TY - CONF A1 - Koclega, D. A1 - Radziszewska, A. A1 - Kranzmann, Axel A1 - Huebner, J. A1 - Kac, S. T1 - High temperature corrosion resistance of Inconel 686 coatings in aggresive environments N2 - The work presents the microstructure, chemical composition and mechanical properties of Inconel 686 coatings after high - temperature corrosion in environment of aggressive gases. To produce the Ni - base weld overlays the QS Nd:YAG laser beam was used. The substrates were 13Mo4-5 boilers plate steel. Ni - base alloys characterize the excellent high temperature corrosion resistance, good strength and good ability to work in aggressive environments. Applied overlays had a proper combination of the metal substrate in particular small amount of Fe. This could be achieved by the reduction of the melting of the substrate and its dissolution into the overlays. The microstructure, chemical composition of the obtained overlays were investigated by means of a light microscope, a scanning electron microscope (SEM) equipped with the EDS detector. The overlays had cellular-dendritic structure. The variations of the chemical composition (especially Mo, Ni and W ) in the interdendritic and dendritic regions were observed. The interdendritic regions were enriched during solidifications in Mo and W and had lower content of Ni. T2 - EUROCORR 2017 CY - Prague, Czech Republic DA - 03.09.2017 KW - Inconel 686 KW - Corrosion resistance KW - Laser cladding PY - 2017 AN - OPUS4-44197 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Koclega, D. A1 - Radziszewska, A. A1 - Kranzmann, Axel A1 - Dymek, S. A1 - KĄc, S. T1 - The microstructure of weld overlay Ni - base alloy deposited on carbon steel by laser QS-Nd:YAG N2 - Ni- base alloys are used as a one of the most important coating material and can be applied in a different environments and elements of devices having various applications. To protect the surface of the material from aggressive gases at high temperature, there are use different kinds of the Ni- base alloys. One of such alloy is Ni-Cr-Mo-W called commercial Inconel 686. This alloy based on NiCr22Mo9Nb (Inconel 625), in which content of molybdenum increased and niobium was replaced with the addition of tungsten, in order to counteract the strong segregation in the microstructure, which results in homogeneity of the chemical composition of the structure. Inconel 686 is also characterized by greater resistance to high temperature corrosion and heat resistance than Inconel 625. The Inconel 686 alloy was deposited on 13CrMo4-5 steel by laser QS - Nd:YAG. In the poster the microstructure (SEM) and chemical composition (EDS) of obtained weld overlays were investigated. T2 - EUROMAT 2017 CY - Thessaloniki, Greece DA - 17.09.2017 KW - Nickel based alloy KW - Laser cludding KW - High temperature corrosion resistance PY - 2017 AN - OPUS4-44195 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -