW - Langzeitverhalten KW - Bodenkontakt PY - 2005 SN - 3-8167-6740-0 IS - T 3071 SP - 1 EP - 45 PB - IRB-Verl. CY - Stuttgart AN - OPUS4-11344 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mietz, Jürgen A1 - Fischer, Joachim T1 - Verifizierung zerstörungsfreier Prüfverfahren zur Detektion von Spannstahlschäden an Spannbetonbauteilen mit nachträglichem Verbund N2 - For an assessment of the risk potential of existing structures where in the case of prestressing steel damage the load-bearing capacity could be significantly affected non-destructive testing techniques which enable reliable evaluation of the condition of the prestressing steels are of utmost importance. During the demolition of the Hohenzollerndamm bridge in Berlin where damage of prestressing wires due to hydrogen-induced stress corrosion cracking were found in former investigations parts of the girders of the bridge superstructure could be taken out. After non-destructive investigation by means of two testing techniques based on magnetic leakage flux measurement and one technique based on electromagnetic resonance measurement the single wires were inspected in order to verify the non-destructive testing results with respect to their reliability. From the results it can be concluded that areas with fractures of several wires could be detected by the two techniques based on magnetic leakage flux measurement. PY - 2005 DO - https://doi.org/10.1002/best.200590181 SN - 0005-9900 SN - 1437-1006 VL - 100 IS - 8 SP - 656 EP - 663 PB - Ernst CY - Berlin AN - OPUS4-11148 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mietz, Jürgen A1 - Burkert, Annette A1 - Burkert, Andreas A1 - Eich, Gerd T1 - Investigations on the protection effect of filling materials for post-tensioning systems under construction conditions N2 - About the long-term protection behaviour of corrosion protection materials (filling materials) for prestressed systems under critical environmental conditions is only little known. The corrosion protection effect is usually based on theoretical considerations and is proven by short-term tests. The selection of the different products is mainly made according to economical or workability criteria. In a research project the barrier effect of different commercial corrosion protection materials (waxes as well as oil-based greases) against water, their tendency for undercutting as well as their additional corrosion protection effect were investigated. The exposure tests were carried out with non-stressed as well as stressed prestressing steel specimens which were subjected to critical conditions (condensed water, artificial soil solution, direct soil contact). Parallel to these long-term exposure tests the applicability of different electrochemical techniques and their significance with respect to testing the corrosion protection ability and water absorption was evaluated. Within the project a suitable method for simple testing the performance of corrosion protection materials under real conditions was developed. By means of a small compact cell submicroscopical reactions of the used sensors could be measured. The high sensitivity of this measuring technique enables the detection of degradation processes at thin protection layers. KW - Prestressed systems KW - Corrosion KW - Corrosion protection KW - Electrochemical tests KW - Grease KW - Wax PY - 2006 DO - https://doi.org/10.1002/maco.200603986 SN - 0947-5117 SN - 1521-4176 VL - 57 IS - 11 SP - 843 EP - 851 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-13931 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Burkert, Andreas A1 - Lehmann, Jens A1 - Burkert, Annette A1 - Mietz, Jürgen A1 - Eich, Gerd T1 - Verzinkte Bauteile im Kontakt mit Spanngliedern T2 - 4. Kolloquium des Kuratoriums Korrosionsschutz (KKF) CY - Düsseldorf, Deutschland DA - 2007-06-20 KW - Spannbeton KW - Spannstahl KW - Wasserstoffinduzierte Spannungsrisskorrosion KW - Verzinkte Einbauteile KW - Zink KW - DIN 1045 PY - 2007 SN - 978-3-935406-34-5 SP - 12 EP - 25 PB - GfKORR CY - Frankfurt am Main AN - OPUS4-15018 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mietz, Jürgen A1 - Fischer, Joachim T1 - Evaluation of NDT methods for detection of prestressing steel damage at post-tensioned concrete structures KW - Prestressing steel KW - Non-destructive testing KW - Post-tensioned concrete KW - Hydrogen-induced stress corrosion cracking PY - 2007 DO - https://doi.org/10.1002/maco.200704074 SN - 0947-5117 SN - 1521-4176 VL - 58 IS - 10 SP - 789 EP - 794 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-16063 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Eich, Gerd A1 - Burkert, Annette A1 - Burkert, Andreas A1 - Mietz, Jürgen T1 - Einsatz des nichtrostenden Duplex-Stahls 1.4362 als preisgünstige Alternative im Bauwesen N2 - Aufgrund der in den letzten Jahren stark angestiegenen Rohstoffpreise sind die im Bauwesen häufig eingesetzten nichtrostenden Standardaustenite in vielen Fällen nicht mehr wettbewerbsfähig. Eine deutlich kostengünstigere Alternative stellt der Duplex-Stahl 1.4362 dar, der bisher aber noch nicht bauaufsichtlich zugelassen ist. Mit Hilfe von Auslagerungsversuchen sowie elektrochemischen Untersuchungen sollte das Korrosionsverhalten dieses Werkstoffs unter neutralen bis leicht sauren, chloridhaltigen Umgebungsbedingungen, wie sie in vielen Bereichen des Bauwesens vorkommen, geklärt werden. Insgesamt belegen die Ergebnisse, dass der kostengünstigere Werkstoff 1.4362 für baupraktische Anwendungen eine Alternative für Anwendungen darstellen kann, in denen bisher die Werkstoffe 1.4404 oder 1.4571 eingesetzt wurden. KW - Duplex-Stähle KW - Nichtrostende Stähle KW - Auslagerungsversuche KW - Elektrochemische Versuche KW - Lochkorrosionspotential KW - Spaltkorrosionspotential PY - 2007 DO - https://doi.org/10.1002/stab.200710094 SN - 0038-9145 SN - 1437-1049 SN - 0932-6375 VL - 76 IS - 12 SP - 898 EP - 904 PB - Ernst CY - Berlin AN - OPUS4-16364 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mietz, Jürgen T1 - Ein halbes Leben für die BAM - Höhepunkte aus 30 Jahren T2 - GfKORR-Symposium CY - Frankfurt am Main, Germany DA - 2008-03-29 PY - 2008 AN - OPUS4-16715 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Burkert, Andreas A1 - Mietz, Jürgen A1 - Lehmann, Jens A1 - Eich, Gerd A1 - Burkert, Annette T1 - Verzinkte Bauteile in Kontakt mit Spanngliedern (Abschlussbericht für den Zeitraum 01.02.2005 bis 31.10.2007; Forschungsvorhaben 14218 N / 1) KW - Spannbeton KW - Spannstahl KW - Wasserstoffinduzierte Spannungsrisskorrosion KW - Verzinkte Einbauteile PY - 2007 SP - 1 EP - 42 PB - Bundesanstalt für Materialforschung und -prüfung CY - Berlin AN - OPUS4-16694 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mietz, Jürgen A1 - Burkert, Andreas A1 - Lehmann, Jens A1 - Burkert, Annette A1 - Eich, Gerd T1 - Galvanised constructional elements in contact with prestressing steel tendons N2 - In order to clarify under which practical conditions real risks for hydrogen-induced stress corrosion cracking of prestressing steels exist laboratory investigations in aqueous solutions and concrete as well as tests with stressed prestressing steels were carried out. While different distances between steel and zinc (cathode and anode) showed only a negligible influence on the polarisation of the steel a significant dependence on the area ratio steel/zinc was observed. A critical area ratio of 10:1 can be defined above which polarisation of the steel to hydrogen evolution potentials is unlikely. The results obtained in the laboratory concerning the critical area ratio were confirmed by on-site investigations in a precasting plant. Exposure tests with hydrogen loading did not lead to fractures during the testing time for approved prestressing steels. The characteristic mechanical values determined immediately after the hydrogen loading tests did not show significant changes. Thus, an indirect contact between prestressing steels and galvanised elements can be estimated as uncritical. But a direct contact has to be excluded by compliance with DIN 1045-1, i.e minimal distance of 2 cm between prestressing steel and galvanised elements. PY - 2008 DO - https://doi.org/10.1002/maco.200804114 SN - 0947-5117 SN - 1521-4176 VL - 59 IS - 2 SP - 131 EP - 138 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-16724 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burkert, Andreas A1 - Lehmann, Jens A1 - Burkert, Annette A1 - Mietz, Jürgen T1 - Damage of stainless steel bars due to atmospheric corrosion N2 - In addition to constructional requirements in civil engineering stainless steels often have to fulfil high visual demands. Unexpected impairments of the visual appearance of stainless steels under low corrosive conditions are a widespread problem today. Frequently it is supposed that this is caused by changes in the alloy composition, worse environmental conditions or improper handling. Within a research project the systematic investigation of several cases of damaged stainless steel bars has shown that the reasons are based on well-known material defects like chemical inhomogeneities (e.g. precipitations or local carburization) or geometrical defects (e.g. undercuts, rolling defects or shell formation). Thus, the failures could be clearly identified as production failures of the respective semi-finished products. KW - Atmospheric corrosion KW - EPR test KW - Failure KW - Intercrystalline corrosion KW - Stainless steel KW - Nichtrostender Stahl KW - Werkstoffauswahl KW - Dauerhaftigkeit KW - Korrosion PY - 2012 DO - https://doi.org/10.1002/maco.201005701 SN - 0947-5117 SN - 1521-4176 VL - 63 IS - 3 SP - 264 EP - 270 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-25702 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Burkert, Andreas A1 - Lehmann, Jens A1 - Burkert, Annette A1 - Mietz, Jürgen A1 - Gümpel, P. T1 - Technische und wirtschaftliche Alternativen zu den klassischen nichtrostenden, austenitischen Stählen unter atmosphärischen Einsatzbedingungen N2 - Durch systematische Labor- und Auslagerungsuntersuchungen ist es möglich, sieben unterschiedliche nichtrostende Stahllegierungen hinsichtlich verschiedenster Anwendungen untereinander und auch in Bezug auf zwei austenitische Standardwerkstoffe (1.4301, 1.4404) zu vergleichen. Die parallele Untersuchung von fünf verschiedenen Oberflächenausführungen der jeweiligen Werkstoffe ermöglicht zudem, branchenspezifische Besonderheiten der Oberflächenausführung beim Werkstoffvergleich zu berücksichtigen. Der Einfluss der Oberflächenausführung wird überwiegend bei den Ergebnissen der Auslagerungsversuche in kritischen Atmosphären sichtbar, weniger bei den elektrochemischen Untersuchungen. Die drei Vertreter aus dem Bereich der Duplexstähle zeigten unter den meisten Untersuchungsbedingungen eine hervorragende Korrosionsbeständigkeit. Insbesondere für Anwendungen im Bauwesen können die Lean-Duplexstähle deutliche Vorteile bieten. Der Manganaustenit 1.4376 sowie der Ferrit 1.4509 sind nur eingeschränkt als Alternativen geeignet, da die Werkstoffe bei einigen Versuchen signifikante Schwächen zeigten.--------------------------------------------------------------------------- The systematic laboratory and field exposure tests allow to compare seven different stainless steels among each other and also regarding two standard austenitic materials (1.4301, 1.4401) with respect to various applications. Parallel investigations with five different surface finishes of the respective materials enable to consider also industry-specific features of the surface finish. The influence of the surface finish can mainly be seen in the results of the exposure tests in critical atmospheres and less in the electrochemical investigations. The three duplex stainless steels showed under most of the test conditions excellent corrosion resistance. Especially for applications in civil engineering the lean duplex steels offer clear advantages. The manganese alloyed 1.4376 and the ferritic steel 1.4509 are only limited suitable as alternatives as these materials showed significant weaknesses in some of the tests. KW - Nichtrostende Stähle KW - Bauwesen KW - Atmosphärische Korrosion PY - 2012 DO - https://doi.org/10.1002/stab.201201624 SN - 0038-9145 SN - 1437-1049 SN - 0932-6375 VL - 81 IS - 11 SP - 875 EP - 888 PB - Ernst CY - Berlin AN - OPUS4-26825 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mietz, Jürgen T1 - Aktueller Stand der Überarbeitung der EN 1993-1-4 T2 - GfKORR-Arbeitskreis Korrosion im Bauwesen CY - Heligoland, Germany DA - 2013-06-03 PY - 2013 AN - OPUS4-28712 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Broomfield, J. A1 - Fischer, Joachim A1 - Mietz, Jürgen A1 - Schneck, U. T1 - Case studies N2 - In this paper, some quite different survey tasks are described, and it can be seen that corrosion surveys will follow a certain scheme of data acquisition (first NDT measurements, than detailed testing on suspect areas), but the individual scope of on-site measurements may have a vast variety according to the local circumstances, and the interpretation always has to refer to a wider set of information than the data readings only. KW - Corrosion surveys KW - Non-destructive testing KW - Reinforcement KW - Concrete KW - Potential mapping KW - Corrosion PY - 2013 DO - https://doi.org/10.1002/maco.201206649 SN - 0947-5117 SN - 1521-4176 VL - 64 IS - 2 SP - 147 EP - 160 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-29730 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mietz, Jürgen A1 - Isecke, Bernd T1 - Stainless steels for applications in civil engineering T2 - Stainless Steel World Conference & Exposition CY - The Hague, The Netherlands DA - 2001-11-13 KW - Civil engineering KW - Atmospheric corrosion conditions KW - Stainless steels KW - Stress corrosion cracking KW - Approval PY - 2001 SN - 90-73168-14-7 IS - P0108 SP - 334 EP - 339 PB - KCI Publ. CY - Zutphen AN - OPUS4-1199 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mietz, Jürgen A1 - Isecke, Bernd ED - Lange, G. T1 - Analyse von Spannbetonschäden und Strategien zu deren Vermeidung T2 - 19. Tagung Werkstoffprüfung CY - Bad Nauheim, Deutschland DA - 2001-12-06 PY - 2001 SN - 3-527-30538-6 SP - 153 EP - 158 PB - Wiley-VCH CY - Weinheim AN - OPUS4-1216 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mietz, Jürgen ED - Banthia, N. T1 - Corrosion behaviour of stainless steels for use in ground anchors T2 - 3rd International Conference on Concrete under Severe Conditions ; 3rd CONSEC '01 CY - Vancouver, Canada DA - 2001-06-18 PY - 2001 SN - 0-88865-790-0 VL - 1 SP - 341 EP - 348 PB - Univ. British Columbia, Dep. of Civil Engineering CY - Vancouver AN - OPUS4-1135 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Isecke, Bernd A1 - Mietz, Jürgen A1 - Fischer, Joachim T1 - Langzeiterfahrungen mit einem kathodischen Korrosionsschutzsystem für Stahl in Beton N2 - Im Jahr 1986 wurde in Deutschland die erste kathodische Korrosionsschutzanlage für ein Stahlbetonbauwerk in Betrieb genommen. Die Installation, die Inbetriebnahme sowie die laufende Überwachung wurden wissenschaftlich begleitet. Im Zuge notwendiger verkehrstechnisch bedingter Umbaumaßnahmen wurde die Anlage nach etwa 15 Jahren außer Betrieb genommen. Die in dieser Zeit durchgeführten Untersuchungen dienten dem Ziel, die an Laborversuchen gewonnenen Ergebnisse an einem praktischen Bauwerk zu überprüfen sowie Informationen über das Langzeitverhalten hinsichtlich Dauerhaftigkeit, Potentialverteilung, Temperaturabhängigkeit, Chloridmigration usw. zu bekommen. Mit zunehmender Betriebsdauer konnten die Schutzkriterien nur durch Erhöhung der Gleichrichterspannung eingehalten werden (die Anlage wurde im Konstantspannungsmodus betrieben). Umfangreiche Untersuchungen an Anodenmaterialproben (leitfähiger Polymerdraht mit einem Kupferkern) nach 15-jährigem Einsatz zeigten, dass irreversible Veränderungen die Leitfähigkeit des Polymers erheblich vermindert haben, wodurch letztendlich die Funktionsfähigkeit der Anode nicht mehr gegeben war. Diese Art von Anoden werden aber heutzutage nicht mehr für den kathodischen Korrosionsschutz von Stahlbetonbauwerken eingesetzt. Translated Abstract Long-term experiences with a cathodic protection system for steel in concrete In 1986 in Germany the first cathodic protection system for reinforced concrete structures was put into service. Installation, commissioning and the regular monitoring were scientifically supported. Due to necessary traffic related reconstruction measures the system was switch off after 15 years of service. Investigations carried out during that period should verify laboratory test results at a real structure and furthermore yield information on the long-term behaviour concerning durability, temperature dependence, potential distribution, chloride migration etc. With increasing time of service the protection criteria could only be met by increasing the transformer rectifier voltage (the system worked in the constant voltage mode). Extensive investigations of the anode material (conductive polymer wire with a copper core) after 15 years of service showed that irreversible changes substantially decreased the polymer's conductivity limiting the functionality. Today, these kind of anodes are not used any more for the application in cathodic protection systems of reinforced concrete structures. PY - 2001 DO - https://doi.org/10.1002/1521-4176(200112)52:12<920::AID-MACO920>3.0.CO;2-J SN - 0947-5117 SN - 1521-4176 VL - 52 IS - 12 SP - 920 EP - 930 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-1222 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mietz, Jürgen A1 - Isecke, Bernd T1 - Assessment of test methods for evaluation stress corrosion cracking susceptibility of prestressing steels N2 - Prestressing steels can be exposed in prestressed concrete structures in construction stage (ungrouted duct) to environmental conditions causing formation and growth of hydrogen induced cracks with brittle fracture of the steel. The risk of this hydrogen induced stress corrosion cracking can be minimized by appropriate treatment, but there is a requirement for construction to approve only prestressing steel having no enhanced susceptibility to stress corrosion cracking. The paper describes the historical development of the different test methods proposed in the past and gives an overview on the general requirements for a suitable test method to assess the hydrogen-induced stress corrosion susceptibility of prestressing steels. Since 1982, based on investigations on construction sites and transfer of the results into laboratory tests, a test method is available enabling realistic estimation of suitable application possibilities of prestressing steels. This so called DIBt-test is approved to distinguish between prestressing steels susceptible to hydrogen induced stress corrosion cracking and those suitable and therefore approvable steels at practical environmental conditions. Furthermore the test enables estimation of corrosion risk for newly developed prestressing steels with higher strength. Translated Abstract Beurteilung der Prüfverfahren zur Untersuchung der Spannungsrisskorrosionsempfindlichkeit von Spannstählen Spannstähle können in Spannbetonbauwerken im Bauzustand (unverpresstes Hüllrohr) Umgebungsbedingungen ausgesetzt sein, die zur Bildung und Ausbreitung wasserstoffinduzierter Risse mit Sprödbruch des Stahles führen können. Das Risiko dieser wasserstoffinduzierten Spannungsrisskorrosion kann einerseits durch eine sachgemäße Verarbeitung der Spannstähle minimiert werden, andererseits besteht die Notwendigkeit nur solche Spannstähle für die Baupraxis zuzulassen, die unter baupraktischen Bedingungen keine erhöhte Empfindlichkeit für Spannungsrisskorrosion besitzen. Die vorliegende Arbeit beschreibt die historische Entwicklung der verschiedenen vorgeschlagenen Prüfverfahren und gibt einen Überblick über die allgemeinen Anforderungen an ein geeignetes Verfahren zur Beurteilung der wasserstoffinduzierten Spannungsrisskorrosionsempfindlichkeit von Spannstählen. Seit 1982 steht, begründet durch Untersuchungen auf Baustellen und Umsetzung der Ergebnisse in Laborversuchen, ein Prüfverfahren zur Verfügung, das eine wesentlich realistischere Einschätzung der Einsatzmöglichkeiten von Spannstählen zulässt. Dieser sog. DIBt-Test hat sich bewährt, um unter praktischen Umgebungsbedingungen gegen H-induzierte Spannungsrisskorrosion empfindliche Spannstähle von geeigneten und damit zulassungswürdigen Stählen zu unterscheiden. Des weiteren erlaubt die Prüfung ebenfalls eine Abschätzung des Korrosionsrisikos für neuentwickelte, höherfeste Spannstähle. PY - 2002 SN - 0947-5117 SN - 1521-4176 VL - 53 IS - 6 SP - 373 EP - 384 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-1402 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mietz, Jürgen A1 - Raupach, M. A1 - Goltermann, P. T1 - Integrated Monitoring System for Reinforced Concrete Structures T2 - 1st FIB congress CY - Osaka, Japan DA - 2002-10-13 KW - Reinforcement corrosion KW - Sensors KW - Inspection KW - Maintenance KW - Bridge management PY - 2002 IS - 15 SP - 29 EP - 38 CY - Osaka AN - OPUS4-1727 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mietz, Jürgen A1 - Isecke, Bernd A1 - Fischer, Joachim T1 - Long-term experiences with cathodic corrosion protection of steel reinforced concrete structures T2 - 15th International Corrosion Congress CY - Granada, Spain DA - 2002-09-22 PY - 2002 PB - CSIC, Spanish Council for Scientific Research CY - Madrid AN - OPUS4-1728 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Isecke, Bernd A1 - Mietz, Jürgen T1 - Einsatz nichtrostender Stähle in Schwimmbädern T2 - Fachtagung des Nederlands Corrosie Centrum CY - Breda, Niederlande DA - 2002-11-14 PY - 2002 AN - OPUS4-1845 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mietz, Jürgen A1 - Baszynski, Joachim A1 - Fischer, Joachim T1 - Untersuchungen zur Spannungsrißkorrosionsbeständigkeit nichtrostender Stähle mit unterschiedlichem Verformungsgrad N2 - Im Rahmen der Erarbeitung einer neuen bauaufsichtlichen Zulassung für nichtrostende Stähle ergab sich die Fragestellung, ob durch eine Kaltverfestigung die Beständigkeit gegenüber Spannungsrißkorrosion negativ beeinflußt wird. Durch experimentelle Versuche an verschiedenen nichtrostenden Stählen sollte geklärt werden, ob kaltverformtes Material bei hoher Chloridbelastung, wie sie z. B. in Schwimmhallenatmosphäre vorkommen kann, eine höhere Empfindlichkeit gegenüber Spannungsrißkorrosion aufweist. Die Untersuchungen wurden mit den hochlegierten Stählen 1.4462 sowie 1.4529 durchgeführt. Als Vergleichswerkstoff mit bekannter Empfindlichkeit gegenüber Spannungsrißkorrosion bei hoher Chloridbelastung wurde der Stahl 1.4301 eingesetzt. Die Versuche erfolgten mittels Bügel- und Zugproben, auf die Tropfen aus gesättigter Magnesiumchloridlösung aufgebracht waren. Hinweise auf eine höhere Spannungsrißkorrosionsempfindlichkeit des kaltverformten Materials wurden aber sowohl bei den Versuchen mit Bügelproben als auch bei den Versuchen mit Zugproben nicht festgestellt. Translated Abstract Investigations on stress corrosion cracking resistivity of stainless steels with different degree of cold straining Within the context of the elaboration of a new approval for stainless steels for civil engineering applications the question arised whether cold straining could adversely affect the resistance against stress corrosion cracking. By means of experimental tests with different stainless steels it should be clarified whether cold straining increase the stress corrosion cracking susceptibility under high chloride loads like e.g. in swimming hall atmospheres. The investigations were carried out using the high-alloyed steels 1.4462 and 1.4529. As reference material with known susceptibility against stress corrosion cracking the steel 1.4301 was used. The tests were performed using U-bent and tension specimens with saturated MgCl2 salt spots. Indications for an increase in stress corrosion cracking susceptibility of the cold drawn steel were not found. KW - Spannungsrißkorrosionsbeständigkeit KW - Nichtrostender Stahl PY - 1999 DO - https://doi.org/10.1002/(SICI)1521-4176(199905)50:5<273::AID-MACO273>3.0.CO;2-4 SN - 0947-5117 SN - 1521-4176 N1 - Sprachen: Deutsch/Englisch - Languages: German/English VL - 50 IS - 5 SP - 273 EP - 281 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-766 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mietz, Jürgen ED - Schwarz, W. T1 - Realkalisierung, Chloridentzug und Kathodischer Korrosionsschutz - Elektrochemische Verfahren zur Instandsetzung von Stahlbetonbauwerken N2 - Referat: In Stahlbeton- und Spannbetonbauwerken wird der Korrosionsschutz des Bewehrungsstahles durch die Alkalität des Beton-Porenwassers und die sich daraus ergebende Passivierung der Stahloberfläche gewährleistet. Als Folge von Mechanismen, die die Passivschicht zerstören, wie z.B. die Karbonatisierung des Betons oder das Eindringen von Chloriden, kann es zu einer Depassivierung des Stahles kommen. In diesen Fällen sind Maßnahmen notwendig, die Korrosionsreaktionen vermeiden bzw. während der Nutzungsdauer des Bauwerkes in tolerierbaren Grenzen halten. Um die Nachteile der traditionellen Sanierungsverfahren zu umgehen, sind in letzter Zeit verschiedene elektrochemische Methoden zur Instandsetzung entwickelt und erfolgreich angewendet worden. Prinzip, Anwendungsmöglichkeiten sowie Forschungsergebnisse der folgenden Verfahren, elektrochemische Realkalisierung bei Karbonatisierung, elektrochemische Entsalzung bei Chloridkontamination und Kathodischer Korrosionsschutz mit Fremdstrom werden beschrieben und diskutiert. T2 - Seminar über Korrosion von Bewehrungsstahl in Beton CY - Wien, Österreich DA - 1999-01-01 KW - Realkalisierung KW - Chloridentzug KW - Kathodischer Korrosionsschutz PY - 1999 UR - http://www.baufachinformation.de/aufsatz.jsp?ul=99079009354 SN - 3-931681-29-7 SN - 0947-6830 N1 - Sprachen: Deutsch/Englisch - Languages: German/English N1 - Serientitel: WTA-Schriftenreihe – Series title: WTA-Schriftenreihe IS - 19 SP - 165 EP - 181 PB - Aedificatio Verl. CY - Freiburg AN - OPUS4-769 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Mietz, Jürgen A1 - Isecke, Bernd ED - Page, C. ED - Bamforth, P. ED - Figg, J. T1 - Risks of failure in prestressed concrete structures due to stress corrosion cracking T2 - 4th International Symposium on Corrosion of Reinforcement in Concrete Construction CY - Cambridge, England, UK DA - 1996-07-01 KW - Betonkonstruktion KW - Korrosion KW - Streßkorrosion KW - Stahlbeton PY - 1996 SN - 0-85404-731-X SN - 0260-6291 N1 - Serientitel: Special publication / Royal Society of Chemistry – Series title: Special publication / Royal Society of Chemistry IS - 183 SP - 200 EP - 209 PB - Royal Society of Chemistry Information Services CY - Cambridge AN - OPUS4-702 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mietz, Jürgen T1 - Wasserstoffinduzierte Spannungsrißkorrosion an vergüteten Spannstählen KW - Baustoffe KW - Spannbetonbau KW - Korrosion KW - Spannungsrißkorrosion PY - 1999 SN - 0005-6650 SN - 1436-4867 N1 - Sprachen: Deutsch/Englisch - Languages: German/English VL - 74 IS - 9 SP - 403 EP - 411 PB - Springer-VDI-Verl. CY - Düsseldorf AN - OPUS4-724 LA - mul AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mietz, Jürgen A1 - Isecke, Bernd T1 - Electrochemical Rehabilitation of Corrosion affected steel reinforced concrete KW - Korrosion KW - Korrosionsschutz KW - Electrochemical realkalisation PY - 1999 SN - 1120-7302 VL - 10 IS - 1 SP - 45 EP - 59 PB - Ed. Communicazioni Tecniche CY - Modena AN - OPUS4-725 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Mietz, Jürgen T1 - Neue bauaufsichtliche Zulassung - Bauteile und Verbindungsmittel aus nichtrostenden Stählen für Schwimmhallen KW - Bauteile KW - Verbindungsmittel KW - Nichtrostender Stahl PY - 1999 SN - 0344-6492 VL - 5 SP - 29 EP - 32 PB - Krammer CY - Düsseldorf AN - OPUS4-726 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -