TY - CONF A1 - Jaunich, Matthias T1 - An update on metal seal tests performed at BAM and implications for interim storage N2 - The investigation of the long-term performance of sealing systems employed in containers for radioactive waste and spent nuclear fuel is one research focus area for division 3.4 “Safety of Storage Containers” at the Bundesanstalt für Materialforschung und -prüfung. Metallic seals are in use in interim storage casks for used fuel and high active waste. Their change in performance over time is of high importance for maintaining safe enclosure. Therefore, investigations on these systems were started at BAM to get a general understanding of the relevant processes. Our investigations comprise investigations on different parameters which influence the seal performance and the main part is focussed on the time and temperature dependent behaviour. In this contribution an update on the performed tests and their respective results will be given in respect to the overview presented in 2020. The understanding of the long-term behaviour of the sealing systems and the performance evaluation during interim storage and subsequent transportation are our goals. T2 - SEDS-Workshop: Sicherheit der längerfristigen trockenen Zwischenlagerung CY - Garching, Germany DA - 15.05.2024 KW - Metal seals KW - Ageing KW - Leakage rate KW - Creep PY - 2024 AN - OPUS4-60640 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias T1 - Tests of metallic seals at Bam 3.4 performed over more than 15 years N2 - The investigation of the long-term performance of sealing systems employed in containers for radioactive waste and spent nuclear fuel is one research focus area for division 3.4 “Safety of Storage Containers” at the Bundesanstalt für Materialforschung und -prüfung (BAM) in Germany. The time dependant behaviour of metallic seals, which are employed in interim storage casks for used fuel and high active waste, is of high importance for ensuring safe enclosure. Therefore, investigations on these systems were started at BAM to get a general understanding of the relevant processes. Our investigations comprise investigations on different parameters which influence the seal performance and the main part is focussed on the time and temperature dependent behaviour. In this contribution an overview of the performed tests and their respective results will be given. T2 - 5th sealing workshop by Maestral CY - Avignon, France DA - 05.11.2024 KW - Metal seal KW - Aging KW - Interim storage PY - 2024 AN - OPUS4-62048 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias T1 - Aging investigations of metal seals used in containers for interim storage of spent fuel N2 - In Germany dual purpose containers with double lid systems are used for the transport and storage of spent fuel and high level radioactive waste. The bolted lids are equipped with metal seals (e.g. Helicoflex®) to ensure the safe enclosure of the inventory for the required time period. The used metal seals have a layered structure consisting of three components. In the center a helical spring is positioned that is surrounded by two C-shaped jackets. The helical spring is mainly responsible for generation of the required restoring force. The inner jacket is made of stainless steel and homogenizes the restoring force generated by the helical spring. The outer jacket is made of silver or aluminum. Both metals are soft in comparison to the contact partners (lid and container body). During bolting of the lid the seal is compressed between lid and container body. The generated restoring force of the helical spring causes a plastic deformation of the outer jacket which adapts to the surfaces of the lid and the container body. Hence, leakage paths are closed and the sealing function is caused. Typical durations for existing interim storage licenses in Germany are 40 years, but due to the challenges in selection and construction of a final repository it can be expected that they have to be extended to longer periods. An extension of license periods requires knowledge of the long-term behavior of the seals. To meet this challenge long-term investigations have been started at Bundesanstalt für Materialforschung und –prüfung (BAM) in 2009. These tests focus on seals assembled in test flanges which are stored at temperatures ranging from room temperature to 150 °C for accelerated aging. The aged seals are tested repeatedly after certain aging steps and the performance is evaluated in respect to the leakage rate, the remaining seal force, and the useable resilience upon decompression. In this contribution an update on the running investigations in respect to earlier publications (Grelle et al. 2019, Goral et al. 2023) will be given and the implications of the results for resilient long-term safety will be presented. New activities will be addressed and their expected outcome be discussed. T2 - PVP2024, Pressure Vessels & Piping Conference CY - Bellevue, WA, USA DA - 29.07.2024 KW - Metal seal KW - Aging KW - Interim storage PY - 2024 AN - OPUS4-61355 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Zaghdoudi, M. A1 - Kömmling, Anja A1 - Jaunich, Matthias A1 - Wolff, Dietmar ED - Altenbach, H. ED - Hitzler, L. ED - Johlitz, M. ED - Merkel, M. ED - Öchsner, A. T1 - Analysis of Heterogeneous Ageing of HNBR O-Rings N2 - Abstract Hydrogenated nitrile butadiene rubber (HNBR) elastomer was thermo-oxidatively aged at different temperatures up to 150 °C. Fourier transform infrared spectroscopy (FTIR), compression stress relaxation (CSR) and international rubber hardness degree (IRHD) microhardness were used to characterise the chemo-mechanical changes of HNBR O-rings during thermo-oxidative ageing. FTIR shows the development of carbonyl, methyl and ester groups but the nitrile content was not affected by ageing. The effect of sample geometry during CSR was investigated. CSR data were converted through integrated kinetic laws. The conversion has proven its sensibility to detect heterogeneous ageing. This was confirmed by the IRHD measure-ments across the section of O-rings. The influence of compression during ageing was assessed through IRHD measurements across the section of compressed and uncom-pressed aged O-rings. The DLO effect was more pronounced in compressed O-rings. By applying the model of Wise et al., theoretical IRHD and oxidation profiles were determined on the basis of IRHD experimental data of compressed O-rings. Good agreements between the experimental and the theoretical IRHD profiles in the core region were obtained. However, near the edge, the theoretical IRHD values were overestimated. KW - Ageing KW - Rubber seals KW - Stress relaxation KW - Modelling PY - 2024 SN - 978-3-031-49042-2 DO - https://doi.org/10.1007/978-3-031-49043-9 SN - 1869-8433 SP - 331 EP - 348 PB - Springer Nature CY - Cham, Switzerland AN - OPUS4-59769 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zaghdoudi, M. A1 - Kömmling, Anja A1 - Jaunich, Matthias A1 - Wolff, Dietmar T1 - Oxidative ageing of elastomers: experiment and modelling N2 - During an extensive test programme at the Bundesanstalt für Materialforschung und prüfung, material property changes of EPDM O-rings were investigated at different ageing times and two ageing temperatures of 125 ◦ C and 150 ◦ C. To exclude possible diffusion-limited oxidation (DLO) effects that can distort the data, IRHD microhardness measurements were taken over the cross section of compressed O-rings. Continuous stress relaxation measurements were taken on samples free of DLO effects. The additional effect of physical processes to irreversible chemical ones during a long-term thermal exposure is quantified by the analysis of compression set measurements under various test conditions. By combining the different experimental methods, characteristic times relative to the degradation processes were determined. On the basis of experimental data, a microphysically motivated model that takes into account reversible and irreversible processes was developed. The parameter identification strategy of the material model is based on our experimental investigations on homogeneously aged elastomer O-rings. The simulated results are in good agreement with the experiments. KW - Compression Set KW - Compression stress relaxation KW - Modelling KW - Ageing KW - Microhardness PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-609332 DO - https://doi.org/10.1007/s00161-022-01093-9 VL - 36 SP - 289 EP - 297 PB - Springer Nature AN - OPUS4-60933 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -