TY - JOUR A1 - Sun, C. A1 - Tian, X. A1 - Wang, L. A1 - Liu, Y. A1 - Wirth, Cynthia A1 - Günster, Jens A1 - Li, D. A1 - Jin, Z. T1 - Effect of particle size gradation on the performance of glass-ceramic 3D printing process N2 - Particle size gradation is regarded as an effective method for overcoming the contradicting requirements in three-dimensional printing (3DP). In present work, particle size gradation was optimized to obtain both acceptable flowability of the powder material and high-strength 3D-printed glass-ceramic products. The effect of gradation on the printing process, sintering process and performance of the 3D-printed glass-ceramic products was investigated comprehensively. The glass-ceramic powders with three size ranges were mixed in certain proportions and applied to print parts. The result showed parts printed with powder mixed by 60 wt% 45–100 µm and 40 wt% 0–25 µm particles had satisfactory density of 1.60 g/cm³ and bending strength of 13.8 MPa. The flowability decreased with an increasing proportion of fine particles. Part density was determined by the powder bulk density in the powder bed as well as the shrinkage during sintering while strength of part was found to be dependent on the sintering degree. KW - Flowability KW - Glass-ceramic KW - Particle size gradation KW - Three-dimensional printing KW - Mechanical properties PY - 2017 DO - https://doi.org/10.1016/j.ceramint.2016.09.197 SN - 0272-8842 VL - 43 IS - 1 SP - 578 EP - 584 PB - Elsevier AN - OPUS4-39783 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Khare, V. A1 - Li, Z. A1 - Mantion, Alexandre A1 - Ayi, A. A. A1 - Sonkaria, S. A1 - Voelkl, A. A1 - Thünemann, Andreas A1 - Taubert, A. T1 - Strong anion effects on gold nanoparticle formation in ionic liquids N2 - Ionic liquids (ILs) have attracted tremendous interest in the recent past for their potential in many chemical fields. The current report explores the effects of a set of ILs based on the 1-ethyl-3-methyl-imidazolium cation and different anions on the formation of gold nanoparticles. X-Ray diffraction finds face-centered cubic gold in all cases, but transmission electron microscopy (TEM) shows that there are distinct differences in particle formation and stabilization with the ethyl sulfate (ES), trifluoromethanesulfonate (TfO) and methanesulfonate (MS) anions. With the MS anion, nanoparticles with diameters between 5 and 7 nm form, which increasingly aggregate at higher reaction temperatures. With TfO, also small 5 to 7 nm particles form, but only at low temperatures. Above ca. 160 °C, large, ill-defined and aggregated particles form. With ES, polydisperse samples form at all temperatures except 160 °C. In this case the nanoparticles appear often surrounded by an IL film, which appears to stabilize individual, ca. 15 to 20 nm particles. Dynamic light scattering and UV/Vis spectroscopy further show that in suspension the particles are, much like seen in the TEM, more strongly aggregated with higher reaction temperatures. In summary, the results suggest that there are very specific IL-gold interactions that are responsible for the formation of gold particles with an IL-specific shape, size, and aggregation behavior. KW - Ionic liquid templating KW - Gold nanoparticle KW - Ionic liquid PY - 2010 DO - https://doi.org/10.1039/b917467b SN - 0959-9428 SN - 1364-5501 VL - 20 SP - 1332 EP - 1339 PB - Royal Society of Chemistry CY - Cambridge AN - OPUS4-20872 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dzugan, J. A1 - Lucon, E. A1 - Koukolikova, M. A1 - Li, Y. A1 - Rzepa, S. A1 - Yasin, M.S. A1 - Shao, S. A1 - Shamsaei, N. A1 - Seifi, M. A1 - Lodeiro, M. A1 - Lefebvre, F. A1 - Mayer, U. A1 - Olbricht, Jürgen A1 - Houska, M. A1 - Mentl, V. A1 - You, Z. T1 - ASTM interlaboratory study on tensile testing of AM deposited and wrought steel using miniature specimens N2 - An interlaboratory study, involving eigth international laboratories and coordinated by COMTES FHT (Czech Republic), was conducted to validate tensile measurements obtained using miniature specimens on additively manufactured (AM) components and artifacts. In addition to AM 316L stainless steel (316L SS), a wrought highstrength steel (34CrNiMo6V, equivalent to AISI 4340) was also used. Based on the results, a precision statement in accordance with ASTM E691 standard practice was developed, intended for inclusion in a proposed annex to the ASTM E8/E8M tension testing method. The primary outcomes of the study highlighted the agreement between yield and tensile strength measured from miniature and standard-sized tensile specimens. Furthermore, most tensile properties exhibited similar standard deviations, offering users insight into the efficacy of miniature specimen applications. KW - 316L stainless steel KW - Additive manufacturing KW - High-strength steel KW - Miniature specimens KW - Tensile tests PY - 2024 DO - https://doi.org/10.1016/j.tafmec.2024.104410 SN - 0167-8442 VL - 131 SP - 1 EP - 13 PB - Elsevier B.V. AN - OPUS4-60180 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Szymoniak, Paulina A1 - Li, Z. A1 - Wang, D.-Y. A1 - Schoenhals, Andreas T1 - Dielectric and flash DSC investigations on an epoxy based nanocomposite system with MgAl layered double hydroxide as nanofiller N2 - Nanocomposites based on MgAL layered double hydroxides (LDH) and an epoxy resin were prepared and investigated by a combination of complementary methods. As epoxy resin Bisphenol A diglycidyl ether (DGEBA) was used with Diethylenetriamine as curing agent. The LDH was modified with taurine, which acts as an additional crosslinking agent due to its amine groups. The epoxy resin was cured in a presence of the nanofiller, which was added to the system in various concentrations. X-ray scattering, by combination of SAXS and WAXS was used to characterize the morphology of the obtained nanocomposites. These investigations show that the filler is distributed in the matrix as small stacks of ca. 10 layers. The molecular dynamics of the system, as probe for structure, was investigated by broadband dielectric spectroscopy. In addition to the - and -relaxation (dynamic glass transition), characteristic for the unfilled materials, a further process was found which was assigned to localized fluctuations of segments physically adsorbed or chemically bonded to the nanoparticles. The dielectric -relaxation is shifted to higher temperatures for the nanocomposites in comparison to the pure material but depends weakly on the content of nanoparticles. Further, for the first time Flash DSC was employed to a thermosetting system to investigate the glass transition behavior of the nanocomposites. The heating rates were converted in to relaxation rates. For low concentrations of the nanofiller the thermal data overlap more or less with that of the pure epoxy. For higher concentrations the thermal data are shifted significantly to higher temperatures. This is discussed in terms the cooperativity approach to the glass transition. KW - Nanocomposites KW - Broadband dielectric spectroscopy KW - Flash DSC PY - 2019 DO - https://doi.org/10.1016/j.tca.2019.01.010 SN - 0040-6031 VL - 677 SP - 151 EP - 161 PB - Elsevier AN - OPUS4-48218 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gao, S. A1 - Hou, J. A1 - Deng, Z. A1 - Wang, T. A1 - Beyer, Sebastian A1 - de Oliveira Guilherme Buzanich, Ana A1 - Richardson, J. J. A1 - Rawal, A. A1 - Seidel, R. A1 - Zulkifli, M. Y. A1 - Li, W. A1 - Bennett, T. D. A1 - Cheetham, A. K. A1 - Liang, K. T1 - Improving the Acidic Stability of Zeolitic Imidazolate Frameworks by Biofunctional Molecules N2 - Zeolitic imidazolate frameworks (ZIFs) have been widely investigated for their use in separation, gas adsorption, catalysis, and biotechnology. Their practical applications, however, can be hampered by their structural instability in humid acidic conditions. Here, guided by density functional theory calculations, we demonstrate that the acidic stability of two polymorphic ZIFs (i.e., ZIF-8 and ZIF-L) can be enhanced by the incorporation of functional groups on polypeptides or DNA. A range of complementary synchrotron investigations into the local chemical structure and bonding environment suggest that the enhanced acidic stability arises from the newly established coordinative interactions between the Zn centers and the inserted carboxylate (for polypeptides) or phosphate (for DNA) groups, both of which have lower pKas than the imidazolate ligand. With functional biomolecular homologs (i.e., enzymes), we demonstrate a symbiotic stability reinforcement effect, i.e., the encapsulated biomolecules stabilize the ZIF matrix while the ZIF exoskeleton protects the enzyme from denaturation. KW - Zeolitic Imidazolate Frameworks KW - Biofunctional Molecules KW - X-ray Absorption Spectroscopy PY - 2019 DO - https://doi.org/10.1016/j.chempr.2019.03.025 VL - 5 IS - 6 SP - 1597 EP - 1608 PB - Elsevier Inc. AN - OPUS4-48702 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Cabeza, Sandra A1 - Cawley, P. A1 - Li, Z. A1 - Dixon, S. A1 - Jarvis, R. A1 - Nagy, P. B. T1 - Experimental studies of the magneto-mechanical memory (MMM) technique using permanently installed magnetic sensor arrays N2 - The magneto-mechanical memory (MMM) method, that is often referred to as the metal magnetic memory method, has been reported to be a non-destructive testing technique capable of quantifying stress concentrations and detecting defects in ferromagnetic materials. The underlying mechanism behind MMM has been explained in the literature, but the sensitivity to stress concentration has not been satisfactorily investigated. In this paper, both the normal and tangential components of the stress-induced MMM signal were measured by permanently installed magnetic sensor arrays on specimens made from three grades of L80 alloy steel and 20 other structural steels; tests were also carried out on a pipe made from the 4140-L80 steel. As expected, the stress history affects the MMM signal, but the experimental results show that significant irreversible change of magnetization always occurs only in the first cycle of loading regardless whether the deformation is purely elastic or partially plastic. If the peak stress level is increased at a given point during cycling, the immediately following next cycle acts as a new “first” cycle at that peak stress level and causes additional significant irreversible change of magnetization, but there is no evidence that plastic deformation might build up a cumulative magnetization. The MMM effect is very small in the steel samples tested, indicating that it will not be useful in field applications. In un-notched specimens the irreversible change in magnetization caused a proportional change in the measured external magnetic field on the order of only 5–10 A/m, while in the case of notched specimens the leakage field was on the order of 30–60 A/m. KW - Magneto-mechanical memory KW - Stress concentration KW - Permanently installed sensors KW - Irreversible change KW - Cumulative magnetization PY - 2017 DO - https://doi.org/10.1016/j.ndteint.2017.07.019 SN - 0963-8695 SN - 1879-1174 VL - 92 SP - 136 EP - 148 PB - Elsevier Ltd. AN - OPUS4-42936 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Westwood, S. A1 - Josephs, R. D. A1 - Choteau, T. A1 - Martos, G. A1 - Wielgosz, R. A1 - Sarzuri, Y. A. A1 - Mendoza, E. A1 - do Rego, E. C. P. A1 - Violante, F. G. M. A1 - da Silva Souza, W. A1 - de Carvalho, L. J. A1 - Fernandes, J. L. N. A1 - Bates, J. A1 - Rajotte, I. A1 - Melanson, J. E. A1 - Li, H. A1 - Guo, Z. A1 - Su, F. A1 - Wang, S. A1 - Huang, T. A1 - Lalerle, B. A1 - Gantois, F. A1 - Piechotta, Christian A1 - Philipp, Rosemarie A1 - Kaminski, Katja A1 - Klyk-Seitz, Urzsula-Anna A1 - Giannikopoulou, P. A1 - Skotidaki, E. A1 - Kakoulides, E. A1 - Pui-Kwan, C. A1 - Kuroe, M. A1 - Itoh, N. A1 - Calderón, M. A. A. A1 - Contreras, L. R. A1 - Osuna, M. A. A1 - Alrashed, M. A1 - Ting, L. A1 - Mei, G. E. A1 - Juan, W. A1 - Sze, C. P. A1 - Lin, T. T. A1 - Quinn, L. A1 - Swiegelaar, C. A1 - Fernandes-Whaley, M. A1 - Ahn, S. A1 - Chaiphet, T. A1 - Sudsiri, N. A1 - Bellazreg, W. A1 - Bilsel, M. A1 - Colombo, G. T1 - Key comparison CCQM-K78.b - non-polar analytes in organic solvent: methoxychlor and trifluralin in acetonitrile N2 - The CCQM-K78.b key comparison was coordinated by the Bureau International des Poids et Mesures (BIPM) on behalf of the CCQM Organic Analysis Working Group (OAWG) of the 'Comité Consultatif pour la Quantité de Matière' (CCQM), for National Measurement Institutes (NMIs) and Designated Institutes (DIs) providing measurement services in organic analysis under the 'Comité International des Poids et Mesures' (CIPM) Mutual Recognition Arrangement (MRA). This key comparison was conducted as a 'Track A' comparison within the OAWG's 10-year strategic plan. The goal of CCQM-K78.b was to underpin capabilities for the value assignment of calibration solutions containing low polarity/non-polar organic analytes in organic solvents. The selected model system consisted of a two-component pesticide solution in acetonitrile, comprising methoxychlor and trifluralin. Participants were tasked with assigning the mass fractions, in units of μg/g, of methoxychlor and trifluralin in acetonitrile solution. The mass fraction levels and analytical challenges of the selected analytes were representative of those encountered for calibration solutions of non-polar organic analytes. Participation in CCQM-K78.b allowed for the benchmarking of capabilities for assigning the mass fraction of non-polar organic compounds (pKow < -2) in solution, at mass fractions above 5 μg/g, in an organic solvent. Additionally, the comparison assessed the capabilities for the quantitative assignment of thermally labile compounds. Participants were provided by the BIPM with ampoules containing methoxychlor and trifluralin in acetonitrile. Each participant reported the mass fraction content of each analyte in μg/g. All participants ensured the metrological traceability of their results through the use of a Primary Reference Material (PRM), which was used to prepare a primary calibrator solution for each analyte using a gravimetric procedure. The twenty participating institutes primarily used analysis procedures based on GC-MS, -IDMS, -MS/MS, -ECD, and -FID, with some participants also using LC-UV for the value assignment. The analysis of methoxychlor and trifluralin in acetonitrile solution presented several challenges, including the thermal stability of the analytes under selected analytical techniques, control of solvent volatility, and considerable variation in some results using MS-based quantification methods. The mass fraction assignments for methoxychlor and trifluralin, consistent with the key comparison reference values (KCRVs), were achieved with associated relative standard uncertainties of (0.38 - 2.9) % for methoxychlor and (0.35 - 2.5) % for trifluralin. To reach the main text of this paper, click on Final Report. Note that this text is that which appears in Appendix B of the BIPM key comparison database https://www.bipm.org/kcdb/. The final report has been peer-reviewed and approved for publication by the CCQM, according to the provisions of the CIPM Mutual Recognition Arrangement (CIPM MRA). KW - Methoxychlor KW - Trifluralin KW - CCQM KW - Key comparison PY - 2025 DO - https://doi.org/10.1088/0026-1394/62/1A/08010 SN - 0026-1394 VL - 62 IS - 1A SP - 1 EP - 37 PB - IOP Publishing AN - OPUS4-64691 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Raab, A. R. A1 - Grießler, T. R. A1 - Rück, D. A1 - Li, Z. A1 - Zens, A. A1 - Bruckner, J. R. A1 - Huber, P. A1 - Schönhals, Andreas A1 - Szymoniak, Paulina A1 - Laschat, S. T1 - Salt complexation drives liquid crystalline selfassembly in crown ether–amino acid hybrids N2 - Crown ether–amino acid hybrids represent a promising class of amphiphilic molecules combining ion recognition with self-assembly capabilities. Despite extensive studies on their binding properties, the influence of inorganic salt complexation on their liquid crystalline behaviour remains underexplored. Here we synthesized amphiphilic [18]-crown-6 derivatives of L-dihydroxyphenylalanine and tetrahydroisoquinoline analogues, systematically investigating the effects of alkyl chain length and salt type on mesophase formation. Complexation with various salts induced liquid crystalline phases, transitioning from smectic A to columnar hexagonal structures as anion size and alkyl chain length increased. Structural analyses and electron density mapping revealed assembly into charged superdiscs forming columnar stacks with tunable ion channels. Broadband dielectric spectroscopy highlighted differences in molecular mobility and conductivity linked to molecular design. These findings establish salt complexation as a key strategy to control self-assembly and ion transport in crown ether–amino acid hybrids, advancing their potential in responsive soft materials and ion-conductive applications. KW - Ionic liquid crystals PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-655986 DO - https://doi.org/10.1039/d5tc04129e SP - 1 EP - 18 PB - Royal Society of Chemistry (RSC) AN - OPUS4-65598 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hu, W.-H A1 - Tang, D.-H. A1 - Wang, M. A1 - Liu, J.-L. A1 - Li, Z.-H. A1 - Lu, W. A1 - Teng, J. A1 - Said, Samir A1 - Rohrmann, R. G. T1 - Resonance Monitoring of a Horizontal Wind Turbine by Strain-Based Automated Operational Modal Analysis N2 - A strain-based automated operational modal analysis algorithm is proposed to track the long-term dynamic behavior of a horizontal wind turbine under operational conditions. This algorithm is firstly validated by a scaled wind turbine model, and then it is applied to the dynamic strain responses recorded from a 5 MW wind turbine system. We observed variations in the fundamental frequency and 1f, 3f excitation frequencies due to the mass imbalance of the blades and aerodynamic excitation by the tower dam or tower wake. Inspection of the Campbell diagram revealed that the adverse resonance phenomenon and Sommerfeld effect causing excessive vibrations of the wind tower. KW - Strain KW - Automated operational modal analysis KW - Resonance KW - Horizontal wind turbine PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-503350 DO - https://doi.org/10.3390/en13030579 VL - 13 IS - 3 SP - 579 EP - 584 PB - MDPI CY - Schweiz, Basel AN - OPUS4-50335 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Deng, C. A1 - Yin, Huajie A1 - Li, R.-M. A1 - Huang, S.-C. A1 - Schartel, Bernhard A1 - Wang, Y.-Z. T1 - Modes of action of a mono-component intumescent flame retardant MAPP in polyethylene-octene elastomer N2 - A mono-component intumescent flame retardant named ethylenediamine-modified ammonium polyphosphate (MAPP) is used in polyethylene-octene elastomer (POE). Insight into the flame-retardant mechanisms of the MAPP is provided from a new perspective. The fire performance of POE/MAPP composites is investigated by oxygen index (OI) and vertical burning (UL-94) tests. POE Composite containing 35 wt% MAPP achieves a V-0 rating, and its OI is 29.3 vol%. The thermogravimetric Analysis (TGA) and Fourier transform infrared spectra (FTIR) confirm that the incorporation of ethylenediamine changes the thermal decomposition of APP, mainly resulting in the formation of char layer with a thermally stable structure. Cone calorimeter analysis revealed the flame-retardant modes of action of MAPP in POE under forced-flaming conditions. Quantitative analysis illustrates that both the residue due to charring and the fuel dilution/flame Inhibition resulting from the release of incombustible products/ phosphorus species decrease the total heat release (fire load) by 20e28%. The residue increases linearly with increasing MAPP content, whereas the reduction in effective heat of combustion levels off. Moreover, the flame-retardant effect resulting from the protective properties of the char is discovered to be the dominant mode of action (up to 85% reduction) with respect to the peak heat release rate, leading to the excellent flame retardancy of POE/MAPP. KW - Ammonium polyphosphate KW - Flame retardant KW - Carbonization KW - Elastomer PY - 2017 DO - https://doi.org/10.1016/j.polymdegradstab.2017.03.006 SN - 0141-3910 SN - 1873-2321 VL - 138 SP - 142 EP - 150 PB - Elsevier AN - OPUS4-39901 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -