TY - JOUR A1 - Klein, Ulrich A1 - Zunkel, Astrid A1 - Eberle, Arno T1 - Breakdown of heat exchangers due to erosion corrosion and fretting caused by inappropriate operating conditions N2 - Damage analyses on two heat exchanger units showed that in both cases inappropriate flow conditions of media caused very different failure mechanisms that resulted in irreparable damage. The first incident was the breakdown of an unalloyed steel condenser, which operated in a coal-fired power plant. A considerably high number of tubes successively leaked. Metallography identified lines of segregation in the microstructure of the tube walls, thus, giving evidence that both uniform corrosion and erosion corrosion caused by low-pressure wet steam were the root cause. The second incident was the breakdown of a recuperator made from chromium–nickel steel due to mechanical damage to tubes and baffle. This unit operated as part of a pilot plant to regain heat from the drying process of sewage sludge. It turned out that soiled vapour caused clogging of the cross-sectional area and therefore accelerating the flow velocity of the vapour. This inappropriate operating condition caused the tubes to oscillate so severely that they even banged together. Abrasive wear especially at the intersection through the holes of the baffle damaged the tubes and the whole unit irreparably. KW - Corrosion KW - Condenser KW - Recuperator KW - Soiled media KW - Leakage of tubes PY - 2014 DO - https://doi.org/10.1016/j.engfailanal.2014.03.019 SN - 1350-6307 SN - 1873-1961 VL - 43 IS - Special Issue 'A Tribute to Prof. A. Martens' SP - 271 EP - 280 PB - Elsevier Science Publ. CY - Oxford AN - OPUS4-31597 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klein, Ulrich T1 - Korrosion an Rohren aus ferritischem Stahl 1.4521 N2 - An Trinkwasserrohren aus ferritischem Stahl (1.4521) sind bei einigen größeren Bauvorhaben massive Korrosionsschäden aufgetreten. Die Leckagen treten ausschließlich durch Spaltkorrosion in Pressverbindungen auf, wo konstruktionsbedingt ein mit Wasser gefüllter Spalt zwischen der Rohr-Außenseite und dem Pressfitting gebildet wird. Im Vortrag werden die gewonnenen Erkenntnisse aus verschiedenen Schadensfällen der jüngeren Vergangenheit vorgestellt. T2 - GfKORR e.V. Arbeitskreis Schadensanalyse CY - Berlin, Germany DA - 09.03.2024 KW - Spaltkorrosion KW - Chromstahl KW - Trinkwasser PY - 2024 AN - OPUS4-60098 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klein, Ulrich T1 - Trinkwasser-Hauptleitungen aus Gusseisen N2 - Infrastruktur aus der industriellen Gründerzeit, im Einsatz bis heute; Schadensanalyse zu verschiedenen Rohrbrüchen. T2 - Sachverständigen-Workshop SHK-Innung Berlin CY - BAM Berlin, Germany DA - 30.05.2017 KW - Grauguss KW - Spongiose KW - Bruchversagen PY - 2017 AN - OPUS4-40500 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klein, Ulrich T1 - Trinkwasser-Hauptleitungen aus Gusseisen N2 - Infrastruktur aus der industriellen Gründerzeit, im Einsatz bis heute T2 - GfKorr Arbeitskreissitzung Schadensuntersuchung 2016 CY - Frankfurt a.M., Germany DA - 19.04.2016 KW - Trinkwasser-Hauptleitungen KW - Gusseisen KW - Sandguss KW - Lamellengraphit KW - Korrosion KW - Spongiose KW - Bruchversagen PY - 2016 AN - OPUS4-37609 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klein, Ulrich T1 - Schäden von Verbindungen an Edelstahlrohren N2 - Spaltkorrosion und Spannungsrisskorrosion als Ursache für das Versagen von Rohrleitungen aus Edelstahl T2 - GfKorr Arbeitskreissitzung Schadensuntersuchung 2015 CY - Frankfurt a.M., Germany DA - 26.05.2015 KW - Pressverbindung KW - Spaltkorrosion KW - Spannungsrisskrorsion KW - Trinkwasserinstallation KW - Feuerlöschanlage PY - 2015 AN - OPUS4-37611 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erning, Johann Wilhelm A1 - Klein, Ulrich T1 - Korrosion von kupfergelöteten Plattenwärmeübertragern - die Folgen T2 - 29. VDI-Jahrestagung "Schadensanalyse, Korrosionsschäden in der Industrie" CY - Würzburg, Deutschland DA - 2003-10-16 KW - Plattenwärmeübertrager KW - Schadensuntersuchung KW - Kupfer PY - 2003 SP - 1(?) EP - 11(?) AN - OPUS4-2642 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Klein, Ulrich A1 - Vollmann, W. A1 - Abatti, P. J. T1 - Contact potential differences measurement: Short history and experimental setup for classroom demonstration N2 - Methods for the measurement of contact potential differences (CPDs) are discussed from a historical point of view. In addition, a simple experimental setup using common laboratory equipment is presented. Experimental results show, for instance, that the measured CPDs between platinum and nickel can be very close to those obtained using sophisticated equipment. Moreover, it is demonstrated that the implemented method, though very simple, is suitable for surface mapping. KW - Contact potential differences (CPDs) KW - Measurement KW - Work function PY - 2003 DO - https://doi.org/10.1109/TE.2003.813896 SN - 0018-9359 SN - 1557-9638 VL - 46 IS - 3 SP - 338 EP - 344 PB - Institute of Electrical and Electronics Engineers CY - New York, NY AN - OPUS4-3705 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Erning, Johann Wilhelm A1 - Zunkel, Astrid A1 - Klein, Ulrich T1 - Spannungsrisskorrosion und Qualitätssicherung an Messinglegierungen PY - 2007 SN - 0026-0746 VL - 61 IS - 11 SP - 548 EP - 552 PB - Giesel Verlag GmbH CY - Isernhagen AN - OPUS4-16152 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erning, Johann Wilhelm A1 - Zunkel, Astrid A1 - Klein, Ulrich T1 - Spannungsrisskorrosion und Qualitätssicherung an Messinglegierungen T2 - Hochschul-Kupfersymposium CY - Berlin, Germany DA - 2007-11-06 PY - 2007 AN - OPUS4-16113 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Erning, Johann Wilhelm A1 - Zunkel, Astrid A1 - Klein, Ulrich T1 - Untersuchungen zu Prüfvorschriften zur Spannungsrisskorrosion an Messinglegierungen T2 - VDI-Jahrestagung Schadensanalyse CY - Würzburg, Germany DA - 2007-09-27 PY - 2007 AN - OPUS4-16114 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Erning, Johann Wilhelm A1 - Zunkel, Astrid A1 - Klein, Ulrich T1 - Untersuchungen zu Prüfvorschriften zur Spannungsrisskorrosion an Messinglegierungen T2 - 33. VDI-Jahrestagung Schadensanalyse "Produktverbesserung durch Schadensanalyse" CY - Würzburg, Deutschland DA - 2007-09-27 PY - 2007 SN - 978-3-18-091985-0 SN - 0083-5560 IS - 1985 (CD-ROM) SP - 151 EP - 163 PB - VDI-Verl. CY - Düsseldorf AN - OPUS4-16197 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gerrits, Ruben A1 - Stepec, Biwen An A1 - Bäßler, Ralph A1 - Becker, Roland A1 - Dimper, Matthias A1 - Feldmann, Ines A1 - Goff, Kira L. A1 - Günster, Jens A1 - Hofmann, Andrea A1 - Hesse, René A1 - Kirstein, Sarah A1 - Klein, Ulrich A1 - Mauch, Tatjana A1 - Neumann-Schaal, Meina A1 - Özcan Sandikcioglu, Özlem A1 - Taylor, Nicole M. A1 - Schumacher, Julia A1 - Shen, Yin A1 - Strehlau, Heike A1 - Weise, Matthias A1 - Wolf, Jacqueline A1 - Yurkov, Andrey A1 - Gieg, Lisa M. A1 - Gorbushina, Anna T1 - A 30-year-old diesel tank: Fungal-dominated biofilms cause local corrosion of galvanised steel N2 - The increased use of biodiesel is expected to lead to more microbial corrosion, fouling and fuel degradation issues. In this context, we have analysed the metal, fuel and microbiology of a fouled diesel tank which had been in service for over 30 years. The fuel itself, a B7 biodiesel blend, was not degraded, and—although no free water phase was visible—contained a water content of ~60 ppm. The microbial community was dominated by the fungus Amorphotheca resinae, which formed thick, patchy biofilms on the tank bottom and walls. The tank sheets, composed of galvanised carbon steel, were locally corroded underneath the biofilms, up to a depth of a third of the sheet thickness. On the biofilm-free surfaces, Zn coatings could still be observed. Taken together, A. resinae was shown to thrive in these water-poor conditions, likely enhancing corrosion through the removal of the protective Zn coatings. KW - Fungal biofilms KW - Biodiesel degradation mechanisms PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-655014 DO - https://doi.org/10.1038/s41529-025-00731-2 SN - 2397-2106 VL - 10 IS - 1 SP - 1 EP - 14 PB - Springer Science and Business Media LLC AN - OPUS4-65501 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klein, Ulrich T1 - Messing unter Druck N2 - Schäden an verschiedenen Rohrverbindungs-Systemen im Sanitärbereich mit Bauteilen aus Messing. T2 - GfKORR Arbeitskreis Schadensanalyse CY - Frankfurt a.M., Germany DA - 17.10.2019 KW - Pressverbindung KW - Spannungsrisskorrosion KW - Messing KW - Schadensanalyse PY - 2019 AN - OPUS4-49335 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Tiebe, Carlo A1 - Zunkel, Astrid A1 - Klein, Ulrich A1 - Schlischka, Jörg A1 - Klinger, Christian T1 - Materialuntersuchungen zur Schadensanalyse an einem explodierten Umlaufkühler N2 - Ein Durchlaufkühler ist im Betrieb explodiert. Die zerborstenen Gehäuseteile aus Kunststoff führten zu einem Austreten der Kühlflüssigkeit am Betriebsort sowie zu einem Personenschaden mit Knalltrauma. Bei Funktionsprüfungen am beschädigten Gerät traten unerwartet, aber reproduzierbar Knalleffekte auf der Kupfer-Kühlschlange auf. Ein möglicher Mechanismus konnte im Labor durch Synthese von Kupferazid auf Kupferproben und Auslösung vergleichbarer Knalleffekte nachgestellt werden. Damit ist die Plausibilität des beschriebenen Schadensereignisses mit diesem oder einem ähnlich reagierenden Stoff belegt. Ein eindeutiger Nachweis darüber, dass beim aufgetretenen Schadensfall dieselbe chemische Reaktion stattgefunden hat ist nicht möglich, da die Belag-Überreste aus dem explodierten Kühlgerät für eine Analyse nicht mehr in ausreichender Menge verfügbar waren. T2 - Erfahrungsaustausch für Sachverständige in der Anlagenüberwachung der Industrie (ESA 2021) CY - Online meeting DA - 20.04.2021 KW - Umlaufkühler KW - Schadensanalyse KW - Materialuntersuchungen KW - Gutachten KW - Kupferazid PY - 2021 AN - OPUS4-52484 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Tiebe, Carlo A1 - Zunkel, Astrid A1 - Klein, Ulrich A1 - Schlischka, Jörg A1 - Klinger, Christian T1 - Materialuntersuchungen an einem explodierten Umlaufkühler N2 - Ein Umlaufkühler ist im Betrieb explodiert. Splitter des zerborstenen Gehäuses aus Kunststoff wurden mit dem Kühlwasser in die Umgebung geschleudert, am Betriebsort entstand Personenschaden. Bei Funktionsprüfungen am beschädigten Gerät traten unerwartet - aber reproduzierbar - Knalleffekte bei Berührung der Außenoberfläche der Kupfer-Kühlschlange auf. Ein möglicher Mechanismus konnte im Labor durch Synthese von Kupferazid auf Kupferproben und Auslösung vergleichbarer Knalleffekte nachgestellt werden. Damit ist die Plausibilität des beschriebenen Schadensereignisses mit diesem oder einem ähnlich reagierenden Stoff belegt. Ein eindeutiger Nachweis darüber, dass bei dem aufgetretenen Schadensfall dieselbe chemische Reaktion stattgefunden hat, war nicht möglich, da die Belag-Überreste aus dem explodierten Kühlgerät für eine Analyse nicht mehr in ausreichender Menge verfügbar gewesen sind. KW - Kupferazid KW - Umlaufkühler KW - Explosion KW - Gutachten KW - Schadensanalyse KW - Materialuntersuchung PY - 2022 SN - 2191-0073 VL - 12 IS - 7/8 SP - 15 EP - 21 PB - VDI Fachmedien CY - Düsseldorf AN - OPUS4-55570 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -