TY - JOUR A1 - Was, G.S. A1 - Bahn, C.-B. A1 - Busby, J. A1 - Cui, B. A1 - Farkas, D. A1 - Gussev, M. A1 - Rigen He, M. A1 - Hesterberg, J. A1 - Jiao, Z. A1 - Johnson, D. A1 - Kuang, W. A1 - McMurtrey, M. A1 - Robertson, I. A1 - Sinjlawi, A. A1 - Song, M. A1 - Stephenson, K. A1 - Sun, K. A1 - Swaminathan, Srinivasan A1 - Wang, M. A1 - West, E. T1 - How irradiation promotes intergranular stress corrosion crack initiation JF - Progress in Material Science N2 - Irradiation assisted stress corrosion cracking (IASCC) is a form of intergranular stress corrosion cracking that occurs in irradiated austenitic alloys. It requires an irradiated microstructure along with high temperature water and stress. The process is ubiquitous in that it occurs in a wide range of austenitic alloys and water chemistries, but only when the alloy is irradiated. Despite evidence of this degradation mode that dates back to the 1960s, the mechanism by which it occurs has remained elusive. Here, using high resolution electron backscattering detection to analyze local stress-strain states, high resolution transmission electron microscopy to identify grain boundary phases at crack tips, and decoupling the roles of stress and grain boundary oxidation, we are able to unfold the complexities of the phenomenon to reveal the mechanism by which IASCC occurs. The significance of the findings impacts the mechanical integrity of core components of both current and advanced nuclear reactor designs worldwide. KW - Irradiation KW - Stress corrosion cracking KW - Grain boundaries KW - Oxidation KW - Austenitic alloys PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-595748 DO - https://doi.org/10.1016/j.pmatsci.2024.101255 SN - 0079-6425 VL - 143 SP - 1 EP - 15 PB - Elsevier AN - OPUS4-59574 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sun, F. A1 - Wang, C. A1 - Osenberg, M. A1 - Dong, K. A1 - Zhang, S. A1 - Yang, C. A1 - Wang, Y. A1 - Hilger, A. A1 - Zhang, J. A1 - Dong, S. A1 - Markötter, Henning A1 - Manke, I. A1 - Cui, G. T1 - Clarifying the Electro-Chemo-Mechanical Coupling in Li10SnP2S12 based All-Solid-State Batteries JF - Advanced Energy Materials N2 - A fundamental clarification of the electro-chemo-mechanical coupling at the solid–solid electrode|electrolyte interface in all-solid-state batteries (ASSBs) is of crucial significance but has proven challenging. Herein, (synchrotron) X-ray tomography, electrochemical impedance spectroscopy (EIS), time-of-flight secondary-ion mass spectrometry (TOF-SIMS), and finite element analysis (FEA) modeling are jointly used to decouple the electro-chemo-mechanical coupling in Li10SnP2S12-based ASSBs. Non-destructive (synchrotron) X-ray tomography results visually disclose unexpected mechanical deformation of the solid electrolyte and electrode as well as an unanticipated evolving behavior of the (electro)chemically generated interphase. The EIS and TOFSIMS probing results provide additional information that links the interphase/electrode properties to the overall battery performance. The modeling results complete the picture by providing the detailed distribution of the mechanical stress/strain and the potential/ionic flux within the electrolyte. Collectively, these results suggest that 1) the interfacial volume changes induced by the (electro)chemical reactions can trigger the mechanical deformation of the solid electrode and electrolyte; 2) the overall electrochemical process can accelerate the interfacial chemical reactions; 3) the reconfigured interfaces in turn influence the electric potential distribution as well as charge transportation within the SE. These fundamental discoveries that remain unreported until now significantly improve the understanding of the complicated electro-chemo-mechanical couplings in ASSBs. KW - All-solid-state batteries KW - Lithium metal batteries KW - Solid electrolytes KW - Sulfide solid electrolytes KW - Synchrotron X-ray tomography PY - 2022 DO - https://doi.org/10.1002/aenm.202103714 SN - 1614-6832 SP - 2103714 PB - Wiley VHC-Verlag AN - OPUS4-54431 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yao, J. A1 - Zhu, G. A1 - Dong, K. A1 - Osenberg, M. A1 - Hilger, A. A1 - Markötter, Henning A1 - Ju, J. A1 - Sun, F. A1 - Manke, I. A1 - Cui, G. T1 - Progress and Perspective of Controlling Li Dendrites Growth in All-Solid-State Li Metal Batteries via External Physical Fields JF - Advanced Energy and Sustainability Research N2 - Li dendrites penetration through solid electrolytes (SEs) challenges the development of solid-state Li batteries (SSLBs). To date, significant efforts are devoted to understand the mechanistic dynamics of Li dendrites nucleation, growth, and propagation in SEs, and various strategies that aim to alleviate and even inhibit Li dendrite formation have been proposed. Nevertheless, most of these conventional strategies require either additional material processing steps or new materials/layers that eventually increase battery cost and complexity. In contrast, using external fields, such as mechanical force, temperature physical field, electric field, pulse current, and even magnetic field to regulate Li dendrites penetration through SEs, seems to be one of the most cost-effective strategies. This review focuses on the current research progress of utilizing external physical fields in regulating Li dendrites growth in SSLBs. For this purpose, the mechanical properties of Li and SEs, as well as the experimental results that visually track Li penetration dynamics, are reviewed. Finally, the review ends with remaining open questions in future studies of Li dendrites growth and penetration in SEs. It is hoped this review can shed some light on understanding the complex Li dendrite issues in SSLBs and potentially guide their rational design for further development. KW - Li dendrites KW - Li dendrites penetration mechanisms KW - Solid electrolytes KW - Solid-state batteries PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-588331 DO - https://doi.org/10.1002/aesr.202300165 SN - 2699-9412 SP - 1 EP - 44 PB - Wiley-VCH CY - Weinheim AN - OPUS4-58833 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Swaminathan, Srinivasan A1 - Sun, K. A1 - Was, G. S. T1 - Decoupling the roles of grain boundary oxidation and stress in IASCC of neutron-irradiated 304L stainless steel JF - Journal of Nuclear Materials N2 - Irradiation assisted stress corrosion cracking (IASCC) is known to be a combination of applied stress, and a corrosive environment in irradiated materials, but an appropriate understanding of how each of these components affects cracking is not yet clear. In this work, we isolate the role of grain boundary (GB) oxidation in IASCC. For this purpose, solution-annealed 304L stainless steel irradiated in reactor to 5.4 or 69 dpa was studied using a miniaturized four-point bend technique. Two modes of bend tests were conducted; straining in simulated pressurized water reactor primary water (PW) at 320 ◦C in an incremental manner, and pre-oxidation in PW at 320 ◦C without application of stress followed by dynamic straining in purified Ar at the same temperature until crack initiation. Exposure of the 5.4 dpa sample for 210 h in high temperature water initiated cracks in Ar at 60% of the yield stress (0.6YS), whereas the companion sample of the same dose exposed for 1010 h cracked in Ar at 0.5YS. The long-term exposure in water led to GB oxidation that ultimately lowered the crack initiation stress. Dynamic straining in water resulted in larger crack lengths and greater crack depths indicating stress accelerated oxidation and cracking. Dislocation pile-ups at dislocation channel-grain boundary sites provide an amplification of the applied stress to a level consistent with the fracture stress of the grain boundary oxide, providing an explanation for IASCC that occurs at applied stresses well below the irradiated yield stress of the alloy. There was no evidence of cracking upon straining of an unoxidized 69 dpa sample in Ar to well above yield, confirming that the irradiated state is not inherently susceptible to intergranular (IG) cracking and that oxidized GBs are responsible for initiation of IG cracking. KW - Stress corrosion cracking KW - Grain boundary oxidation KW - Stainless steel KW - Crack initiation KW - IASCC PY - 2023 DO - https://doi.org/10.1016/j.jnucmat.2023.154604 SN - 0022-3115 VL - 585 SP - 1 EP - 15 PB - Elsevier B.V. AN - OPUS4-58233 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zhang, X. A1 - Zhang, S. A1 - Lu, J. A1 - Tang, F. A1 - Dong, K. A1 - Yu, Z. A1 - Hilger, A. A1 - Osenberg, M. A1 - Markötter, Henning A1 - Wilde, F. A1 - Zhang, S. A1 - Zhao, J. A1 - Xu, G. A1 - Manke, I. A1 - Sun, F. A1 - Cui, G. T1 - Unveiling the Electro-Chemo-Mechanical Failure Mechanism of Sodium Metal Anodes in Sodium–Oxygen Batteries by Synchrotron X-Ray Computed Tomography JF - Advanced Functional Materials N2 - Rechargeable sodium–oxygen batteries (NaOBs) are receiving extensive research interests because of their advantages such as ultrahigh energy density and cost efficiency. However, the severe failure of Na metal anodes has impeded the commercial development of NaOBs. Herein, combining in situ synchrotron X-ray computed tomography (SXCT) and other complementary characterizations, a novel electro-chemo-mechanical failure mechanism of sodium metal anode in NaOBs is elucidated. It is visually showcased that the Na metal anodes involve a three-stage decay evolution of a porous Na reactive interphase layer (NRIL): from the initially dot-shaped voids evolved into the spindle-shaped voids and the eventually-developed ruptured cracks. The initiation of this three-stage evolution begins with chemical-resting and is exacerbated by further electrochemical cycling. From corrosion science and fracture mechanics, theoretical simulations suggest that the evolution of porous NRIL is driven by the concentrated stress at crack tips. The findings illustrate the importance of preventing electro-chemo-mechanical degradation of Na anodes in practically rechargeable NaOBs. KW - Synchrotron radiation KW - X-ray imaging KW - NaO-battery PY - 2024 DO - https://doi.org/10.1002/adfm.202402253 SN - 1616-301X SP - 1 EP - 12 PB - Wiley VHC-Verlag AN - OPUS4-59820 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Tang, F A1 - Wu, Z A1 - Yang, C A1 - Osenberg, M A1 - Hilger, A A1 - Dong, K A1 - Markötter, Henning A1 - Manke, I A1 - Sun, F A1 - Chen, L A1 - Cui, G T1 - Synchrotron X-ray tomography for rechargeable battery research: Fundamentals, setups and applications JF - Small Methods N2 - Understanding the complicated interplay of the continuously evolving electrode materials in their inherent 3D states during the battery operating condition is of great importance for advancing rechargeable battery research. In this regard, the synchrotron X-ray tomography technique, which enables non-destructive, multi-scale, and 3D imaging of a variety of electrode components before/during/after battery operation, becomes an essential tool to deepen this understanding. The past few years have witnessed an increasingly growing interest in applying this technique in battery research. Hence, it is time to not only summarize the already obtained battery-related Knowledge by using this technique, but also to present a fundamental elucidation of this technique to boost future studies in battery research. To this end, this review firstly introduces the fundamental principles and experimental Setups of the synchrotron X-ray tomography technique. After that, a user guide to ist application in battery research and examples of its applications in Research of various types of batteries are presented. The current review ends with a discussion of the future opportunities of this technique for next-generation rechargeable batteries research. It is expected that this review can enhance the reader’s understanding of the synchrotron X-ray tomography technique and stimulate new ideas and opportunities in battery research. KW - 3D imaging KW - Batteries KW - Synchrotron X-Ray KW - Tomography PY - 2021 DO - https://doi.org/10.1002/smtd.202100557 VL - 5 IS - 9 SP - 2100557 PB - Wiley-VCH AN - OPUS4-53394 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Venugopalan, T. A1 - Yeo, T. L. A1 - Basedau, Frank A1 - Henke, Anna-Sophia A1 - Sun, T. A1 - Grattan, K.T.V. A1 - Habel, Wolfgang T1 - Evaluation and calibration of FBG-based relative humidity sensor designed for structural health monitoring T2 - Proceedings of SPIE 7503 N2 - In this paper, the evaluation and testing of a fibre optic relative humidity sensor specifically designed for structural health monitoring is discussed in detail. The sensor is based on a polymer coated Fibre Bragg Grating (FBG) where with the increase of the moisture level, the polymer coating swells and thus applies strain to the FBG, causing a Bragg wavelength shift. The device is designed so that the temperature effect on the humidity sensor can be compensated by the inclusion of a second un-coated FBG packaged inside the same sensor probe. The sensor thus produced has been tested extensively and calibrated using both a humidity chamber and standard salt solutions. The probe has demonstrated a very good performance for relative humidity measurements. PY - 2009 DO - https://doi.org/10.1117/12.835611 SN - 0277-786X SN - 0038-7355 SN - 0361-0748 VL - 7503 SP - 750310-1 - 750310-5 PB - VDE-Verl. CY - Berlin ; Offenbach AN - OPUS4-20109 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -