TY - JOUR A1 - Sachse, René A1 - Bernsmeier, D. A1 - Schmack, R. A1 - Häusler, I. A1 - Hertwig, Andreas A1 - Kraffert, K. A1 - Nissen, J. A1 - Kraehnert, R. T1 - Colloidal bimetallic platinum–ruthenium nanoparticles in ordered mesoporous carbon films as highly active electrocatalysts for the hydrogen evolution reaction N2 - Hydrogen features a very high specific energy density and is therefore a promising candidate for clean fuel from renewable resources. Water electrolysis can convert electrical energy into storable and transportable hydrogen gas. Under acidic conditions, platinum is the most active and stable monometallic catalyst for the hydrogen evolution reaction (HER). Yet, platinum is rare and needs to be used efficiently. Here, we report a synthesis concept for colloidal bimetallic platinum–ruthenium and rhodium–ruthenium nanoparticles (PtRuNP, RhRuNP) and their incorporation into ordered mesoporous carbon (OMC) films. The films exhibit high surface area, good electrical conductivity and well-dispersed nanoparticles inside the mesopores. The nanoparticles retain their size, crystallinity and composition during carbonization. In the hydrogen evolution reaction (HER), PtRuNP/OMC catalyst films show up to five times higher activity per Pt than Pt/C/Nafion® and PtRu/C/Nafion® reference catalysts. KW - Ordered mesoporous carbon KW - Bimetallic noble metal nanoparticles KW - Platinum-ruthenium colloid KW - Electrolysis KW - Hydrogen evolution reaction PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-506868 DO - https://doi.org/10.1039/C9CY02285F SN - 2044-4753 VL - 10 IS - 7 SP - 2057 EP - 2068 PB - Royal Society of Chemistry AN - OPUS4-50686 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schmack, R. A1 - Eckhardt, B. A1 - Koch, G. A1 - Ortel, Erik A1 - Kraehnert, R. T1 - ZnO coatings with controlled pore size, crystallinity and electrical conductivity N2 - Zinc oxide is a wide bandgap semiconductor with unique optical, electrical and catalytic properties. Many of its practical applications rely on the materials pore structure, crystallinity and electrical conductivity. We report a synthesis method for ZnO films with ordered mesopore structure and tuneable crystallinity and electrical conductivity. The synthesis relies on dip-coating of solutions containing micelles of an amphiphilic block copolymer and complexes of Zn2+ ions with aliphatic ligands. A subsequent calcination at 400 °C removes the template and induces crystallization of the pore walls. The pore structure is controlled by the template polymer, whereas the aliphatic ligands control the crystallinity of the pore walls. Complexes with a higher thermal stability result in ZnO films with a higher content of residual carbon, smaller ZnO crystals and therefore lower electrical conductivity. The paper discusses the ability of different types of ligands to assist in the synthesis of mesoporous ZnO and relates the structure and thermal stability of the precursor complexes to the crystallinity and electrical conductivity of the zinc oxide. KW - conductivity KW - EISA KW - pore templating KW - pore size control KW - ligands KW - zinc oxide PY - 2016 DO - https://doi.org/10.5755/j01.ms.22.1.8634 SN - 1392–1320 VL - 22 IS - 1 SP - 74 EP - 81 PB - Kaunas University of Technology, Lithuania AN - OPUS4-35550 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ortel, Erik A1 - Bernicke, M. A1 - Eckhardt, B. A1 - Bernsmeier, D. A1 - Schmack, R. A1 - Kraehnert, R. A1 - Lippitz, Andreas T1 - Synthesis and OER activity of NiO coatings with N2 - Catalysts based on nickel oxide are some of the most active catalysts for the oxygen evolution reaction (OER) in alkaline media. However, preparing catalytic coatings with high surface area and good accessibility of the active sites remains challenging. We present a new approach for the synthesis of homogeneous and binder-free nickel oxide coatings comprising a highly accessible ordered mesopore structure. The synthesis is achieved via evaporation induced self assembly utilizing PEOPB-PEO triblock copolymers as pore template and a chemical complex of Ni2+ and citric acid as precursor. Excessive crystallization behaviour of NiO is avoided by thermal conversion of the precursor into an amorphous Ni carbonate intermediate, followed by transition of the carbonate into the metal oxide. We present a comprehensive analysis of the obtained materials in terms of morphology, crystallinity, surface area, composition, and OER activity of differently calcined catalysts. Retaining a low crystallinity and high surface area during the Synthesis proofs to be the most important factor in obtaining a highly active OER catalyst. KW - XPS KW - nanoparticle KW - catalysis PY - 2016 UR - http://onlinelibrary.wiley.com/doi/10.1002/slct.201600110/abstract DO - https://doi.org/10.1002/slct.201600110 VL - 2016 IS - 3/2016 SP - 482 EP - 489 PB - Wiley Online Library CY - Weinheim AN - OPUS4-35725 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Frisch, M. A1 - Raza, M. H. A1 - Ye, M.-Y. A1 - Sachse, René A1 - Paul, B. A1 - Gunder, R. A1 - Pinna, N. A1 - Kraehnert, R. T1 - ALD-coated mesoporous iridium-titanium mixed oxides: Maximizing iridium utilization for an outstanding OER performance N2 - With the increasing production of renewable energy and concomitant depletion of fossil resources, the demand for efficient water splitting electrocatalysts continues to grow. Iridium (Ir) and iridium oxides (IrOₓ) are currently the most promising candidates for an efficient oxygen evolution reaction (OER) in acidic medium, which remains the bottleneck in water electrolysis. Yet, the extremely high costs for Ir hamper a widespread production of hydrogen (H₂) on an industrial scale. Herein, the authors report a concept for the synthesis of electrode coatings with template-controlled mesoporosity surface-modified with highly active Ir species. The improved utilization of noble metal species relies on the synthesis of soft-templated metal oxide supports and a subsequent shape-conformal deposition of Ir species via atomic layer deposition (ALD) at two different reaction temperatures. The study reveals that a minimum Ir content in the mesoporous titania-based support is mandatory to provide a sufficient electrical bulk conductivity. After ALD, a significantly enhanced OER activity results in dependency of the ALD cycle number and temperature. The most active developed electrocatalyst film achieves an outstanding mass-specific activity of 2622 mA mg(Ir)⁻¹ at 1.60 V(RHE) in a rotating-disc electrode (RDE) setup at 25 °C using 0.5 m H₂SO₄ as a supporting electrolyte. KW - Acidic oxygen evolution reaction KW - Atomic layer deposition KW - Electrocatalysis KW - Iridium oxide KW - Soft-templated mesoporous films PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-542651 DO - https://doi.org/10.1002/admi.202102035 SN - 2196-7350 SP - 1 EP - 11 PB - Wiley-VCH CY - Weinheim AN - OPUS4-54265 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kraffert, K. A1 - Karg, M. A1 - Schmack, R. A1 - Clavel, G. A1 - Boissiere, C. A1 - Wirth,, Thomas A1 - Pinna, N. A1 - Kraehnert, R. T1 - Stabilization of Mesoporous Iron Oxide Films against Sintering and Phase Transformations via Atomic Layer Deposition of Alumina and Silica N2 - The stabilization of crystal phases and nanostructured morphologies is an essential topic in application-driven design of mesoporous materials. Many applications, e.g. catalysis, require high temperature and humidity. Typical metal oxides transform under such conditions from a metastable, low crystal-line material into a thermodynamically more favorable form, i.e. from ferrihy-drite into hematite in the case of iron oxide. The harsh conditions induce also a growth of the crystallites constituting pore walls, which results in sintering and finally collapse of the porous network. Herein, a new method to stabi-lize mesoporous templated metal oxides against sintering and pore collapse is reported. The method employs atomic layer deposition (ALD) to coat the internal mesopore surface with thin layers of either alumina or silica. The authors demonstrate that silica exerts a very strong influence: It shifts hematite formation from 400 to 600 °C and sintering of hematite from 600 to 900 °C. Differences between the stabilization via alumina and silica are rationalized by a different interaction strength between the ALD material and the ferrihydrite film. The presented approach allows to stabilize mesoporous thin films that require a high crystallization temperature, with submonolayer quantity of an ALD material, and to apply mesoporous materials for high temperature applications. KW - Mesoporous oxides KW - Atomic layer deposition KW - Stabilization PY - 2018 DO - https://doi.org/10.1002/admi.201800360 VL - 5 IS - 14 SP - 1800360-1 EP - 1800360-9 PB - Wiley-VCH AN - OPUS4-47869 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bernsmeier, D. A1 - Bernicke, M. A1 - Ortel, Erik A1 - Bergmann, A. A1 - Lippitz, Andreas A1 - Nissen, J. A1 - Schmack, R. A1 - Strasser, P. A1 - Polte, J. A1 - Kraehnert, R. T1 - Nafion-free carbon-supported electrocatalysts with superior hydrogen evolution reaction performance by soft templating N2 - Efficient water electrolysis requires electrode coatings with high catalytic activity. Platinum efficiently catalyzes the hydrogen evolution reaction in acidic environments, but is a rare and expensive metal. The activity achieved per metal atom can be increased if small Pt particles are dispersed onto electrically conductive, highly accessible and stable support materials. However, the addition of Nafion, a typical binder material used in the manufacture of electrode coatings, can decrease catalytic activity by the blocking of pores and active surface sites. A new approach is reported for the direct synthesis of highly active Nafion-free Pt/C catalyst films consisting of small Pt nanoparticles supported in size-controlled mesopores of a conductive carbon film. The synthesis relies on the co-deposition of suitable Pt and C precursors in the presence of polymer micelles, which act as pore templates. Subsequent carbonization in an inert atmosphere produces porous catalyst films with controlled film thickness, pore size and particle size. The catalysts clearly outperform all Nafion-based Pt/C catalysts reported in the literature, particularly at high current densities. KW - XPS KW - SEM KW - TEM KW - SAXS KW - Catalysis KW - Electrochemistry PY - 2017 DO - https://doi.org/10.1002/celc.201600444 SN - 2196-0216 VL - 4 IS - 1 SP - 221 EP - 229 PB - Wiley Online Library CY - Weinheim AN - OPUS4-39733 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kraehnert, R. A1 - Ortel, Erik A1 - Paul, B. A1 - Eckhardt, B. A1 - Kanis, M. A1 - Liu, R. A1 - Antoniou, A. T1 - Electrochemically dealloyed platinum with hierarchical pore structure as highly active catalytic coating N2 - Micro structured reactors are attractive candidates for further process intensification in heterogeneous catalysis. However, they require catalytic coatings with significantly improved space-time yields compared to traditional supported catalysts. We report the facile synthesis of homogeneous nanocrystalline Pt coatings with hierarchical pore structure by electrochemical dealloying of amorphous sputter-deposited platinum silicide layers. Thickness, porosity and surface composition of the catalysts can be controlled by the dealloying procedure. XPS analysis indicates that the catalyst surface is primarily composed of metallic Pt. Catalytic tests in gas-phase hydrogenation of butadiene reveal the typical activity, selectivity and activation energy of nanocrystalline platinum. However, space time yields are about 13 to 200 times higher than values reported for Pt-based catalysts in literature. The highly open metallic pore structure prevents heat and mass transport limitations allowing for very fast reactions and reasonable stability at elevated temperatures. KW - Pt catalysts KW - Pt–Si layers KW - Scanning Electron Microscopy (SEM) KW - Transmission Electron Microscopy (TEM) KW - pore structure KW - electrochemical dealloying PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-351393 DO - https://doi.org/10.1039/C4CY00851K SN - 2044-4753 SN - 2044-4761 VL - 5 IS - 1 SP - 206 EP - 216 PB - RSC Publ. CY - Cambridge AN - OPUS4-35139 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Seidel, R. A1 - Kraffert, K. A1 - Kabelitz, Anke A1 - Pohl, M.N. A1 - Kraehnert, R. A1 - Emmerling, Franziska A1 - Winter, B. T1 - Detection of the electronic structure of iron-(III)-oxo oligomers forming in aqueous solutions N2 - The nature of the small iron-oxo oligomers in iron-(III) aqueous solutions has a determining effect on the chemical processes that govern the formation of nanoparticles in aqueous phase. Here we report on a liquid-Jet photoelectron-spectroscopy experiment for the investigation of the electronic structure of the occurring iron-oxo oligomers in FeCl3 aqueous solutions. The only iron species in the as-prepared 0.75 M solution are Fe3+ monomers. Addition of NaOH initiates Fe3+ hydrolysis which is followed by the formation of iron-oxo oligomers. At small enough NaOH concentrations, corresponding to approximately [OH]/[Fe] = 0.2–0.25 ratio, the iron oligomers can be stabilized for several hours without engaging in further aggregation. Here, we apply a combination of non-resonant as well as iron 2p and Oxygen 1s resonant photoelectron spectroscopy from a liquid microjet to detect the electronic structure of the occurring species. Specifically, the oxygen 1s partial electron yield X-ray absorption (PEY-XA) spectra are found to exhibit a peak well below the onset of liquid water and OH (aq) absorption. The iron 2p absorption gives rise to signal centered between the main absorption bands typical for aqueous Fe3+. Absorption bands in both PEY-XA spectra are found to correlate with an enhanced photoelectron Peak near 20 eV binding energy, which demonstrates the sensitivity of resonant photoelectron (RPE) spectroscopy to mixing between iron and ligand orbitals. These various signals from the iron-oxo oligomers exhibit Maximum intensity at [OH]/[Fe] = 0.25 ratio. For the same ratio, we observe changes in the pH as well as in complementary Raman spectra, which can be assigned to the Transition from monomeric to oligomeric species. At approximately [OH]/[Fe] = 0.3 we begin to observe particles larger than 1 nm in radius, detected by small-angle X-ray scattering. KW - Iron-oxo oligomers KW - XPS KW - Electronic structure PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-433468 DO - https://doi.org/10.1039/c7cp06945f SN - 1463-9076 SN - 1463-9084 VL - 19 IS - 48 SP - 32226 EP - 32234 AN - OPUS4-43346 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kabelitz, Anke A1 - de Oliveira Guilherme Buzanich, Ana A1 - Joester, Maike A1 - Reinholz, Uwe A1 - Radtke, Martin A1 - Bienert, Ralf A1 - Schulz, K. A1 - Schmack, R. A1 - Kraehnert, R. A1 - Emmerling, Franziska T1 - Time-resolved in situ studies on the formation mechanism of iron oxide nanoparticles using combined fast-XANES and SAXS N2 - The reaction of iron chlorides with an alkaline reagent is one of the most prominent methods for the synthesis of iron oxide nanoparticles. We studied the particle formation mechanism using triethanolamine as reactant and stabilizing agent. In situ fast-X-ray absorption near edge spectroscopy and small-angle X-ray scattering provide information on the oxidation state and the structural information at the same time. In situ data were complemented by ex situ transmission electron microscopy, wide-angle X-ray scattering and Raman analysis of the formed nanoparticles. The formation of maghemite nanoparticles (γ-Fe2O3) from ferric and ferrous chloride was investigated. Prior to the formation of these nanoparticles, the formation and conversion of intermediate phases (akaganeite, iron(II, III) hydroxides) was observed which undergoes a morphological and structural collapse. The thus formed small magnetite nanoparticles (Fe3O4) grow further and convert to maghemite with increasing reaction time. KW - oxidation state KW - structural information KW - maghemite PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-351376 DO - https://doi.org/10.1039/C5CE01585E SN - 1466-8033 VL - 17 IS - 44 SP - 8463 EP - 8470 CY - London, UK AN - OPUS4-35137 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kraffert, K. A1 - Kabelitz, Anke A1 - Siemensmeyer, K. A1 - Schmack, R. A1 - Bernsmeier, D. A1 - Emmerling, Franziska A1 - Kraehnert, R. T1 - Nanocasting of superparamagnetic iron oxide films with ordered mesoporosity N2 - Maghemite and magnetite show superparamagnetic behavior when synthesized in a nanostructured form. The material’s inducible magnetization enables applications ranging from contrast enhancing agents for magnetic resonance imaging to drug delivery systems, magnetic hyperthermia, and separation. Superparamagnetic iron oxides with templated porosity have been synthesized so far only in the form of hard-templated powders, where silicon retained from the template severely degrades the material’s magnetic properties. Here, for the first time, the synthesis of superparamagnetic iron oxides with soft-templated mesopore structure is reported. The synthesis of nanostructured maghemite and magnetite films succeeds using micelles of amphiphilic block-copolymers as templates. A thermal treatment of the initially formed mesoporous ferrihydrite in nitrogen produces maghemite, which can be partly reduced to magnetite via thermal treatment in hydrogen while retaining the templated mesopore structure. The resulting materials feature a unique combination of high surface area, controlled pore diameter, and tunable magnetic properties. KW - Iron oxide films KW - Mesoporosity KW - Soft-templated PY - 2018 DO - https://doi.org/10.1002/admi.201700960 SN - 2196-7350 VL - 5 IS - 3 SP - 1700960, 1 EP - 1700960, 7 PB - Wiley-VCH CY - Weinheim AN - OPUS4-43560 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schulz, K. A1 - Schmack, R. A1 - Klemm, H. W. A1 - Kabelitz, Anke A1 - Schmidt, T. A1 - Emmerling, Franziska A1 - Kraehnert, R. T1 - Mechanism and kinetics of hematite crystallization in air: Linking bulk and surface models via mesoporous films with defined nanostructure N2 - Iron can form numerous oxides, hydroxides, and oxide−hydroxides. Despite their relevance, many of the transformation processes between these phases are still poorly understood. In particular the crystallization of quasi-amorphous hydroxides and oxide−hydroxides is difficult to assess, since typical diffraction and scattering methods provide only sampleaveraged information about the crystallized phases. We report a new approach for the investigation of the crystallization of oxide−hydroxides. The approach relies on model-type films that comprise a defined homogeneous nanostructure. The nanostructure allows quantitative linking of Information obtained by bulk-averaging diffraction techniques (XRD, SAXS) with locally resolved information, i.e., Domain sizes (SEM, TEM, LEEM) and phase composition (SAED). Using time-resolved imaging and diffraction we deduce mechanism and kinetics for the crystallization of ferrihydrite into hematite. Hematite forms via nucleation of hematite domains and subsequent Domain growth that terminates only upon complete transformation. A Johnson−Mehl−Avrami−Kolmogorov model describes the kinetics over a wide temperature range. The derived understanding enables the first synthesis of ferrihydrite films with ordered mesoporosity and quantitative control over the films’ hematite and ferrihydrite content. KW - Iron oxide KW - Crystallization KW - Mesoporous films KW - Nanostructure PY - 2017 DO - https://doi.org/10.1021/acs.chemmater.6b05185 SN - 0897-4756 SN - 1520-5002 VL - 29 IS - 4 SP - 1724 EP - 1734 AN - OPUS4-39690 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bernicke, M. A1 - Ortel, Erik A1 - Reier, T. A1 - Bergmann, A. A1 - De Araujo, J.F. A1 - Strasser, P. A1 - Kraehnert, R. T1 - Iridium oxide coatings with templated porosity as highly active oxygen evolution catalysts: Structure-activity relationships N2 - Iridium oxide is the catalytic material with the highest stability in the oxygen evolution reaction (OER) performed under acidic conditions. However, its high cost and limited availability demand that IrO2 is utilized as efficiently as possible. We report the synthesis and OER performance of highly active mesoporous IrO2 catalysts with optimized surface area, intrinsic activity, and pore accessibility. Catalytic layers with controlled pore size were obtained by soft-templating with micelles formed from amphiphilic block copolymers poly(ethylene oxide)-b-poly(butadiene)-b-poly(ethylene oxide). A systematic study on the influence of the calcination temperature and film thickness on the morphology, phase composition, accessible surface area, and OER activity reveals that the catalytic performance is controlled by at least two independent factors, that is, accessible surface area and intrinsic activity per accessible site. Catalysts with lower crystallinity show higher intrinsic activity. The catalyst surface area increases linearly with film thickness. As a result of the templated mesopores, the pore surface remains fully active and accessible even for thick IrO2 films. Even the most active multilayer catalyst does not show signs of transport limitations at current densities as high as 75 mA cm-2. KW - Electrochemistry KW - Iridium KW - Structure–activity relationships KW - Template synthesis KW - Water splitting PY - 2015 DO - https://doi.org/10.1002/cssc.201402988 SN - 1864-5631 SN - 1864-564X VL - 8 IS - 11 SP - 1908 EP - 1915 PB - Wiley-VCH CY - Weinheim AN - OPUS4-33503 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Frisch, M. A1 - Laun, J. A1 - Marquardt, Julien A1 - Arinchtein, A. A1 - Bauerfeind, K. A1 - Bernsmeier, D. A1 - Bernicke, M. A1 - Bredow, T. A1 - Kraehnert, R. T1 - Bridging experiment and theory: enhancing the electrical conductivities of soft-templated niobium-doped mesoporous titania films† N2 - Theoretical calculations suggest a strong dependence of electrical conductivity and doping concentration in transition-metal doped titania. Herein, we present a combined theoretical and experimental approach for the prediction of relative phase stability and electrical conductivity in niobium-doped titania as model system. Our method paves the way towards the development of materials with improved electrical properties. KW - Electrical conductivity KW - Prediction relative KW - Transition-metal doped KW - System method PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-521371 DO - https://doi.org/10.1039/d0cp06544g SN - 1463-9084 VL - 23 IS - 5 SP - 3219 EP - 3224 PB - Royal Society of Chemistry AN - OPUS4-52137 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kraehnert, R. T1 - Electrochemically dealloyed Platinum with hierarchical pore structure as highly active catalytic coating T2 - 27. Deutsche Zeolith-Tagung CY - Oldenburg, Germany DA - 2015-02-25 PY - 2015 AN - OPUS4-32932 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sachse, René A1 - Hodoroaba, Vasile-Dan A1 - Kraehnert, R. A1 - Hertwig, Andreas T1 - Multilevel effective material approximation for modeling ellipsometric measurements on complex porous thin films N2 - Catalysts are important components in chemical processes because they lower the activation energy and thus determine the rate, efficiency and selectivity of a chemical reaction. This property plays an important role in many of today’s processes, including the electrochemical splitting of water. Due to the continuous development of catalyst materials, they are becoming more complex, which makes a reliable evaluation of physicochemical properties challenging even for modern analytical measurement techniques and industrial manufacturing. We present a fast, vacuum-free and non-destructive analytical approach using multi-sample spectroscopic ellipsometry to determine relevant material parameters such as film thickness, porosity and composition of mesoporous IrOx–TiOy films. Mesoporous IrOx–TiOy films were deposited on Si wafers by sol–gel synthesis, varying the composition of the mixed oxide films between 0 and 100 wt%Ir. The ellipsometric modeling is based on an anisotropic Bruggeman effective medium approximation (a-BEMA) to determine the film thickness and volume fraction of the material and pores. The volume fraction of the material was again modeled using a Bruggeman EMA to determine the chemical composition of the materials. The ellipsometric fitting results were compared with complementary methods, such as scanning electron microscopy (SEM), electron probe microanalysis (EPMA) as well as environmental ellipsometric porosimetry (EEP). KW - Electrochemical catalysts KW - Mixed metal oxide KW - Multi-sample analysis KW - Spectroscopic ellipsometry KW - Thin mesoporous films PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-551026 DO - https://doi.org/10.1515/aot-2022-0007 SN - 2192-8584 SN - 2192-8576 VL - 11 IS - 3-4 (Topical issue: Ellipsometry) SP - 137 EP - 147 PB - De Gruyter CY - Berlin AN - OPUS4-55102 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sachse, René A1 - Hertwig, Andreas A1 - Kraehnert, R. A1 - Hodoroaba, Vasile-Dan T1 - Analysis of mesoporous iridium oxide thin films by the combined methodical approach SEM/EDS/STRATAGem N2 - For the determination of porosity of Ir oxide thin films, electron probe microanalysis (EPMA) can be used as part of a combined SEM/EDS/STRATAGem analysis. The mass deposition (in μg cm-2) of films was calculated with the analysis software STRATAGem via k-values measured with EDS. The average density of coated films was obtained from the mass deposition and the film thickness as measured by the cross-section SEM. The porosity was calculated by dividing the average film density by the bulk (theoretical) density of the film material. Film porosities were counterchecked by spectroscopic ellipsometry (SE) using the Bruggeman effective medium approximation (BEMA). The results obtained by both analytical approaches/methods used, SEM/EDS/STRATAGem and SE were in good agreement. KW - Porous thin films KW - Iridium oxide KW - Electron probe microanalysis (EPMA) KW - Spectroscopic ellipsometry PY - 2018 UR - https://www.cambridge.org/core/journals/microscopy-and-microanalysis/article/analysis-of-mesoporous-iridium-oxide-thin-films-by-the-combined-methodical-approach-semedsstratagem/7607018338B542D8B8C4D944392781EF DO - https://doi.org/10.1017/S1431927618004300 SN - 1431-9276 SN - 1435-8115 VL - 24 IS - S1 (August) SP - 762 EP - 763 PB - Cambridge University Press CY - New York, NY, U.S.A. AN - OPUS4-45951 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ortel, Erik A1 - Hertwig, Andreas A1 - Berger, D. A1 - Esposito, P. A1 - Rossi, A. M. A1 - Kraehnert, R. A1 - Hodoroaba, Vasile-Dan T1 - New approach on quantification of porosity of thin films via electron-excited X‑ray spectra N2 - One of the crucial characteristics of functionalized thin films is their porosity (i.e., the ratio between the pore volume and the volume of the whole film). Due to the very low amount of material per coated area corresponding to thin films, it is a challenge for analytics to measure the film porosity. In this work, we present an Approach to determine the porosity of thin films by means of electron probe microanalysis (EPMA) either by wavelength-dispersive X-ray spectrometry (WDX) or by energy-dispersive X-ray spectrometry (EDX) with a scanning electron microscope (SEM). The procedure is based on the calculation of the film mass deposition from electron-excited X-ray spectra. The mass deposition is converted into film density by division of measured film thickness. Finally, the film porosity is calculated from the measured film density and the density of bulk, nonporous film material. The general applicability of the procedure to determine the porosity is demonstrated on thin templated mesoporous TiO₂ films, dip-coated on silicon wafer, with controlled porosity in the range of 15 to 50%. The high accuracy of the mass deposition as determined from X-ray spectra was validated with independent methods (ICP-OES and weighing). Furthermore, for the validation of the porosity results, ellipsometry, interference fringes method (IFM), and focused ion beam (FIB) cross sectioning were employed as independent techniques. Hence, the approach proposed in the present study is proven to be suited as a new analytical tool for accurate and relatively fast determination of the porosity of thin films. KW - Porosity KW - X-rays KW - EDX KW - Thin film KW - TiO2 KW - Density KW - Mass deposition KW - STRATAGem PY - 2016 UR - http://pubs.acs.org/doi/abs/10.1021/acs.analchem.6b00847 DO - https://doi.org/10.1021/acs.analchem.6b00847 VL - 88 IS - 14 SP - 7083 EP - 7090 PB - ACS Publications CY - 1155 Sixteenth Street N.W., Washington, DC 20036 AN - OPUS4-36911 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Arinchtein, A. A1 - Ye, M.-Y. A1 - Yang, Q. A1 - Kreyenschulte, C. A1 - Wagner, Andreas A1 - Frisch, M. A1 - Brückner, A. A1 - Kondratenko, E. A1 - Kraehnert, R. T1 - Dynamics of Reaction-Induced Changes of Model-Type Iron Oxide Phases in the CO2-Fischer-Tropsch-Synthesis N2 - Iron-based catalysts are employed in CO2-FTS due to their ability to convert CO2 into CO in a first step and their selectivity towards higher hydrocarbons in a second CO hydrogenation step. According to the literature, iron carbides represent the active phase for hydrocarbon formation and are claimed to emerge in the presence of CO. We propose nanostructured FeOx films as model systems to assess information about the complex phase transformations during CO2-FTS. Mesoporous hematite, ferrihydrite, maghemite, maghemite/magnetite films were exposed to CO2-FTS atmospheres at 20 bar and 300°C. Up to three distinct phases were observed depending on the timeon-stream (TOS): a sintered maghemite/magnetite phase, a carbidic core-shell structure, and a low-crystalline, needle-type oxide phase. Our findings indicate that the formation of an intermediary maghemite/magnetite phase, predominant after short TOS (30 h), precedes the evolution of the carbide phase. Yet, even after prolonged TOS (185 h), no full conversion into a bulk carbide is observed. KW - Nanostructured FeOx films KW - CO2 KW - Scanning Auger Spectroscopy PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-549709 DO - https://doi.org/10.1002/cctc.202200240 SN - 1867-3880 VL - 14 IS - 14 SP - 1 EP - 11 PB - Wiley-VCH AN - OPUS4-54970 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sachse, René A1 - Hodoroaba, Vasile-Dan A1 - Hertwig, Andreas A1 - Kotil, L. A1 - Kraehnert, R. T1 - Analysis of elemental composition and porosity of mesoporous iridium titanium mixed oxide thin films for energy application by SEM/EDS N2 - Porous materials play an important role in several fields of technology, especially for energy applications like photovoltaics, electrolysis or batteries. The activity of porous films is affected by properties like porosity, film thickness, chemical composition of the material as well as the crystallinity of the framework. The complex morphology of such porous films constitutes a challenge even for modern analytical techniques and requires new approaches employing the combination/complementation of data of different analytical methods. In this contribution we characterize thin mesoporous iridium-titanium mixed oxide film properties by Electron Probe Microanalysis (EPMA) with energy dispersive X-ray spectroscopy (EDS) at an SEM. KW - Electron probe microanalysis (EPMA) KW - Iridium-titanium mixed oxides KW - Spectroscopic ellipsometry KW - Mesoporous thin films KW - NanoSIMS PY - 2019 DO - https://doi.org/10.1017/S1431927619009589 SN - 1431-9276 (Print) SN - 1435-8115 (Online) VL - 25 IS - S2 (August) SP - 1770 EP - 1771 PB - Cambridge University Press CY - New York, NY, U.S.A. AN - OPUS4-48768 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kraehnert, R. T1 - Porosity of highly porous thin films studied by X-rays at SEM T2 - 27. Deutsche Zeolith-Tagung CY - Oldenburg, Germany DA - 2015-02-25 PY - 2015 AN - OPUS4-32933 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -