TY - JOUR A1 - Kjaervik, Marit A1 - Müller, Anja A1 - Dietrich, P. A1 - Thissen, A. A1 - Bahr, S. A1 - Ritter, B. A1 - Kemnitz, E. A1 - Unger, Wolfgang T1 - Detection of suspended nanoparticles with near-ambient pressure x-ray photoelectron spectroscopy N2 - Two systems of suspended nanoparticles have been studied with near-ambient pressure x-ray photoelectron spectroscopy: silver nanoparticles in water and strontium fluoride—calcium fluoride core-shell nanoparticles in ethylene glycol. The corresponding dry samples were measured under ultra high vacuum for comparison. The results obtained under near-ambient pressure were overall comparable to those obtained under ultra high vacuum, although measuring silver nanoparticles in water requires a high pass energy and a long acquisition time. A shift towards higher binding energies was found for the silver nanoparticles in aqueous Suspension compared to the corresponding dry sample, which can be assigned to a change of surface potential at the water-nanoparticle interface. The shell-thickness of the core-shell nanoparticles was estimated based on simulated spectra from the National Institute of Standards and Technology database for simulation of electron spectra for surface analysis. With the instrumental set-up presented in this paper, nanoparticle suspensions in a suitable Container can be directly inserted into the analysis chamber and measured without prior sample preparation. KW - Nanoparticles KW - Suspensions KW - Core-shell nanoparticles KW - NAP-XPS PY - 2017 DO - https://doi.org/10.1088/1361-648X/aa8b9d SN - 1361-648X SN - 0953-8984 N1 - Geburtsname von Müller, Anja: Hermanns, A. - Birth name of Müller, Anja: Hermanns, A. VL - 29 IS - 47 SP - 474002, 1 EP - 474002, 9 PB - IOP Publishing CY - UK AN - OPUS4-42951 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Guo, Y. A1 - Lippitz, Andreas A1 - Saftien, P. A1 - Unger, Wolfgang A1 - Kemnitz, E. T1 - Tuning the surface properties of novel ternary iron(III) fluoride-based catalysts using the template effect of the matrix N2 - Sol–gel prepared ternary FeF3–MgF2 materials have become promising heterogeneous catalysts due to their porosity and surface Lewis/Brønsted acidity (bi-acidity). Despite the good catalytic performance, nanoscopic characterisations of this type of material are still missing and the key factors controlling the surface properties have not yet been identified, impeding both a better understanding and further development of ternary fluoride catalysts. In this study, we characterised the interaction between the bi-acidic component (FeF3) and the matrix (MgF2) on the nano-scale. For the first time, the formation pathway of FeF3–MgF2 was profiled and the template effect of MgF2 during the synthesis process was discovered. Based on these new insights two novel materials, FeF3–CaF2 and FeF3–SrF2, were established, revealing that with decreasing the atomic numbers (from Sr to Mg), the ternary fluorides exhibited increasing surface acidity and surface area but decreasing pore size. These systematic changes gave rise to a panel of catalysts with tuneable surface and bulk properties either by changing the matrix alkaline earth metal fluoride or by adjusting their ratios to Fe or both. The template effect of the alkaline earth metal fluoride matrix was identified as the most probable key factor determining the surface properties and further influencing the catalytic performance in ternary fluoride based catalysts, and paves the way to targeted design of next-generation catalysts with tunable properties. KW - Catalysis KW - Surface analysis KW - XPS PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-327410 DO - https://doi.org/10.1039/c4dt03229b SN - 1477-9226 SN - 1477-9234 SN - 1364-5447 VL - 44 IS - 11 SP - 5076 EP - 5085 PB - RSC CY - Cambridge AN - OPUS4-32741 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - König, R. A1 - Scholz, G. A1 - Scheurell, K. A1 - Heidemann, D. A1 - Buchem, I. A1 - Unger, Wolfgang A1 - Kemnitz, E. T1 - Spectroscopic characterization of crystalline AIF3 phases N2 - A comprehensive spectroscopic characterization of all known crystalline AlF3 phases (α-, β-, η-, κ-, θ-AlF3) is presented for the first time in this study. Beside their X-ray diffraction powder patterns, which were already published in the literature, 27Al and 19F MAS NMR, FT IR and XPS spectroscopic techniques were applied for all phases in a consistent manner. For all phases prepared the utilization of 27Al satellite transition (SATRAS) NMR allowed to determine the quadrupolar parameters of the aluminium sites including their distributions. In addition, η-AlF3 was isolated with high phase purity and characterized following a new preparation path different from those known so far in the literature. KW - Crystalline aluminium fluorides KW - Solid state NMR KW - FT IR KW - XPS PY - 2010 DO - https://doi.org/10.1016/j.jfluchem.2009.10.015 SN - 0022-1139 SN - 1873-3328 VL - 131 IS - 1 SP - 91 EP - 97 PB - Elsevier CY - Amsterdam AN - OPUS4-20991 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gross, Thomas A1 - Treu, Dieter A1 - Ünveren, E. A1 - Kemnitz, G. A1 - Unger, Wolfgang T1 - Characterization of Cr(III) compounds of O, OH, F and Cl by XPS N2 - Cr2O3, CrCl3, α-CrF3, CrF3·3H20 and Cr(OH)3 were investigated by x-ray photoelectron (XPS) and x-ray excited Auger electron spectroscopy (XAES) using a latest generation XPS spectrometer. Non-conductive powders are analyzed with ultimate energy resolution. Multiplet splitting features and/or satellite emission were observed in the Cr 2p and Cr 3s spectra. Cr(III) compounds are of interest in many applications as for example in corrosion and catalysis. Chromia and chromium-III-fluoride activated by reaction with fluoroalkanes are very promising industrial catalysts. It is the aim of this selection of spectral reference data to enable deeper insight in the formation of catalytically active fluorinated chromia phases by using XPS analysis. KW - Chromium(III) compound KW - Cr2O3 KW - CrCl3 KW - Cr(OH)3 KW - CrF3 KW - CrF3.3H2O KW - XPS KW - XAES KW - Multiplet splitting KW - Satellite KW - Powder chromium(III) compounds PY - 2008 DO - https://doi.org/10.1116/11.20080801 SN - 1055-5269 SN - 1520-8575 VL - 15 SP - 77 EP - 123 PB - AIP CY - Woodbury, NY AN - OPUS4-23387 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ünveren, Ercan A1 - Kemnitz, E. A1 - Hutton, S. A1 - Lippitz, Andreas A1 - Unger, Wolfgang T1 - Analysis of highly resolved x-ray photoelectron Cr 2p spectra obtained with a Cr2O3 powder sample prepared with adhesive tape KW - High-resolution XPS KW - Cr2O3 powder KW - Multiplet splitting PY - 2004 SN - 0142-2421 SN - 1096-9918 VL - 36 SP - 92 EP - 95 PB - Wiley CY - Chichester AN - OPUS4-3427 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ünveren, Ercan A1 - Kemnitz, E. A1 - Oran, Umut A1 - Unger, Wolfgang T1 - Static TOF-SIMS Surface Analysis of a CCl2F2 Activated Chromia Catalyst Used for a Cl/F Exchange Reaction N2 - Static TOF-SIMS results strongly underpin earlier conclusions from ESCA, XANES, and tracer studies that the accumulation of fluorine and chlorine at the surface of chromia by a heterogeneous reaction with a chlorofluorocarbon compound results in the formation of mixed chromium oxide halide species and not in the nucleation of CrCl3 and/or CrF3 phases. KW - Oberflächenanalytik KW - Katalyse PY - 2004 DO - https://doi.org/10.1021/jp046773h SN - 1520-6106 SN - 1520-5207 SN - 1089-5647 VL - 108 SP - 15454 EP - 15456 PB - Soc. CY - Washington, DC AN - OPUS4-4718 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Böse, Olaf A1 - Unger, Wolfgang A1 - Kemnitz, E. A1 - Schroeder, S. L. M. T1 - Active sites on an oxide catalyst for F/Cl-exchange reactions: X-ray spectroscopy of fluorinated y-Al2O3 N2 - The dismutation of CHClF2 to CHF3 and CHCl3 was used to probe the effect of γ-Al2O3 fluorination on fluorine-against-chlorine (Cl/F) exchange reactions. X-ray photoelectron spectroscopy (XPS), X-ray excited Auger electron spectroscopy (XAES) and X-ray absorption near edge structure (XANES) spectroscopy were employed to probe the modifications at the surface of γ-Al2O3 accompanying the initial stages of fluorination. The results suggest that fluorine uptake by γ-Al2O3 starts initially at the surface of the oxide particles, with the formation of a fluorine species that is characterised by a single bond and a high effective charge q. Catalytic Cl/F-exchange is only observed after accumulation of higher fluorine concentrations, for which insertion of fluorine into the sub-surface region of the oxide crystallites has commenced. Quantitative XPS shows that the fluorination level must exceed approximately 10 atom% of the anions to achieve catalytic activity. The spectroscopic evidence suggests that the formation of aluminium oxofluorides is sufficient to provide catalytic activity. The presence of an AlF3 phase is not a condition for the observation of catalytic activity, even though defect-rich AlF3 is ultimately the endpoint of the fluorination process and is itself a Cl/F exchange catalyst. PY - 2002 DO - https://doi.org/10.1039/b110792e SN - 1463-9076 SN - 1463-9084 VL - 4 IS - 12 SP - 2824 EP - 2832 PB - The Royal Soc. of Chemistry CY - Cambridge AN - OPUS4-6940 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Krishna Murthy, J. A1 - Gross, U. A1 - Rüdiger, St. A1 - Ünveren, Ercan A1 - Unger, Wolfgang A1 - Kemnitz, E. T1 - Synthesis and characterization of chromium(III)-doped magnesium fluoride catalysts N2 - Cr3+-doped MgF2 systems are synthesised by a novel non-aqueous soft chemistry route using different Cr precursors and varying Cr loading. These systems have been characterized by X-ray powder diffraction (XRD), BET surface area, TPD of ammonia, FT-IR pyridine adsorption analysis and X-ray photoelectron spectroscopy, and tested for their catalytic activity in dismutation of CCl2F2 and CF3–CHClF. Catalysts synthesised starting from CrO3 or (CH3CO2)7Cr3(OH)2 showed better catalytic activity than those prepared with CrCl3. FT-IR pyridine adsorption studies reveal that the catalytic activity is highly correlated with the Lewis acid strength. In TPD of NH3 catalysts prepared from CrO3 and (CH3CO2)7Cr3(OH)2, precursors showed a similar behaviour, different from that of catalysts prepared from CrCl3. KW - Lewis acid KW - Heterogeneous catalysis KW - Metal fluoride KW - Doped systems PY - 2005 UR - http://www.sciencedirect.com/science/journal/0926860X DO - https://doi.org/10.1016/j.apcata.2004.12.004 SN - 0947-8396 VL - 282 IS - 1-2 SP - 85 EP - 91 PB - Springer CY - Berlin AN - OPUS4-7442 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ünveren, Ercan A1 - Kemnitz, E. A1 - Lippitz, Andreas A1 - Unger, Wolfgang T1 - Surface Characterization of Chromia for Chlorine/Fluorine Exchange Reactions N2 - The dismutation of CCl2F2 was used to probe the effect of halogenation of chromia by Cl/F exchange reactions to find out the difference between the halogenated inactive and active catalysts. The heterogeneous reactions were performed in a continuous flow Ni reactor and also under simulated reaction conditions in a reactor where after the reaction X-ray photoelectron spectroscopy (XPS) and X-ray excited Auger electron spectroscopy (XAES) analyses are possible without air exposure of the catalyst, i.e., under so-called "in situ" conditions. The Cr(III) 2p XP spectra, which revealed multiplet splitting features and satellite emission, were used for chemical analysis by using a simple evaluation procedure which neglects this inherent complexity. Chemical analysis was also applied by using chemical state plots for Cr 3s in order to cross-check Cr 2p related results. Both ex and in situ XPS show that as soon as Cr2O3 is exposed to CCl2F2 at 390°C fluorination as well as chlorination takes place at the catalyst surface. When the XPS surface composition reaches approximately 4 at. % fluorination and 6 at. % chlorination, maximum catalytic activity was obtained. Application of longer reaction times did not change significantly the obtained surface composition of the activated chromia. The fluorination and chlorination of chromia was further investigated by various HF and HCl treatments. The activated chromia samples and the Cr2O3, Cr(OH)3, CrF2OH, CrF3·H2O, α-CrF3, β-CrF3, and CrCl3 reference samples with well-known chemical structures were also characterized by X-ray absorption near edge structure (XANES), time-of-flight secondary ion mass spectroscopy (TOF-SIMS), pyridine-FTIR, wet chemical (F and Cl) analysis, X-ray powder diffraction (XRD), and surface area (BET) analysis. The results suggest that the formation of chromium oxide chloride fluoride species, e.g., chromium oxide halides, at the surface is sufficient to provide catalytic activity. The presence of any CrF3 and/or CrCl3 phases on the activated chromia samples was not found. PY - 2005 DO - https://doi.org/10.1021/jp045902r SN - 1520-6106 SN - 1520-5207 SN - 1089-5647 VL - 109 IS - 5 SP - 1903 EP - 1913 PB - Soc. CY - Washington, DC AN - OPUS4-10531 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Murthy, J.K. A1 - Gross, U. A1 - Rüdiger, S. A1 - Ünveren, Ercan A1 - Unger, Wolfgang A1 - Kemnitz, E. T1 - Synthesis and characterization of chromium(III)-doped magnesium fluoride catalysts N2 - Cr3+-doped MgF2 systems are synthesised by a novel non-aqueous soft chemistry route using different Cr precursors and varying Cr loading. These systems have been characterized by X-ray powder diffraction (XRD), BET surface area, TPD of ammonia, FT-IR pyridine adsorption analysis and X-ray photoelectron spectroscopy, and tested for their catalytic activity in dismutation of CCl2F2 and CF3–CHClF. Catalysts synthesised starting from CrO3 or (CH3CO2)7Cr3(OH)2 showed better catalytic activity than those prepared with CrCl3. FT-IR pyridine adsorption studies reveal that the catalytic activity is highly correlated with the Lewis acid strength. In TPD of NH3 catalysts prepared from CrO3 and (CH3CO2)7Cr3(OH)2, precursors showed a similar behaviour, different from that of catalysts prepared from CrCl3. KW - Lewis acid KW - Heterogeneous catalysis KW - Metal fluoride KW - Doped systems PY - 2005 SN - 0926-860X SN - 1873-3875 VL - 282 IS - 1-2 SP - 85 EP - 91 PB - Elsevier CY - Amsterdam AN - OPUS4-11953 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -