TY - JOUR A1 - Musyanovych, A. A1 - Grimmer, Christoph A1 - Sadak, A. E. A1 - Heßling, L. A1 - Lüdicke, M. A1 - Bilsel, M. A1 - Horn, Wolfgang A1 - Richter, Matthias T1 - Polymer Capsules with Volatile Organic Compounds as Reference Materials for Controlled Emission N2 - Encapsulation of volatile organic compounds (VOCs) that could evaporate at a defined rate is of immense interest for application in emission reference materials (ERMs). Polyurethane/polyurea microcapsules with various VOC active ingredients (limonene, pinene, and toluene) were successfully produced by interfacial polymerization with Shirasu porous glass membrane emulsification in a size range between 10 and 50 μm. The effect of surfactant, VOC, monomer(s) type, and ratio has a great effect on the formulation process and morphology of capsules. The type of VOC played a significant role in the encapsulation efficiency. Due to the difference in vapor pressure and VOC/water interfacial tension, the formulation for encapsulation was optimized for each individual VOC. Furthermore, to achieve effective stability of the large droplets/capsules, a combination of ionic and nonionic surfactants was used. Optical and scanning electron microscopy, Fourier transform infrared spectroscopy (FTIR), and thermogravimetric analysis (TGA), were used to characterize the optimized microcapsules. The results showed that the obtained microcapsules exhibited a spherical shape and core–shell morphology and featured characteristic urethane-urea bonds. The amount of encapsulated VOC ranges between 54 and 7 wt %. The emission tests were performed with the help of the emission test chamber procedure (EN 16516). The limonene-loaded polyurethane/polyurea microcapsules show a change in emission rate of less than 10% within 14 days and can be considered as a potential candidate for use as an ERM. KW - Polymer microcapsules KW - Membrane emulsification KW - Polyaddition KW - Volatile organic compound (VOC) KW - Emission testing PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-619227 DO - https://doi.org/10.1021/acsami.4c12826 SN - 1944-8252 VL - 16 IS - 50 SP - 69999 EP - 70009 PB - ACS AN - OPUS4-61922 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lasota, S. A1 - Horn, M. A1 - Noll, M. A1 - Stephan, Ina A1 - Otto, W. T1 - Copper in wood preservatives delayed wood decomposition and shifted soil fungal but not bacterial community composition N2 - Copper-based fungicides are routinely used for wood and plant protection, which can lead to an enrichment of copper-tolerant microbial communities in soil. To investigate the effect of such wood preservatives on the soil fungal and bacterial community compositions, five different vineyard and fruit-growing soil environments were evaluated using incubation studies over time. Pine sapwood specimens were impregnated with either water or different biocide treatment solutions containing a mixture of copper, triazoles, and quaternary ammonium compounds (CuTriQAC), a mixture of triazoles and quaternary ammonium compounds (TriQAC), or copper alone (Cu). Specimens were incubated in soil from each sample site for 8, 16, 24, and 32 weeks. The effects of preservative treatment on the modulus of elasticity (MOE) of the wood specimens and on the soil fungal as well as bacterial community composition at the soil-wood interface were assessed by quantitative PCR and amplicon sequencing of the fungal internal transcribed spacer (ITS) region and bacterial 16S rRNA gene. Specimens impregnated with CuTriQAC and Cu showed decreased MOE and reduced fungal and bacterial copy numbers over time compared to those impregnated with water and TriQAC. Fungal but not bacterial community composition was significantly affected by wood preservative treatment. The relative abundance of members of the family Trichocomaceae compared to other genera increased in the presence of the Cu and CuTriQAC treatments at three sites, suggesting these to be Cu-tolerant fungi. In conclusion, the copper-containing treatments resulted in marginally increased MOE, lowered microbial gene copy numbers compared to those in the TriQAC and water treatments, and thus enhanced wood protection against soil microbial wood degradation KW - 16S rRNA gene KW - ITS region KW - Amplicon sequencing KW - Community composition KW - Copper-based wood preservatives KW - Soil incubation study PY - 2019 DO - https://doi.org/10.1128/AEM.02391-18 SN - 1098-5336 SN - 0099-2240 VL - 85 IS - 4 SP - e02391-18, 1 EP - 13 PB - American Society for Microbiology CY - Washington, DC AN - OPUS4-47370 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Horn, Wolfgang A1 - Wilke, Olaf A1 - Mull, B. A1 - Richter, Matthias A1 - Brödner, Doris A1 - Mölders, N. A1 - Renner, M. T1 - Reproducibly emitting reference material for quality assurance/quality control of emission test chamber measurements N2 - Volatile Organic Compounds (VOC) are ubiquitous in the indoor air, since they emit from materials used indoors. Investigations of these materials are mostly carried out in test chambers under controlled climatic conditions. Quality control of these test chamber measurements is important but there is a lack of commercially available homogenous reference materials as required for round robin tests or quality assurance of laboratories. The approach of the present study is the impregnation of a supporting material with VOC, which are reproducibly released in measurable chamber air concentrations under standardised test conditions. A polymer made of Thermoplastic Polyurethane (TPU) was chosen as carrier material. It was impregnated with the VOC trimethyl pentanediol isobutyrat (texanol). T2 - Healthy Buildings 2017 Europe CY - Lublin, Poland DA - 02.07.2017 KW - Emissions testing KW - Volatile organic compounds KW - Polymeric material KW - CO2 assisted impregnation PY - 2017 SN - 978-83-7947-232-1 SP - Paper 0172, 1 EP - 2 AN - OPUS4-42348 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Richter, Matthias A1 - Mull, Birte A1 - Horn, Wolfgang A1 - Brödner, Doris A1 - Mölders, N. A1 - Renner, M. T1 - Reproducibly emitting reference material on thermoplastic polyurethane basis for quality assurance/quality control of emission test chamber measurements N2 - Volatile Organic Compounds (VOC) are ubiquitous in the indoor air since they are emitted from materials used indoors. Investigations of these materials are mostly carried out in emission test chambers under controlled climatic conditions. Reference materials are an important tool for quality assurance/Quality control of emission test chamber measurements but so far they are not commercially available. In this study, a new approach was tested to develop an appropriate reference material with homogenous and reproducible emission of the VOC with well measurable air concentrations in emission test Chambers larger than 20 L at air change rates of 0.5 - 1 /h. Thermoplastic Polyurethane (TPU) was selected as Matrix material which was impregnated with 2,2,4- trimethyl-1,3-pentanediol monoisobutyrate (texanol) as test VOC using compressed carbon dioxide. An optimization of the impregnation parameters such as temperature, pressure, time, VOC injection volume and TPU sample size was performed until the targeted area specific Emission rate (SERa) value was reached. Further aspects like process control, storage effects and correlation of the sample size to the emission rate were investigated. It was found that the SERa immediately after sample preparation were not reproducible between the batches but became unified 10 days after loading into the test chamber indicating the necessity of aging before use. SERa between 13,000 and 18,000 mg m-2 h-1 were obtained, and the impregnated materials could be well stored in aluminum-coated polyethylene foil for at least seven weeks without significant losses. Furthermore, the impregnation of styrene and the SVOC 2,6-diisopropylnaphthalene was tested. KW - Reference material KW - Emissions testing KW - Volatile organic compounds KW - Polymer material KW - CO2 assisted impregnation PY - 2017 DO - https://doi.org/10.1016/j.buildenv.2017.06.005 SN - 0360-1323 SN - 1873-684X VL - 122 SP - 230 EP - 236 PB - Elsevier AN - OPUS4-40646 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, B. A1 - Dahms, A. A1 - Bitter, F. A1 - Wargocki, P. A1 - Olesen, B. A1 - Knudsen, H.N. A1 - Afshari, A. A1 - Jann, Oliver A1 - Horn, Wolfgang A1 - Müller, D. A1 - Airaksinen, M. A1 - Järnström, H. A1 - Tirkkonen, T. A1 - Witterseh, T. T1 - Material labelling: Combined material emission tests and sensory evaluations T2 - Indoor Air 2008, 11th International Conference on Indoor Air Quality and Climate CY - Copenhagen, Denmark DA - 2008-08-17 KW - Material labelling KW - Emission test KW - Sensory evaluation KW - Odour intensity KW - Acceptability PY - 2008 IS - Paper 1066 SP - 1 EP - 8 AN - OPUS4-18047 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Pfuch, A. A1 - Horn, K. A1 - Mix, Renate A1 - Ramm, M. A1 - Heft, A. A1 - Schimanski, A. ED - Suchentrunk, R. T1 - Direct and remote plasma assisted CVD at atmospheric pressure for the preparation of oxide thin films N2 - In this paper the preparation of silicon and titanium oxide thin films using an atmospheric pressure plasma process will be reported. To obtain these oxide films hexamethyldisiloxane and titanium tetraisopropoxide were used as precursor materials. Based on the different chemical reaction mechanisms the film deposition processes were carried out in the direct as well as in the remote PACVD mode. The deposition parameters were varied and the influence on different film properties was studied. The deposited oxide films were characterised by profilometry, ellipsometry, SEM, UV-VIS-NIR-transmission measurements. FT-IR spectroscopy and contact angle measurements. Additionally, first results will be presented concerning the creation of composite films using a combination of plasma and liquid dye nebulization technique. KW - FTIR KW - Ellipsometry KW - Profilometry KW - SEM KW - PACVD KW - Silicon oxide PY - 2010 SN - 978-3-87480-259-8 VL - 66 SP - 114 EP - 124 PB - Eugen G. Leuze CY - Bad Saulgau AN - OPUS4-22798 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stegemann, Bert A1 - Klemm, M. A1 - Horn, S. A1 - Woydt, Mathias T1 - Switching adhesion forces by crossing the metal-insulator transition in Magnéli-type vanadium oxide crystals N2 - Magnéli-type vanadium oxides form the homologous series VnO2n-1 and exhibit a temperature-induced, reversible metal–insulator first order phase transition (MIT). We studied the change of the adhesion force across the transition temperature between the cleavage planes of various vanadium oxide Magnéli phases (n = 3 ... 7) and spherical titanium atomic force microscope (AFM) tips by systematic force–distance measurements with a variable-temperature AFM under ultrahigh vacuum conditions (UHV). The results show, for all investigated samples, that crossing the transition temperatures leads to a distinct change of the adhesion force. Low adhesion corresponds consistently to the metallic state. Accordingly, the ability to modify the electronic structure of the vanadium Magnéli phases while maintaining composition, stoichiometry and crystallographic integrity, allows for relating frictional and electronic material properties at the nano scale. This behavior makes the vanadium Magnéli phases interesting candidates for technology, e.g., as intelligent devices or coatings where switching of adhesion or friction is desired. KW - Adhesion force KW - Atomic force microscopy KW - Magnéli phases KW - Metal-insulator transition KW - Vanadium oxide PY - 2011 DO - https://doi.org/10.3762/bjnano.2.8 SN - 2190-4286 VL - 2 SP - 59 EP - 65 CY - Frankfurt, M. AN - OPUS4-23155 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Müller, B. A1 - Panasková, J. A1 - Danielak, M. A1 - Horn, Wolfgang A1 - Jann, Oliver A1 - Müller, D. T1 - Sensory-based evaluation of building product emissions - Integration into the Blue Angel award criteria and assessment scheme of the Committee for Health Evaluation of Building Products (UBA-FB 001500 / Förder-Kennz. 370762300) N2 - Emissions from building products can considerably impair the quality of indoor air. The AgBB scheme is employed to evaluate the emissions of volatile organic compounds (VOC) from building products. The hygienic evaluation according to the AgBB scheme requires product-specific measuring procedures. These are available for a range of products. They have been validated in co-operation with several research and testing institutes and have been included in the criteria for awarding the Blue Angel ecolabel. The evaluation is, however, stricter and generally has lower limits. VOC emissions and odours can cause health problems so testing using sensors is an important element in the evaluation of building products and has – for reasons of precaution – been set down in the AgBB scheme. The main goal of the project was to derive a method of evaluation using sensors and limits for awarding the Blue Angel and for the AgBB scheme. Based on the research conducted (see Chapter 5 Results and Discussion), perceived intensity and hedonics were suggested as a suitable Evaluation method. The derivation of limits for the evaluation using sensors on the 28th day was effected in the present study through the additional questioning of the test subjects on the reasonability of a sample. For the Blue Angel, there could be different limits of perceived intensity and hedonics for each group of products. A preliminary suggestion for possible limits – for all product groups – is a perceived intensity of 7 pi (5 pi + 2 pi as confidence coefficient, Chapter 5.1.5) and -1 (0+/-0.8, rounded to -1) for the hedonic value. KW - Labelsysteme KW - VOC KW - Geruch KW - Geruchstest KW - Emissionsmessungen KW - Building product KW - Directive KW - Health care KW - Pollutant KW - Test method KW - Hydrocarbon KW - Testing using sensors KW - Emission KW - Emission test chamber KW - Odour KW - AgBB scheme KW - Health assessment KW - Assessment procedure KW - Volatile organic compounds KW - Very volatile organic compounds KW - VVOC KW - Semi volatile organic compounds KW - SVOC KW - Thermal desorption KW - GC/MS KW - GC-ODP KW - Odour standard of comparison KW - Floor coverings KW - Coverings KW - Blue Angel KW - Odour evaluation KW - Acceptability KW - Perceived intensity KW - Hedonic KW - Reasonability KW - Standardization KW - Environmental sign KW - Volatile emission KW - Product labelling PY - 2011 UR - http://www.umweltbundesamt.de/publikationen/sensory-based-evaluation-of-building-product SN - 1862-4804 IS - 61 SP - 1-133, Annex 1-109 PB - Umweltbundesamt CY - Dessau-Roßlau AN - OPUS4-25200 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wiegner, Katharina A1 - Nohr, Michael A1 - Farke, M. A1 - Horn, Wolfgang A1 - Kalus, Sabine A1 - Jann, Oliver A1 - Hahn, Oliver T1 - Frische Luft für Museumsvitrinen - Neue Methode zur Untersuchung von Vitrinenbaumaterialien als Beitrag zur Präventiven Konservierung N2 - Nicht nur Schadstoffe aus der Umwelt können Museumsexponate schädigen. Auch interne Schadstoffquellen wie objektimmanente Exhalate und Emissionen von Lösemitteln oder organischen Säuren können den wertvollen Gu¨tern Schaden zufu¨gen. Auf Schadstoffe zu pru¨fen sowie geeignete Messmethoden zu entwickeln und zu optimieren, ist daher von großer Bedeutung. Neuste Forschungen stellen die Autoren vor. KW - VOC KW - Präventive Konservierung KW - Emissionsmessungen KW - AgBB-Schema KW - Ausstellungsvitrinen KW - Verpackungsmaterialien PY - 2011 SN - 0933-4017 VL - 117 IS - 5 SP - 30 EP - 35 PB - Callwey CY - München AN - OPUS4-23877 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wiegner, Katharina A1 - Hahn, Oliver A1 - Farke, M. A1 - Kalus, Sabine A1 - Horn, Wolfgang T1 - Determination of formic and acetic acids in air N2 - Formic and acetic acids are often responsible for damage of cultural objects, e. g. glass and metal corrosion or changing and fading of colours. Museums all around the world are equipped with different show cases. Display cases should protect cultural objects from dust as well as from mechanical damage. Several construction materials which are used for display cases, including wood, glue and coatings, are possible sources of very volatile organic compounds (VVOCs), volatile organic compounds (VOCs) and semi volatile organic compounds (SVOCs). These construction products can emit formic and acetic acids into the indoor or display case air. Modern display cases with small air change rates can cause higher concentrations of formic and acetic acids if any source is installed in the display case (Salthammer and Uhde, 2009). To minimize the risk of damage emissions from building products must be quantified. There is a need for a method for identification and quantification of acetic and formic acid. Some possibilities for the identification of acetic acid exist. The quantification of acetic acid for example after sampling on TENAX® or CARBOTRAP and thermal desorption-GC in accordance with ISO 16000-6 and ISO 16017-1 results in very low recovery rates. A new method should be stabile, robust, reproducible and comparable, with an easy local sampling and determination in laboratories. Miniaturised emission test chambers and model display cases were used to study the recovery rates. T2 - Indoor Air 2011, 12th International conference on indoor air quality and climate CY - Austin, TX, USA DA - 05.06.2011 KW - VOCs KW - Detection of formic and acetic acid KW - Quantification of formic and acetic acid KW - Air sampling PY - 2011 IS - Paper 768 SP - 1 EP - 2 AN - OPUS4-23876 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -