TY - JOUR A1 - Lee, Jun-Seob A1 - Radnik, Jörg A1 - Bäßler, Ralph T1 - Passivity of alloy 31 in green-death solution N2 - The passivation behavior of alloy 31 was investigated as a function of passivation potential in a green-death solution at 40 °C. The alloy 31 surface is in a stable passive state during cyclic potentiodynamic polarization. In potentiostatic polarization of alloy 31, passive current density increases with an increase in the passivation potential. Electrochemical impedance spectroscopy (EIS) and Mott–Schottky (M–S) analysis showed that a more defective n-type semiconductive passive film forms as the potential increases. X-ray photoelectron spectroscopy (XPS) revealed that passive film consists of mainly chromium and minor iron and nickel oxides. The increase of the applied potential is considered to be a reason for the change in passive film stability. KW - Passive film KW - Steel KW - Alloy 31 KW - X-ray photoelectron spectroscopy PY - 2018 DO - https://doi.org/10.1002/maco.201709996 SN - 0947-5117 SN - 1521-4176 VL - 69 IS - 9 SP - 1218 EP - 1226 PB - Wiley-VCH CY - Weinheim AN - OPUS4-45938 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lee, Jun-Seob A1 - Bäßler, Ralph T1 - Aging of passive film on UNS N08031 in a Green-Death solution N2 - Aging of passive film formed on UNS N08031 was investigated as a function of passivation time in Green-Death solution at 40°C. The specimen surface was in a stable passive state in the solution. The passive current density increased with an increase in the passivation potential. Electrochemical Impedance Spectroscopy and Mott–Schottky (M–S) analyses revealed that a more defective n-type semiconductive passive film formed as the potential increased while the film became stable as the defects in the film decreased at potential lower than 1.0 VSSE. The increase of the applied potential and the polarisation time are likely reasons for the change in passive film stability. KW - Iron–chromium–nickel alloy KW - Passivity KW - Green-Death solution KW - Flue gas desulphurisation facilities KW - Alloy 31 KW - Semiconductive layer PY - 2018 DO - https://doi.org/10.1080/1478422X.2018.1459077 SN - 1743-2782 SN - 1478-422X VL - 53 IS - 4 SP - 302 EP - 308 PB - Taylor & Francis AN - OPUS4-44923 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -