TY - JOUR A1 - Kolmangadi, Mohamed Aejaz A1 - Yildirim, Arda A1 - Sentker, K. A1 - Butschies, M. A1 - Bühlmeyer, A. A1 - Huber, P. A1 - Lachat, S. A1 - Schönhals, Andreas T1 - Molecular dynamics and electrical conductivity of Guanidinium based Ionic liquid crystals: Influence of cation headgroup configuration N2 - Molecular mobility and conductivity of four bent shaped tetramethylated guanidinium based ionic liquid crystals (ILCs) with varying head group configuration (cyclic or acyclic) and alkyl chain length is investigated by a combination of broadband dielectric spectroscopy (BDS) and specific heat spectroscopy (SHS). Two dielectrically active processes observed in the plastic crystalline phase at low and high temperatures are denoted as γ and α1 relaxation. The former is assigned to localized fluctuations of methyl groups including nitrogen atoms in the guanidinium head groups. SHS investigations reveal one calorimetrically active process termed as α2 relaxation process. The temperature dependencies of the relaxation rates of α1 and α2 are similar for the cyclic ILC while for the acyclic counterpart they are different. Possible molecular assignments for the α1 and α2 relaxation are discussed in detail. Alongside relaxation processes, a significant conductivity contribution was observed for all ILCs, where the absolute value of DC conductivity increases by 4 orders of magnitude at the transition from the crystalline to the hexagonal columnar phase. The increase is traced to the change in the underlying conduction mechanism from the delocalized electrical conduction in the Cry phase to ionic conduction in the quasi 1D ion columns formed in the hexagonal columnar mesophase. KW - Ionic liquid crystal PY - 2021 DO - https://doi.org/10.1016/j.molliq.2021.115666 VL - 330 SP - 115666 PB - Elsevier B.V. AN - OPUS4-52284 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kinne, R. W. A1 - Gunnella, F. A1 - Kunisch, E. A1 - Heinemann, S. A1 - Nies, B. A1 - Maenz, S. A1 - Horbert, V. A1 - Illerhaus, Bernhard A1 - Huber, R. A1 - Firkowska-Boden, I. A1 - Bossert, J. A1 - Jandt, K. D. A1 - Sachse, A. A1 - Bungartz, M. A1 - Brinkmann, O. T1 - Performance of calcium phosphate cements in the augmentation of sheep vertebrae - An ex vivo study N2 - Oil-based calcium phosphate cement (Paste-CPC) shows not only prolonged shelf life and injection times, but also improved cohesion and reproducibility during application, while retaining the advantages of fast setting, mechanical strength, and biocompatibility. In addition, poly(L-lactideco-glycolide) (PLGA) fiber reinforcement may decrease the risk for local extrusion. Bone defects (diameter 5 mm; depth 15 mm) generated ex vivo in lumbar (L) spines of female Merino sheep (2–4 years) were augmented using: (i) water-based CPC with 10% PLGA fiber reinforcement (L3); (ii) Paste-CPC (L4); or (iii) clinically established polymethylmethacrylate (PMMA) bone cement (L5). Untouched (L1) and empty vertebrae (L2) served as controls. Cement performance was analyzed using micro-computed tomography, histology, and biomechanical testing. Extrusion was comparable for Paste-CPC(-PLGA) and PMMA, but significantly lower for CPC + PLGA. Compressive strength and Young’s modulus were similar for Paste-CPC and PMMA, but significantly higher compared to those for empty defects and/or CPC + PLGA. Expectedly, all experimental groups showed significantly or numerically lower compressive strength and Young’s modulus than those of untouched controls. Ready-to-use Paste-CPC demonstrates a performance similar to that of PMMA, but improved biomechanics compared to those of water-based CPC + PLGA, expanding the therapeutic arsenal for bone defects. O, significantly lower extrusion of CPC + PLGA fibers into adjacent lumbar spongiosa may help to reduce the risk of local extrusion in spinal surgery. KW - Sheep KW - PMMA KW - Calcium phosphate bone cement KW - Oil-based KW - Ready-to-use KW - Water-based KW - Micro-CT KW - Compressive strength KW - Young’s modulus PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-569072 DO - https://doi.org/10.3390/ma14143873 SN - 1996-1944 VL - 14 IS - 14 SP - 1 EP - 12 PB - MDPI CY - Basel AN - OPUS4-56907 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -