TY - CONF A1 - Kömmling, Anja A1 - Jaunich, Matthias A1 - Wolff, Dietmar T1 - Aging of elastomeric seals for storage casks N2 - Elastomeric seals are used in many containers, including casks for radioactive waste. However, like all polymers, elastomers are prone to aging, which leads to a loss of sealing force and the ability for recovery which can ultimately result in leakage. Therefore it is important to be able to define an end-of-lifetime criterion and to judge the lifetime of elastomeric seals. For this reason, we started an aging program on three kinds of rubbers (HNBR, EPDM, FKM), monitoring the change of properties at four different aging temperatures over extended periods up to five years. The measured data is used for lifetime prediction by applying a suitable model. T2 - WM2015 Conference CY - Phoenix, Arizona, USA DA - 15.03.2015 KW - Aging KW - Elastomer KW - Seal KW - Leakage KW - Compression PY - 2015 SN - 978-0-9828171-4-8 SP - 15080, 1 EP - 12 AN - OPUS4-33253 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Jaunich, Matthias A1 - Stark, Wolfgang A1 - Wolff, Dietmar T1 - Low temperature properties of rubber seals T2 - 9th Fall rubber colloquium CY - Hannover, Germany DA - 2010-11-03 KW - Dichtungen KW - Elastomere KW - Tieftemperaturverhalten PY - 2010 SN - 978-3-9814076-0-0 SP - 175 EP - 178 AN - OPUS4-22331 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias T1 - Ageing under Hydrogen: effects on O-ring seals N2 - In this work we present results for three typical sealing materials (EPDM, HNBR, FKM) after up to 100 days ageing at high temperature under hydrogen. To allow for a better evaluation of the occurring changes the results are compared with effects of ageing in air on the material properties. Despite the common assumption that ageing under hydrogen atmosphere is expected to be less severe for the material in com-parison to air ageing, this is not seen for every material. T2 - Technomer 2023 CY - Chemnitz, Germany DA - 09.11.2023 KW - Hydrogen KW - Ageing KW - Seal KW - Compression set PY - 2023 AN - OPUS4-58818 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias T1 - Understanding the low temperature properties of rubber seals T2 - PATRAM 2010 CY - London, England DA - 2010-10-03 PY - 2010 AN - OPUS4-21502 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Jaunich, Matthias A1 - Stark, Wolfgang A1 - Wolff, Dietmar T1 - Low temperature properties of rubber seals N2 - Rubber is widely used as sealing material in various applications. In many fields the sealing function at low temperatures is necessary. Therefore the understanding of failure mechanisms is of high importance. Rubbers are normally used above their glass-rubber transition region but the minimum working temperature limit is not defined precisely. Therefore the lower operation temperature limit of rubber seals should be determined in dependence of the material properties. The results of Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Analysis (DMA) are combined with the results of the standardized compression set according to ISO 815 respectively a modified test using the DMA equipment. N2 - Tiefentemperaturverhalten von Elastomerdichtungen Elastomere werden vielfach als Dichtungsmaterial für verschiedene Anwendungen eingesetzt. In vielen Bereichen ist die Funktion der Dichtung auch bei tiefen Temperaturen erforderlich. Daher ist das Verständnis des Versagensmechanismus von großer Bedeutung. Normalerweise werden Elastomere oberhalb ihres Glass-Gummi Übergangsbereiches eingesetzt aber die minimale Einsatztemperatur ist nicht exakt definiert. Daher ist es sinnvoll diese untere Temperatureinsatzgrenze in Abhängigkeit von den Materialeigenschaften zu bestimmen. Die Ergebnisse der DSC und der DMA werden mit den Ergebnissen des standardisierten Druckverformungsrestes nach ISO 815 und einer abgewandelten Messung mit der DMA kombiniert. KW - Sealing material KW - Elastomer KW - Compression set KW - Dynamic mechanical analysis KW - Low temperature behaviour PY - 2011 SN - 0948-3276 SN - 0022-9520 IS - 03 SP - 52 EP - 55 PB - Hüthig CY - Heidelberg AN - OPUS4-23422 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias T1 - Requirements for the use of elastomer seals in casks for final disposal of low and intermediate level waste N2 - Elastomer seals are widely used as barrier seals in containers for low and intermediate level radioactive waste and in some countries for spent fuel transportation casks. Depending on the area of use, the rubber materials have to demonstrate proper sealing performance with regard to mechanical, thermal and environmental conditions as well as irradiation during the entire operation period. In Germany the low and intermediate level radioactive waste is planned to be disposed in the Konrad repository in standardized containers. Many of these containers use an elastomer seal between lid and container body. Depending on the radiactive inventory and a possible containment of the waste in inner barrels and/or concrete structures, such containers may require a specific leak tightness. In such cases, specified leakage rates are shall not be exceeded by the the seals to keep potential activity releases from the inventories well below defined limits. Generally, all waste containers have to fulfill the waste acceptance criteria for the Konrad repository as defined by the reports BfS SE-IB-29/08 and SE-IB-30/08. From these criteria several requirements for seal performance are derived. The seals have to: - ensure full functionality until final container disposal, - maintain its function in case of a thermal or mechanical accident, - ensure encapsulation also at -20 °C. This combination of requirements is challenging especially as a seal exchange, which is typical for many other applications, is hardly possible and thus a sound understanding of how to perform safety evaluation of containers is required. Therefore BAM has initiated investigations on elastomer seal behaviour. This work focuses on low temperature behaviour and sealing performance concerning static conditions as well as partial loss of compression and ageing of elastomer seals. Concerning ageing, property changes caused by long-term thermooxidative conditions as well as gamma irradiation are investigated. This contribution presents an overview and explanation of the aims of the ongoing research and gives an update of the most relevant results. T2 - 13th International Symposium "Conditioning of Radioactive Operational & Decomissioning Wastes" CY - Dresden, Germany DA - 22.03.2017 KW - Disposal KW - Konrad repository KW - Seal KW - Ageing PY - 2017 AN - OPUS4-39868 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias T1 - Investigations of Aged Metal Seals for Interim Storage N2 - The storage of spent fuel and high level radioactive waste in Germany is performed in interim storage containers with double lid systems. The lids are bolted and equipped with metal seals (e.g. Helicoflex®) to ensure the safe enclosure of the inventory. The used metal seals have a layered structure consisting of three components as can be seen schematically in the cross-sectional view in Fig. 1. In the center a helical spring is positioned that is surrounded by two C-shaped jackets and is mainly responsible for generation of the required restoring force. The inner jacket is made of stainless steel and homogenizes the restoring force of the helical spring. The outer jacket is made of silver or aluminium which both are soft metals in comparison to the contact partners (lid and container body). During bolting of the lid to the container body the seal is compressed. The generated restoring force of the helical spring causes a plastic deformation of the outer jacket and adapts to the surfaces of the lid and the container body. Hence, leakage paths are closed and the sealing function is generated. Typical durations for existing interim storage licenses in Germany are 40 years, but it can be expected that they have to be extended to longer periods as a final repository will not be available before the end of the running licence periods. This extension of license periods requires a solid understanding of the long-term behaviour of the seals under storage conditions. To meet this challenge long-term investigations have been started at Bundesanstalt für Materialforschung und –prüfung (BAM) in 2009. These tests focus on seals assembled in test flanges which are stored at temperatures ranging from room temperature to 150 °C for accelerated ageing. The aged seals are tested repeatedly after certain ageing steps and the leakage rate as indicator for sealing performance, the remaining seal force, and the useable resilience upon decompression are determined. In the poster an update on the performed investigations in respect to earlier publications (Grelle et al. 2019, Goral et al. 2023) will be given and the implications of the results for resilient long term safety will be presented. Additionally, a focus will be laid on the currently planned further investigations and the question “What is additionally needed for evaluation of an interim storage period extension in regard to the used metal seals?” will be addressed. T2 - safeND2023: Forschungssymposium des BASE CY - Berlin, Germany DA - 13.09.2023 KW - Metal seal KW - Interim storage KW - Ageing PY - 2023 AN - OPUS4-58568 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias T1 - Comparison of Ageing Behavior of O-Ring Seals Under Hydrogen and Air N2 - Elastomeric seals are essential components in the infrastructure which prevent leakage of gas and ensure proper function of technical devices and are therefore highly safety relevant. For proper function a remaining resilience and tolerance to pressure changes is required. The ageing of elastomers is an undesirable but inevitable process leading to a limited lifetime of rubber products such as seals. Independent of the application, as e.g. automotive, piping or container applications, a long lifetime or at least a timely exchange of a seal before occurrence of critical failure is desired. Hydrogen is a key element for the energy turnaround and therefore the compatibility of seals with hydrogen is essential. In addition to the effect of hydrogen uptake and release, which might also cause destructive effects such as rapid gas decompression, ageing at high temperature under hydrogen atmosphere is of interest too. Most of the existing work is addressing the performance of new materials and comprises only very limited investigations concerning long-term use and the behaviour of aged materials in contact with hydrogen. As ageing can lead to substantial changes of material properties, it must be evaluated whether these changes are beneficial or deteriorating for the component function. In this work we present and compare results of the characterization of three sealing materials (EPDM, HNBR, FKM) after ageing at high temperature under hydrogen and air. Despite the common assumption that ageing under hydrogen atmosphere should be less severe for the material in comparison to air ageing, this is not the case for every material. T2 - ASME PVP2025, Pressure Vessels & Piping Conference CY - Montreal, Canada DA - 20.07.2025 KW - Aging KW - Seal KW - Compression set KW - Atomic force microscopy PY - 2025 AN - OPUS4-63888 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias T1 - Elastomerdichtungen für Wasserstoffanwendungen - Vergleich des Alterungsverhaltens in Luft und Wasserstoff N2 - In diesem Beitrag soll ein Fokus auf das Alterungsverhalten von Elastomerdichtungen unter Wasserstoff gelegt werden. Hierfür wurden Untersuchungen bei einem mittleren Wasserstoffdruck über Alterungszeiten von bis zu 100 Tagen durchgeführt. Das Alterungsverhalten wird im Vergleich der Alterungseffekte unter thermooxidativen Bedingungen betrachtet und bewertet. Die Annahme, dass der Alterungseffekt unter Wasserstoff stets weniger ausgeprägt ist als an Luft bestätigt sich nicht durch die Ergebnisse. T2 - 4. O-Ring-Forum der Firma ISGATEC CY - Bad Schönborn, Germany DA - 15.05.2025 KW - Wasserstoff KW - Dichtung KW - Thermische Alterung KW - Elastomer PY - 2025 AN - OPUS4-63135 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias T1 - Können UF-Formmassen überhärten? Die Aussage des Kochversuchs! T2 - 1. Wildauer Duromer-Tagung CY - Wildau, Germany DA - 2008-03-11 PY - 2008 AN - OPUS4-16730 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Jaunich, Matthias A1 - Stark, Wolfgang A1 - Wolff, Dietmar T1 - Comparison of low temperature properties of different elastomer materials investigated by a new method for compression set measurement N2 - The method for the determination of compression set values with a Dynamic Mechanical Analysis (DMA) setup at low temperatures, which was presented previously, allows a much faster and readily automated procedure than the standardized compression set test according to ISO 815-2. This method is applied to a series of different elastomeric materials that are commonly used for sealing applications. The results of the compression set test are compared with results from thermal analysis to allow an in depth comparison of the material behaviour at low temperatures. Furthermore, a comparison between two EPDM materials is presented. These materials show very similar properties determined by thermo analytical methods such as Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Analysis (DMA) but differ clearly in their compression set behaviour. This comparison shows the importance and value of information of the compression set test in addition to thermal analysis to judge the behaviour of sealing materials and confirms the relevance of the new compression set test method for the investigation of low temperature properties of elastomers. KW - Sealing material KW - Elastomer KW - Compression set KW - Dynamic mechanical analysis KW - Low temperature behaviour PY - 2012 DO - https://doi.org/10.1016/j.polymertesting.2012.07.016 SN - 0142-9418 VL - 31 IS - 8 SP - 987 EP - 992 PB - Elsevier Science CY - Amsterdam [u.a.] AN - OPUS4-26538 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -