TY - CONF A1 - Schneider, Joachim T1 - Usage of BOF slag and next generation EAF slag in the cement industry N2 - Increasing amounts of new types of EAFS from the DRP-EAF-route and still significant amounts of BOFS from the DRP-SAF-BOF-route will be produced while BFS will vanish. In two BMBF funded research projects, BAM and FEhS examine the application of slags from future steel production in the cement industry. The project “SlagCEM” investigated the recovery of iron from BOFS while producing a mineral product with good cementitious properties. The reduction of BOFS to recover metallic iron along with the generation of a clinker-like material for the cement industry increases the viscosity of the BOFS. This would require a process at unfeasibly high temperatures of >1.700 °C. Therefore, SlagCEM aimed to modify the BOFS to reduce the viscosity to suitable ranges at lower temperatures of ~1.600 °C. A demonstration trial (20 tons) was carried out and the potential for substitution of OPC was determined. DRI-EOS investigates the utilization of increasing amounts of DRI-based EAFS in the cement industry to compensate the reduced production of GBFS. This requires an adjustment of the slag’s chemical composition and a rapid quenching to create an amorphous structure with latent hydraulic characteristics. The project studies the behavior of the modified slag during the metallurgical process and during solidification, any possibly negative impact on the cementitious or environmental properties as well as the potential to recover metals such as Fe, Cr, Mo and V. The final results of the project “SlagCEM”, finished in 2024, as well as the current state and insights of the project “DRI-EOS”, started in July 2022, shall be presented in this talk. T2 - 9th International Slag Valorisation Symposium CY - Leuven, Belgium DA - 08.04.2025 KW - Steel slags KW - Basic oxygen furnace (BOF) KW - Electric arc furnace (EAF) KW - Cement KW - Slag valorisation PY - 2025 AN - OPUS4-64712 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schneider, Joachim T1 - Production of raw materials for the cement industry based on steel making slags from future hydrogen based steel production routes N2 - Increasing amounts of new types of EAFS from the DRP-EAF-route and still significant amounts of BOFS from the DRP-SAF-BOF-route will be produced while BFS will vanish. In two BMBF funded research projects, BAM and FEhS examine the application of slags from future steel production in the cement industry. The project “SlagCEM” investigated the recovery of iron from BOFS while producing a mineral product with good cementitious properties. The reduction of BOFS to recover metallic iron along with the generation of a clinker-like material for the cement industry increases the viscosity of the BOFS. This would require a process at unfeasibly high temperatures of >1.700 °C. Therefore, SlagCEM aimed to modify the BOFS to reduce the viscosity to suitable ranges at lower temperatures of ~1.600 °C. A demonstration trial (20 tons) was carried out and the potential for substitution of OPC was determined. DRI-EOS investigates the utilization of increasing amounts of DRI-based EAFS in the cement industry to compensate the reduced production of GBFS. This requires an adjustment of the slag’s chemical composition and a rapid quenching to create an amorphous structure with latent hydraulic characteristics. The project studies the behavior of the modified slag during the metallurgical process and during solidification, any possibly negative impact on the cementitious or environmental properties as well as the potential to recover metals such as Fe, Cr, Mo and V. The final results of the project “SlagCEM”, finished in 2024, as well as the current state and insights of the project “DRI-EOS”, started in July 2022, shall be presented in this talk. T2 - Euroslag 2024 CY - Bilbao, Spain DA - 23.10.2024 KW - Slag KW - Steel KW - Cement KW - Electric Arc Furnace (EAF) KW - Basic Oxygen Furnace (BOF) PY - 2024 AN - OPUS4-61839 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -