TY - CONF A1 - Weltschev, Margit A1 - Haufe, Manuela A1 - Kohl, Anka A1 - Rehfeldt, Rainer T1 - Resistance of polyethylene grades with permeation barriers in biofuels N2 - Biofuels including ethanol and biodiesel (FAME) represent a renewable fuel alternative to petroleum-derived transport fuels. The aim of this work was to study the interaction between high density polyethylene (HDPE) with permeation barriers in form of polyamide (PA) and fluorination, and biofuels such as E85 (fuel with 85 % ethanol), biodiesel and B10 (heating oil with 10 % biodiesel). 10 l jerrycans made of polyethylene with permeation barrier of PA were filled with E85 and biodiesel and exposed to temperatures of 20 °C and 40 °C for 5 years. Half of the 20 l jerrycans of HDPE for filling with B10 were fluorinated at the inner layer to prevent permeation before the exposure. Tensile properties were determined once a year, and FTIR-spectroscopy was used to evaluate possible changes. The tensile properties tensile strength and breaking elongation of HDPE jerrycan cuttings with permeation barrier decreased, but not significantly, after immersion in E85, biodiesel and B10. The elasticity modulus of the polyethylene grades was especially reduced during exposure to E85. The FTIR spectra of HDPE jerrycan cuttings with permeation barrier showed that immersion tests for five years with the test fuels at 20 °C and 40 °C did not lead to a decomposition of the permeation barriers. T2 - CORROSION 2018 CY - Phönix, Arizona, USA DA - 16.04.2018 KW - Polyethylene grades KW - Biofuels KW - Permeation barriers KW - FTIR spectra PY - 2018 SP - Paper 10543, 1 EP - Paper 10543, 12 PB - NACE International CY - Houston, Texas, USA AN - OPUS4-44768 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Peuker, Christel A1 - Bessau, Waltraud A1 - Brzezinka, Klaus-Werner A1 - Kohl, Anka A1 - Reinholz, Uwe A1 - Geißler, Heinz T1 - IR and Raman study of calcium aluminosilicate glasses of the composition xCaO.xAl2O3.(100-2x)SiO2 PY - 2002 SN - 0927-4472 VL - 75 IS - 6 SP - 313 EP - 322 PB - Elsevier CY - Amsterdam AN - OPUS4-2304 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weltschev, Margit A1 - Kohl, Anka A1 - Haufe, Manuela A1 - Werner, Jan T1 - Use of Fourier transform infrared spectroscopy to characterize nitric acid oxidation of polyethylene grades N2 - Resistance to oxidative degradation by nitric acid has been selected for a comparison of polyethylene grades in a European standard on suitability proof for alternative plastic resins used for packagings and intermediate bulk containers (IBCs) for the transport of dangerous goods. Measurements of the infrared (IR) absorption spectra of microtome slices cut from the walls of jerricans, which were pre-stored with 55% nitric acid for 21 and 42 days at 40°C, showed changes in the structure of the polyethylene. The penetration depths of 55% nitric acid into the polyethylene grades are, in principle, suitable for evaluating the resistance to oxidative degradation of polyethylene grades after pre-storage of the packagings for 21 days. After this period the packaging wall is not fully penetrated. The intensities of the IR bands at 1565 cm-1 (-NO2), 1630 cm-1 (-C=C) and 1654 cm-1 (-O-NO2) increased with the treatment time with 55% nitric acid as a result of oxidative damage by the nitric acid. The high increase in absorbance of the -C=C band in the region 1630 - 1690 cm-1 is attributable to paraffinic chain cracks. The absorbance of the -O-NO2 band, formed as result of the nitration process was still low at a test temperature of 40°C. T2 - NACE International Corrosion Conference 2013 CY - Orlando, FL, USA DA - 17.03.2013 KW - Polyethylenformstoffe KW - Beständigkeit gegen oxidativen Abbau KW - Salpetersäure KW - Eindringtiefen KW - FTIR KW - Verpackungen zum Transport von Gefahrgütern PY - 2013 SN - 978-1-627-48145-8 SP - 1 EP - 11 (Paper No. 2070) PB - Curran CY - Red Hook, NY AN - OPUS4-27981 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Geißler, Heinz A1 - Peuker, Christel A1 - Brzezinka, Klaus-Werner A1 - Gaber, Martin A1 - Kohl, Anka T1 - OD bands in the IR spectra of a deuterated soda-lime-silica glass PY - 2001 SN - 0946-7475 VL - 74 IS - 7 SP - 210 EP - 214 PB - Verl. d. Dt. Glastechn. Ges. CY - Offenbach AN - OPUS4-1146 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Geißler, Heinz A1 - Peuker, Christel A1 - Brzezinka, Klaus-Werner A1 - Kohl, Anka A1 - Pilz, Walter T1 - OH- und H2O-Schwingungsbanden in den IR- und Raman-Spektren von Gläsern T2 - 74. Glastechnische Tagung CY - Ulm, Deutschland DA - 2000-05-29 KW - Raman-Spektren KW - IR-Spektren PY - 2000 SP - 164 EP - 167 PB - DGG, Dt. Glastechn. Ges. CY - Frankfurt/M. AN - OPUS4-889 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rabin, Ira A1 - Kohl, Anka A1 - Bicchieri, M. A1 - Sodo, A. A1 - Piantanida, G. T1 - New results in Dead Sea Scrolls non-destructive characterisation. Evidence of different parchment manufacture in the fragments fromReed collection N2 - This work presents the non-destructive spectroscopic characterisation of original Dead Sea Scrolls (DSS)parchment fragments from Ronald Reed collection. The fragments are of paramount importance becausethey have never been subjected to any treatment of preservation and restoration, this allows to investi-gate the manufacturing method of real original Jewish parchments. The manufacture of “sacred” Jewishparchments, in fact, is traditionally supposed to use a superficial tannin treatment. To study the DSS frag-ments, it was necessary both to analyse mock-up samples, especially manufactured in order to reproduceancient Oriental Jewish ritual parchments, and to compare the results with those obtained in the analysisof modern and ancient Western Jewish ritual parchments, in order to test the effectiveness of the selectedspectroscopic techniques. Traditionally, the main difference between Oriental and Western traditionalparchment preparation consisted in the dehairing method: enzymatic for Oriental and lime-based forWestern. Moreover, a finishing treatment with tannin was supposed to be applied on ritual Jewish parch-ments. The need of reference samples derives from the knowledge that each parchment preparation,treatment and degradation can induce structural modifications that affect the spectral features. FourierTransform Infrared Spectroscopy by Attenuated Total Reflection (ATR-FTIR), FT-Raman and m-Ramanwere used in this study. The experimental results allowed us to recognise, with different sensitivity, thepresence of tannin by using m-Raman and IR spectroscopies and to prove that not all the archaeologicalsamples were manufactured in the same way with vegetal extracts. Many salts (tschermigite, dolomite,calcite, gypsum and iron carbonate) were found on the surface of DSS fragments. They can derive fromthe degradation processes and storage environment before the discovery or from the manufacture. More-over, the different sensitivities and instrumental characteristics of the used techniques permitted us toestablish an analytical protocol, useful for further studies of similar materials. KW - ATR-FTIR KW - Tannins KW - Dead Sea Scrolls KW - Raman KW - FT-Raman PY - 2018 DO - https://doi.org/10.1016/j.culher.2018.01.014 VL - 32 SP - 22 EP - 29 PB - Elsevier Masson SAS AN - OPUS4-49533 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Aristia, Gabriela A1 - Bäßler, Ralph A1 - Nofz, Marianne A1 - Sojref, Regine A1 - Kohl, Anka T1 - Short-term exposure tests of ɣ-Al2O3 Sol-gel coating on X20Cr13 in artificial geothermal waters with different pH N2 - The suitability of an Al2O3 coating for corrosion protection on X20Cr13 was evaluated in various artificial geothermal brines, focusing on the influence of different pH (4, 6 and 8) and their chemical compositions on the coating properties. All experiments were performed in the laboratory using autoclaves at 150 ◦C and 1 MPa in deaerated condition for 1 and 7 days. Results showed that the pH of geothermal waters is the most detrimental factor in the transformation of ɣ-Al2O3 and its protective abilities. Delaminations were found in the Coating exposed to geothermal brines with pH 4. FTIR spectra indicated a transformation of ɣ-Al2O3 to boehmite AlOOH after exposure to pH 4 and 6, and bayerite Al(OH)3 was formed after exposure to pH 8. Different Crystal structures of the hydrated Al2O3 also contribute to the stability of the coatings, observed by the SEM- EDX of the surface and cross-section of coatings. This study indicated that ɣ-Al2O3 sol-gel coating presents a promising aspect of corrosion protection in geothermal environment with a neutral pH. KW - Al2O3 KW - Corrosion KW - Coating KW - Martensitic steel PY - 2021 DO - https://doi.org/10.1016/j.geothermics.2021.102193 SN - 0375-6505 VL - 96 SP - 102193 PB - Elsevier Ltd. CY - Amsterdam AN - OPUS4-52931 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Torge, Manfred A1 - Sabel, Martin A1 - Feldmann, Ines A1 - Kohl, Anka T1 - Naturwissenschaftliche Untersuchungen im Rahmen des Projektes 'Konservierung mittelalterlicher Glasmalerei im Kontext spezieller materieller und umweltbedingter Gegebenheiten' N2 - Nachsicherung geschädigter Zaponlack-Wachs-Sicherungen an den um 1410/20 entstandenen Glasmalereien des Helenafensters nord VIII am Erfurter Dom - Untersuchungen zu Schadensursachen, Schadensphänomenen, Methoden der Nachbehandlung und des Monitorings KW - Glasmalerei KW - Restaurierung KW - Zaponlack PY - 2011 SN - 978-3-8167-8470-8 VL - D 1012 SP - 36 EP - 75 PB - Fraunhofer IRB Verl. CY - Stuttgart AN - OPUS4-23631 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rabin, Ira A1 - Schütz, R. A1 - Kohl, Anka A1 - Wolff, Timo A1 - Tagle, R. A1 - Pentzien, Simone A1 - Hahn, Oliver A1 - Emmel, S. T1 - Identification and classification of historical writing inks in spectroscopy: a methodological overview N2 - The identification of the type of ink should be among the primary goals of manuscript description. Several techniques of instrumental analysis are available, and new tools have been appearing on the market, the main development having been to more portability and user friendliness. In this article, we would like to give an overview of several existing methods and of their respective advantages and the results (on the example of a Coptic manuscript) that can be obtained with their help. KW - Archaeometry KW - Non-destructive testing KW - Spectroscopy KW - Manuscript studies PY - 2012 SN - 2078-3841 VL - 3 SP - 26 EP - 30 PB - ESF CY - Strasbourg AN - OPUS4-26940 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -