TY - GEN A1 - Brehme, Sven A1 - Schartel, Bernhard A1 - Bykov, Y. A1 - Ciesielski, M. A1 - Döring, M. A1 - Fischer, O. A1 - Pospiech, D. A1 - Köppl, T. A1 - Altstädt, V. T1 - Flame retardancy mechanisms and performance of a halogen-free phosphorus polyester in PBT N2 - PET-P-DOPO is a phosphorus-containing polyester prepared from the glycol ether of the hydroquinone derivative of 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) and dimethyl terephthalate. PET-P-DOPO and a blend of PBT with PET-PDOPO were investigated with respect to pyrolysis and fire behavior. PET-P-DOPO achieves a V-0 rating in the UL 94 test and exhibits a high LOI of 39.3%. The outstanding flame-retardant properties of PET-P-DOPO are the result of three different mechanisms (flame inhibition, charring and a protection effect of the intumescent char) that are active in PET-P-DOPO. The fire load and the peak of heat release rate (pHRR) are reduced to 34% and 17%, respectively. The char exhibits an intumescent multicellular structure enabling it to act as an efficient protection layer. As PET-P-DOPO is immiscible with PBT, the blend shows a lower breaking elongation than pure PBT. Compared to pure PET-P-DOPO, the flame retardancy of the blend is decreased according to the fraction of PET-P-DOPO used. Nevertheless, the flame-retardancy of PET-P-DOPO in the blend was good enough to compete with PBT flame-retarded by AlPi-Et (aluminum diethylphosphinate) that was used as a Benchmark. KW - PBT KW - DOPO KW - Flame retardancy PY - 2011 SN - 1-59623-795-3 SP - 1 EP - 15 CY - Wellesley, USA AN - OPUS4-24617 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yusenko, Kirill A1 - Khandarkhaeva, S. A1 - Bykov, M. A1 - Fedotenko, T. A1 - Hanfland, M. A1 - Sukhikh, A. A1 - Gromilov, S. A1 - Dubrovinsky, L. T1 - Face-centered cubic refractory alloys prepared from single-source precursors N2 - Three binary fcc-structured alloys (fcc–Ir0.50Pt0.50, fcc Rh0.66Pt0.33 and fcc–Rh0.50Pd0.50) were 14 prepared from [Ir(NH3)5Cl][PtCl6], [Ir(NH3)5Cl][PtBr6], [Rh(NH3)5Cl]2[PtCl6]Cl2 and 15 [Rh(NH3)5Cl][PdCl4]·H2O, respectively, as single-source precursors. All alloys were prepared by 16 thermal decomposition in gaseous hydrogen flow below 800 °C. Fcc–Ir0.50Pt0.50 and fcc–Rh0.50Pd0.50 17 correspond to miscibility gaps on binary metallic phase diagrams and can be considered as 18 metastable alloys. Detailed comparison of [Ir(NH3)5Cl][PtCl6] and [Ir(NH3)5Cl][PtBr6] crystal 19 structures suggests that two isoformular salts are not isostructural. In [Ir(NH3)5Cl][PtBr6], specific 20 Br…Br interactions are responsible for crystal structure arrangement. Room temperature 21 compressibility of fcc–Ir0.50Pt0.50, fcc–Rh0.66Pt0.33 and fcc–Rh0.50Pd0.50 has been investigated up to 50 GPa 22 in diamond anvil cells. All investigated fcc-structured binary alloys are stable under compression. 23 Atomic volumes and bulk moduli show good agreement with ideal solutions model. For fcc–24 Ir0.50Pt0.50, V0/Z = 14.597(6) Å3·atom-1, B0 = 321(6) GPa, B0' = 6(1); for fcc–Rh0.66Pt0.33, V0/Z = 14.211(3) 25 Å3·atom-1, B0 =259(1) GPa, B0' = 6.66(9); for fcc–Rh0.50Pd0.50, V0/Z = 14.18(2) Å3·atom-1, B0 =223(4) GPa, 26 B0' = 5.0(3). KW - High-pressure KW - Refractory alloys KW - Platinum group metals KW - Single-source precursors PY - 2020 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-508176 VL - 13 IS - 6 SP - 1418 PB - MDPI CY - Basel AN - OPUS4-50817 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Brehme, Sven A1 - Schartel, Bernhard A1 - Goebbels, Jürgen A1 - Fischer, O. A1 - Pospiech, D. A1 - Bykov, Y. A1 - Döring, M. T1 - Phosphorus polyester versus aluminium phosphinate in poly(butylene terephthalate) (PBT): Flame retardancy performance and mechanisms N2 - Pyrolysis and fire behaviour of a phosphorus polyester (PET-P-DOPO) have been investigated. The glycol ether of the hydroquinone derivative of 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide was used as a reactive halogen-free flame retardant in PET-P-DOPO. PET-P-DOPO is proposed as an alternative to poly(butylene terephthalate) (PBT) with established halogen-free additives. It exhibits a high LOI (39.3%) and achieves V-0 classification in the UL 94 test. Three different mechanisms (flame inhibition, charring and a protection effect by the intumescent char) contribute to the flame retardancy in PET-P-DOPO and were quantified with respect to different fire risks. The fire load was reduced by 66% of the PBT characteristic. The reduction is the superposition of the relative reduction due to flame inhibition (factor 0.625) and charring (factor 0.545). The peak of heat release rate (pHRR) was reduced by 83% due to flame inhibition, charring and the protection properties of the char (factor 0.486). The strength of all three mechanisms is in the same order of magnitude. The intumescent multicellular structure enables the char to act as an efficient protection layer. PBT flame-retarded with aluminium diethylphosphinate was used as a benchmark to assess the performance of PET-P-DOPO absolutely, as well as versus the phosphorus content. PET-P-DOPO exhibits superior fire retardancy, in particular due to the additional prolongation of the time to ignition and increase in char yield. PET-P-DOPO is a promising alternative material for creating halogen-free flame-retarded polyesters. KW - Poly(butylene terephthalate) (PBT) KW - Fire retardancy KW - Aluminium phosphinate KW - 9,10-Dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) PY - 2011 U6 - https://doi.org/10.1016/j.polymdegradstab.2011.01.035 SN - 0141-3910 SN - 1873-2321 VL - 96 IS - 5 SP - 875 EP - 884 PB - Applied Science Publ. CY - London AN - OPUS4-23469 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bykov, M. A1 - Yusenko, Kirill A1 - Bykova, E. A1 - Pakhomova, A. A1 - Kraus, Werner A1 - Dubrovinskaia, N. A1 - Dubrovinsky, L. T1 - Synthesis of arsenopyrite-type rhodium pernitride RhN2 from a single-source azide precursor N2 - Nitrogen-rich noble metal nitrides possess unique mechanical and catalytic properties, therefore their synthesis and characterization is of interest for fundamental solid state chemistry and materials science. In this study we have synthesized a singlesource precursor [Rh(NH3)6]3(N3)5Cl4 (Rh:N ratio 1:11). Its controlled decomposition in a laser-heated diamond anvil cell at 39 GPa resulted in a formation of rhodium pernitride, RhN2. According to the results of single-crystal X-ray diffraction RhN2 has arsenopyrite structure type crystal structure previously unknown for this compound (P21/c (no. 14). KW - EOS KW - High-pressure KW - Nitrides PY - 2019 U6 - https://doi.org/10.1002/ejic.201900488 IS - 32 SP - 3667 EP - 3671 PB - Wiley AN - OPUS4-48924 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -