TY - JOUR A1 - Dreßler, Martin A1 - Nofz, Marianne A1 - Saliwan Neumann, Romeo A1 - Dörfel, Ilona A1 - Griepentrog, Michael T1 - Sol-gel derived alumina layers on nickel-base superalloy Inconel-718 (IN-718) JF - Thin solid films N2 - Modified Yoldas sols can be used to prepare crack-free well adherent layers on different substrate materials such as soda–lime glass, corundum and metal (IN-718). These layers having thicknesses of 0.6 µm are strain tolerant and withstand thermal cycling between 810 °C and room temperature. Introducing alpha-Al2O3 filler particles into modified Yoldas sols allows the preparation of thicker layers of 1.6 µm, which as well can be thermally cycled without noticeable delaminations. Chemical bonding seems to be the predominant layer bonding mechanism. KW - Sol-gel KW - Alumosol KW - Filler particles KW - Inconel-718 KW - Scanning electron microscopy PY - 2008 DO - https://doi.org/10.1016/j.tsf.2008.08.124 SN - 0040-6090 VL - 517 IS - 2 SP - 786 EP - 792 PB - Elsevier CY - Amsterdam AN - OPUS4-18263 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dreßler, Martin A1 - Nofz, Marianne A1 - Dörfel, Ilona A1 - Saliwan Neumann, Romeo T1 - Influence of sol-gel derived alumina coatings on oxide scale growth of nickel-base superalloy Inconel-718 JF - Surface and coatings technology N2 - Alumina coatings with differing phase compositions were deposited on Inconel-718 (IN-718) Ni-base superalloy substrates using sol–gel processing. Mass gain measurements served for studying the oxidation behavior of coated metal surfaces if exposed to 800°C and 900°C for up to 4000 h in static air. Itwas found, that alumina coatings significantly reduce the oxidation related mass gain of IN-718 even after heating to 900°C for 4000 h. Transmission electron microscopy (TEM) studies revealed diffusion of elements from the metal substrate (IN-718) into the alumina coatings and — to a much lower degree — from the coating into the substrate. These diffusion processes are greatly influenced by the phase composition of the coatings, especially by the presence of alpha-alumina. KW - Oxide scale growth KW - Inconel-718 KW - Alumina coating KW - TEM PY - 2008 DO - https://doi.org/10.1016/surfcoat.2008.07.018 SN - 0257-8972 VL - 202 SP - 6095 EP - 6102 PB - Elsevier Science CY - Lausanne AN - OPUS4-17857 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nofz, Marianne A1 - Sojref, Regine A1 - Dreßler, Martin A1 - Hünert, Daniela A1 - Dörfel, Ilona A1 - Saliwan Neumann, Romeo T1 - Sol-gel alumina coatings for high-temperature corrosion protection of Ni-base alloy SC16 in water vapour containing atmosphere JF - Interceram N2 - Alumosols in combination with well dispersed corundum were successfully used to form up to 2.5 ìm thick coatings on the Ni-base alloy SC16. These coatings withstood heat treatments at 700 °C in a water vapour containing atmosphere. The heat treatment caused formation of delta-alumina in the coating and diffusion of chromium and titanium into the coating. KW - Alumina KW - Coating KW - Sol-gel KW - Corrosion KW - Protection PY - 2009 SN - 0020-5214 VL - 58 IS - 4 SP - 192 EP - 195 PB - DVS-Verl. CY - Düsseldorf AN - OPUS4-19726 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dreßler, Martin A1 - Nofz, Marianne A1 - Dörfel, Ilona A1 - Saliwan Neumann, Romeo T1 - Diffusion of Cr, Fe, and Ti ions from Ni-base alloy inconel-718 into a transition alumina coating JF - Thin solid films N2 - Heat treating metals at high temperatures trigger diffusion processes which may lead to the formation of oxide layers. In this work the diffusion of Cr, Fe and Ti into an alumina coating applied to Inconel-718 is being investigated. Mass gain measurements, UV–vis spectroscopy and transmission electron microscopy were applied in order to study the evolution of the diffusion process. It was found that mainly Cr as well as minor amounts of Fe and Ti are being incorporated into the alumina coating upon prolonged heat treatment at 700 °C. It could be shown that alumina coatings being void of Cr have the same oxidation related mass gain as uncoated samples. However, incorporation of Cr into the alumina coating decreased their mass gain below that of uncoated substrates forming a Cr oxide scale only. KW - Diffusion KW - UV–vis spectroscopy KW - Transmission electron microscopy KW - Alumina coatings KW - Sol-gel deposition PY - 2012 DO - https://doi.org/10.1016/j.tsf.2012.02.006 SN - 0040-6090 VL - 520 IS - 13 SP - 4344 EP - 4349 PB - Elsevier CY - Amsterdam AN - OPUS4-25830 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -