TY - CONF A1 - Rhode, Michael A1 - Schaupp, Thomas A1 - Muenster, C. A1 - Mente, Tobias A1 - Boellinghaus, Thomas A1 - Kannengießer, Thomas T1 - "On how to influence your results" - A review on carrier gas hot extraction parameters for hydrogen determination in welded specimens N2 - Carrier gas hot extraction (CGHE) is a commonly applied technique for determination of hydrogen in welded joints using a thermal conductivity device (TCD) for quantitative measurement. The CGHE is based on the accelerated hydrogen effusion due to thermal activation at elevated temperatures. The ISO 3690 standard suggests different specimen geometries as well as necessary minimum extraction time vs. temperature. They have the biggest influence on precise hydrogen determination. The present study summarizes the results and experience of numerous test runs with different specimen temperatures, geometries and factors that additionally influence hydrogen determination. They are namely: specimen surface (polished/as-welded), limited TCD sensitivity vs. specimen volume, temperature measurement vs. effects of PID-furnace controller as well as errors due to insufficient data assessment. Summarized, the temperature is the driving force of the CGHE. Two different methods are suggested to increase the heating rate up the reach the desired extraction temperature without changing the experimental equipment. Suggestions are made to improve the reliability of hydrogen determination depended on the hydrogen signal stability during extraction accompanied by evaluation of the recorded data. Generally, independent temperature measurement with calibration specimens is useful for further data analysis, especially if this data is used for calculation of trapping kinetics by thermal desorption analysis (TDA). T2 - IIW Annual Assembly and International Conference 2018, Meeting of Commission II-E CY - Nusa Dua, Bali Island, Indonesia DA - 15.07.2018 KW - Carrier gas hot extraction (CGHE) KW - Welding KW - ISO 3690 KW - Hydrogen KW - Experimental design PY - 2018 AN - OPUS4-45520 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Schröpfer, Dirk A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Adaption of Heat Control Concepts for Welding Stress Optimization in High-strength Steel Components N2 - High-strength structural steels from 690 MPa are increasingly applied at present. Major reasons are lightweight design trends and potential cost reductions. The structural design of welds and their manufacturing become more challenging with increasing material strength. By reasons of a higher yield ratio of these steels, the development of high residual stresses has to be avoided, since they are detrimental to the components safety and performance. Local restraint stresses and welding loads due to external shrinkage restraints occur. Frequently, this leads to critical tensile residual stresses in the weld and HAZ. In this study, influences of welding process parameters and restraint conditions on the residual stress state in welded components of high-strength steels were investigated. Multilayer GMAW tests under free shrinkage and experiments under well-defined restraints in special in-house developed testing facilities were accomplished. The tests permitted analyses of the resulting local residual stresses measured by means of X-ray diffraction and global reaction stress build-up while welding and cooling. Significant effects were found for heat control, seam configuration and restraint condition. Besides high restraints, elevated preheating and interpass temperatures lead to increased welding stresses. An adaption of welding parameters considering heat control, weld run sequence and seam configuration proved to be beneficial. T2 - 10th Conference on Trends in Welding Research CY - Tokyo, Japan DA - 11.10.2016 KW - Weld heat input KW - Residual Stress KW - High-strength Steel KW - Welding KW - Component Test PY - 2016 AN - OPUS4-37828 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Kannengiesser, Thomas T1 - Call for interested people to contribute to series of comprehensive papers on welding and joining of components for sustainable energy systems N2 - Joining and welding technologies are of high importance for the manufacturing of components and parts used in sustainable energy generation, conversion, and transport. In that connection, offshore and on-shore installed wind turbines are of high interest for the generation of electrical energy as well as photo-voltaic systems (solar cells). The electricity can be either directly transported or conversed via power-to-gas e.g., to hydrogen. In that scope, electrolyzer up to MW-range are of interest as well as the conver-sion back to electricity via fuel cells. In addition, hydrogen is a key element of the decarburization of in-dustries as well as the mobility sector encompassing sea, air and land transportation driven by hydrogen or its derivates. Well-known examples cover the direct reduction of iron ore to replace the conventional blast furnace process up to gas turbines or fuel cells for home-end use. All mentioned technologies re-quire reliable components, which are to a high extend dependent on joining and especially welding pro-cessing of materials. Especially, the (petro-) chemical industry has many years of experience with both materials used in hydrogen applications. The challenge is e.g., the transition to mass production of sys-tem components of electrolyzers/fuel cells and for distribution grids. At this point, the scalability of cur-rently applied joining processes often limits the economic efficiency, whereas especially laser welding or additive manufacturing will be of high interest. In that connection, it is very important to provide answers by joint research of universities, institutes, and industrial companies. Very often, solutions are already available and “just” have to be investigated and adapted for the new application, like repair welding of NG pipelines. For that reason, we want to set up a series of comprehensive papers with the aforementioned title. The idea is to get an in-depth but manageable overview of the importance of joining technologies in sustaina-ble energy generation, conversion, and transport encompassing current processes, limitations, and fur-ther perspectives. In that connection, the additive manufacturing is gaining more and more attention. If applicable, current challenges in the adaption or creation of new standards/regulations shall be addressed. T2 - IIW Intermediate Meeting, Com. II-A CY - Incheon, Republic of Korea DA - 12.03.2024 KW - Hydrogen KW - Welding KW - Comprehensive study KW - Component manufatcturing KW - Additive manufacturing PY - 2024 AN - OPUS4-59676 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Czeskleba, Denis A1 - Kannengiesser, Thomas T1 - Combined effect of heating rate and restraint condition on stress relief cracking susceptibility during PWHT of thick-walled Cr-Mo-V steel submerged arc welded joints N2 - Contemporary steels creep-resistant steels like the 13CrMoV9-10 are used as thick plates e.g., for applications in hydrocrackers. The large plate thickness requires high efficiency welding processes like submerged arc welding (SAW) and a mandatory post weld heat treatment (PWHT). The PWHT-parameters stem from a combination of empirical knowledge and traditional experiments on free shrinking (FS) welds. In that connection, the formation of so-called stress-relief cracking (SRC) must be anticipated. The SRC susceptibility of a welded component is a complex combination and interaction of com-ponent specific, thermal, and metallurgical factors. Many of which have to date not been conclusively researched. For example, it is well known that SRCs develop during PWHT due to formation and growth of carbides on prior austenite grain boundaries, resulting in a significant hardness increase (secondary hardening) and toughness decrease. This leads to a high SRC susceptibility of the coarse grain heat-affected zone (CGHAZ) of the last weld bead during PWHT. This is intensified in case of high residual stresses from the component-specific, structurally induced stiffness. In combination with multi-layer welding this leads to a multiaxial stress distribution. Nonetheless, the combined effect of PWHT and high-residual stresses on the SRC formation is merely unknown. For that reason, this study presents the effect of different heating rates in conjunction with a certain component stiffness. For that reason, SAW joints of 13CrMoV9-10 steel were investigated under FS and defined external restraint condition. T2 - IIW Intermediate Meeting, Com. II-A CY - Incheon, Republic of Korea DA - 12.03.2024 KW - Stress relief cracking KW - Welding KW - Post weld heat treatment KW - Submerged arc welding KW - Cr-Mo-V steel KW - Creep-resisting steel PY - 2024 AN - OPUS4-59673 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Schroeder, Nina A1 - Kannengiesser, Thomas A1 - Kadoke, Daniel A1 - Kruse, Julius T1 - Evaluation of local strain behavior of cross-weld tensile specimens of micro-alloyed high-strength steels by digital image correlation N2 - Microalloying elements such as Nb and Ti play a decisive function in achieving the desired mechanical strength of quenched and tempered, high-strength fine-grain structural steels with a nominal yield strength ≥ 690 MPa. The current specifications for the chemical composition only provide manufacturers with upper limits. However, even minor deviations in the alloy concept can have a significant impact on the mechanical properties. Consequently, accurate prediction of weldability and the integrity of welded joints becomes difficult or even impossible due to differences in composition and the resulting microstructures. Undesirable consequences include a possible softening of the heat-affected zone (HAZ) or, conversely, hardening effects. In view of these challenges, various microalloying strategies with different Ti and Nb contents are being systematically investigated for the first time using specially developed laboratory casting alloys. Each alloying route is based on the common S690QL, maintaining both the chemical composition and the heat treatment parameters. To analyse the weldability, three-layer welds were performed using gas metal arc welding (GMAW) and critical microstructures, such as areas of the heat-affected zone (HAZ) that exhibit significant softening or hardening, were identified. The effect of the softened HAZ region on failure was evaluated using transverse tensile specimens. Digital image correlation (DIC) is used to image changes in local strains in different HAZ regions in situ. Using a specially developed mirror system, the local strains of the microstructure zones on the top and bottom of the weld are recorded simultaneously. This makes it possible to analyse how the weld seam geometry (e.g., V-seam) influences the strain gradients. In addition, the analysis of the local deformation helps to understand the effects of the softened HAZ on the global strain, the fracture constriction, the fracture position, and the overall fracture behavior. T2 - IIW Intermediate Meeting, Com. II-A CY - Incheon, Republic of Korea DA - 12.03.2024 KW - Welding KW - High-strength steel KW - Alloy concept KW - Cross-weld tensile sample KW - Mechanical properties PY - 2024 AN - OPUS4-59675 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Richter, Tim A1 - Schröpfer, Dirk T1 - HEA Processing - SURDIA - Current R&D at BAM N2 - This presentation summarizes the latest results on the BAM-Themenfeld project SURDIA on processing of high-entropy alloys (HEAs) at BAM. At first, the influence of machining by ultrasonic-assisted milling on the surface integrity is presented. Second, the weld processing by Tungsten Inert Gas (TIG) welding is presented and the results of the Friction Stir Welding (FSW), which is conducted at BAM for the first time. T2 - DFG SSP 2006 - Subgroup meeting on the synthesis and processing of CCAs/HEAs CY - Online meeting DA - 08.10.2021 KW - High-entropy alloy KW - Ultrasonic-assisted milling KW - Welding KW - Processing KW - Surface integrity PY - 2021 AN - OPUS4-53497 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Boellinghaus, Thomas T1 - Hydrogen absorption and diffusion in T24 steel weld joints and effect on mechanical properties N2 - The present contribution summarizes results obtained from experiments with low-alloyed boiler steel grades T24 (CrMoV alloy), T22 (CrMo) and thermally simulated T24 HAZ microstructure and pure weld metal. The hydrogen absorption and diffusion behavior was investigated by permeation experiments and thermal desorption analysis (TDA). The results showed significant weld microstructure influence on diffusion by hydrogen trapping. Trapped hydrogen was determined in the T24 BM at temperatures up to 120 °C compared to 75 °C in the T22. In addition, the T24 HAZ showed decreased diffusion coefficients (at room temperature) of approximately one magnitude compared to the BM. For the mechanical properties, tensile tests were conducted with electrochemically hydrogen charged specimens and compared to results obtained from slow strain rate tests (SSRT) in high-temperature water up to 200 °C. The as-welded HAZ had remarkably increased susceptibility compared to the BM already at low hydrogen concentration of 1-2 ppm. The SSRT were conducted for free corrosion and acidic environment and confirmed this behavior at elevated temperatures for both HAZ microstructures of T24 and T22. Summarized, each weld microstructure has specific diffusion coefficients and shows different susceptibility to degradation of the mechanical properties, i.e. delayed hydrogen assisted cracking or stress corrosion cracking. T2 - NACE Italia - 2nd Conference & Expo 2018 CY - Genoa, Italy DA - 28.05.2018 KW - Hydrogen KW - Stress corrosion cracking KW - Welding KW - Creep-resistant steel KW - T24 / 7CrMoVTiB10-10 PY - 2018 AN - OPUS4-45080 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Mente, Tobias T1 - Hydrogen embrittlement of steels N2 - Hydrogen assisted cracking of metals is a serious issue in the safety of components, espcially in case of welding. The current presentation gives an overview on specialized testing procedures at Department 9 including the quantitative determination of hydrogen. T2 - HYDROGENIUS BAM Joint Hydrogen Symposium CY - Online meeting DA - 06.07.2021 KW - Hydrogen KW - Embrittlement KW - Degradation KW - Carrier gas hot extraction KW - Welding PY - 2021 AN - OPUS4-53049 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Kannengießer, Thomas A1 - Schaupp, Thomas A1 - Mente, Tobias T1 - Hydrogen in weld joints - An underestimated risk? - Utilization potential of gas analytics versus safety of welded components N2 - Hydrogen was once called “the versatile embrittler” [1], which summarizes very well the effect on reduction of ductility and/or toughness in technical alloys like steel. In that connection, welding is one of the most important component fabrication technologies. During welding, hydrogen can be transferred to the weld pool from manifold sources (like contaminations, residuals at the surface, etc.). As hydrogen embrittles a material, the safety of welded components with hydrogen is always a critical issue. Weld heat input causes additional changes in the microstructure like grain growth or partial dissolution of precipitates and many more. All these things influence the mechanical properties and also represent hydrogen traps. These traps decrease the hydrogen diffusion compared to the ideal lattice. The result can be so-called delayed hydrogen assisted cracking (HAC) of the weld joint due to the significantly decreased diffusivity by trapped hydrogen. This is often an underestimated risk as those cracks can appear in the weld joint even after some days! It is essential to know about hydrogen ingress during welding and the microstructure specific hydrogen diffusion. Both are depended on weld parameter influence and the chemical composition of the base material and weld metal. For that purpose, gas analytic methods like solid-state carrier gas hot extraction (CGHE) are useful tools to: (1) identify detrimental hydrogen concentrations from weld joints, (2) binding energies from hydrogen traps by thermal desorption analysis or (3) high-temperature diffusion coefficients. Those values are extremely important for welding practice in terms of recommendations on realistic hydrogen removal heat treatment (HRHT) after welding. Considering the increasing use of “digital” experiments, the data is also needed for reliable numerical simulations of HAC process or HRHT-effectiveness. The present contribution gives an overview on the influence of hydrogen on weld joints, the necessity, methods and standards for hydrogen determination (CGHE) with the aim of fabrication of safe welded and crack-free components. [1] R. A. Oriani (1987), Corrosion 43(7):390-397. doi: 10.5006/1.3583875 T2 - 20. Tagung Festkörperanalyse - FKA20 CY - Vienna, Austria DA - 01.07.2019 KW - Hydrogen KW - Welding KW - Gas analytic PY - 2019 AN - OPUS4-48402 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rhode, Michael A1 - Mente, Tobias A1 - Steppan, Enrico A1 - Steger, Joerg A1 - Kannengießer, Thomas T1 - Hydrogen trapping in T24 steel weld joints - microstructure influence vs. experimental design effect on activation energy for diffusion N2 - In general, hydrogen assisted cracking is a result of a critical combination of local microstructure, mechanical load and hydrogen concentration. In that connection, welded microstructures of low-alloyed creep-resistant steels can show different hydrogen trapping kinetics. That influences the adsorbed hydrogen concentration as well as the diffusion itself in terms of moderate or strong trapping. A common approach to describe trapping is by the activation energy that is necessary to release hydrogen from a specific trap site. In the present study, T24 base material and weld metal were investigated. For that purpose, electrochemically hydrogen charged specimens were analyzed by thermal desorption analysis(TDA) with linear heating using a mass spectrometer. The results showed a microstructure effect on hydrogen trapping kinetics at elevated temperatures. Additionally, it is necessary to monitor the specimen temperature. A comparison between idealized temperature profile and real specimen temperature showed that the calculated activation energy varied up to a factor of two. Thus, the assigned trap character(moderate or strong) changed. In case of high temperature peaks, this effect could be more important compared to the microstructure effect itself. T2 - 70th IIW Annual Assembly, Commission II-A CY - Shanghai, People's Republic of China DA - 25.06.2017 KW - Creep resisting materials KW - Welding KW - Hydrogen diffusion KW - Thermal desorption analysis KW - Microstructure KW - Experimental design PY - 2017 AN - OPUS4-40954 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -