TY - JOUR A1 - Bruna, F. G. A1 - Prokop, M. A1 - Bystron, T. A1 - Loukrakpam, R. A1 - Melke, J. A1 - Lobo, C. M. S. A1 - Fink, M. A1 - Zhu, M. A1 - Voloshina, E. A1 - Kutter, M. A1 - Hoffmann, H. A1 - Yusenko, Kirill A1 - de Oliveira Guilherme Buzanich, Ana A1 - Röder, B. A1 - Bouzek, K. A1 - Paulus, B. A1 - Roth, C. T1 - Following adsorbed intermediates on a platinum gas diffusion electrode in H3PO3‑containing electrolytes using in situ X‑ray absorption spectroscopy JF - ACS catalysis N2 - One of the challenges of high-temperature polymer electrolyte membrane fuel cells is the poisoning of the Pt catalyst with H3PO4. H3PO4 is imbibed into the routinely used polybenzimidazole-based membranes, which facilitate proton conductivity in the temperature range of 120−200 °C. However, when leached out of the membrane by water produced during operation, H3PO4 adsorbs on the Pt catalyst surface, blocking the active sites and hindering the oxygen reduction reaction (ORR). The reduction of H3PO4 to H3PO3, which occurs at the anode due to a combination of a low potential and the presence of gaseous H2, has been investigated as an additional important contributing factor to the observed poisoning effect. H3PO3 has an affinity toward adsorption on Pt surfaces even greater than that of H2PO4 −. In this work, we investigated the poisoning effect of both H3PO3 and H3PO4 using a half-cell setup with a gas diffusion electrode under ambient conditions. By means of in situ X-ray absorption spectroscopy, it was possible to follow the signature of different species adsorbed on the Pt nanoparticle catalyst (H, O, H2PO4 −, and H3PO3) at different potentials under ORR conditions in various electrolytes (HClO4, H3PO4, and H3PO3). It was found that H3PO3 adsorbs in a pyramidal configuration P(OH)3 through a Pt−P bond. The competition between H3PO4 and H3PO3 adsorption was studied, which should allow for a better understanding of the catalyst poisoning mechanism and thus assist in the development of strategies to mitigate this phenomenon in the future by minimizing H3PO3 generation by, for example, improved catalyst design or adapted operation conditions or changes in the electrolyte composition. KW - H3PO4 life cycle KW - XAS KW - In situ coupling KW - High-temperature fuel cells KW - Δμ XANES KW - H3PO3 PY - 2022 DO - https://doi.org/10.1021/acscatal.2c02630 SN - 2155-5435 VL - 12 IS - 18 SP - 11472 EP - 11484 PB - ACS CY - Washington, DC AN - OPUS4-55815 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Brieger, C. A1 - Melke, J. A1 - van der Bosch, N. A1 - Reinholz, Uwe A1 - Riesemeier, Heinrich A1 - de Oliveira Guilherme Buzanich, Ana A1 - Krishna Kayarkatte, M. A1 - Derr, I. A1 - Schökel, A. A1 - Roth, C. ED - de Oliveira Guilherme Buzanich, Ana T1 - A combined in-situ XAS–DRIFTS study unraveling adsorbate induced changes on Pt nanoparticle structure JF - Journal od Catalysis N2 - The adsorption behavior of Platinum nanoparticles was studied for the as-received catalyst (under inert gas), under hydrogen and CO atmosphere using our newly designed in-situ cell. X-ray Absorption Spectroscopy (XAS) and Diffuse Reflectance Infrared Fourier Transform Spectroscopy (DRIFTS) experiments were performed simultaneously with high data quality. Structural information and the type of adsorbate could be revealed via Extended X-ray Absorption Fine Structure (EXAFS) analysis, Δμ X-ray Absorption Near Edge Structure analysis (Δμ XANES) and in-situ DRIFTS. The as-received catalyst showed sub-surface oxygen and O(n-fold). Under CO atmosphere only CO(atop) was found. Reversible adsorbate induced changes of the Pt nanoparticle structure were derived from changes in the Pt-Pt coordination number and the corresponding bond distance. Under reducing conditions (H2, CO) a significant increase in both values occurred. Temperature dependent desorption of CO revealed a gradual shift from Pt-CO to Pt-O. Reoxidation was clearly assigned to strong metal support interaction from the SiO2 support. KW - X-ray absorption spectroscopy KW - DRIFTS KW - XANES KW - CO adsoprtion KW - Platinum KW - String metal support interaction KW - Silica support KW - Adsorbates KW - Infrared spectroscopy PY - 2016 DO - https://doi.org/10.1016/j.jcat.2016.03.034 SN - 0021-9517 VL - 339 SP - 57 EP - 67 PB - Elsevier AN - OPUS4-38367 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Brieger, C. A1 - Melke, J. A1 - van der Bosch, N. A1 - Reinholz, Uwe A1 - Riesemeier, Heinrich A1 - de Oliveira Guilherme Buzanich, Ana A1 - Krishna Kayarkatte, M. A1 - Schoeckel, A. A1 - Roth, C. T1 - A combined in-situ XAS-DRIFTS study unraveling adsorbate induced changes on the Pt nanoparticle structure JF - Journal of Catalysis N2 - The adsorption behavior of Platinum nanoparticles was studied for the as-received catalyst (under inert gas), under hydrogen and CO atmosphere using our newly designed in-situ cell. X-ray Absorption Spectroscopy (XAS) and Diffuse Reflectance Infrared Fourier Transform Spectroscopy (DRIFTS) experiments were performed simultaneously with high data quality. Structural information and the type of adsorbate could be revealed via Extended X-ray Absorption Fine Structure (EXAFS) analysis, Dl X-ray Absorption Near Edge Structure analysis (Dl XANES) and in-situ DRIFTS. The as-received catalyst showed sub-surface oxygen and O(n-fold). Under CO atmosphere only CO(atop) was found. Reversible adsorbate induced changes of the Pt nanoparticle structure were derived from changes in the PtAPt coordination number and the corresponding bond distance. Under reducing conditions (H2, CO) a significant increase in both values occurred. Temperature dependent desorption of CO revealed a gradual shift from PtACO to PtAO. Reoxidation was clearly assigned to strong metal support interaction from the SiO2 support. KW - X-ray absorption spectroscopy KW - DRIFTS KW - XANES KW - CO adsorption KW - Platinum KW - Strong metal support interaction KW - Silica support KW - Adsorbates KW - Infrared spectroscopy PY - 2016 DO - https://doi.org/10.1016/j.jcat.2016.03.034 IS - 339 SP - 57 EP - 67 PB - Elsevier Inc. CY - Philadelphia, Pennsylvania, USA AN - OPUS4-35815 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -