TY - CONF A1 - Sunder, S. A1 - Jauregui Rozo, Maria A1 - Schartel, Bernhard A1 - Ruckdäschel, H. T1 - Adapting intumescent/low-melting glass flame-retardant formulations for transfer to glass-fiber-reinforced composites and post-fire mechanical analysis N2 - The residual post-fire mechanical properties of fiber-reinforced epoxy composites are influenced by their fire residues after burning. This study uses intumescent/low-melting glass flame retardants to tailor fire residues in epoxy resin. Processibility of prepregs and their quality are analysed for transfer of the flame-retardant epoxy resins to layered glass-fiber reinforced composites. Minimal effects were found on the pre-fire flexural strengths of the composites due to low loading of the flame retardants. However, when transferred to glass-fiber reinforced composites, the fire residues diminish significantly. Further studies are required to improve theoretical and experimental estimations of the post-fire mechanics of the composites. T2 - SAMPE Europe Conference 2023 CY - Madrid, Spain DA - 03.10.2023 KW - Fire residue KW - Prepregs KW - Mechanics KW - Lightweight materials KW - Composites KW - Flame retardancy PY - 2023 SP - 1 EP - 7 AN - OPUS4-59138 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jauregui Rozo, Maria A1 - Sunder, Sruthi A1 - Schartel, Bernhard A1 - Ruckdäschel, Holger T1 - Weaving through fire and force: Fire behavior, fire stability and modes of action between epoxy resin and glass-fiber composites N2 - Several investigation groups have studied the flame-retardancy modes of action and properties of epoxy resins in the past; nevertheless, the selection of suitable flame retardants for epoxy resins remains challenging, and the transfer to fiber composites is difficult. The addition of flame retardants and glass fibers (GFs) to a polymeric system in a fire scenario changes the polymer's pyrolytic path and burning characteristics, reduces the heat released in the combustion, and suppresses the modes of action in the condensed and gas phase. In this study, the thermal analysis, flammability, fire behavior, residue analysis, fire stability, and quantification of modes of action of three different systems with three halogen-free flame retardants (melamine polyphosphate (MPP), ammonium polyphosphate (APP), and silane ammonium polyphosphate (SiAPP)) and three different types of GFs (unidirectional (UD), bidirectional (BD), and woven roving (WR)) will be compared with pure epoxy resin as a reference. T2 - Fire & Polymers CY - New Orleans, LA, USA DA - 12.05.2024 KW - Glass-fiber-composites KW - Epoxy Resins KW - Flame Retardancy KW - Fire Stability KW - Bench-scale Fire Resistance Test PY - 2024 AN - OPUS4-60150 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jauregui Rozo, Maria A1 - Sruthi, Sunder A1 - Ruckdäschel, Holger A1 - Schartel, Bernhard T1 - Transfer of the modes of action from polymer materials to glass-fiber-reinforced plastics: flame retardancy – fire resistance – post-fire mechanics N2 - Fire resistance of fiber-reinforced polymers (FRPs) has been an important area of research for many years since FRPs are mainly used in the transportation and construction sectors. This study presents the fire behavior, and mechanical performance between the flame retarded pure epoxy resin and flame retarded glass-fiber composites before, during, and after a fire event. This enables a deeper understanding of the transferability of flame retardants on composite materials. T2 - 19th European Meeting on Fire Retardant Polymeric Materials (FRPM23) CY - Dübendorf, Switzerland DA - 26.06.2023 KW - Glass-fiber Reinforced Polymer KW - Flame Retardancy KW - Fire Behavior KW - Flammability KW - Modes of Action PY - 2023 AN - OPUS4-57846 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jauregui Rozo, Maria A1 - Sunder, S. A1 - Ruckdäschel, H. A1 - Schartel, Bernhard T1 - Transfer of the Flame Retardancy and Post-Fire Mechanics from Polymer Materials to Glass-Fiber-Reinforced Plastics N2 - This study presents the processability, fire behavior, and mechanical performance between the flame retarded pure epoxy resin and flame retarded glass-fiber-reinforced plastic before, during, and after a fire event. This enables a deeper understanding of the transferability of flame retardants, modes of action, char enhancement, and flame inhibition on composite materials T2 - Twenty-third international conference on composite materials (ICCM23) CY - Belfast, United Kingdom DA - 31.07.2023 KW - Glass-Fiber Reinforced Polymer KW - Flame Retardancy KW - Mechanical Testing KW - Epoxy Resin KW - Modes of Action PY - 2023 AN - OPUS4-58086 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sunder, S. A1 - Jauregui Rozo, Maria A1 - Inasu, S. A1 - Schartel, Bernhard A1 - Ruckdäschel, H. T1 - A systematic investigation of the transfer of polyphosphate/inorganic silicate flame retardants from epoxy resins to layered glass fiber-reinforced composites and their post-furnace flexural properties N2 - The systematic transfer of solvent-free, additive flame retardant (FR) formulations from epoxy resins to glass fiber-reinforced epoxy composites (GFRECs) through prepregs is difficult. Additionally, obtaining data on their post-fire mechanics is often challenging. Utilizing melamine polyphosphate (MPP), ammonium polyphosphate (APP), and silane-coated ammonium polyphosphate (SiAPP) FRs with low-melting inorganic silicates (InSi) in an 8:2 proportion and 10% loading by weight in a diglycidyl ether of bisphenol A (DGEBA) resin, a systematic investigation of the processing properties, room-temperature mechanics, and temperature-based mechanics of the systems was performed. The resin was cured with a dicyandiamide hardener (DICY) and a urone accelerator. The results revealed no substantial impact of these FRs at the current loading on the resin's glass transition temperature or processability. However, the fire residues from cone calorimetry tests of the composites containing FRs were found to be only 15-20% of the thickness of the resins, implying a suppression of intumescence upon transfer. At room temperature, the decrease in the flexural modulus for the composites containing FRs was negligible. Exposure of the composites in a furnace at 400°C as a preliminary study before ignition tests was shown to cause significant flexural moduli reductions after 2.5 min of exposure and complete delamination after 3 min making further testing unviable. This study emphasizes the need for future research on recovering modes of action upon transfer of FR formulations from resins to composites. Based on the challenges outlined in this investigation, sample adaptation methods for post-fire analysis will be developed in a future study. KW - DGEBA KW - Prepregs KW - Glass fiber-reinforced composites KW - Post-fire testing PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-605239 DO - https://doi.org/10.1002/pc.28416 SN - 1548-0569 SN - 0272-8397 VL - 45 IS - 10 SP - 9389 EP - 9406 PB - Wiley AN - OPUS4-60523 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -