TY - JOUR A1 - Henning, L. M. A1 - Diaz Cubas, D. A1 - Colmenares, M. G. A1 - Schmidt, J. A1 - Bekheet, M. F. A1 - Pauw, Brian Richard A1 - Gurlo, A. A1 - Simon, U. T1 - High specific surface area ordered mesoporous silica COK-12 with tailored pore size N2 - Ordered mesoporous silica materials such as COK-12, analogous to the well-known SBA-15, are characterized by high surface areas and unique features such as defined pore sizes in the meso-size range and high pore ordering. The aim of this work was to prove the washing step and choice of calcination and aging temperature during the COK-12 synthesis as effective tools in tailoring, markedly improving the specific surface area, pore size, and pore volume. By controlling the aging temperature, the pore size was linearly adjusted between 5.7 and 8.1 nm, while preserving the hexagonal ordering of the pores. The synthesized COK-12 powders possess pore volumes and specific surface areas up to 1.23 cm3 g−1 and 860m2 g−1, respectively, which is markedly higher than what has previously been reported about COK-12. The presented results and the environmentally friendly character of the synthesis will make COK-12 more interesting for future adaption to the industrial processes, for example in catalysis, adsorption, or drug delivery. KW - Ordered mesoporous silica KW - Pore size tailoring KW - High specific surface area KW - SAXS KW - Small angle scattering PY - 2019 DO - https://doi.org/10.1016/j.micromeso.2019.01.050 SN - 1387-1811 VL - 280 SP - 133 EP - 143 PB - Elsevier AN - OPUS4-47378 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gili, A. A1 - Bischoff, B. A1 - Simon, U. A1 - Schmidt, Franziska A1 - Kober, D. A1 - Görke, O. A1 - Bekheet, M. A1 - Gurlo, A. T1 - Ceria-based dual-phase membranes for high-temperature Carbon dioxide separation: Effect of iron doping and pore generation with MgO template N2 - Dual-phase membranes for high-temperature carbon dioxide Separation have emerged as promising technology to mitigate anthropogenic greenhouse gases emissions, especially as a pre- and post-combustion separation technique in coal burning power plants. To implement These membranes industrially, the carbon dioxide permeability must be improved. In this study, Ce_(0.8) Sm_(0.2) O_(2-d) (SDC) and Ce_(0.8)Sm_(0.19)Fe_(0.01)O_(2-d) (FSDC) ceramic powders were used to form the skeleton in dual-Phase membranes. The use of MgO as an environmentally friendly pore generator allows control over the membrane porosity and microstructure in order to compare the effect of the membrane’s ceramic phase. The ceramic powders and the resulting membranes were characterized using ICP-OES, HSM, gravimetric analysis, SEM/EDX, and XRD, and the carbon dioxide flux density was quantified using a high-temperature membrane permeation setup. The carbon dioxide permeability slightly increases with the addition of iron in the FSDC membranes compared to the SDC membranes mainly due to the reported scavenging effect of iron with the siliceous impurities, with an additional potential contribution of an increased crystallite size due to viscous flow sintering. The increased permeability of the FSDC system and the proper microstructure control by MgO can be further extended to optimize carbon dioxide permeability in this membrane system. KW - Samarium doped ceria KW - SDC KW - FSDC KW - CO2 separation membranes KW - Scavenging effect of iron KW - Permeability PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-488612 DO - https://doi.org/10.3390/membranes9090108 SN - 2077-0375 VL - 9 IS - 9 SP - 108, 1 EP - 15 PB - MDPI AN - OPUS4-48861 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -