TY - CONF A1 - Hübner, Martin A1 - Reichel, Levin A1 - Schröpfer, Dirk A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Modern welding processes for optimising repair welds on high strength offshore steels N2 - The successful energy transition in Germany will require offshore wind turbines with outputs >10 MW in the future. To achieve these high outputs, turbines far from coast are required with large subsea jacket structures (30 m up to 50 m) and tall towers (up to 200 m). High-strength steels with a yield strength up to 500 MPa and wall thicknesses up to 150 mm are increasingly being used for these structures. This plac-es high demands on welding manufacturing, especially for high-strength offshore steels. During the manu-facturing process detected defects by NDT require localized repair of welds by gouging and rewelding. Due to a lack of investigations, there are no repair concepts and information in standards and guidelines, par-ticularly for high-strength thick plate joints made of high-strength offshore steels. However, these are ur-gently needed to enable manufacturers, especially SMEs, to carry out safe and economical repairs. There-fore, BAM started the FOSTA project P1629 (IGF 01IF22746N) to investigate the stress-optimized repair (local gouging and welding) of high-strength thick plate joints made of offshore grades in the yield strength range off 355 to 460 MPa and similar weld metal with controlled high-performance GMAW pro-cesses and optimized narrow gouging grooves. The experimental analyses take into account the complex interaction of process, material, and design-related influences on the formation of weld induced stresses and the special microstructure of high-strength fine-grain structural steels. Welding-related material degra-dation and crack-critical residual tensile stresses need to be avoided to ensure high component safety and performance. A reduction in residual stress in the presence of high restraint conditions can be achieved by adapted heat control (if no disassembly measures are possible). The repair process involves manual thermal gouging, which allows the groove configuration to be modi-fied. Modern welding processes using high frequency arc control provide deep root penetration and focused energy input capable of welding narrow seams. A comparison was made between the traditional weld con-figuration with a wide 45° groove and transition arc welding and a narrow 30° groove with modern welding process. Even in the case of free shrinkage specimens, the narrow groove weld exhibits a significant reduc-tion of residual stresses, cf. Figure 1, especially in the HAZ and toward the adjacent base material. This can be attributed to the lower weld metal volume needed and the reduction of heat input per layer due to the controlled arc process. For the purposes of this comparison, the same weld seam build-up (but different number of layers) has been applied to both seam configurations. Note that in industrial application (manu-al welding), the wider groove would be welded with several off-center weld beads with conventional weld-ing process. In this analysis this would cause asymmetric effects regarding the residual stress state, diffi-cult to compare to each other. Component-related welding experiments on special testing equipment, adapted process and heat control concepts along with variable groove configurations will be developed and recommendations for guidelines elaborated. This is the prerequisite for fully utilizing the strength potential of high-strength steels and making a valuable contribution to the energy transition in Germany, especially for steel-processing SMEs. T2 - IIW Intermediate Meeting CII CY - Trollhättan, Sweden DA - 10.03.2025 KW - Repair welding KW - Gouging KW - Residual stress KW - Offshore wind turbines KW - High-strength steels PY - 2025 AN - OPUS4-62743 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Martin A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Dittmann, Florian A1 - Varfolomeev, Igor T1 - Untersuchung der Ermüdungsfestigkeit von LTT-geschweißten Längssteifen mit variierender Nahtausführungen N2 - Low Transformation Temperature (LTT) Schweißzusätze erzeugen während der Abkühlung Druckeigenspannungen in die Schweißnaht und Wärmeeinflusszone durch eine Volumenexpansion, wodurch die Ermüdungsfestigkeit erhöht werden kann. Um das Potential dieser neuartigen Schweißzusätze besser zu quantifizieren, wurden konventionelle Längssteifen als Probenkörper verwendet, welche an den Stirnseiten mit einer LTT-Zusatznaht geschweißt wurden. Durch Variation der Schweißparameter konnten unterschiedliche Nahtformen realisiert werden. Es konnte, je nach Nahtausführung, eine Erhöhung der Ermüdungsfestigkeit bei 2 Millionen Lastwechsel von 64 MPa bis 100 MPa in Gegensatz zu konventionellen Proben festgestellt werden. Somit sind LTT-Zusätze grundsätzlich geeignet, um die Ermüdungsfestigkeit zu erhöhen. T2 - Frühjahrssitzung 2025 des Fachausschusses Eigenspannungen der AWT CY - Karlsruhe, Germany DA - 07.04.2025 KW - LTT (Low Transformation Temperature) KW - Eigenspannungen KW - Ermüdungsfestigkeit KW - Aufmischung PY - 2025 AN - OPUS4-62930 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Martin A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Dittmann, Florian A1 - Varfolomeev, Igor T1 - Wechselwirkung zwischen Nahtgestaltung und Ermüdungsfestigkeit in LTT-geschweißten Längssteifen N2 - Schweißzusätze mit niedriger Martensitstarttemperatur (Low Transformation Temperature, LTT) induzieren während der Abkühlphase infolge einer volumeninduzierten Martensitumwandlung Druckeigenspannungen in der Schweißnaht sowie in der angrenzenden Wärmeeinflusszone (WEZ). Diese Spannungen können zu einer signifikanten Erhöhung der Ermüdungsfestigkeit führen. Zur quantitativen Bewertung des Potenzials dieser innovativen Werkstoffe wurden konventionelle Längssteifen als Versuchsproben herangezogen, bei denen an den Stirnseiten Schweißnähte unter Verwendung von LTT-Zusatzwerkstoffen appliziert wurden. Durch gezielte Variation der Schweißparameter konnten unterschiedliche Nahtgeometrien realisiert werden. In Abhängigkeit von der Nahtausführung zeigte sich bei einer Belastungszahl von 2 Millionen Zyklen eine Steigerung der Ermüdungsfestigkeit im Bereich von 64 MPa bis 100 MPa im Vergleich zu Referenzproben mit herkömmlichen Schweißzusätzen. Die Ergebnisse belegen, dass der Einsatz von LTT-Schweißzusätzen grundsätzlich geeignet ist, die Ermüdungsfestigkeit geschweißter Strukturen zu verbessern. T2 - Din Sitzung: Gemeinschaftsarbeitsausschuss NAS/NMP, Zerstörende Prüfung von Schweißverbindungen CY - Online meeting DA - 20.03.2025 KW - LTT (Low Transformation Temperature) KW - Eigenspannungen KW - Ermüdungsfestigkeit KW - high-strength steels PY - 2025 AN - OPUS4-62929 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Martin T1 - Hybrider Einsatz von LTT-Schweißzusatzwerkstoffen N2 - LTT (Low Transformation Temperature) - Schweißzusätze stellen eine Alternative zur Verfügung, um die Schwingfestigkeit in Schweißnähten zu erhöhen. Ziel dieses Vortages ist es zum einem die Thematik der LTT - Schweißzusätze, insbesondere in hybrider Ausführung zu erläutern, Zum anderen werden die Ergebnisse der Vorversuche präsentiert. T2 - BMDK CY - Magdeburg, Germany DA - 25.10.2023 KW - LTT (Low Transformation Temperature) KW - Martensitstarttemperatur KW - Baustähle KW - Eigenspannungen KW - Aufmischung PY - 2023 AN - OPUS4-58690 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Martin T1 - Residual stress reduction using LTT welding consumables with focus on the weld geometry N2 - Low Transformation Temperature (LTT) welding consumables represent an innovative approach to realize compressive residual stress in weld and HAZ. LTT welding consumables use the volume-expanding martensitic phase transformation near room temperature to generate compressive residual stress during cooling. This article focusses on the weld geometry of LTT welding consumables and their influence on residual stress reduction. For this purpose, LTT layers were additionally applied to the front sides of conventionally welded longitudinal stiffeners. By varying parameters such as offset and welding speed, different weld geometries could be realized. These were analyzed for geometric parameters, chemical composition and residual stress using X-ray diffraction and fatigue testing. While the chemical composition was only slightly influenced by parameters changes, a clear influence was observed regarding to weld geometry and residual stress. The conventionally weld was characterized by tensile residual stress of ≈350 MPa at the weld toe, the additional LTT weld bead exhibits compressive and tensile residual stress of ≈-150MPa to ≈+150MPa depending to the parameter variation. T2 - International Institut of Welding 2024 CY - Rhodos, Greece DA - 07.07.2024 KW - LTT (Low Transformation Temperature) KW - Residual stress KW - Fatigue strength KW - High-strength steels PY - 2024 AN - OPUS4-60825 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Martin T1 - Einfluss der Nahtgeometrie auf den Eigenspannungsabbau unter Verwendung von Low Transformation Temperature (LTT) – Schweißzusätzen N2 - Low Transformation Temperature (LTT)-Schweißzusätze stellen einen innovativen Ansatz zur Erhöhung der Ermüdungsfestigkeit geschweißter Konstruktionen dar. LTT-Schweißzusätze zeichnen sich durch eine martensitische Phasenumwandlung nahe der Raumtemperatur aus, welche Druckeigenspannungen in der Schweißnaht und der Wärmeeinflusszone (WEZ) generieren. Dieser Vortrag fokussiert sich auf die gezielte Einbringung zusätzlicher LTT-Lagen an ermüdungskritischen Stellen von konventionell geschweißten Verbindungen. Dies ermöglicht eine ökonomische Anwendung, ohne dass die Schweißnahtintegrität zu stark beeinflusst wird. Die Auswirkungen zusätzlicher LTT-Lagen wurden anhand geschweißter Längssteifen aus hochfestem Stahl hinsichtlich der chemischen Zusammensetzung und der Eigenspannungen untersucht. Unter Variation der Schweißgeschwindigkeit und Abstand zur konventionellen Naht konnten 3 unterschiedliche Nahtausführungen des Chrom-Nickellegierten LTT-Zusatzes bewertet werden. Die chemische Zusammensetzung wurde mittels OES-Analysen untersucht. Dabei stellte heraus, dass die Aufmischung in allen Varianten sehr ähnlich war trotz teils unterschiedlicher LTT-Volumina. Härtebestimmungen ergaben in allen 3 Varianten eine ähnliche Härte. Daraus lässt sich annehmen, dass die Martensitstarttemperatur bei allen Nahtvarianten ähnlich ist. Röntgenografische Eigenspannungsmessungen belegen, dass die Eigenspannungen am versa-genskritischen Nahtübergang bei Einsatz von LTT-Schweißzusätzen deutlich abgesenkt werden. Während die konventionelle Schweißnaht Zugeigenspannungen von ca. 350 MPa aufweist, können an den LTT-Nähten teilweise Druckeigenspannungen von bis zu -150 MPa nachgewiesen werden. Je höher der Abstand zur konventionellen Naht und je größer das eingebrachte LTT-Volumen ist, umso stärker sind die Eigenspannungsreduzierungen am Nahtübergang. Da in allen 3 Varianten eine ähnliche Martensitstarttemperatur angenommen werden kann, ist somit die Geometrische Komponente der LTT-Zusatzlage ein entscheidender Faktor für die Eigenspannungsreduzierung. T2 - AWT FA 13 CY - Wolfsburg, Germany DA - 19.03.2024 KW - Chemische Zusammensetzung, KW - LTT KW - Nahtgeometrie KW - Eigenspannungen PY - 2024 AN - OPUS4-60135 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Martin T1 - Hybrid use of LTT welding filler N2 - Through a hybrid use of Low Transforamtion Temperature welding filler, fatigue strength of welds should be increased. Through the hybrid use of LTT welding filler the Integrity of a weld will be less affected. By creating several variants of LTT weld geometries an idea of the optimum residual stress reduction is given. T2 - European Academy of Wind Energy (EAWE) CY - Hannover, Germany DA - 06.09.2023 KW - Welding KW - LTT (Low Transformation Temperature) KW - Fatigue strength KW - High-strength steels KW - Residual stress PY - 2023 AN - OPUS4-58362 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Martin A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Influence of the weld geometry on the residual stress reduction using low transformation temperature welding consumables N2 - Low transformation temperature (LTT) welding consumables offer an innovative approach to increase the fatigue strength of welded high-strength steel structures. LTT welding consumables are characterized by a martensitic phase transformation near ambient temperature, which generates compressive residual stresses in the weld and heat affected zone (HAZ). The aim is to achieve a weld geometry, which generate high compressive residual stresses at the fatigue crack critical weld toe. Longitudinal stiffeners were gas metal arc welded using a conventional welding consumable; the base material was a high strength steel S700M. A chromium-nickel alloyed LTT consumable was deposit subsequently just on front sides of the stiffeners. Different welding parameters led to varying cross sections of the weld. The residual stresses were determined using X-ray diffraction (XRD) in the crack critical HAZ. When using only the conventional, the HAZ is characterized by high tensile residual stresses. The additional application of the LTT alloy leads to a significant reduction of the tensile residual stresses. Depending on the weld geometry, even compressive residual stresses can be observed at the weld toe T2 - ECRS 2024 CY - Prague, Czech Republic DA - 03.06.2024 KW - LTT (Low Transformation Temperature) KW - Residual stress reduction KW - Fatigue PY - 2024 AN - OPUS4-60305 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Martin A1 - Kromm, Arne A1 - Kannengießer, Thomas A1 - Dittmann, Florian A1 - Varfolomeev, Igor T1 - Effect of weld design on fatigue strength of welded components using LTT filler materials N2 - Low transformation temperature (LTT) filler metals are an innovative approach to reduce tensile residual stress in weld seams and the surrounding heat affected zone (HAZ). The reduced tensile stress leads to an improvement in the fatigue strength of welded components. LTT filler metals are characterized by a reduced martensite start temperature (Ms), which is close to room temperature because of their chemical composition. This paper focuses on the hybrid use of LTT filler metals, where the LTT filler is applied as an additional layer to conventional welds on fatigue-critical spots. Conventional gas metal arc welded longitudinal stiffeners are used as specimens and at the face ends of the stiffeners, a second LTT layer was added with various weld modifications. These modifications were achieved by changing the welding parameters such as welding speed and offset to the first layer. These samples were used to analyze shape, dilution and resulting Ms, residual stress and fatigue strength. The dilution and dilatometer verified Ms did not change significant, although the surface of the 2nd LTT weld seam was varying clear with each modification. However, the weld modification had a significant effect on the residual stress state and the fatigue strength. The X-ray determined residual stress in the HAZ became lower when the weld toe of the LTT layer was further away from the stiffener. The Fatigue strength is clearly dependent on the residual stress state. The lower the residual stress at weld toe, the higher the fatigue strength. All samples with LTT weld exhibit significantly higher fatigue strength values than conventionally single and double-layer welded samples. The results show that on the one hand LTT filler metals increase the fatigue strength, and on the other hand the impact of LTT fillers materials is not restricted to the dilution and Ms, the shape of the weld seam must also be considered. T2 - IIW Intermediate Meeting CII CY - Trollhättan, Sweden DA - 10.03.2025 KW - LTT (Low Transformation Temperature) KW - Residual stress reduction KW - Fatigue strength KW - High-strength steels KW - Welding PY - 2025 AN - OPUS4-62708 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Martin A1 - Kromm, Arne A1 - Kannengießer, Thomas T1 - Eigenspannungsabbau mittels LTT – Schweißzusätzen unter Berücksichtigung der Nahtgeometrie N2 - Low Transformation Temperature (LTT)-Schweißzusätze sind ein innovativer Ansatz, um Eigenspannungen in Schweißnähten zu reduzieren. Dieser Vortrag behandelt neben den Einfluss der LTT-Schweißzusätze auch deren Naht-Ausführungen. Die unterschiedlichen LTT-Nahtgeometrien haben einen signifikanten Einfluss auf den Eigenspannungsabbau in der Schweißnaht und der Wärmeeinflusszone (WEZ). T2 - SFB 1120 Summer School CY - Steinfeld, Germany DA - 11.06.2024 KW - LTT (Low Transformation Temperature) KW - Eigenspannungen KW - Ermüdungsfestigkeit KW - Aufmischung PY - 2024 AN - OPUS4-60306 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Martin A1 - Dittmann, Florian A1 - Kromm, Arne A1 - Varfolomeev, Igor A1 - Kannengießer, Thomas T1 - Residual stress reduction using a low transformation temperature welding consumable with focus on the weld geometry N2 - Low transformation temperature (LTT) welding consumables represent an innovative approach to realize compressive residual stress in the weld seam and HAZ. LTT welding consumables use the volume-expanding martensitic phase transformation near room temperature to generate compressive residual stress during cooling. This article focuses on the weld geometry and its influence on residual stress reduction using an LTT welding consumable. For this purpose, layers with an LTT welding consumable were additionally applied to the front sides of conventionally welded longitudinal stiffeners. Different weld geometries of the second weld seam could be realized by varying the welding parameters. These samples were analyzed for geometric parameters, chemical composition, and residual stress. While the chemical composition and martensite start temperature (MS) were only slightly influenced by parameter changes, a clear influence with regard to residual stress and weld geometry was observed. Depending on the shape of the second LTT weld seam, residual stress reductions of 200 to 500 MPa were achieved using the same LTT welding consumable. T2 - IIW Annual Assembly and International Conference CY - Rhodes Island, Dodecanisa, Greece DA - 07.07.2024 KW - Low transformation temperature (LTT) KW - Martensite start temperature KW - Dilution KW - Weld geometry KW - Residual stress PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-633707 DO - https://doi.org/10.1007/s40194-025-02094-3 SN - 1878-6669 SP - 1 EP - 11 PB - Springer Nature CY - Berlin ; Heidelberg AN - OPUS4-63370 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Martin T1 - Effect of weld design on fatigue strength of welded components using LTT filler materials N2 - The fatigue strength of weld seams was increased by using residual stress-reducing Low Transformation Temperature (LTT) filler metals. Conventional single-layer welded longitudinal stiffeners were welded at the end faces with an additional layer (LTT and conventional welding consumable). The weld geometry was varied by changing the welding parameters. The residual stress reduction determined using XRD depended significantly on the weld geometry. The increase in fatigue strength, on the other hand, was significantly improved in all LTT seam variants compared to conventional single-layer and double-layer layers. T2 - The 78th IIW annual assembly and international conference on welding and joining CY - Genua, Italy DA - 22.07.2025 KW - Low transformation temperature (LTT) KW - Residual stress reduction KW - Fatigue strength KW - Weld geometry PY - 2025 AN - OPUS4-63708 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Martin T1 - Verbesserung der Ermüdungsfestigkeit von Längssteifen durch Low Transformation Temperature (LTT) Schweißzusätze N2 - In diesem Beitrag wird die gezielte Applikation zusätzlicher LTT-Schweißraupen zur Erhöhung der Ermüdungsfestigkeit in Schweißverbindungen erläutert. Der Einfluss der Eigenspannungen auf die Ermüdungsfestigkeit kann besonders durch Längssteifen verdeutlicht werden, da diese durch Verzugsbehinderungen oftmals hohe Eigenspannungen in der ermüdungskritischen Wärmeeinflusszone (WEZ) aufweisen. Daher wurden konventionell einlagig geschweißte Längssteifen aus hochfestem Baustahl mit LTT-Zusatzlagen an den Stirnseiten versehen, um lokal Druckeigenspannungen zu erzeugen, welche durch Schweißparametervariationen geometrisch variierten. Zusätzlich wurde als Kontrolle auch der Fall der zweilagig konventionell geschweißten Längssteife betrachtet. Die mittels XRD bestimmten Schweißeigenspannungen konnten in der WEZ durch die zusätzliche LTT-Naht reduziert werden. Je weiter weg die Nahtspitze der Zusatzlage ist, umso geringer sind die Schweißeigenspannungen in der WEZ. Bei konstanter Amplitudenlast und einem R-Verhältnis von 0,1 konnte die Ermüdungsfestigkeit der LTT-Proben deutlich verbessert werden. Die Ermüdungsfestigkeit bei 2 Millionen Lastwechsel beträgt für konventionelle Proben 87 MPa und für die LTT-Proben 156 bis 196 MPa. Auch eine Steigung der Zeitfestigkeitsgeraden konnte an den LTT-Proben beobachtet werden. Der Umfang dieser Steigerung war ähnlich bzw. höher als bei höherfrequenten gehämmerten Proben. Ein Zusammenhang zwischen der bestimmten Eigenspannung und der Ermüdungsfestigkeit konnte beobachtet werden, wenn auch nur im geringeren Umfang. LTT-Schweißzusätze können verwendet werden, um die Ermüdungsfestigkeit in Längssteifen zu erhöhen. T2 - 15. Vollversammlung des SFB 1120: Summer School 2025 CY - Kall, Germany DA - 08.07.2025 KW - Low transformation temperature (LTT) KW - Eigenspannungen KW - Ermüdungsfestigkeit KW - Längssteife PY - 2025 AN - OPUS4-63710 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Martin T1 - Einfluss der Low Transformation Temperature-Schweißzusätze auf die Ermüdungsfestigkeit von Längssteifen N2 - In dem vorliegenden Beitrag wird die gezielte Applikation zusätzlicher LTT-Schweißlagen zur Einbringung von Druckeigenspannungen in ermüdungskritischen Bereichen an Schweißverbindungen untersucht. Ziel ist die Entwicklung eines wirtschaftlichen Verfahrens zur Erhöhung der Ermüdungslebensdauer, ohne die strukturelle Integrität einer Schweißnaht zu beeinträchtigen. Zu diesem Zweck wurden zunächst Längssteifen aus hochfestem Stahl in der ersten Lage mittels Metall-Lichtbogenschweißen unter Verwendung eines konventionellen Schweißzusatzwerkstoffs geschweißt. Anschließend erfolgte die Auftragung eines Chrom-Nickel-legierten LTT-Schweißzusatzwerkstoffs an die Stirnseiten der Längssteifen. T2 - OVGU BMDK Seminar CY - Magdeburg, Germany DA - 17.06.2025 KW - Low transformation temperature (LTT) Schweißzusätze KW - Schweißeigenspannungen KW - Ermüdungsfestigkeit PY - 2025 AN - OPUS4-63702 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Martin T1 - Bericht zum Fortschritt des laufenden Projekts: "Hybrider Einsatz von LTT-Schweißzusätzen zur Schwingfestigkeitsverbesserung hochfester Stahlbauteile" N2 - Dieses Dokument fasst den Projektfortschritt des BAM-Projektes "Hybrider Einsatz von LTT-Schweißzusätzen zur Schwingfestigkeitsverbesserung hochfester Stahlbauteile" im Rahmen des Sitzung des DVS Fachausschuss FA09 - Konstruktion und Festigkeit für die Projektquartale Q4 2024 und Q1 2025 zusammen und stellt die wichtigsten Ergebnisse in Kurzform vor. T2 - Sitzung des DVS Fachausschuss FA09 - Konstruktion und Festigkeit CY - Berlin, Germany DA - 21.05.2025 KW - Low transformation temperature (LTT) KW - Eigenspannungen KW - Ermüdungsfestigkeit KW - Makroproben PY - 2025 AN - OPUS4-63699 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Martin T1 - Enhancement of the Fatigue Strength by Application of a Low Transformation Temperature Welding Consumable N2 - To improve the fatigue strength of weld seams, a project is being carried out at BAM using Low Transformation Temperature (LTT) welding consumables to reduce residual stress at weld seams. Longitudinal stiffeners, which were welded conventionally in the first layer and additionally with an LTT or conventional layer on the end faces, were tested for fatigue strength. The mean fatigue strength at 2 million load cycles was increased from 87 MPa to at least 156 MPa. A comparison of HFMI-treated samples with conventional filler metal showed an increase in fatigue strength of 146 MPa. This means that LTT filler metals achieve a similar increase in fatigue strength as conventional post-treatment methods. T2 - The 78th IIW annual assembly and international conference on welding and joining CY - Genua, Italy DA - 22.07.2025 KW - Low transformation temperature (LTT) KW - Fatigue strength KW - Weld geometry PY - 2025 AN - OPUS4-63704 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Martin T1 - Effects of weld seam design on the fatigue strength of welded components with LTT welding filler N2 - Low Transformation Temperature (LTT) welding fillers offer an innovative approach to increase the compressive residual stresses in weld seams which have a positive impact on the fatigue strength of welded structures. LTT welding fillers exhibit a martensitic phase transformation close to ambient temperature which generates compressive residual stresses through a volume expansion in the weld seam and the heat affected zone (HAZ). This article focuses on the punctually placement of additional LTT layers to generate compressive residual stresses in fatigue-critical areas of conventional weld joints. This enables an economical solution without effecting the integrity of welded joints. For this, longitudinal stiffeners made of high-strength steel were gas metal arc welded using conventional welding consumable in the first layer. Afterwards, a chromium-nickel alloyed LTT welding consumable was applied on front sides of the stiffeners. By varying the welding parameters, three different weld geometries of the LTT weld bead could be realized. The effects of additional LTT layers were investigated with regards to dilution, residual stresses, and fatigue strength. The dilution does not exhibit much difference regards to the chemical composition. Therefore, it can be assumed that all three variants have a similar martensite start temperature. X-ray residual stresses measurements show that the residual stresses at the critical weld toe are significantly reduced by using LTT welding filler. While the conventional weld is characterized by tensile residual stresses, compressive residual stresses can be detected at the LTT weld. The level of residual stresses is influenced by the geometry of the LTT layer. LTT layers with a high offset to the conventional weld generate more compressive residual stresses in the HAZ than with a low offset. Therefore, the weld geometry has a considerable impact on the residual stress profile. The fatigue testing results shows that the LTT layers in all three variants has a positive impact to the fatigue strength. T2 - MPA Seminar Stuttgart 2024 CY - Stuttgart, Germany DA - 08.10.2024 KW - LTT (Low Transformation Temperature) KW - Fatigue strength KW - Weld geometry KW - Residual stress PY - 2024 AN - OPUS4-61615 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Behnke, Thomas A1 - Würth, Christian A1 - Hoffmann, Katrin A1 - Hübner, Martin A1 - Panne, Ulrich A1 - Resch-Genger, Ute T1 - Encapsulation of hydrophobic dyes in polystyrene micro- and nanoparticles via swelling procedures N2 - Aiming at the derivation of a generalized procedure for the straightforward preparation of particles fluorescing in the visible and near-infrared (NIR) spectral region, different swelling procedures for the loading of the hydrophobic polarity-probe Nile Red into nano- and micrometer sized polystyrene particles were studied and compared with respect to the optical properties of the resulting particles. The effect of the amount of incorporated dye on the spectroscopic properties of the particles was investigated for differently sized beads with different surface chemistries, i.e., non-functionalized, aminomodified and PEG-grafted surfaces. Moreover, photostability and leaking studies were performed. The main criterion for the optimization of the dye loading procedures was a high and thermally and photochemically stable fluorescence output of the particles for the future application of these systems as fluorescent labels. KW - Fluorescence KW - Nile red KW - Polystyrene KW - Nanoparticles KW - Microparticles KW - Encapsulation KW - Swelling PY - 2011 DO - https://doi.org/10.1007/s10895-010-0632-2 SN - 1053-0509 SN - 1573-4994 VL - 21 IS - 3 SP - 937 EP - 944 PB - Plenum Publ. Corp. CY - New York, NY AN - OPUS4-22692 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Martin A1 - Dittmann, Florian A1 - Kromm, Arne A1 - Varfolomeev, Igor A1 - Kannengiesser, Thomas T1 - Improvement of Fatigue Resistance through the Application of a Low-Transformation-Temperature Welding Consumable N2 - Low transformation temperature (LTT) welding consumables are an innovative approach to reduce tensile residual stress in weld seams and the surrounding heat affected zone (HAZ). The reduced tensile stress can lead to an improvement in fatigue strength of welded components. LTT alloys are characterized by a chemical composition which reduce the martensite start temperature (Ms) close to room temperature. This article focuses on a hybrid use of LTT filler metals, where the LTT filler is applied as an additional layer to conventional welds on fatigue-critical spots. Conventional gas metal arc welded longitudinal stiffeners are used as specimens. At the face ends of the stiffeners, a second LTT layer was added with various modifications in weld shapes. These different shapes were achieved by changing the welding parameters such as welding speed and offset to the first layer. These samples were used to analyze shape, dilution, resulting Ms, residual stress and fatigue strength. The dilatometer verified Ms and dilution did not change significant, although the area of the 2nd LTT weld seam was varying clear with each modification. However, the weld modification had a significant effect on the residual stress state and the fatigue strength. The X-ray determined residual stress in the HAZ became lower when the weld toe of the LTT layer was further away from the stiffener. All samples with LTT weld exhibit significantly higher fatigue strength values than conventionally single and double-layer welded samples. The lower the residual stress at weld toe, the higher the fatigue strength. The results show that on the one hand LTT filler metals increase the fatigue strength, and on the other hand the impact of LTT fillers materials is not restricted to the dilution and Ms, the shape of the weld seam must also be considered. T2 - 4th international Conference on Advanced Joining Processes AJP CY - Combria, Portugal DA - 16.10.2025 KW - Low transformation temperature (LTT) KW - Residual stress reduction KW - Fatigue strength KW - Longitudenal stiffener PY - 2025 AN - OPUS4-65090 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hübner, Martin T1 - Bericht zum Fortschritt des laufenden Projekts: "Hybrider Einsatz von LTT-Schweißzusätzen zur Schwingfestigkeitsverbesserung hochfester Stahlbauteile" N2 - Low Transformation Temperature (LTT) Schweißzusätze erzeugen während der Abkühlung Druckeigenspannungen in die Schweißnaht und Wärmeeinflusszone durch eine Volumenexpansion, wodurch die Ermüdungsfestigkeit erhöht werden kann. Um das Potential dieser neuartigen Schweißzusätze besser zu quantifizieren, wurden konventionelle Längssteifen als Probenkörper verwendet, welche an den Stirnseiten mit einer LTT-Zusatznaht geschweißt wurden. Durch Variation der Schweißparameter konnten unterschiedliche Nahtformen realisiert werden. Es konnte, je nach Nahtausführung, eine Erhöhung der Ermüdungsfestigkeit bei 2 Millionen Lastwechseln von 140% festgestellt werden. Somit sind LTT-Zusätze grundsätzlich geeignet, um die Ermüdungsfestigkeit zu erhöhen. Weiterhin wurde festgestellt, dass das Reparaturschweißen mit LTT Schweißzusätzen als Decklage ebenfalls zu einem deutlichen Ermüdungsfestigkeitsanstieg führte. T2 - Sitzung des DVS Fachausschuss FA09 - Konstruktion und Festigkeit CY - Düsseldorf, Germany DA - 10.12.2025 KW - Low transformation temperature (LTT) KW - Eigenspannungen KW - Ermüdungsfestigkeit KW - hochfeste Stähle KW - Mikroproben PY - 2025 AN - OPUS4-65089 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -